CN106427346A - Painted stone and preparation method thereof - Google Patents
Painted stone and preparation method thereof Download PDFInfo
- Publication number
- CN106427346A CN106427346A CN201610797889.XA CN201610797889A CN106427346A CN 106427346 A CN106427346 A CN 106427346A CN 201610797889 A CN201610797889 A CN 201610797889A CN 106427346 A CN106427346 A CN 106427346A
- Authority
- CN
- China
- Prior art keywords
- stone
- paint
- coloured
- layer
- paint film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a painted stone. Colored paint liquid is prepared; according to the formula of the colored paint liquid, the mass ratio of paint, to a colored powder material to oil capable of being dried is 1:0.1 to 1.5:0.01 to 1.2; the colored paint liquid is taken to perform single-color or multi-color single-layer painting on a base material, and after painting, a first layer of paint film with the thickness ranging from 0.01 mm to 1 mm is obtained after standing, drying and curing; the first layer of paint film is ground till the paint film is ground matte; the paint film is thoroughly washed with clean water and is dried in the air after being ground; and repeated operation is performed on the ground first layer of paint film for 1-1000 times, a plurality of layers of paint films with the thickness ranging from 0.02 mm to 1000 mm are prepared, the multiple layers of paint films are separated from the base material, and then the painted stone is prepared. According to the method, no mold is needed for performing molding firstly, a plurality of paint layers are stacked, the painted stone is prepared at first, cutting and carving then are performed on the painted stone, the limitation of mold molding is broken through, and painted stone products in various shapes can be prepared at will.
Description
Technical field
The present invention relates to a kind of stone and preparation method thereof.
Background technology
Tradition lacquer is ancient to be claimed, and is the skin of all things on earth, never depart from various carcass (other implements) for thousands of years and
Exist, the even bodiless lacquer of Foochow, Fujian, also be unable to do without for the moulding burlap of carcass.
Lacquerware is of a great variety.Its making step typically first makees tire, then coats with lacquer paint.Tire bone mainly has bamboo tire, wood tire, folder tire
Deng.Folder tire lacquerware is also known as bodiless lacquer, if being with raw lacquer sticky dried layer burlap or silk, smears outward after paint ash makes tire, through mill
Light, coat with lacquer paint, paint coloured silk and form.
Molding is the first step of bodiless lacquer tire making process.Tread flaking technique is divided into yin exhaustion method and Yang Tuofa two kinds.Craftsman is first
It as model, is coiled on implements outline line with mud bar with gypsum or directly use finished product, and brush the insulating liquid of upper suds one class.
It is cast in gypsum on implements.In the ancient times not having gypsum, first people can only be with dry that very slow yellow mud does mould.Several tens minutes
After, gypsum becomes stiff, and edge trimming is smooth, obtains gypsum mold, through repairing further, just can paste brush on mould
There is the burlap of paint mud.
After burlap posts, repeatedly to brush dark grey on it and the paint mud becoming.Ramie in folder ramie, refer to knits burlap institute exactly
Ramie.
After many everywhere that grain thickness is different dark grey paint mud brushes are on burlap repeatedly, the burlap carcass parching completely is unexpectedly
So become hard shell.Craftsman beats burlap shell with hard thing, and the gypsum carcass of the inside attachment is shattered and comes off, this process
It is just tread flaking (note：This is Yang Tuofa, and yin exhaustion method is not required to beat, and only need to take off i.e. the burlap tyre carcase being attached to gypsum mold inwall
Can).The burlap tire obtaining after tread flaking is merrily and lightheartedly hard, compared with for plastics, is not afraid of water logging, indeformable, colour-fast, firm, heatproof, resistance to
Acid and alkali corrosion.
Make bodiless lacquer process, it is simply that one piece of burlap and a pile dark grey paint mud make one as bright as a sixpence, light
It is full of and have the art work of texture.Repeatedly polish particularly significant.
The Making programme of Foochow bodiless lacquer carcass is：Pasted the burlap of the full dark grey paint mud of brush on mould after, first with
The thick dark grey of grain and the full carcass of japanning mud brush, typically need brush 2 road, because lacquer to be waited parches, and every time-consuming 2～3 days together.It
After, with in, the dark grey paint mud multi-fold of the particle such as thin, each of which walks, and all needing to wait for lacquer parches, and also needs constantly to repair
Hole on tyre surface, the complicated ordinary people of order of operation is difficult to imagine.
