CN106450325A - Modified nanometer silicon-based oxide composite lead-acid battery of electric baby carriage - Google Patents
Modified nanometer silicon-based oxide composite lead-acid battery of electric baby carriage Download PDFInfo
- Publication number
- CN106450325A CN106450325A CN201610787255.6A CN201610787255A CN106450325A CN 106450325 A CN106450325 A CN 106450325A CN 201610787255 A CN201610787255 A CN 201610787255A CN 106450325 A CN106450325 A CN 106450325A
- Authority
- CN
- China
- Prior art keywords
- parts
- based oxide
- oxide composite
- type electric
- composite modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of a storage battery, and in particular to a modified nanometer silicon-based oxide composite lead-acid battery of an electric baby carriage. A negative electrode material comprises the following constituents based on parts by weight: 50 parts of aluminum powder, 5 parts of sulfuric acid, 2 parts of barium sulfate, 3 parts of carboxymethylcellulose, 5 parts of active carbon, 0.05 part of thorium nitrate, 0.3 part of cerium chloride, 0.8 part of bismuth hydroxide, 0.3 part of zinc source, nanometer SiO<x> and 1.5 parts of bismuth trioxide. By improving a deposition potential of hydrogen, hydrogen deposition is reduced, and the capacity of the storage battery is improved by over 15%, the acid consumption can be reduced by 5%, and the safety lifetime of the battery is prolonged by 8-12 months.
Description
Technical field
The present invention relates to battery technology field, be specifically related to a kind of nano silicon-based oxide composite modified type electric children vehicle
Lead accumulator.
Background technology
With the raising of people's living standard, children's type toy, leisure goods demand day by day vigorous, perambulator is by youngster
Virgin " luxury goods " develop into the necessity in developmental process.According to statistics, by current neonate be born quantity accumulation, the whole world 6 years old with
Under children's quantity more than 800,000,000.The consumption figure of annual whole world perambulator will exceed 100,000,000,000 yuans, wherein provisioned perambulator electricity
Pond is a huge consumption market.According to market feedback information, existing perambulator battery generally exists that service life is long, after charging
Discharge capacity is relatively low, there is the problems such as certain leakage risk.The reason that cause these problems a lot, one of them reason is analysis
Go out substantial amounts of hydrogen.
Content of the invention
The invention aims to solve the problems referred to above, a kind of electronic child of the composite modified type of nano silicon-based oxide is provided
Car lead accumulator.
In order to reach foregoing invention purpose, the present invention is by the following technical solutions:
A kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator, described negative material includes following parts by weight
Component:50 parts of lead powder, 5 parts of sulfuric acid, 2 parts of barium sulfate, carboxymethylcellulose calcium 3 parts, activated carbon 5 parts, thorium nitrate 0.05 part, trichlorine
Change cerium 0.3 part, bismuth hydroxide 0.8 part, 0.3 part of zinc source, Nano-meter SiO_2x, bismuth oxide 1.5 parts.
Above-mentioned each component guarantees that electrode different parts CURRENT DISTRIBUTION is equal on the basis of ensureing stability and distributing homogeneity
Even, in charging process, negative pole oxygen combined efficiency is high, and reduces negative pole hydrogen-separating quantity, decreases self-discharge of battery.
Add carboxymethylcellulose calcium and can improve discharge capacity in negative material, thus improve discharge capacity.
Adding cerous chloride, bismuth hydroxide and bismuth oxide in negative material, the cooperation of three enables to electric power storage
The overpotential of hydrogen evolution of pond negative plate is more negative, increases liberation of hydrogen difficulty, thus reduces hydrogen and separate out, reduces electrolyte during using
Consumption.Carboxymethylcellulose calcium, is conducive to improving the life of storage battery, reduces the dangerous accidents such as blast also to a certain extent
The possibility occurring
As preferably, described zinc source be zinc oxide, zinc sulphide, zinc sulfate one or more.
As preferably, described Nano-meter SiO_2xIn x=1.55-1.85.
As preferably, the oxidizability of described lead powder is 82-90%.
As preferably, Nano-meter SiO_2xParticle diameter be 10-50 nanometer.
