CN106429059A - Composite material double-layer oil tank and manufacturing method - Google Patents
Composite material double-layer oil tank and manufacturing method Download PDFInfo
- Publication number
- CN106429059A CN106429059A CN201610900144.1A CN201610900144A CN106429059A CN 106429059 A CN106429059 A CN 106429059A CN 201610900144 A CN201610900144 A CN 201610900144A CN 106429059 A CN106429059 A CN 106429059A
- Authority
- CN
- China
- Prior art keywords
- fiberglass
- outer tank
- tank
- structure sheaf
- inner canister
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a composite material double-layer oil tank and a manufacturing method. A tank body (1) includes a glass steel outer tank (11), a glass steel inner tank (13) manufactured by a male mold, and a 3D through gap layer (12) arranged between the inner tank (13) and the outer tank (11); the inner surface of the inner tank (13) adopts a rich resin containing a static electricity conducting material; and the surface roughness thereof is Ra 0.8-0.2. The inner surface layer of the inner tank adopts the rich resin with the static electricity conducting function, and the formed surface roughness is Ra 0.8-0.2; and compared with a female mold closing manufacturing process, a method for manufacturing the inner tank by the male mold is more convenient, can guarantee enough compactness of the inner surface of the inner tank, largely reduces the friction resistance of contact surfaces between oil and the tank body, reduces the weak of the contact surfaces, guarantees the quality of the oil in long-time use process to the greatest extent, improves the corrosion resistance and the safety of the inner surface of the inner tank, and prolongs the service life of the oil tank.
Description
Technical field
The present invention relates to gas station with sunken tankers technical field and in particular to a kind of composite two-compartment oil tank and its system
Make method.
Background technology
In recent years, with the high speed development of national economy, the steadily improving of living standards of the people, traffic transport industry is swift and violent
Development, automobile pollution increases substantially, and large-scale oil enterprise strengthens gas station's network construction at home energetically, national every year newly-built
The thousands of seat in gas station.With the progress of China's expanding economy and society, the environmental consciousness of people is more and more stronger, and country is to environmental protection
Requirement also more and more higher.At present, the gas station of most domestic is all using underground metalliferous individual layer oil tank, due to oil tank itself
The mechanical damages such as scratch, cut, impression, the quality problems during tank body welding and sunken tankers external anti-corrosion layer are older old
Change, lose protective effect, steel tank inner surface can not can bring about ring fully against the corrosion of fuel oil once there is seepage
Border pollution or the serious consequence of underground harm water resource.And because the iron oil tank of individual layer is embedded in underground, is subject to underground throughout the year
The corrosion of water and electrolytic etching, the iron oil tank of individual layer has obvious potential safety hazard in use quality and service life, is related to
To safety, economy, environmental protection.Additionally, individual layer irony oil tank is required for being keeped in repair and detecting every year, also increase maintenance time and
Cost.
Two-compartment oil tank has the unrivaled safe and environment-friendly, economic performance than common individual layer steel oil tank, and country is big at present
Push the application of row two-compartment oil tank, prior art outer tank typically adopts glass steel material to make, and inner canister is steel material so that interior
Housing has reinforcement and supports, and outer tank has insulation effect such as patent document CN 104816897A and CN 102582980B institute public affairs
The two-compartment oil tank opened, but due to inner canister for steel body material so that its weight greatly increases, impact is carried and is installed, and it is resistance to
Erosion effect is also poor, and the life-span is shorter, automatic recovery of can not rebounding after steel inner canister local compression.
In existing at present nonmetallic two-compartment oil tank, in manufacturing process adopt former matched moulds technique, product external surfaces according to
Pattern has surface forming, and inner surface relies on artificial roll forming, thus the tank body being obtained presents smooth outer surface, inner surface
Coarse phenomenon.Tank inner surface is contacted with oil product, and its inner surface is more coarse, the friction of the tank inner surface contacting with oil product
Resistance is bigger, and inner surface worn composite is faster, when loading and unloading oil product, repeatedly tank inner surface is rushed for a long time
Hit, abrasion can be caused to come off to forming repeated stock at tank inner surface microcosmic injustice, reduce oil quality;Additionally, former system
The product made, its tank inner surface compactness is poor, laminated between combine closely, easily make the gas or liquid microcosmic by surface
Trench penetrates into composite inner, causes surface corrosion.When used over time, its inner surface can occur part particle detachment existing
As oil supply brings new composition, badly influences the quality of storage oil.