When last one fine ash parches, after repairing, just can go up just paint, typically need to repeatedly go up 3 roads.Just paint relatively paint mud holds
Yi Gan, but after being dried every time, all need through careful hole repair and polishing operation.Generally, the high bodiless vase of one and half people,
Need time-consuming 30～35 days, and baroque yin exhaustion method implements, then need 40 days even more long-time, this does not also include that the later stage coats with lacquer
That adorns is time-consuming.
In prior art, it is that carcass is moulding that the making of lacquerware is required for mould, determines paint in the shape making front mold
The shape of device.Always after painting, do not carry out moulding manufacture craft again.
Content of the invention
The present invention provides a kind of stone and preparation method thereof.
The technical solution used in the present invention is：
The preparation method of a kind of stone, said method comprising the steps of：
(1) being formulated with colored paint liquid, the formula of described coloured enamel liquid is：, coloured powder, can the mass ratio of drying oil be 1：
0.1～1.5：0.01～1.2, preferably 1：0.3～1.2：0.1～1.2；
Described for lacquer
Further,：Have another name called lacquer, raw lacquer, soil paint, state's paint, general term Chinese lacquer, for a kind of natural resin coating, be
Cut open sumac bark, a kind of white sticky emulsion flowing out from tough intracutaneous, the processed and coating made.
Described coloured powder is vermilion, pellet is red, minium, germanite, cadmium red, alum are red, toluidine red, orpiment, lead chromate yellow, iron
The husky Huang of Huang, cadmium yellow, the Chinese, azurite, ultramarine, indigo, phthalocyanine blue, barba hispanica, Chinese blue, Prussian blue, titanium white, lithopone, bismoclite,
Malachite green, chrome oxide green, chrome green, phthalocyanine green, pine soot, carbon black, iron oxide black, dark grey, Cu-Zn alloy powder, one or more in aluminium silver powder
Mixing.
Described can drying oil be tung oil, turpentine oil, camphorated oil, banana oil, one or more the mixing in gasoline.
Use different coloured powders, prepare the coloured enamel liquid of two or more different colours；
(2) take coloured enamel liquid on base material, carry out the individual layer brushing of monochrome or polychrome, after brushing 20～25 DEG C, 85～
Under the relative humidity of 95% (preferably 90%), after standing and drying solidification, obtain the ground floor paint film of 0.01mm-1mm thickness；
Described base material is smooth Plastic or glass plate；Also one layer of preservative film can be covered on flat board as base
Material.
(3) ground floor paint film is polished, be polishing to paint film dumb light；After polishing, clear water is rinsed well, dries；
Described polishing can use gauze, sand paper, hang all kinds of instrument such as mill, platform mill
(4) repeat on the ground floor paint film after polishing step (2), (3) 1～1000 times, prepare 0.02～
Multi-layer paint films is separated by the multi-layer paint films of 1000mm thickness with base material, i.e. prepares stone.
In described step (2), the individual layer brushing of described polychrome is at same layer by the coloured enamel liquid brushing of different colours, can
To constitute different patterns or shape.
In described step (2), the dry solidification of paint film is it is generally required to 1 hour-90 days, and the speed of drying varniss solidification is general
Depend on the thickness of the paint film of brushing.Paint film is thicker, then the dry solidification time is longer.
In described step (2), during the individual layer brushing of underway monochrome or polychrome, can be sprinkled into coloured in painting process
Solid fragment, described colored solid fragment can be the natural gemstone after pulverizing, natural jade, natural color stone, natural organic treasured
One or more mixing in stone, metal material, pottery, coloured glaze, eggshell, stone flour.
Described colored solid fragment is typically crushed between 4 mesh-100 mesh.
The addition of described colored solid fragment is generally 0.1～80% (preferably 10～40%) of coloured enamel liquid quality,
Last layer fragment can be spread uniformly, it is also possible to design needs according to stone, privileged site or pattern sprinkle colored solid
Fragment.
Described natural gemstone can be diamond, ruby, sapphire, emerald, emerald, crystal, olivine etc.；
Described natural jade can for Huanglong's jade, agate, jasper, Khotan jade, emerald, white marble, noctilucence jade, Green OnyxB,
Malachite etc.；
Described natural color stone can be agalmatolite, orpiment, stone from Qingtian county in Zhejiang Province, used to make seals, bloodstoen etc.；
Described natural organic gemstone can be pearl, amber, coral, ivory, jet etc.
