CN106477236B - A kind of anti-mining unitary-core flame-resistant conveying belt of extraction of edge - Google Patents
A kind of anti-mining unitary-core flame-resistant conveying belt of extraction of edge Download PDFInfo
- Publication number
- CN106477236B CN106477236B CN201610897524.4A CN201610897524A CN106477236B CN 106477236 B CN106477236 B CN 106477236B CN 201610897524 A CN201610897524 A CN 201610897524A CN 106477236 B CN106477236 B CN 106477236B
- Authority
- CN
- China
- Prior art keywords
- parts
- core
- edge
- extraction
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of anti-mining unitary-core flame-resistant conveying belts of extraction of edge, it includes by more woven fabric cores of latitude reconnection lock construction, the two sides of the fabric core are equipped with 3-4 centimetres of three axial and orthogonal and interconnect the woven edge fabric core (6) of lock construction, the fabric core and edge fabric core (6) are by rolling impregnation and vacuum-latexed, full penetration core is pasted to form casing play (5), the casing play (5) enters plasticizing box plasticizing forming, bonding layer sizing is scraped using painting in the upper and lower part of the casing play (5) after molding, it is again introduced into plasticizing box secondary plasticizing and forms auxiliary adhesive layer (2), then lid glue sizing material is squeezed out through extruder high temperature, the rubber cover of melting is squeezed by grinding tool and is attached on the casing play (5) and the auxiliary adhesive layer (2) of high temperature, finally rolling cooling and shaping forms rubber cover (1 );Using the above structure, it is simple to realize structure, wearability is good, reduces the extraction of edge warp thread and can prevent the effect of edge warp thread winding carrying roller.
Description
Technical field
The present invention relates to a kind of anti-mining unitary-core flame-resistant conveying belts of extraction of edge.
Background technique
Currently, mining Fabric Solid-woven Fire-resistant Conveyer Belt is in use, when conveyer belt is run on a conveyor often
Sideslip wears edge, is easy to extract out the warp of belt carcass edge after edge abrasion, the warp thread after extraction can be wrapped on carrying roller, make
It at serious sideslip or generates more seriously to fall with disconnected band accident, influences normal production and safety.
Summary of the invention
The object of the present invention is to provide a kind of structure is simple, wearability is good, reduces the extraction of edge warp thread and can prevent side
Portion's warp thread winds the anti-mining unitary-core flame-resistant conveying belt of extraction of edge of carrying roller.
The technical scheme is that a kind of anti-mining unitary-core flame-resistant conveying belt of extraction of edge, it is characterised in that: it includes
By more woven fabric cores of latitude reconnection lock construction, the two sides of the fabric core are equipped with 3-4 centimetres of three axial and orthogonal and interconnect lock construction
Woven edge fabric core 6, the fabric core and edge fabric core 6 are by rolling impregnation and vacuum-latexed, full penetration core paste
Casing play 5 is formed, the casing play 5 enters plasticizing box plasticizing forming, and the upper and lower part of the casing play 5 after molding passes through again
It crosses painting and scrapes bonding layer sizing, be again introduced into plasticizing box secondary plasticizing and form auxiliary adhesive layer 2, then lid glue sizing material is through extruder height
Warm extrusion goes out, and squeezes the rubber cover of melting by grinding tool and is attached on the casing play 5 and the auxiliary adhesive layer 2 of high temperature, finally
It rolls cooling and shaping and forms rubber cover 1.
Technical solution of the present invention can also be that more latitude reconnection lock constructions of the fabric core are five heavy tentering chain structures, institute
Stating edge fabric core is three-dimensional hollow structure.
Technical solution of the present invention can also be more latitude reconnection lock constructions of the fabric core by two kinds or both or more
The body warp 3 and weft yarn 4 that chemical fibre is spun into are interwoven.
Technical solution of the present invention can also be that the three-dimensional hollow structure of the edge fabric core by body warp 3 is acrylic fibers
Yarn, seam warp thread 7 are acrylic yarn, and weft yarn is that two kinds or both or more of chemical fibre is interwoven.
