CN106480582A - A kind of new skirt fabric and preparation method thereof - Google Patents

A kind of new skirt fabric and preparation method thereof Download PDF

Info

Publication number
CN106480582A
CN106480582A CN201610905190.0A CN201610905190A CN106480582A CN 106480582 A CN106480582 A CN 106480582A CN 201610905190 A CN201610905190 A CN 201610905190A CN 106480582 A CN106480582 A CN 106480582A
Authority
CN
China
Prior art keywords
fiber
fabric
banana stem
soaping
degummed ramie
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610905190.0A
Other languages
Chinese (zh)
Inventor
饶琼仙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201610905190.0A priority Critical patent/CN106480582A/en
Publication of CN106480582A publication Critical patent/CN106480582A/en
Pending legal-status Critical Current

Abstract

The invention provides a kind of new skirt fabric and preparation method thereof, cotton fiber and banana stem fiber degummed ramie be first woven into covering yarn, blending is carried out with cocoon fiber again, the blend fibre not only has the pro-skin feature of cocoon fiber, and its moisture permeability is also further enhanced；The present invention using banana stem fiber degummed ramie be that the banana stem of discarded object is recycled, meet the requirement of national recycling economy, reduce the cost of high-grade fabric；The present invention is with banana stem fiber degummed ramie as core, outside is wrapped up with natural high-quality cotton, it is woven into covering yarn, banana stem fiber degummed ramie shaggy shortcoming is not only overcome, but also the moisture permeability of blended yarn weaved fabric is improved, it is a kind of Optimum utilization technique of new type natural fiber.

