CN106400148A - 阻燃性能好的粘胶面料 - Google Patents
阻燃性能好的粘胶面料 Download PDFInfo
- Publication number
- CN106400148A CN106400148A CN201611006614.6A CN201611006614A CN106400148A CN 106400148 A CN106400148 A CN 106400148A CN 201611006614 A CN201611006614 A CN 201611006614A CN 106400148 A CN106400148 A CN 106400148A
- Authority
- CN
- China
- Prior art keywords
- fabric
- viscose
- fire resistance
- good
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了阻燃性能好的粘胶面料,所述的面料由粘胶纤维纺织而成,所述的粘胶纤维经过以下方法制备:a)前处理工序;b)纺丝工序;c)后处理工序;本发明与现有技术相比,面料所用的粘纤纤维的极限氧指数为28‑29%,干伸长为16.5‑17%,湿伸长为20‑22%。
Description
技术领域
本发明属于粘胶面料,特别属于阻燃的粘胶面料。
背景技术
粘胶面料是由粘胶纤维纺织而成,粘胶纤维是一种机械性能优良,穿着舒适的再生纤维素纤维,其性质与棉纤维相似,尤其适用于气候炎热的地区穿着,我国是粘胶纤维的生产大国,但粘胶纤维最大的缺点是易燃,粘胶纤维的极限氧指数(LOI)小于19%,极容易引起火灾。
发明内容
本发明所要解决的技术问题是提供一种极限氧指数大于25%的阻燃的粘胶面料。
本发明解决技术问题的技术方案为:阻燃性能好的粘胶面料,所述的面料由粘胶纤维纺织而成,所述的粘胶纤维经过以下方法制备:
a)前处理工序;b)纺丝工序;c)后处理工序;
所述的b)纺丝工序为:在前处理溶液中加入阻燃溶液,经喷丝孔喷入到凝固浴中,进行凝固纺丝;
所述的阻燃溶液由以下重量份的物质组成:
1,2,3-三(5,5-二甲基-1,3-二氧杂环己内磷酰氧基)苯占纤维素的质量分数为16-18%。
所述的焦磷酸酯类阻燃剂的型号为NLD-02。
所述的表面活性剂为YM312,由上海雨木化工有限公司生产。
所述的凝固液包括以下物质:硫酸130-140克/升、硫酸钠250-280克/升、硫酸锌10-15克/升。
所述的a)前处理工序为将粘胶原液(纤维素质量分数为8-9%)过滤、脱泡,形成前处理溶液;
所述的c)后处理工序为将纺丝工序纺好的丝进行洗涤、脱硫、漂白、酸洗、上油、脱水、烘干、给湿、络丝。
本发明与现有技术相比,面料所用的粘胶纤维的极限氧指数为28-29%,干伸长为16.5-17%,湿伸长为20-22%。
具体实施方式
下面结合实施例对本发明作详细的说明。
实施例1:
阻燃性能好的粘胶面料,所述的面料由粘胶纤维纺织而成,所述的粘胶纤维经过以下方法制备:
a)前处理工序;粘胶原液(纤维素质量分数为9%)过滤、脱泡,形成前处理溶液;
b)纺丝工序;
所述的b)纺丝工序为:在前处理溶液中加入阻燃溶液,经喷丝孔喷入到凝固浴中,进行凝固纺丝;
所述的阻燃溶液由以下重量份的物质组成:
所述的表面活性剂为YM312,由上海雨木化工有限公司生产。
1,2,3-三(5,5-二甲基-1,3-二氧杂环己内磷酰氧基)苯占纤维素的质量分数为16%。
