CN106479436A - Fibrous composite for internal wall pot body of polishing - Google Patents
Fibrous composite for internal wall pot body of polishing Download PDFInfo
- Publication number
- CN106479436A CN106479436A CN201610730278.3A CN201610730278A CN106479436A CN 106479436 A CN106479436 A CN 106479436A CN 201610730278 A CN201610730278 A CN 201610730278A CN 106479436 A CN106479436 A CN 106479436A
- Authority
- CN
- China
- Prior art keywords
- fibrous composite
- polishing
- parts
- internal wall
- pot body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of fibrous composite for internal wall pot body of polishing, and is related to composite material field, is made up of the raw material of following weight proportion:6 parts of glass fibre, 0.2 part of sodium lignin sulfonate, 3.5 parts of 180 mesh calcium carbonate, 8 parts of 230 mesh calcium carbonate, 12 parts of quartz sand, 0.6 part of palmitic acid.Fibrous composite prepared by the present invention, for the inwall of pot of polishing, the particle surface hardness of the fibrous composite diamond that compares is smaller, but the particle of fibrous composite is formed by the particle agglomeration of multiple material, with irregular corner angle, effect of polishing is good.
Description
Technical field
The present invention relates to composite material field, more particularly to a kind of fibrous composite for internal wall pot body of polishing.
Background technology
Pot requires, after the pot shaping for making, there are much irregular burr according to mould in the middle of manufacturing process,
Traditional processing mode is polished by the way of manual polishing, and inefficiency is time-consuming, and defect ware rate is high, existing
Sanding and polishing is carried out using mill pot machine most, but in emery wheel and iron pan bruting process, can sanding apparatus be adjusted well
Perfect square is polished to laminating pot wall, is the key of pot shaping, but the process is difficult to hold, and leverages pot finished product
Qualification rate, and very big noise and dust can be produced when polishing, environment and the healthy of staff are had necessarily
Harm.
Content of the invention
It is an object of the invention to provide a kind of fibrous composite for internal wall pot body of polishing, to solve above-mentioned technology
Problem.Using the fibrous composite, with air-flow as carrier, the fibrous composite is made with higher speed impacts in pot table
Face, polishes to pot surface, and efficiency high is easily controlled, and enforcement difficulty is little.
The technical problem to be solved is employed the following technical solutions to realize:
A kind of fibrous composite for internal wall pot body of polishing, it is characterised in that:Raw material system by following weight proportion
Become:
6 parts of glass fibre, 0.2 part of sodium lignin sulfonate, 3.5 parts of 180 mesh calcium carbonate, 8 parts of 230 mesh calcium carbonate, quartz sand
12 parts, 0.6 part of palmitic acid.
Preferably, also including the hydroxyethyl cellulose that weight proportion is 0.5 part in raw material.
Preferably, the fineness of the glass fibre is 0.05-0.2mm.
Preferably, the particle diameter of the quartz sand is 0.3-1.2mm.
The preparation method of fibrous composite, step is:
(1) sodium lignin sulfonate is added in 60 DEG C of its 8 times of weight of hot water, dissolving configuration mixed liquor A, mixed liquor A
80 DEG C are warming up to, palmitic acid is added, be uniformly mixed, obtain mixed liquid B;
(2) quartz sand is mixed to obtain mixed material A with 180 mesh calcium carbonate, 230 mesh calcium carbonate, mixed material A is uniformly added
Heat is to 75 DEG C, then as in closed container, so that mixed material A is seethed with excitement by air-flow, and by mixed liquid B atomized spray in mixture
Material A, in the presence of air-flow, in the particle surface of mixed material A, the temperature of air-flow is 75 DEG C to mixed liquid B uniform adhesion;
(3), after mixed material A is mixed with mixed liquid B, glass fibre is added, in the presence of air-flow, solids
Material boiling, reaches batch mixing purpose, and liquid material uniform adhesion is in the particle surface of solid material, and the moisture in liquid material
Gradually evaporate, reach the purpose of pneumatic conveying drying;After material is completely dried, gas flow temperature is down to 20 DEG C;Treat that temperature of charge is down to 20
After DEG C, discharging, obtain fibrous composite.
The invention has the beneficial effects as follows:
Fibrous composite prepared by the present invention, for the inwall of pot of polishing, the particle surface of fibrous composite is hard
Spend the diamond that compares smaller, but the particle of fibrous composite is formed by the particle agglomeration of multiple material, with irregular
Corner angle, polishing effect good;After the granule impact internal wall pot body of reunion, while polishing to internal wall pot body, reunion
Grain also can gradually be dispersed into little particle, continue to carry out internal wall pot body careful polishing, and sodium lignin sulfonate and palmitic acid make inorganic
Reunion is produced between material granule;And in bruting process, particles hit internal wall pot body, particle surface produce high temperature, make palm fibre
Palmitic acid acid fusing, in the presence of palmitic acid, so as to promote sodium lignin sulfonate to fail the agglomeration between electrodeless composition granule;
After particles hit internal wall pot body terminates, under airflow function, particle is collected again, again during, temperature reduce, particle it
Between can reunite again.