As preferably, described negative material also includes the cuprous sulfate of 0.3 part.The deposition potential of hydrogen can be improved, thus
Reduce the precipitation of hydrogen.On the basis of above-mentioned each component, 5% is reduced to the eduction rate of hydrogen.
As preferably, described negative material also includes the nickel acetylacetonate of 0.1 part.
The ratio that can improve the discharge capacity after charging is 5-8%.
The present invention compared with prior art, provides the benefit that:By improving the deposition potential of hydrogen, reduce the precipitation of hydrogen, store
Battery capacity improves more than 15%;The consumption of acid can reduce by 5%;Improve the safe life of battery, improve 8-12 month.
Detailed description of the invention
Below by specific embodiment, explanation is further described to technical scheme.
If without specified otherwise, the raw material employed in embodiments of the invention is raw material commonly used in the art, implements
Method employed in example, is the conventional method of this area.
Embodiment 1:
A kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator, described negative material includes following parts by weight
Component:50 parts of lead powder, 5 parts of sulfuric acid, 2 parts of barium sulfate, carboxymethylcellulose calcium 3 parts, activated carbon 5 parts, thorium nitrate 0.05 part, trichlorine
Change cerium 0.3 part, bismuth hydroxide 0.8 part, 0.3 part of zinc source, Nano-meter SiO_2x, bismuth oxide 1.5 parts.Zinc source is zinc oxide.Nanometer
SiOxIn x=1.55-1.85.The oxidizability of lead powder is 82-90%.SiOxParticle diameter be 10-50 nanometer.
Embodiment 2:
A kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator, described negative material includes following parts by weight
Component:50 parts of lead powder, 5 parts of sulfuric acid, 2 parts of barium sulfate, carboxymethylcellulose calcium 3 parts, activated carbon 5 parts, thorium nitrate 0.05 part, trichlorine
Change cerium 0.3 part, bismuth hydroxide 0.8 part, 0.3 part of zinc source, Nano-meter SiO_2x, bismuth oxide 1.5 parts, cuprous sulfate 0.3 part.Zinc source
For zinc sulphide.Nano-meter SiO_2xIn x=1.55-1.85.The oxidizability of lead powder is 82-90%.SiOxParticle diameter be 10-50 nanometer.
Embodiment 3:
A kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator, described negative material includes following parts by weight
Component:50 parts of lead powder, 5 parts of sulfuric acid, 2 parts of barium sulfate, carboxymethylcellulose calcium 3 parts, activated carbon 5 parts, thorium nitrate 0.05 part, trichlorine
Change cerium 0.3 part, bismuth hydroxide 0.8 part, 0.3 part of zinc source, Nano-meter SiO_2x, bismuth oxide 1.5 parts, cuprous sulfate 0.3 part and second
0.1 part of acyl acetone nickel.Zinc source is zinc sulphide.Nano-meter SiO_2xIn x=1.55-1.85.The oxidizability of lead powder is 82-90%.SiOx
Particle diameter be 10-50 nanometer.
Claims (7)
1. the composite modified type electric children vehicle lead accumulator of a nano silicon-based oxide, it is characterised in that described negative material bag
Include the component of following parts by weight:50 parts of lead powder, 5 parts of sulfuric acid, 2 parts of barium sulfate, carboxymethylcellulose calcium 3 parts, activated carbon 5 parts, nitre
Acid thorium 0.05 part, cerous chloride 0.3 part, bismuth hydroxide 0.8 part, 0.3 part of zinc source, Nano-meter SiO_2x, bismuth oxide 1.5 parts.
2. a kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator according to claim 1, its feature
Be, described zinc source be zinc oxide, zinc sulphide, zinc sulfate one or more.
3. a kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator according to claim 1, its feature
It is, described Nano-meter SiO_2xIn x=1.55-1.85.
4. a kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator according to claim 1, its feature
Being, the oxidizability of described lead powder is 82-90%.
5. a kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator according to claim 1, its feature
It is, Nano-meter SiO_2xParticle diameter be 10-50 nanometer.
6. a kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator according to claim 1, its feature
Being, described negative material also includes the cuprous sulfate of 0.3 part.
7. a kind of nano silicon-based oxide composite modified type electric children vehicle lead accumulator according to claim 1, its feature
Being, described negative material also includes nickel acetylacetonate.