Content of the invention
Therefore, the technical problem to be solved in the present invention is to overcome that steel wall oil tank corrosion resistance of the prior art is poor, uses
Short life, installation difficulty are big, can not rebound after local pressure deformation the defects such as recovery automatically, and existing nonmetallic two-compartment oil tank exists
There is a problem of during Long-Time Service having a strong impact on oil quality, thus providing a kind of composite two-compartment oil tank and its making
Method.
For solving above-mentioned technical problem, the present invention adopts the following technical scheme that:
On the one hand, the invention provides a kind of composite two-compartment oil tank, described tank body includes fiberglass outer tank, by formpiston
Mould be obtained fiberglass inner canister and be arranged at the 3D insertion clearance layer between described inner canister and described outer tank;In described inner canister
Surface is the resin-rich layer containing conducting electrostatic materials, and its surface roughness is Ra0.8~Ra0.2.
Described outer tank is made up of outer tank impervious barrier and outer tank structure sheaf, and described outer tank structure sheaf is located at described outer tank impervious barrier
Outside, the outer surface roughness that it is formed be Ra32~Ra50;It is interval with ring on described outer tank structure sheaf outer surface
Reinforcement.
Described modal circumferential stiffening rib is winding-type glass reinforcing rib, and it passes through the glass fibers of winding with described outer tank structure sheaf
Dimension forms an entirety.
What modal circumferential stiffening rib described in adjacent two was formed is spaced apart 350~550mm;It is highly 100~150mm.
On the other hand, present invention also offers a kind of composite two-compartment oil tank preparation method, comprise the steps:
S1. fiberglass inner canister makes
The resin-rich layer containing conducting electrostatic materials for the spraying on steel formpiston, makes fiberglass successively using injection rolling technology
Interior tank shell and two ends end socket;Shaping, prepared glass are docked with two ends end socket one respectively in the two ends of tank shell in fiberglass
The interior surface layers roughness of steel inner canister, wherein fiberglass inner canister is Ra0.8~Ra0.2;
S2.3D insertion clearance layer is laid
In prepared fiberglass inner canister outer surface brushing resin material, using pasted technique, 3D hollow glass fibre is knitted
Thing posts on the resin material surface brushed, and fibrae obliquae opposite direction pushes glass fabric upper surface along along 3D hollow,
Glass fibre is made to be thoroughly impregnated with resin, because the strong capillarity of fiber itself makes felt body along highly square when resin solidification
To erecting, form 3D insertion clearance layer;
S3. fiberglass outer tank makes
Using spray technology, fiberglass outer tank impervious barrier is wrapped in 3D insertion clearance layer;
After fiberglass outer tank impervious barrier gel, glass fiber reinforced plastics composite material is wrapped in by fiberglass using rotation winding process
On outer tank impervious barrier, prepared fiberglass outer tank structure sheaf;Fiberglass outer tank structure sheaf is polished and brush coating is processed, make outer tank
Outer surface roughness reaches Ra32~Ra50.
Ring is carried out along the fiberglass outer tank impervious barrier after gel using horizontal winding method and is wound around prepared fiberglass outer tank
Structure sheaf, the resin glue weight percent content in fiberglass outer tank impervious barrier therein:65-75%, fiberglass outer tank antiseepage
Thickness degree:1~2mm, the resin glue weight percent content in fiberglass outer tank structure sheaf:33%~35%.
Described preparation method also includes:
S4. reinforcement is installed:
Make prefabricated reinforcement skeleton on mould in reinforcement, and be disposed on the fiberglass having good positioning in advance
In outer tank structure layer surface;Reinforcement skeleton and fiberglass outer tank structure sheaf are carried out by spiral winding using winding process, makes two
Person forms entirety.
Described preparation method also includes:
S5. the installation of leakage detector:
Make detection well, and liquid medium is added into the continuous cavity of 3D insertion clearance layer by made detection well
Matter;In detection well, leakage detector is installed, makes leakage detector from fiberglass detection well top insertion, and make its bottom and 3D
Insertion clearance layer is connected, and the liquid level of liquid medium is in the middle part of leak detection instrument probe.
