CN106479402A - 一种耐久型阻燃中空玻璃丁基密封胶及其制备方法 - Google Patents
一种耐久型阻燃中空玻璃丁基密封胶及其制备方法 Download PDFInfo
- Publication number
- CN106479402A CN106479402A CN201610968837.4A CN201610968837A CN106479402A CN 106479402 A CN106479402 A CN 106479402A CN 201610968837 A CN201610968837 A CN 201610968837A CN 106479402 A CN106479402 A CN 106479402A
- Authority
- CN
- China
- Prior art keywords
- fire
- sealant
- retardant
- double glazing
- viscosifier
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种耐久型阻燃中空玻璃丁基密封胶,包括以下主要成分:聚异丁烯、丁基橡胶、二硫化钼、阻燃剂、炭黑、增粘剂、受阻酚类抗氧化剂、沸石和重质碳酸钙。在传统的热熔丁基密封胶的配方基础上加入了微米级的阻燃剂,一方面,纳米级的二氧化硅均匀的分散在体系中,阻燃效果好,另一方面,六铝酸钙不但有超过1000℃的高温性能,同时其具有非常好的耐酸碱腐蚀、耐金属腐蚀的性能;加入二硫化钼可以大大提高各物质的分散效果,特别是对纳米级的阻燃剂的分散效果影响非常大,从而达到更好的阻燃效果;用松香树脂和萜烯树脂的混合物做增粘剂,不但增粘效果好,而且有防滑的效果,减少密封胶的冷流性,粘结玻璃以后长期使用不变形。
Description
技术领域
本发明涉及密封胶技术领域,特别地,涉及一种耐久型阻燃中空玻璃丁基密封胶及其制备方法。
背景技术
随着科技的进步,生活水平的提高,人们对生活环境的要求也越来越高,尤其是七十年代末期,世界范围的能源紧张,各国对节能、环保型产品的推广使用比较重视,中空玻璃产品的研制、生产也逐步向节能、环保型方向发展。 针对目前国内高能耗建筑比例较大、建筑节能状况欠佳,国家日益重视建筑节能产品的应用以及相关法规标准的制定,2005年国家公布了《 公共建筑节能设计标准》,***也随之颁发了《 关于发展节能省地型住宅和公共建筑的指导意见》,其中指出,到 2010 年,全国城镇建筑实现节能 50%,2020 年,北方和沿海经济发达地区和大城市新建建筑实现节能 65%的目标。 为达到这些目标,中空玻璃生产使用量急剧增长,2003 年的生产使用量超过 3000 万平方米,2005 年中空玻璃的年生产使用量已达到 6000 万平方米,2010 年预计使用量将增加到 1.5 亿平方米。由于中空玻璃产量的提高,中空玻璃所必须的密封胶产量也在持续增长。
在制作中空玻璃时,选用合适的边部密封材料和良好的周边框架材料,是提高中空玻璃使用性能的关键。 中空玻璃的密封结构主要为双道密封,第一道密封为内道密封,起隔绝水汽和空气作用 ;第二道密封为外道密封,起结构作用。因此中空玻璃的第一道密封必须使用水蒸气透过率极低的热熔丁基密封胶。 如果一道密封胶水蒸气透过率较高,水蒸气透过第一道密封胶渗透到中空玻璃中,中空玻璃就容易出现露点现象,使中空玻璃失效。 中空玻璃长期在户外使用,受阳光直射,夏天温度可能高达 60℃,密封胶在高温下会发生冷流现象,影响使用效果,因此,应用在中空玻璃上的密封胶不能有太高的冷流性,粘结玻璃以后需要长期使用不变形。
同时目前我国高层建筑的火灾时有发生,而发生高层建筑火灾时,人员不易疏散,在室内待的时间比较长,故对建筑材料的安全性要求更高,不但对热熔丁基密封胶的阻燃性能提出更高的要求,而且要求其在火灾时,不会散发有毒气体,从而更好的保障人员的安全。
发明内容