Described metal fragment can be gold, silver, copper etc..
Described stone flour is acquisition after just stone pulverizing, can continue on for making stone as colored solid fragment.
In described step (2), temperature about 25 degree, humidity about 90 percent, enzyme reaction is the most active, temperature mistake
Height is too low, humidity is lower, is dried conjunctiva speed slower.The thickness of (paint) film depends on factors, and such as material mixture ratio is warm and humid
The control of degree, the mode etc. of brushing.
In described step (4), the coloured enamel liquid color that preferably each layer paint film of adjacent two layers is used is different, further,
Use not homochromy coloured enamel liquid matched combined, the stone of various different color matched combined can be prepared.
In described step (4), multi-layer paint films separates with base material, when described base material is the flat board being coated with preservative film, directly
Multi-layer paint films is torn, when described base material is smooth glass or plastic board, hot and cold water can be used alternately repeatedly to soak,
Multi-layer paint films can be peeled off with base material.
In described step (3), preferably repeat on the ground floor paint film after polishing step (2), (3) 10～1000
Secondary, more preferably 10～500 times, the thickness of the multi-layer paint films preparing preferably 0.1～1000mm, more preferably 1～100mm.
The present invention also provides stone prepared by said method, and described stone is made up of 2～1000 layers of coloured paint film stacking, often
The thickness of the coloured paint film of layer is 0.01mm-1mm.
Preferably described stone is made up of 10～1000 layers of coloured paint film stacking, more preferably by 10～500 layers of coloured paint film layer
It is stacked.
The thickness of preferably every layer coloured paint film is 0.01mm-0.5mm.
The thickness of described stone is 0.02～1000mm, preferably 0.1～1000mm, more preferably 1～100mm.
The color of preferably adjacent coloured paint film is different.
Obtained stone, then the cutting technique for grinding with craft or machine makes the handicraft of all kinds of shape, such as treasured
Stone or bowls and chopsticks, beading, engraving etc..
The stone that the present invention prepares, is made up of mutliplayered coats of enamel stacking, the first constraint departing from mould, can design and produce
The product of arbitrary shape, it is not necessary to additionally make new mould to develop new product.And adhesion is strong between each enamelled coating,
The stone preparing is the entirety of a uniform in material, and after polishing or cutting, material remains an entirety, and stability is high, make moist or
After being heated not easy to crack.
The beneficial effects of the present invention is：
The production method of a kind of brand-new lacquer craftwork product is provided, first moulding completely without mould, but pass through multilayer paint
Layer stackup, first prepares stone, then carries out cutting again on stone and chisels and carves, has broken the moulding restriction of mould, institute of can following one's inclinations
It is intended to prepare the stone product of all kinds of shape.And multi-layer paint films can use different colours matched combined, cutting polishing forms disconnected
After Ceng, the angle of thickness that tomography effect is brushed because of every layer (paint) during the initial stage and color and later stage polishing cutting and thousand become ten thousand
Change.
The properties of the stone that the present invention prepares is also very outstanding, Mohs' hardness be 3-4, higher than the amber in organic gemstone
Amber (Mohs' hardness 2.5), easily processes.Stone ring is protected, and has natural sex, fossil, dicoration, does not dissolves in ketone, lipid, benzene
The strong solvents such as class, alcohols, ethers, acid-fast alkali-proof is anticorrosive.High temperature resistant, can under the conditions of 150 DEG C Long-Time Service, be resistant to moment
250 DEG C of hot environments.Therefore the kitchen tools such as bowls and chopsticks cup can be made, can microwave disinfection.Under 686.42Pa frictional force effect
It is hardly damaged.Anti-electric breakdown strength reaches 50～80KV/mm, has extremely strong electrical insulation capability.Stone also has excellent anti-radiation.
Brief description
Schematic diagram when paint film is polished by Fig. 1.
After Fig. 2 is to the polishing of ground floor paint film, clear water is rinsed well, the coating surface figure after the coloured enamel liquid of brushing formula 2.
Fig. 3, after the coloured enamel liquid of brushing formula 2, is sprinkled into the coating surface figure of 20 mesh stone flours on surface.