Technical solution of the present invention, has the advantage that:
A. composite two-compartment oil tank provided by the present invention, its inner and outer tank is all mixed using by resin and glass fibre
The glass-reinforced plastic material closing makes so that it is lightweight, intensity is high, anti-seismic performance good, easy for installation, most important using containing
, as inner canister inner surface, its corrosion resistance and good conductivity, by table in the inner canister that formed for the rich resin having conducting electrostatic materials
The surface roughness in face is Ra0.8~Ra0.2, and compared with former matched moulds manufacture craft, the method making inner canister using anode membrane is more
Simplicity is it can be ensured that while inner canister inner surface has enough consistency, greatly reduce the friction resistance of oil product and tank body contact surface
Power, decreases the abrasion of contact surface, ensure that the quality of oil product during Long-Time Service to greatest extent, improves table in inner canister
The corrosion resistance in face and security, simultaneously because glass steel material elasticity is big, can recover after compressive deformation in fast automatic bounce-back,
Extend the service life of oil tank.
B. the present invention adopts winding-type glass reinforcing rib, and it is fitted with outer tank structure sheaf, and is wound around work by overall
Skill, reinforcement is formed an entirety with outer tank structure sheaf, because the two is all using glass steel material, can make the overall strong of outer tank
Degree is strengthened, thus avoiding in corrosion phenomenon generated here, substantially prolongs the service life of oil tank, it uses the longevity
Life is not less than 30 years.
C. 3D insertion clearance layer of the present invention is 3D glass fabric hollow layer, middle filling bittern, and insertion clearance layer can
24 hours complete monitorings are carried out to the sealing property of inner canister and outer tank, make the response time fast using bittern, detection is more accurate,
No matter there is seepage in inner canister or outer tank, all can automatically detect, so that it is guaranteed that people adopt before interlevel dielectrics ooze and leak into underground
Take counter-measure, significant to soil protection and groundwater resources;Further, since 3D insertion clearance layer is hollow layer,
Even if inner canister produces leakage, also can guarantee that held liquid flows in outer void, outside contamination environment will not be overflowed, efficiently at once
Environmental protection.Meanwhile, 3D insertion clearance layer can improve the integral rigidity of oil tank, and the partial cut intensity of tank body.
Brief description
In order to be illustrated more clearly that the specific embodiment of the invention, below by use required in specific embodiment
Accompanying drawing be briefly described it should be apparent that, drawings in the following description are some embodiments of the present invention, for this area
For those of ordinary skill, on the premise of not paying creative work, other accompanying drawings can also be obtained according to these accompanying drawings.
Fig. 1 is the two-compartment oil tank structural representation being provided of the present invention;
Fig. 2 is the I portion schematic enlarged-scale view of the present invention.
Description of reference numerals:
1- tank body;2- reinforcement;3- resin-rich layer;11- outer tank;12- insertion clearance layer;13- inner canister;111- outer tank antiseepage
Layer;112- outer tank structure sheaf;113- manhole;114- detects well;115- earth conductor;116- manhole cover;117- leak detector.
Specific embodiment
Below in conjunction with accompanying drawing, technical scheme is clearly and completely described with the enforcement it is clear that described
Example is a part of embodiment of the present invention, rather than whole embodiments.Based on the embodiment in the present invention, ordinary skill
The every other embodiment that personnel are obtained under the premise of not making creative work, broadly falls into the scope of protection of the invention.