本发明目的在于提供一种耐久型阻燃中空玻璃丁基密封胶及其制备方法,以解决技术问题。
一种耐久型阻燃中空玻璃丁基密封胶,包括以下重量百分比的成分:
聚异丁烯 35-50%
丁基橡胶 10-20%
二硫化钼 0.5-1%
阻燃剂 0.2-0.5%
炭黑 5-8%
增粘剂 1-3%
受阻酚类抗氧化剂 0.5-2%
沸石 0.2-0.5%
重质碳酸钙 余量。
优选的,所述的增粘剂为松香树脂和萜烯树脂的混合物。
优选的,所述的阻燃剂为六铝酸钙和纳米级二氧化硅的混合物。
优选的,所述的丁基橡胶的分子量为15000-25000。
一种耐久型阻燃中空玻璃丁基密封胶的制备方法,包括以下步骤:
A、把捏合机预热到80-90℃,将聚异丁烯和丁基橡胶加入到预热的捏合机中进行捏合;
B、在物料温度达到110-130℃,加入碳黑、重质碳酸钙和增粘剂;
C、继续升高至140-150℃加入二硫化钼和阻燃剂,在真空度0.08-0.1Mpa继续捏合50-80min,获得密封胶捏合物;
D、挤出、成型、冷却得到中空玻璃密封胶。
本发明具有以下有益效果:本发明的耐久型阻燃中空玻璃丁基密封胶,在传统的热熔丁基密封胶的配方基础上加入了微米级的阻燃剂,一方面,纳米级的二氧化硅均匀的分散在体系中,阻燃效果好,另一方面,六铝酸钙不但有超过1000℃的高温性能,同时其具有非常好的耐酸碱腐蚀、耐金属腐蚀的性能,特别适合于中空玻璃使用;2、加入二硫化钼可以大大提高各物质的分散效果,特别是对纳米级的阻燃剂的分散效果影响非常大,从而达到更好的阻燃效果;3、用松香树脂和萜烯树脂的混合物做增粘剂,不但防滑效果好,而且有增粘的效果,减少密封胶的冷流性,粘结玻璃以后长期使用不变形;4、加入受阻酚类抗氧化剂可以加强密封胶的抗老化性能;5、加入沸石则可以利用其内部中空的结构,在夏季高温膨胀和冬季低温收缩时提供缓冲,从而降低密封胶的老化速度。
除了上面所描述的目的、特征和优点之外,本发明还有其它的目的、特征和优点。下面将对本发明作进一步详细的说明。
具体实施方式
以下对本发明的实施例进行详细说明,但是本发明可以根据权利要求限定和覆盖的多种不同方式实施。
实施例1
一种耐久型阻燃中空玻璃丁基密封胶,包括以下重量百分比的成分:
聚异丁烯 40%
丁基橡胶 15%
二硫化钼 0.8%
六铝酸钙 0.2%
纳米级二氧化硅0.1%
炭黑 7.5%
增粘剂 2.5%
受阻酚类抗氧化剂 1 %
沸石 0.35%
重质碳酸钙 余量;
所述的丁基橡胶的分子量为15000-25000;
所述的增粘剂为松香树脂和萜烯树脂的混合物,质量比为1:1。
一种耐久型阻燃中空玻璃丁基密封胶的制备方法,包括以下步骤:
A、把捏合机预热到85℃,将聚异丁烯和丁基橡胶加入到预热的捏合机中进行捏合;
B、在物料温度达到115℃,加入碳黑、重质碳酸钙和增粘剂;
C、继续升高至142℃加入二硫化钼和阻燃剂,在真空度0.085Mpa继续捏合65min,获得密封胶捏合物;
D、挤出、成型、冷却得到中空玻璃密封胶;
实施例2
一种耐久型阻燃中空玻璃丁基密封胶,包括以下重量百分比的成分:
聚异丁烯 50%
丁基橡胶 10%
二硫化钼 1%
六铝酸钙 0.18%
纳米级二氧化硅0.02%
炭黑 8%
增粘剂 1%
受阻酚类抗氧化剂 2%
沸石 0.2%
重质碳酸钙 余量。
所述的增粘剂为松香树脂和萜烯树脂的混合物,质量比为1:4。
所述的丁基橡胶的分子量为15000-25000。
一种耐久型阻燃中空玻璃丁基密封胶的制备方法,包括以下步骤:
A、把捏合机预热到80℃,将聚异丁烯和丁基橡胶加入到预热的捏合机中进行捏合;
B、在物料温度达到130℃,加入碳黑、重质碳酸钙和增粘剂;
C、继续升高至140℃加入二硫化钼和阻燃剂,在真空度0.1Mpa继续捏合50min,获得密封胶捏合物;
D、挤出、成型、冷却得到中空玻璃密封胶。
实施例3
一种耐久型阻燃中空玻璃丁基密封胶,包括以下重量百分比的成分:
聚异丁烯 35%
丁基橡胶 20%
二硫化钼 0.5%