Technical solution of the present invention can also be that the core paste is formulated by the component of following weight ratio: PVC paste resin
100 parts, 50 parts of dioctyl ester, 2-3 parts of stabilizer, 52% 25-30 parts of chlorinated paraffin, 3.5 4.5-5.5 parts of hydrate zinc borates, triaryl
13-15 parts of phosphate, 20 parts of aluminium hydroxide, 10-11 parts of antimony oxide, 0.3 part of colour carbon black, PVC adhesion promotor 0.5-
0.7 part, 1.3-1.5 parts of novel bonding resin CyrezCRA132,7 parts of silicon-series five-retardant.
Technical solution of the present invention can also be that the bonding layer sizing is formulated by the component of following weight ratio: PVC
100 parts of resin of paste, 45 parts of dioctyl ester, 2-3 parts of stabilizer, 52% 20-25 parts of chlorinated paraffin, 2-3 parts of antistatic agent, 3.5 water boron
Sour zinc 5.5-7.5 parts, 10-12 parts of triaryl phosphate, 10-15 parts of aluminium hydroxide, 10-11 parts of antimony oxide, colour carbon black
0.3 part, 1.3-1.5 parts of novel bonding resin CyrezCRA132,7 parts of silicon-series five-retardant.
Technical solution of the present invention can also be that the lid glue sizing material is formulated by the component of following weight ratio: PVCSG3
100 parts of resin, 64-66 parts of dioctyl ester, 2.5-3.5 parts of high-efficiency compound stabilizer, 52% 2.5-3.5 parts of chlorinated paraffin is antistatic
3-5 parts of agent, 1.0-2.0 parts of lubricating type heat stabilizer, 12-15 parts of triaryl phosphate, 5 parts of aluminium hydroxide, 8 parts of magnesium hydroxide,
6-8 parts of environment-friendly type antimony oxide, 0.8 part of colour carbon black, 1.5-2.0 parts of antifatigue AT-K, 3-5 parts of rubber and plastic anti-wear agent,
4-6 parts of antimony fire retardant, 10-12 parts of nitrile rubber powder P830 is complexed.
The beneficial effects of the invention are as follows by the way that in more woven fabric cores of latitude reconnection lock construction, the two sides of the fabric core are set
There is the 3-4 centimetres of three axial and orthogonal interconnection woven edge fabric core 6 of lock construction, the fabric core and edge fabric core 6 pass through stone roller
Impregnation and vacuum-latexed are pressed, full penetration core is pasted to form casing play 5, and the casing play 5 enters plasticizing box plasticizing forming, after molding
The upper and lower part of the casing play 5 scrape bonding layer sizing using painting, be again introduced into plasticizing box secondary plasticizing and form auxiliary
Adhesive layer 2, then lid glue sizing material is squeezed out through extruder high temperature, and the rubber cover of melting is squeezed to the bone for being attached to high temperature by grinding tool
In rack-layer 5 and the auxiliary adhesive layer 2, finally rolls cooling and shaping and form rubber cover 1;When work, since 3-4 is arranged in edge
Centimetre edge fabric core, the three-dimensional hollow structure body warp 3 of the edge fabric core is acrylic yarn, and seam warp thread 7 is acrylic yarn, latitude
Yarn is that two kinds or both or more of chemical fibre is interwoven, and edge yarn bonding force after impregnation is plasticized is strong, the anti-extraction of edge warp thread
Ability enhancing, the acrylic yarn of edge is also not easy to release, even if conveyer belt edge is worn, acrylic yarn and other with yarn count change
Fine yarn is lower compared to power resistance strength, since edge fabric core 6 is that three axial and orthogonal interconnects lock construction, at acrylic yarn and weft yarns
It forms shearing to be easy to be pulled off, warp thread will not be wrapped on carrying roller, to realize, structure is simple, and wearability is good, reduce side
Portion's warp thread is extracted out and can prevent the effect of edge warp thread winding carrying roller.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention
Fig. 2 is the A-A cross-sectional view in Fig. 1
Fig. 3 is the B-B direction cross-sectional view in Fig. 1
Fig. 4 is the warp and weft interweaving figure of Fig. 2
1, rubber cover in Fig. 1 to 4,2, auxiliary adhesive layer, 3, body warp, 4, weft yarn, 5, casing play, 6, edge fabric core,
7, warp thread is stitched.