As shown in Figure 1 and Figure 2, composite two-compartment oil tank provided by the present invention, including the inner canister being made up of fiberglass
13rd, outer tank 11 and the tank body 1 being arranged at 3D insertion clearance layer 12 composition between inner canister and outer tank;Inner canister 13 passes through formpiston system
Become, inner canister inner surface forms can be with the resin-rich layer of static conductive, and its thickness is 0.5~1mm, can be arranged at described outer
Earth conductor 115 on tank lateral surface connects, and the electrostatic for producing during liquid flowing friction imports the earth, it is to avoid produce
Raw electrostatic hazard, the roughness of the inner surface of inner canister 13 being formed here is Ra0.8~Ra0.2, preferably Ra0.32;And glass
Glass steel outer tank 11 is made up of outer tank impervious barrier 111 and outer tank structure sheaf 112, and outer tank structure sheaf 112 is located at outer tank impervious barrier 111
Outside, is provided with modal circumferential stiffening rib 2 in outer jar structure layer 112 outer surface, and modal circumferential stiffening rib 2 adopted here is winding-type glass
Steel reinforcement, the glass fibre that it passes through to be wound around with outer tank structure sheaf 112 forms an entirety, greatly strengthen the entirety of tank body
Intensity, solves stress concentration and the etching problem of the presence of ring stiffener 2 position.Inner canister 13 and outer tank 11 by glass fibre and
Resin compounded forms, and the wall thickness of inner canister 13 is more than 4mm, and the wall thickness of outer tank 11 is more than 5mm.
Manhole 113 and detection well are additionally provided with the top longitudinal centre line of fiberglass inner canister 13 and fiberglass outer tank 11
114;Manhole 113 is communicated with the tank chamber of fiberglass inner canister 13, and in addition manhole 113 is provided with manhole cover 116;Detection well 114 and 3D
Insertion clearance layer 12 connects, and is provided with leak detector 117 in detection well 114.
3D insertion clearance layer 12 is 3D hollow glass fibre fabric, and it is bonded in table in inner canister 13 outer surface and outer tank 11
Face, being inside filled with liquid medium is bittern, and the thickness of 3D insertion clearance layer is 1~3.5mm.
Composite two-compartment oil tank provided by the present invention, its inner and outer tank is all using by resin and glass fibre mixing
Glass-reinforced plastic material make so that it is lightweight, intensity is high, anti-seismic performance good, easy for installation it is most important that corrosion-resistant
Property is good, and can rebound after compressive deformation recovery automatically.Equally lose electronics because glass-reinforced plastic material is not as metal, therefore by glass
The two-compartment oil tank that Steel material is made can not perplexed by corrosive medium completely, fundamentally solves etching problem, and then improves
The use quality of oil tank and increasing the service life;Meanwhile, the inner canister inner surface of composite two-compartment oil tank is additionally provided with containing static conductive
The resin-rich layer of material, it is integrally formed with inner canister, and directly contacts with oil product in use, and it is with outer tank outermost top
The earth conductor installed on portion's longitudinal centre line connects, and imports the earth for the electrostatic that liquid flow movable property is raw, it is to avoid produce quiet
Electricity is dangerous, improves the security of tank body.
In addition, 3D insertion clearance layer of the present invention adopts 3D glass fabric hollow layer, middle filling bittern, insertion clearance layer
The sealing property of inner canister and outer tank can be carried out with 24 hours complete monitorings, make the response time fast using bittern, detection is more
Accurately, no matter there is seepage in inner canister or outer tank, all can automatically detect, so that it is guaranteed that people are oozed in interlevel dielectrics leaks into underground
Before take counter-measure, significant to soil protection and groundwater resources;Further, since 3D insertion clearance layer is hollow
Layer, even if inner canister produces leakage, also can guarantee that held liquid flows in outer void, will not overflow outside contamination environment at once,
High-efficiency environment friendly.Meanwhile, 3D insertion clearance layer can improve the integral rigidity of oil tank, and the partial cut intensity of tank body.
Provided by the present invention composite two-compartment oil tank preparation method is presented herein below, specifically includes following steps:
S1. fiberglass inner canister makes
Polyester film is sprayed on steel formpiston, coats one layer of rich tree containing conducting electrostatic materials in steel formpiston appearance
Fat, is aided with rolling technology using injection and makes tank shell and two ends end socket in fiberglass successively;Then by tank shell in fiberglass
Two ends respectively at two ends end socket one docking shaping, prepared fiberglass inner canister, the interior surface layers of wherein fiberglass inner canister are coarse
Spend for Ra0.8~Ra0.2, if the lean glue in local occurs or roughness phenomenon not up to standard can carry out the later stage and strike off so as to meet the requirements;
Under room temperature, internal pressure air test is adopted for test(ing) medium to fiberglass inner canister with pure air, inner canister is slowly forced into 35kPa, protect
Pressure 30min, not to be depressured, No leakage be qualified, test(ing) medium adopts pure air, and test temperature should be normal temperature, internally simultaneously
Tank superficial layer carries out planarization detection and reparation;Resin glue content wherein in glass fiber reinforced plastics composite material:65-75%;In injection
In moulding process, atomisation pressure is 0.5~0.7MPa, and lance ejection shaping angle is 65~70 °, the spray of spray gun and steel formpiston
Penetrate distance for 350~500mm.