Description

A kind of new skirt fabric and preparation method thereof
Technical field
The present invention relates to field of textile, especially, is related to a kind of new skirt fabric and preparation method thereof.
Background technology
Banana industry is one of pillar industry of China's tropical agriculture, is that the Important Economic of China's hot-zone increasing peasant income is made Thing.The huge banana stem the like waste of yield is produced after banana is plucked.It is suitable that quantity is can extract out in banana stem Considerable banana fiber, every plant of Banana tree can produce 200-500g banana fiber, and the extractible banana stem fiber of China has 100,000 More than ton.Banana stem fiber have moisture absorption and moisture releasing fast many advantages, such as, have the big application prospect of tool in textile industry.And its His natural plant cellulose fiber is the same, banana fiber main component be cellulose, hemicellulose, lignin, adipocere matter and fruit Glue etc., but content of cellulose will be less than flax, jute, and the content of hemicellulose and lignin is then higher.Due to banana fiber Research is started late, and its extractive technique and degumming tech are immature.In the selection of banana stem fiber degumming tech, can use for reference The Degumming method of the crudefiber crop process of fiber such as flax, jute, hemp, mainly has chemical Degumming and biological degumming method.
Due to hemicellulose and content of lignin high, cellulose crystallity is relatively low, fibre strength is relatively low the features such as, complete The degumming that full reference tradition crudefiber crop degumming tech parameter carries out banana stem fiber is difficult to reach promising result, its degummed ramie Rate is low, and the high energy consumption of production, alkali lye consumption amount are big, pollution is big.
Chinese invention patent CN105821487A discloses a kind of production method of banana stem fiber degummed ramie, improves essence The yield of dry fiber crops, the intensity of degummed ramie can also basically reach the requirement of weaving, but the fiber surface of the flaxen fiber is rougher, such as What is applied to fabric especially in high-grade fabric, still requires study.
Content of the invention
Present invention aim at a kind of new skirt fabric and preparation method thereof is provided, to solve technical problem.
For achieving the above object, the invention provides a kind of new skirt fabric and preparation method thereof.
A kind of new skirt fabric, including the composition of following percentage by weight：
Banana stem fiber degummed ramie 8-15%
Cotton fiber 40-50%
Cocoon fiber surplus.
Preferably, the long number of the keen-witted and capable harl of described banana stem fiber is 200-220Nm, single fiber intensity >=3cN/ dtex.
Preferably, described cotton fiber and banana stem fiber degummed ramie are first woven into covering yarn and reuse, wherein banana Stalk fiber degummed ramie is core, and outside is wrapped up with natural high-quality cotton.
A kind of preparation method of new skirt fabric, it is characterised in that comprise the following steps：
A, with banana stem fiber degummed ramie as core, outside wrapped up with natural high-quality cotton, using Technology of Air Vortex Spinning spin It is made into covering yarn；
B, covering yarn and cocoon fiber are carried out blending it is made into fabric；
C, fabric is carried out bleaching, actual conditions is as follows：Fabric is processed in the bleaching liquid of 50-55 DEG C of temperature 20-25min, then with cold water treatment 8-15min of 25-30 DEG C of temperature；Dry；
D, fabric is dyeed using compregnate method, actual conditions is as follows：Temperature control is padded at 50-55 DEG C, pad rate 70- 80%, the natural plants coloring agent containing 2-8% in treatment fluid is padded, bath raio is 1：（15-25）, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carry out clear water and pad, be put in pond of soaping and 15- processed with 45-50 DEG C of liquid of soaping 20min, bath raio are 1：（50-60）；Described liquid of soaping is reusable；
F, fabric is placed on stenter drying and shaping is carried out, stenter speed is 60-70m/min, temperature is 130-140 DEG C, Shaping time controls in 25-30s.
Preferably, described bleaching liquid includes the composition of following percentage by weight：Hydrogen peroxide 0.1-0.3%, water glass Glass 0.2-0.3%, scouring agent 0.5-1%, balance of water.
Preferably, described liquid of soaping includes the composition of following percentage by weight：Efficient neutral soaping agent consumption is 0.1- 0.2%, balance of water.
The invention has the advantages that：
1st, the blend fibre of the present invention not only has the pro-skin feature of cocoon fiber, and its moisture permeability is also obtained into one The enhancing of step；2nd, the banana stem fiber degummed ramie used in the present invention is to recycle the banana stem of discarded object, meets state The requirement of family's recycling economy, reduces the cost of high-grade fabric；3rd, the present invention with banana stem fiber degummed ramie as core, use by outside Natural high-quality cotton is wrapped up, and is woven into covering yarn, not only overcomes banana stem fiber degummed ramie shaggy scarce Point, but also the moisture permeability of blended yarn weaved fabric is improved, it is a kind of Optimum utilization technique of new type natural fiber.
Specific embodiment
Hereinafter embodiments of the invention are described in detail, but the present invention can be limited according to claim and be covered Multitude of different ways implement.
Embodiment 1
A kind of new skirt fabric, including the composition of following percentage by weight：
Banana stem fiber degummed ramie 10%
Cotton fiber 45%
Cocoon fiber surplus.
The long number of the keen-witted and capable harl of described banana stem fiber is 200-220Nm, single fiber intensity >=3cN/dtex.
A kind of preparation method of new skirt fabric, it is characterised in that comprise the following steps：
A, with banana stem fiber degummed ramie as core, outside wrapped up with natural high-quality cotton, using Technology of Air Vortex Spinning spin It is made into covering yarn；
B, covering yarn and cocoon fiber are carried out blending it is made into fabric；
C, fabric is carried out bleaching, actual conditions is as follows：Fabric is processed in the bleaching liquid of 52 DEG C of temperature 23min, then with cold water treatment 12min of 28 DEG C of temperature；Dry；Described bleaching liquid includes following weight percent The composition of ratio：Hydrogen peroxide 0.2%, waterglass 0.25%, scouring agent 0.7%, balance of water；
D, fabric is dyeed using compregnate method, actual conditions is as follows：Temperature control is padded at 52 DEG C, pad rate 75%, pad Natural plants coloring agent containing 2-8% in treatment fluid, bath raio are 1：20, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carry out clear water and pad, be put in pond of soaping and 18min, bath raio processed with 48 DEG C of liquid of soaping For 1：55；Described liquid of soaping is reusable；Described liquid of soaping includes the composition of following percentage by weight：Efficient neutral soap Lotion consumption is 0.1-0.2%, balance of water；
F, fabric is placed on stenter drying and shaping is carried out, stenter speed is 65m/min, temperature is 135 DEG C, during sizing Between control in 25-30s.
Embodiment 2
A kind of new skirt fabric, including the composition of following percentage by weight：
Banana stem fiber degummed ramie 15%
Cotton fiber 50%
Cocoon fiber surplus.
The long number of the keen-witted and capable harl of described banana stem fiber is 200-220Nm, single fiber intensity >=3cN/dtex.
A kind of preparation method of new skirt fabric, it is characterised in that comprise the following steps：
A, with banana stem fiber degummed ramie as core, outside wrapped up with natural high-quality cotton, using Technology of Air Vortex Spinning spin It is made into covering yarn；
B, covering yarn and cocoon fiber are carried out blending it is made into fabric；
C, fabric is carried out bleaching, actual conditions is as follows：Fabric is processed in the bleaching liquid of 55 DEG C of temperature 20min, then with cold water treatment 8min of 30 DEG C of temperature；Dry；Described bleaching liquid includes following weight percent The composition of ratio：Hydrogen peroxide 0.3%, waterglass 0.2%, scouring agent 1%, balance of water；
D, fabric is dyeed using compregnate method, actual conditions is as follows：Temperature control is padded at 50 DEG C, pad rate 80%, pad Natural plants coloring agent containing 2% in treatment fluid, bath raio are 1：25, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carry out clear water and pad, be put in pond of soaping and 20min, bath raio processed with 45 DEG C of liquid of soaping For 1：50；Described liquid of soaping is reusable；Described liquid of soaping includes the composition of following percentage by weight：Efficient neutral soap Lotion consumption is 0.1-0.2%, balance of water；
F, fabric is placed on stenter drying and shaping is carried out, stenter speed is 60m/min, temperature is 140 DEG C, during sizing Between control in 25-30s.
Embodiment 3
A kind of new skirt fabric, including the composition of following percentage by weight：
Banana stem fiber degummed ramie 8%
Cotton fiber 40%
Cocoon fiber surplus.
The long number of the keen-witted and capable harl of described banana stem fiber is 200-220Nm, single fiber intensity >=3cN/dtex.
A kind of preparation method of new skirt fabric, it is characterised in that comprise the following steps：
A, with banana stem fiber degummed ramie as core, outside wrapped up with natural high-quality cotton, using Technology of Air Vortex Spinning spin It is made into covering yarn；
B, covering yarn and cocoon fiber are carried out blending it is made into fabric；
C, fabric is carried out bleaching, actual conditions is as follows：Fabric is processed in the bleaching liquid of 50 DEG C of temperature 25min, then with cold water treatment 15min of 25 DEG C of temperature；Dry；Described bleaching liquid includes following weight percent The composition of ratio：Hydrogen peroxide 0.1%, waterglass 0.3%, scouring agent 0.5%, balance of water；
D, fabric is dyeed using compregnate method, actual conditions is as follows：Temperature control is padded at 55 DEG C, pad rate 70%, pad Natural plants coloring agent containing 8% in treatment fluid, bath raio are 1：15, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carry out clear water and pad, be put in pond of soaping and 15min, bath raio processed with 50 DEG C of liquid of soaping For 1：60；Described liquid of soaping is reusable；Described liquid of soaping includes the composition of following percentage by weight：Efficient neutral soap Lotion consumption is 0.1-0.2%, balance of water
F, fabric is placed on stenter drying and shaping is carried out, stenter speed is 70m/min, temperature is 130 DEG C, during sizing Between control in 25-30s.
Comparative example 1
Covering yarn in embodiment 1 is replaced with cotton fiber, remaining preparation condition is constant.
Fabric to embodiment 1-3 and comparative example 1 is tested below, obtains following data.
Embodiment 1 Embodiment 2 Embodiment 3 Comparative example 1
Dampness RET RET K/W 7.5 7.5 7.5 8.2
Thermal resistance RCT RCT K/W 0.07 0.07 0.07 0.09
From above detection data, new skirt fabric prepared by the present invention possesses more compared to traditional staple blended yarn weaved fabric Good moisture permeability.
The preferred embodiments of the present invention are the foregoing is only, the present invention is not limited to, for the skill of this area For art personnel, the present invention can have various modifications and variations.All within the spirit and principles in the present invention, made any repair Change, equivalent, improvement etc., should be included within the scope of the present invention.