Specific embodiment
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further, but following embodiments is only the preferred embodiments of the present invention, and not all.
Based on the embodiment in embodiment, those skilled in the art are obtained other realities on the premise of creative work is not made
Example is applied, belongs to protection scope of the present invention.
Embodiment 1
A kind of fibrous composite for internal wall pot body of polishing, is made up of the raw material of following weight proportion:
6 parts of glass fibre, 0.5 part of hydroxyethyl cellulose, 0.2 part of sodium lignin sulfonate, 3.5 parts of 180 mesh calcium carbonate, 230
8 parts of mesh calcium carbonate, 12 parts of quartz sand, 0.6 part of palmitic acid.
Glass fibre, the fineness of hydroxyethyl cellulose are 0.05-0.2mm, and the particle diameter of quartz sand is 0.3-1.2mm.
The preparation method of fibrous composite, step is:
(1) sodium lignin sulfonate is added in 60 DEG C of its 8 times of weight of hot water, dissolving configuration mixed liquor A, mixed liquor A
80 DEG C are warming up to, palmitic acid is added, be uniformly mixed, obtain mixed liquid B;
(2) quartz sand is mixed to obtain mixed material A with 180 mesh calcium carbonate, 230 mesh calcium carbonate, mixed material A is uniformly added
Heat is to 75 DEG C, then as in closed container, so that mixed material A is seethed with excitement by air-flow, and by mixed liquid B atomized spray in mixture
Material A, in the presence of air-flow, in the particle surface of mixed material A, the temperature of air-flow is 75 DEG C to mixed liquid B uniform adhesion;
(3), after mixed material A is mixed with mixed liquid B, glass fibre, hydroxyethyl cellulose are added, in air-flow
Under effect, solid material seethes with excitement, and reaches batch mixing purpose, and liquid material uniform adhesion is in the particle surface of solid material, and liquid
Moisture in body material gradually evaporates, and reaches the purpose of pneumatic conveying drying;After material is completely dried, gas flow temperature is down to 20 DEG C;Treat
After temperature of charge is down to 20 DEG C, discharging, obtain fibrous composite.
Internal wall pot body polishing process, step is:
By the pot blank after shaping, send in closed polishing, pot fixed mount between polishing, is provided with, pot passes through
Pot fixed mount is suspended vacantly, and pot can be around the center rotation of pot, and pot is opening down, below the opening of pot
The high-pressure spray gun being reciprocally moveable is provided with, fibrous composite is sprayed from high-pressure spray gun with high pressure nitrogen as carrier, directive pot
The inwall of body, the inwall to pot are polished;At the uniform velocity rotation in pot bruting process, high-pressure spray gun reciprocally swinging, to pot
Inwall carries out uniform grinding.
Fibrous composite after polishing, is collected in the presence of air-flow directed flow, re-uses.
The method polishing after internal wall pot body finer and smoother, and requirement of the bruting process to personnel's technical ability be not very high,
Committed step all can be realized automatically controlling by equipment, can be very good control product quality.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are only the present invention described in above-described embodiment and specification it should be appreciated that the present invention is not restricted to the described embodiments
Preference, be not intended to limit the present invention, without departing from the spirit and scope of the present invention, the present invention also has various
Changes and improvements, these changes and improvements are both fallen within scope of the claimed invention.The claimed scope of the invention is by institute
Attached claims and its equivalent thereof.
Claims (4)
1. a kind of fibrous composite for internal wall pot body of polishing, it is characterised in that:It is made up of the raw material of following weight proportion:
6 parts of glass fibre, 0.2 part of sodium lignin sulfonate, 3.5 parts of 180 mesh calcium carbonate, 8 parts of 230 mesh calcium carbonate, 12 parts of quartz sand,
0.6 part of palmitic acid.
2. the fibrous composite for internal wall pot body of polishing according to claim 1, it is characterised in that:Also wrap in raw material
Include the hydroxyethyl cellulose that weight proportion is 0.5 part.
3. the fibrous composite for internal wall pot body of polishing according to claim 1, it is characterised in that:The glass fibers
The fineness of dimension is 0.05-0.2mm.
4. the fibrous composite for internal wall pot body of polishing according to claim 1, it is characterised in that:The quartz sand
Particle diameter be 0.3-1.2mm.