Fig. 4 use formula 3 coloured enamel liquid brushing, after dry solidification, be polishing to the paint film schematic diagram after sub-light.
Obtain the tomography schematic diagram of the thick stone of 1mm after Fig. 5 brushing 10 layers.
The stone of the 1cm thickness that Fig. 6 embodiment 1 prepares.
Detailed description of the invention
Embodiment 1
With specific embodiment, technical scheme is described further below, but protection scope of the present invention is not
It is limited to this.
1., with timber drawing board as base material, attached one layer of preservative film follow-up coats with lacquer painting to isolate.
2. being formulated with colored paint liquid, including formula as below, the raw material of each formula is mass ratio
Formula 1：?：Vermilion：Tung oil mass ratio=1:0.5:0.2
Formula 2：?：Malachite green：Turpentine oil=1:0.2:1
Formula 3：?：Barba hispanica：Quality of gasoline ratio=1:0.4:1
Formula 4：?：Prussian blue：Tung oil：Camphorated oil：40 mesh egg-shell meal=1：0.1：0.3：0.2：0.4
Formula 5：?：Iron oxide yellow：Turpentine oil=1：0.9：1.2
The coloured enamel liquid taking formula 1 carries out monochromatic individual layer brushing on base material, in shady room, and 25 DEG C of temperature, phases of 90%
To under humidity, standing and drying obtains the ground floor paint film of 0.1mm thickness after solidifying 1 day；
Then ground floor paint film is polished, as it is shown in figure 1, dip in dark grey and a small amount of water with gauze, be polishing to dumb light, with
Increase the attachment degree of follow-up paint.After polishing, clear water is rinsed well, is dried；
3. on the ground floor paint film after polishing, the coloured enamel liquid taking formula 2～5 respectively repeats above-mentioned steps 2, multiple
Mill overcoating, every layer thickness 0.1mm.After the polishing of ground floor paint film, clear water is rinsed well, dries, the coloured enamel liquid of brushing formula 2
After coating surface figure as in figure 2 it is shown, then brushing formula 2 coloured enamel liquid after, be sprinkled on surface formula 2 paint liquid quality
The 20 mesh stone flours of 50%, coating surface figure is as shown in Figure 3.
As seen from Figure 3, the stone flour in particle mesh number 20 is employed, it is contemplated that effect during following cutting polishing.
Stone flour is to obtain after stone pulverizing after making in advance obtains stone, can continue to use as colored solid fragment
In making stone.
4. use formula 3 coloured enamel liquid brushing, after dry solidification, be polishing to the paint film after sub-light as shown in Figure 4, brushing
After 10 layers, obtaining the thick paint film of about 1mm, now separating the stone obtaining and cut tomography, tomography is as shown in Figure 5
5., after according to 100 layers of paint film of step 2～3 preparation, separate with base material, prepare the stone of thickness 1cm, such as Fig. 6
Shown in.
6. the cutting technique for grinding with craft or machine makes jewel again.
7. the spall obtaining after stone cutting can obtain stone flour after pulverizing, and is sprinkled into paint as colored solid fragment
Liquid surface, continues on for making stone
The performance detection of the stone preparing is as follows：The Mohs' hardness of stone is 3-4, higher than the amber in organic gemstone
(2.5).Stone is insoluble in strong solvents such as ketone, lipid, benzene class, alcohols, ethers, and acid-fast alkali-proof is anticorrosive.Resistance to elevated temperatures is excellent
Show, can under the conditions of 150 DEG C Long-Time Service, be resistant to 250 DEG C of hot environments of moment.It is difficult under 686.42Pa frictional force effect
Damage.Anti-electric breakdown strength reaches 50～80KV/mm, has extremely strong electrical insulation capability.
Embodiment 2
Step 1 is with embodiment 1.
In step 2, coloured enamel formula of liquid is
Formula 1：?：Orpiment：Tung oil mass ratio=1:1.5:0.2
Formula 2：?：Phthalocyanine blue：Turpentine oil：50 mesh egg-shell meal=1:0.1:1：0.1
Formula 3：?：Pine soot：Quality of gasoline ratio=1:0.1:0.01
Formula 4：?：Carbon black：Camphorated oil=1：0.3：0.8
Formula 5：?：Cu-Zn alloy powder：Banana oil=1：0.9：1.2
Formula 6：?：Aluminium silver powder：Tung oil mass ratio=1:0.5:0.2
Formula 7：?：Titanium white：Turpentine oil=1:0.3:0.5
Formula 8：?：Germanite：Gasoline：Stone flour=1:0.4:0.2：1
Formula 9：?：Dark grey：Tung oil：Camphorated oil：40 mesh pearl powder=1：0.2：0.4：0.6
Formula 10：?：Ultramarine：Turpentine oil=1：0.9：1.2
Prepare paint film, every layer of paint film 0.3mm according to step 2-3 of embodiment 1, prepare 100 layers, obtain thickness 3cm's
Stone.