阻燃溶液使用前用胶体磨研磨48小时,使阻燃剂溶液的粒度小于2μm,阻燃溶液的粒度直接影响了阻燃的效果,不同的分散剂及表面活性剂直接影响阻燃溶液的研磨的粒度。
所述的凝固液包括以下物质:硫酸130克/升、硫酸钠250克/升、硫酸锌10克/升。
c)后处理工序:将纺丝工序纺好的丝进行洗涤、脱硫、漂白、酸洗、上油、脱水、烘干、给湿、络丝。
实施例2:
阻燃的粘胶面料,所述的面料由粘胶纤维纺织而成,所述的粘胶纤维经过以下方法制备:
a)前处理工序;胶原溶液(纤维素质量分数为9%)过滤、脱泡,形成前处理溶液;
b)纺丝工序;
所述的b)纺丝工序为:在前处理溶液中加入阻燃溶液,经喷丝孔喷入到凝固浴中,进行凝固纺丝;
所述的阻燃溶液由以下重量份的物质组成:
所述的表面活性剂为YM312,由上海雨木化工有限公司生产。
1,2,3-三(5,5-二甲基-1,3-二氧杂环己内磷酰氧基)苯占纤维素的质量分数为17%。
所述的凝固液包括以下物质:硫酸135克/升、硫酸钠260克/升、硫酸锌11克/升。
c)后处理工序:将纺丝工序纺好的丝进行洗涤、脱硫、漂白、酸洗、上油、脱水、烘干、给湿、络丝。
实施例3:
阻燃性能好的粘胶面料,所述的面料由粘胶纤维纺织而成,所述的粘胶纤维经过以下方法制备:
a)前处理工序;将粘胶原液(纤维素质量分数为9%)溶液过滤、脱泡,形成前处理溶液;
b)纺丝工序;
所述的b)纺丝工序为:在前处理溶液中加入阻燃溶液,经喷丝孔喷入到凝固浴中,进行凝固纺丝;
所述的阻燃溶液由以下重量份的物质组成:
所述的表面活性剂为YM312,由上海雨木化工有限公司生产。
1,2,3-三(5,5-二甲基-1,3-二氧杂环己内磷酰氧基)苯占纤维素的质量分数为18%。
所述的凝固液包括以下物质:硫酸140克/升、硫酸钠280克/升、硫酸锌15克/升。
c)后处理工序:将纺丝工序纺好的丝进行洗涤、脱硫、漂白、酸洗、上油、脱水、烘干、给湿、络丝。
本发明的极限氧指数于YG813氧指数测量仪上测量。
纤维的力学性能于单纤维电子强力仪上测量:
极限氧指数(%) | 干伸长(%) | 湿伸长(%) | |
实施例1 | 28.5 | 16.5 | 21.3 |
实施例2 | 28.3 | 16.8 | 20.7 |
实施例3 | 28.9 | 16.6 | 21.8 |
Claims (7)
1.阻燃性能好的粘胶面料,所述的面料由粘胶纤维纺织而成,所述的粘胶纤维经过以下方法制备:
a)前处理工序;b)纺丝工序;c)后处理工序;
所述的b)纺丝工序为:在前处理溶液中加入阻燃溶液,经喷丝孔喷入到凝固浴中,进行凝固纺丝。
2.根据权利要求1所述的阻燃性能好的粘胶面料,其特征在于:
所述的阻燃溶液由以下重量份的物质组成:
1,2,3-三(5,5-二甲基-1,3-二氧杂环己内磷酰氧基)苯占纤维素的质量分数为18%。
3.根据权利要求2所述的阻燃性能好的粘胶面料,其特征在于:所述的焦磷酸酯类阻燃剂的型号为NLD-02。
4.根据权利要求2所述的阻燃性能好的粘胶面料,其特征在于:所述的表面活性剂为YM312。
5.根据权利要求1所述的阻燃性能好的粘胶面料,其特征在于:
所述的凝固液包括以下物质:硫酸130-140克/升、硫酸钠250-280克/升、硫酸锌10-15克/升。
6.根据权利要求1所述的阻燃性能好的粘胶面料,其特征在于:
所述的a)前处理工序为将纤维素质量分数为8-9%的粘胶原液过滤、脱泡,形成前处理溶液。
7.根据权利要求1所述的阻燃性能好的粘胶面料,其特征在于:
所述的c)后处理工序为将纺丝工序纺好的丝进行洗涤、脱硫、漂白、酸洗、上油、脱水、烘干、给湿、络丝。