S2.3D insertion clearance layer is laid
In fiberglass one layer of resin material of inner canister outer surface brushing of above-mentioned preparation, using the method that pastes by 3D double glazing
Fabric posts on resin material surface, and along along 3D hollow, fibrae obliquae opposite direction pushes glass fabric upper surface, makes
Glass fibre is thoroughly impregnated with resin, because the strong capillarity of fiber itself makes felt body along short transverse when resin solidification
Erect, form 3D insertion clearance layer;Process of deployment should be carried out to 3D hollow glass fibre fabric splicing seams corresponding and
Necessary process, the 3D fabric overlap joint that will splice (>20mm), cut from overlap joint center with cutter, remove excess fiber, make two
Layer splicing end face coincide.
To ensure interlayer continuously smoothly insertion and meet specification volume requirement as bottom line, with interlayer laying no circumferential deformation,
Laminate, omit and surfacing is qualified.
S3. fiberglass outer tank makes:
Using spray technology, fiberglass outer tank impervious barrier is wrapped in 3D insertion clearance layer, in sprayup process, spray
Mist pressure is 0.5~0.7MPa, and lance ejection shaping angle is 65 °~70 °, and spray gun is 350~500mm with the distance of mould.
In glass fiber reinforced plastics composite material, the weight percent content of resin glue controls in 65-75%, fiberglass outer tank impervious barrier THICKNESS CONTROL
In 1~2mm.
Winding technology is adopted to be wound around outer tank structure sheaf, the outer surface roughness of outer tank by the line style of regulation and thickness after gel
For Ra32~Ra50, in glass fiber reinforced plastics composite material, resin glue weight percent content controls 33%~35%;During winding, adopt
Horizontal winding method carries out ring winding, steel die each rotation, and conductive filament head moves a yarn sheet width, by this reciprocation cycle,
It is covered with till core stack shell reaches process stipulation thickness until yarn sheet.Outer tank structure sheaf should be wound around using equilibrium, and winding angle is
85 °~90 °.After fiberglass outer tank completes, outer surface layer is polished using 45 mesh sand tables, polishing finish after to tank body outside
Surface carries out brush coating (gel coat) and processes;Gel coat in the curing process, because mould has been at rotation status, by Self-leveling
Principle ensures the flatness of outer surface.
S4. reinforcement is installed:
Make prefabricated reinforcement skeleton on mould in reinforcement, and be disposed on the fiberglass having good positioning in advance
In outer tank structure layer surface;Reinforcement skeleton and fiberglass outer tank structure sheaf are carried out by spiral winding using winding process, makes two
Person forms entirety.
Reinforcement is pre-formed for mold ejector rolling, after tank body completes, prefabricated reinforcement is adopted hand
Paste technique is fixed on the orientation that tank body is had good positioning in advance, is entered reinforcement and outermost layer tank body using winding process on wrapping machine
Row is wound around, and is allowed to form overall, the tank body bearing height being formed:100~150mm.
S5. the installation of leakage detector:
Make detection well;Liquid medium is added into the continuous cavity of 3D insertion clearance layer by made detection well,
Liquid level is in the middle part of leak detection instrument probe, installs leakage detector in fiberglass detection well, makes leakage detector from fiberglass
Detection well top is inserted and so that its bottom is connected with 3D insertion clearance layer;Thus completing the system of whole composite two-compartment oil tank
Make.
Obviously, above-described embodiment is only intended to clearly illustrate example, and the not restriction to embodiment.Right
For those of ordinary skill in the art, can also make on the basis of the above description other multi-forms change or
Change.There is no need to be exhaustive to all of embodiment.And the obvious change thus extended out or
Change among still in the protection domain of the invention.