Claims (10)
1. the preparation method of a stone, it is characterised in that said method comprising the steps of：
(1) being formulated with colored paint liquid, the formula of described coloured enamel liquid is：, coloured powder, can the mass ratio of drying oil be 1：0.1
～1.5：0.01～1.2；
Described for lacquer；
Described coloured powder is vermilion, pellet is red, minium, germanite, cadmium red, alum are red, toluidine red, orpiment, lead chromate yellow, iron oxide yellow, cadmium
The husky Huang of yellow, the Chinese, azurite, ultramarine, indigo, phthalocyanine blue, barba hispanica, Chinese blue, Prussian blue, titanium white, lithopone, bismoclite, malachite green,
Chrome oxide green, chrome green, phthalocyanine green, pine soot, carbon black, iron oxide black, dark grey, Cu-Zn alloy powder, one or more mixed in aluminium silver powder
Close；
Described can drying oil be tung oil, turpentine oil, camphorated oil, banana oil, one or more the mixing in gasoline；
Use different coloured powders, prepare the coloured enamel liquid of two or more different colours；
(2) take coloured enamel liquid on base material, carry out the individual layer brushing of monochrome or polychrome, after brushing 20～25 DEG C, 85～95%
Under relative humidity, after standing and drying solidification, obtain the ground floor paint film of 0.01mm-1mm thickness；Described base material is smooth plastics
Class or glass plate；Or on flat board, cover one layer of preservative film as base material；
(3) ground floor paint film is polished, be polishing to paint film dumb light；After polishing, clear water is rinsed well, is dried；
(4) repeat on the ground floor paint film after polishing step (2), (3) 1～1000 times, prepare 0.02～
Multi-layer paint films is separated by the multi-layer paint films of 1000mm thickness with base material, i.e. prepares stone.
2. the method for claim 1, it is characterised in that described stone is made with the cutting technique for grinding of craft or machine
The stone artwork of all kinds of shapes or stone daily necessities.
3. the method for claim 1, it is characterised in that in described step (2), the individual layer brushing of described polychrome is by not
With the coloured enamel liquid brushing of color at same layer, may be constructed different patterns or shape.
4. the method for claim 1, it is characterised in that in described step (2), the individual layer of underway monochrome or polychrome
During brushing, being sprinkled into colored solid fragment in painting process, described colored solid fragment is the natural gemstone after pulverizing, natural jade
One or more mixed in stone, natural color stone, natural organic gemstone, metal material, pottery, coloured glaze, eggshell, stone flour
Close；Described colored solid fragment is between 4 mesh-100 mesh.
5. method as claimed in claim 4, it is characterised in that the addition of described colored solid fragment is coloured enamel liquid quality
0.1～80%.
6. the method for claim 1, it is characterised in that in described step (3), described polishing uses gauze, sand paper, hangs
Mill or all kinds of instrument of platform mill are polished.
7. the method for claim 1, it is characterised in that in described step (4), each layer paint film of adjacent two layers is used
Coloured enamel liquid color different.
8. the method for claim 1, it is characterised in that in described step (4), multi-layer paint films separates with base material, described base
When material is the flat board being coated with preservative film, directly multi-layer paint films is torn；When described base material is smooth glass or plastic board,
Use hot and cold water alternately repeatedly to soak, multi-layer paint films can be peeled off with base material.
9. the stone that prepared by the method as described in one of claim 1～8, described stone is laminated by 2～1000 layers of coloured paint film
Composition, the thickness of every layer of coloured paint film is 0.01mm-1mm.
10. stone as claimed in claim 9, it is characterised in that described stone is made up of 10～500 layers of coloured paint film stacking, often
The thickness of the coloured paint film of layer is 0.01mm-0.5mm, and the thickness of described stone is 1～100mm.