Specific embodiment
According to Fig. 1 to 4, the present invention relates to a kind of anti-mining unitary-core flame-resistant conveying belts of extraction of edge, it includes by more
The woven fabric core of latitude reconnection lock construction, more latitude reconnection lock constructions of the fabric core are five heavy tentering chain structures, the fabric
The body warp 3 and weft yarn 4 that more latitude reconnection lock constructions of core are spun by two kinds or both or more of chemical fibre are interwoven, the fabric
The two sides of core are equipped with 3-4 centimetres of three axial and orthogonal and interconnect the woven edge fabric core 6 of lock construction, and the edge fabric core is three-dimensional
Hollow structure, the three-dimensional hollow structure of the edge fabric core are acrylic yarn by body warp 3, and seam warp thread 7 is acrylic yarn, and weft yarn is
Two kinds or both or more of chemical fibre is interwoven, and the fabric core and edge fabric core 6 are filled by rolling impregnation and vacuum-latexed
The saturating core of sub-dip is pasted to form casing play 5, specifically: the core paste is formulated by the component of following weight ratio: PVC paste resin
100 parts, 50 parts of dioctyl ester, 2-3 parts of stabilizer, 52% 25-30 parts of chlorinated paraffin, 3.5 4.5-5.5 parts of hydrate zinc borates, triaryl
13-15 parts of phosphate, 20 parts of aluminium hydroxide, 10-11 parts of antimony oxide, 0.3 part of colour carbon black, PVC adhesion promotor 0.5-
0.7 part, 1.3-1.5 parts of novel bonding resin CyrezCRA132,7 parts of silicon-series five-retardant;The casing play 5 enters plasticizing box and moulds
Bonding layer sizing is scraped using painting in the upper and lower part of chemical conversion type, the casing play 5 after molding, specifically: the bonding
Layer sizing is formulated by the component of following weight ratio: 100 parts of PVC paste resin, 45 parts of dioctyl ester, and 2-3 parts of stabilizer, 52% chlorine
20-25 parts of fossil waxes, 2-3 parts of antistatic agent, 3.5 5.5-7.5 parts of hydrate zinc borates, 10-12 parts of triaryl phosphate, hydroxide
10-15 parts of aluminium, 10-11 parts of antimony oxide, 0.3 part of colour carbon black, 1.3-1.5 parts of novel bonding resin CyrezCRA132,
7 parts of silicon-series five-retardant;It is again introduced into plasticizing box secondary plasticizing and forms auxiliary adhesive layer 2, then lid glue sizing material is through extruder high temperature
It squeezes out, specifically: the lid glue sizing material is formulated by the component of following weight ratio: 100 parts of PVCSG3 resin, dioctyl ester
64-66 parts, 2.5-3.5 parts of high-efficiency compound stabilizer, 52% 2.5-3.5 parts of chlorinated paraffin, 3-5 parts of antistatic agent, lubricating type
1.0-2.0 parts of heat stabilizer, 12-15 parts of triaryl phosphate, 5 parts of aluminium hydroxide, 8 parts of magnesium hydroxide, the oxidation of environment-friendly type three two
6-8 parts of antimony, 0.8 part of colour carbon black, 1.5-2.0 parts of antifatigue AT-K, 3-5 parts of rubber and plastic anti-wear agent, antimony fire retardant is complexed
4-6 parts, 10-12 parts of nitrile rubber powder P830;The rubber cover of melting is squeezed to 5 He of the casing play for being attached to high temperature by grinding tool
On the auxiliary adhesive layer 2, finally rolls cooling and shaping and form rubber cover 1;When work, due to being arranged 3-4 centimetres in edge
Edge fabric core, the three-dimensional hollow structure body warp 3 of the edge fabric core are acrylic yarn, and seam warp thread 7 is acrylic yarn, weft yarn two
Chemical fibre more than kind or both is interwoven, and edge yarn bonding force after impregnation is plasticized is strong, and the anti-extraction ability of edge warp thread increases
By force, the acrylic yarn of edge is also not easy to release, even if conveyer belt edge is worn, acrylic yarn is with other with the man-made fibre yarn phase of yarn count
It is more lower than power resistance strength, since edge fabric core 6 is to be formed at three axial and orthogonal interconnection lock construction and acrylic yarn and weft yarns
Shearing is easy to be pulled off, and acrylic yarn i.e. warp thread will not be wrapped on carrying roller, so that it is simple to realize structure, wearability
It is good, it reduces the extraction of edge warp thread and the effect of edge warp thread winding carrying roller can be prevented.