Claims (6)

1. a kind of new skirt fabric, it is characterised in that including the composition of following percentage by weight：
Banana stem fiber degummed ramie 8-15%
Cotton fiber 40-50%
Cocoon fiber surplus.
2. new skirt fabric as claimed in claim 1, it is characterised in that the keen-witted and capable harl of described banana stem fiber Long number is 200-220Nm, single fiber intensity >=3cN/dtex.
3. new skirt fabric as claimed in claim 1, it is characterised in that described cotton fiber and banana stem fiber keen-witted and capable Fiber crops are first woven into covering yarn and reuse, and wherein banana stem fiber degummed ramie is core, and outside is wrapped with natural high-quality cotton Wrap up in.
4. a kind of preparation method of new skirt fabric, it is characterised in that comprise the following steps：
A, with banana stem fiber degummed ramie as core, outside wrapped up with natural high-quality cotton, using Technology of Air Vortex Spinning spin It is made into covering yarn；
B, covering yarn and cocoon fiber are carried out blending it is made into fabric；
C, fabric is carried out bleaching, actual conditions is as follows：Fabric is processed in the bleaching liquid of 50-55 DEG C of temperature 20-25min, then with cold water treatment 8-15min of 25-30 DEG C of temperature；Dry；
D, fabric is dyeed using compregnate method, actual conditions is as follows：Temperature control is padded at 50-55 DEG C, pad rate 70- 80%, the natural plants coloring agent containing 2-8% in treatment fluid is padded, bath raio is 1：（15-25）, pH value 6.5-6.8；
E, stamp is carried out to fabric, then carry out clear water and pad, be put in pond of soaping and 15- processed with 45-50 DEG C of liquid of soaping 20min, bath raio are 1：（50-60）；Described liquid of soaping is reusable；
F, fabric is placed on stenter drying and shaping is carried out, stenter speed is 60-70m/min, temperature is 130-140 DEG C, Shaping time controls in 25-30s.
5. the preparation method of new skirt fabric as claimed in claim 4, it is characterised in that described bleaching liquid includes The composition of following percentage by weight：Hydrogen peroxide 0.1-0.3%, waterglass 0.2-0.3%, scouring agent 0.5-1%, balance of water.
6. the preparation method of new skirt fabric as claimed in claim 4, it is characterised in that described liquid of soaping includes following The composition of percentage by weight：Efficient neutral soaping agent consumption is 0.1-0.2%, balance of water.
CN201610905190.0A 2016-10-18 2016-10-18 A kind of new skirt fabric and preparation method thereof Pending CN106480582A (en)