Claims (8)
1. a kind of composite two-compartment oil tank it is characterised in that:Described tank body (1) includes fiberglass outer tank (11), by formpiston mould
Have the fiberglass inner canister (13) being obtained and be arranged at the 3D insertion clearance layer between described inner canister (13) and described outer tank (11)
(12);Described inner canister (13) inner surface is the resin-rich layer containing conducting electrostatic materials (3), its surface roughness be Ra0.8~
Ra0.2.
2. composite two-compartment oil tank according to claim 1 is it is characterised in that described outer tank (11) is by outer tank impervious barrier
(111) form with outer tank structure sheaf (112), described outer tank structure sheaf (112) is located at the outside of described outer tank impervious barrier (111),
The outer surface roughness that it is formed is Ra32~Ra50;It is interval with ring on described outer tank structure sheaf (112) outer surface to add
Strong muscle (2).
3. composite two-compartment oil tank according to claim 2 is it is characterised in that described modal circumferential stiffening rib (2) is to be wound around
Type glass reinforcing rib, the glass fibre that it passes through to be wound around with described outer tank structure sheaf (112) forms an entirety.
4. composite two-compartment oil tank according to claim 3 is it is characterised in that modal circumferential stiffening rib (2) described in adjacent two
Formed is spaced apart 350~550mm;It is highly 100~150mm.
5. a kind of composite two-compartment oil tank preparation method is it is characterised in that comprise the steps:
S1. fiberglass inner canister makes
The resin-rich layer containing conducting electrostatic materials for the spraying on steel formpiston, makes fiberglass inner canister successively using injection rolling technology
Housing and two ends end socket;Shaping is docked with two ends end socket one respectively in the two ends of tank shell in fiberglass, in prepared fiberglass
The interior surface layers roughness of tank, wherein fiberglass inner canister is Ra0.8~Ra0.2;
S2.3D insertion clearance layer is laid
In prepared fiberglass inner canister outer surface brushing resin material, using pasted technique, 3D hollow glass fibre fabric is covered
It is attached to brushed resin material surface, and fibrae obliquae opposite direction pushes glass fabric upper surface along along 3D hollow, makes glass
Glass fiber is thoroughly impregnated with resin, because the strong capillarity of fiber itself makes felt body erect along short transverse when resin solidification
Erect, form 3D insertion clearance layer;
S3. fiberglass outer tank makes
Using spray technology, fiberglass outer tank impervious barrier is wrapped in 3D insertion clearance layer;
After fiberglass outer tank impervious barrier gel, glass fiber reinforced plastics composite material is wrapped in by fiberglass outer tank using rotation winding process
On impervious barrier, prepared fiberglass outer tank structure sheaf;Fiberglass outer tank structure sheaf is polished and brush coating is processed, make outer tank appearance
Surface roughness reaches Ra32~Ra50.
6. preparation method according to claim 5 is it is characterised in that adopt horizontal winding method along the fiberglass after gel
Outer tank impervious barrier carries out ring and is wound around prepared fiberglass outer tank structure sheaf, the resin glue weight in fiberglass outer tank impervious barrier therein
Amount degree:65-75%, fiberglass outer tank impervious barrier thickness:1~2mm, the resin glue weight in fiberglass outer tank structure sheaf
Amount degree:33%~35%.
7. preparation method according to claim 7 is it is characterised in that described preparation method also includes:
S4. reinforcement is installed:
Make prefabricated reinforcement skeleton on mould in reinforcement, and be disposed on the fiberglass outer tank having good positioning in advance
In structure layer surface;Reinforcement skeleton and fiberglass outer tank structure sheaf are carried out by spiral winding using winding process, makes the two shape
Integral.
8. preparation method according to claim 7 is it is characterised in that described preparation method also includes:
S5. the installation of leakage detector:
Make detection well, and liquid medium is added into the continuous cavity of 3D insertion clearance layer by made detection well;?
In detection well, leakage detector is installed, makes leakage detector from fiberglass detection well top insertion, and make its bottom and 3D insertion
Clearance layer is connected, and the liquid level of liquid medium is in the middle part of leak detection instrument probe.