Claims (5)
1. a kind of anti-mining unitary-core flame-resistant conveying belt of extraction of edge, it is characterised in that: it includes being weaved by more latitude reconnection lock constructions
Fabric core, the two sides of the fabric core are equipped with 3-4 centimetres of three axial and orthogonal and interconnect the woven edge fabric core (6) of lock construction,
The fabric core and edge fabric core (6) are pasted to form casing play (5), institute by rolling impregnation and vacuum-latexed, full penetration core
Casing play (5) are stated into plasticizing box plasticizing forming, bonding is scraped using painting in the upper and lower part of the casing play (5) after molding
Layer sizing is again introduced into plasticizing box secondary plasticizing and forms auxiliary adhesive layer (2), and then rubber cover sizing material is through the high warm extrusion of extruder
Out, the rubber cover of melting is squeezed by grinding tool and is attached on the casing play (5) and the auxiliary adhesive layer (2) of high temperature, finally
It rolls cooling and shaping and forms rubber cover (1), more latitude reconnection lock constructions of the fabric core are five heavy tentering chain structures, the edge
Fabric core is three-dimensional hollow structure, and the three-dimensional hollow structure of the edge fabric core is acrylic yarn by body warp (3), stitches warp thread
It (7) is acrylic yarn, weft yarn (4) is that two or more chemical fibres is interwoven.
2. the anti-mining unitary-core flame-resistant conveying belt of extraction of a kind of edge according to claim 1, it is characterised in that: the fabric
The body warp (3) and weft yarn (4) that more latitude reconnection lock constructions of core are spun by two or more chemical fibres are interwoven.
3. the anti-mining unitary-core flame-resistant conveying belt of extraction of a kind of edge according to claim 1 or 2, it is characterised in that: described
Core paste is formulated by the component of following weight ratio: 100 parts of PVC paste resin, 50 parts of dioctyl ester, and 2-3 parts of stabilizer, 52% chlorination
25-30 parts of paraffin, 3.5 4.5-5.5 parts of hydrate zinc borates, 13-15 parts of triaryl phosphate, 20 parts of aluminium hydroxide, antimony oxide
10-11 parts, 0.3 part of colour carbon black, 0.5-0.7 parts of PVC adhesion promotor, novel bonding resin CyrezCRA132 1.3-1.5
Part, 7 parts of silicon-series five-retardant.
4. the anti-mining unitary-core flame-resistant conveying belt of extraction of a kind of edge according to claim 3, it is characterised in that: the bonding
Layer sizing is formulated by the component of following weight ratio: 100 parts of PVC paste resin, 45 parts of dioctyl ester, and 2-3 parts of stabilizer, 52% chlorine
20-25 parts of fossil waxes, 2-3 parts of antistatic agent, 3.5 5.5-7.5 parts of hydrate zinc borates, 10-12 parts of triaryl phosphate, hydroxide
10-15 parts of aluminium, 10-11 parts of antimony oxide, 0.3 part of colour carbon black, 1.3-1.5 parts of novel bonding resin CyrezCRA132,
7 parts of silicon-series five-retardant.
5. the anti-mining unitary-core flame-resistant conveying belt of extraction of a kind of edge according to claim 3, it is characterised in that: the lid glue
Sizing material is formulated by the component of following weight ratio: 100 parts of PVCSG3 resin, 64-66 parts of dioctyl ester, and high-efficiency compound stabilizer
2.5-3.5 parts, 52% 2.5-3.5 parts of chlorinated paraffin, 3-5 parts of antistatic agent, 1.0-2.0 parts of lubricating type heat stabilizer, triaryl
12-15 parts of phosphate, 5 parts of aluminium hydroxide, 8 parts of magnesium hydroxide, 6-8 parts of environment-friendly type antimony oxide, 0.8 part of colour carbon black, resist
3-5 parts of rubber and plastic anti-wear agent, 4-6 parts of antimony fire retardant, nitrile rubber powder P830 10-12 is complexed in 1.5-2.0 parts of tired agent AT-K
Part.