六铝酸钙 0.4%
纳米级二氧化硅0.1%
炭黑 5%
增粘剂 3%
受阻酚类抗氧化剂 0.5%
沸石 0.5%
重质碳酸钙 余量。
所述的增粘剂为松香树脂和萜烯树脂的混合物,质量比为1:2.5。
所述的丁基橡胶的分子量为15000-25000。
一种耐久型阻燃中空玻璃丁基密封胶的制备方法,包括以下步骤:
A、把捏合机预热到90℃,将聚异丁烯和丁基橡胶加入到预热的捏合机中进行捏合;
B、在物料温度达到110℃,加入碳黑、重质碳酸钙和增粘剂;
C、继续升高至150℃加入二硫化钼和阻燃剂,在真空度0.08Mpa继续捏合80min,获得密封胶捏合物;
D、挤出、成型、冷却得到中空玻璃密封胶。
对本发明实施例1-3的密封胶进行检测,得到如下数据:
表1:实施例1-3的密封胶的检测数据:
实施例1 | 实施例2 | 实施例3 | 检测标准 | |
针入度1/10mm 25℃ | 35 | 32 | 32 | GJB785.1989 |
针入度1/10mm 130℃ | 285 | 270 | 275 | GJB785.1989 |
剪切强度MPa | 0.10 | 0.11 | 0.12 | JC/T914-2003 |
紫外线照射发雾性 | 无雾 | 无雾 | 无雾 | GB11944/T-2002 |
水蒸气透过率 | 0.75 | 0.72 | 0.72 | GB/T1037-1988 |
热失重% | 0.12 | 0.13 | 0.13 | JC/T914-2003 |
阻燃性 | FV-0 | FV-0 | FV-0 | GB/T2408-2008 |
以上所述仅为本发明的优选实施例而已,并不用于限制本发明,对于本领域的技术人员来说,本发明可以有各种更改和变化。凡在本发明的精神和原则之内,所作的任何修改、等同替换、改进等,均应包含在本发明的保护范围之内。
Claims (6)
1. 一种耐久型阻燃中空玻璃丁基密封胶,其特征在于,包括以下重量百分比的成分:
聚异丁烯 35-50%
丁基橡胶 10-20%
二硫化钼 0.5-1%
阻燃剂 0.2-0.5%
炭黑 5-8%
增粘剂 1-3%
受阻酚类抗氧化剂 0.5-2%
沸石 0.2-0.5%
重质碳酸钙 余量。
2.如权利要求1所述的耐久型阻燃中空玻璃丁基密封胶,其特征在于,所述的增粘剂为松香树脂和萜烯树脂的混合物。
3.如权利要求1所述的耐久型阻燃中空玻璃丁基密封胶,其特征在于,所述的阻燃剂为六铝酸钙和纳米级二氧化硅的混合物。
4.如权利要求1所述的耐久型阻燃中空玻璃丁基密封胶,其特征在于,所述的丁基橡胶的分子量为15000-25000。
5.一种耐久型阻燃中空玻璃丁基密封胶的制备方法,包括以下步骤:
A、把捏合机预热到80-90℃,将聚异丁烯和丁基橡胶加入到预热的捏合机中进行捏合;
B、在物料温度达到110-130℃,加入碳黑、重质碳酸钙和增粘剂;
C、继续升高至140-150℃加入二硫化钼和阻燃剂,在真空度0.08-0.1Mpa继续捏合50-80min,获得密封胶捏合物;
D、挤出、成型、冷却得到中空玻璃密封胶。
6.如权利要求5所述的耐久型阻燃中空玻璃丁基密封胶的制备方法,其特征在于,包括以下步骤:
A、把捏合机预热到85℃,将聚异丁烯和丁基橡胶加入到预热的捏合机中进行捏合;
B、在物料温度达到115℃,加入碳黑、重质碳酸钙和增粘剂;
C、继续升高至142℃加入二硫化钼和阻燃剂,在真空度0.085Mpa继续捏合65min,获得密封胶捏合物;
D、挤出、成型、冷却得到中空玻璃密封胶;
所述的耐久型阻燃中空玻璃丁基密封胶,包括以下重量百分比的成分:
聚异丁烯 40%
丁基橡胶 15%
二硫化钼 0.8%
六铝酸钙 0.2%
纳米级二氧化硅0.1%
炭黑 7.5%
增粘剂 2.5%
受阻酚类抗氧化剂 1%
沸石 0.35%
重质碳酸钙 余量;
所述的丁基橡胶的分子量为15000-25000;
所述的增粘剂为松香树脂和萜烯树脂的混合物,质量比为1:1。