CN106398846A - Plastic gear lubricating grease - Google Patents
Plastic gear lubricating grease Download PDFInfo
- Publication number
- CN106398846A CN106398846A CN201610722222.3A CN201610722222A CN106398846A CN 106398846 A CN106398846 A CN 106398846A CN 201610722222 A CN201610722222 A CN 201610722222A CN 106398846 A CN106398846 A CN 106398846A
- Authority
- CN
- China
- Prior art keywords
- plastic gear
- parts
- essence
- gear grease
- diethanolamine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to plastic gear lubricating grease including the following components by mass: 30-40 parts of chlorinated paraffin, 3-5 parts of diethanolamine, 3-6 parts of polyisobutenyl succinimide, 7-10 parts of an inorganic thickener, 50-70 parts of absolute ethanol, 3-5 parts of essence, 5-9 parts of T202 and 2-6 parts of aluminium isopropoxide. The plastic gear lubricating grease is prepared by an advanced biotechnology, is high performance grease used in plastic gears and metal sliding parts, contains a special polymer to achieve excellent sound attenuation properties, is suitable for the plastic gears of office equipment, has sound attenuation, noise reduction, lubrication and resistance reduction effects, and is high-temperature-resistant, high-viscosity, durable and efficient, and oil is not easy to run.
Description
Technical field
A kind of a kind of the present invention relates to lubriation material, in particular it relates to plastic gear grease.
Background technology
Grease is to solve in the state of equipment produces centrifugal force in the running, to need for reducing equipment fretting wear
A kind of lubriation material.
Compared with lubricating oil, due to using due to being more prone to, being widely applied to lubricate all kinds of industrial machines
Lubrication portion.
Current universal phenomenon is to be used with domestic high temperature grease, frequent shutdown, oiling, and impact is normal to be produced, and wastes the energy, pollution
Environment, high labor intensive, equipment maintenance cost is high.A part of enterprise imported product(1275 fat of such as U.S. LE company),
Expensive, the haul-cycle time is long, and cost is high.
Content of the invention
For deficiency above-mentioned present in prior art, the technical problem to be solved is to provide a kind of maintenance effect
Really good plastic gear grease.
The technical solution adopted for the present invention to solve the technical problems is:There is provided a kind of plastic gear grease, including chlorine
Fossil waxes, diethanolamine, polyisobutylene succinamide, inorganic thickening agent, dehydrated alcohol, essence, sulfur phosphorus fourth octyl group zinc salt,
Aluminum isopropylate., the mass fraction of each component is:Chlorinated paraffin 30-40, diethanolamine 3-5, polyisobutylene succinamide 3-
6th, inorganic thickening agent 7-10, dehydrated alcohol 50-70, essence 3-5, sulfur phosphorus fourth octyl group zinc salt 5-9, aluminum isopropylate. 2-6.
Preferably, described plastic gear grease also includes chlorinated paraffin 40, diethanolamine 3, polyisobutenyl fourth two
Acid imide 4, inorganic thickening agent 9, dehydrated alcohol 55, essence 4, sulfur phosphorus fourth octyl group zinc salt 5, aluminum isopropylate. 5.
Preferably, described aluminum isopropylate. is dissolved in the aluminium hydroxide of alcohol.
Preferably, described essence is preferably Fructus Citri Limoniae essence, improve plastic gear grease taste.
Preferably, described inorganic thickening agent is amination bentonite.
A kind of plastic gear preparation of greases method as described above, it comprises the steps:
Described chlorinated paraffin, amination bentonite and dehydrated alcohol are added in reactive tank and is stirred with 400-600 rev/min of speed
Mix, add diethanolamine, polyisobutylene succinamide, sulfur phosphorus fourth octyl group zinc salt, aluminum isopropylate. stirring 20-60 minute
Afterwards, Fructus Citri Limoniae essence, 300-500 rev/min of speed stirring of speed governing are added, after one hour to one and a half hours, standing completes cream-coloured moulding
Material gear grease finished product.
Claims (6)
1. a kind of plastic gear grease it is characterised in that:Sub- including chlorinated paraffin, diethanolamine, polyisobutenyl succinyl
Amine, inorganic thickening agent, dehydrated alcohol, essence, sulfur phosphorus fourth octyl group zinc salt, aluminum isopropylate., the mass fraction of each component is:Chlorination stone
Wax 30-40, diethanolamine 3-5, polyisobutylene succinamide 3-6, inorganic thickening agent 7-10, dehydrated alcohol 50-70, essence
3-5, sulfur phosphorus fourth octyl group zinc salt 5-9, aluminum isopropylate. 2-6.
2. plastic gear grease according to claim 1 it is characterised in that:Described plastic gear grease also includes chlorine
Fossil waxes 40, diethanolamine 3, polyisobutylene succinamide 4, inorganic thickening agent 9, dehydrated alcohol 55, essence 4, sulfur phosphorus fourth
Octyl group zinc salt 5, aluminum isopropylate. 5.
3. plastic gear grease according to claim 2 it is characterised in that:Described aluminum isopropylate. is dissolved in the hydrogen-oxygen of alcohol
Change aluminum.
4. plastic gear grease according to claim 2 it is characterised in that:Described essence is preferably Fructus Citri Limoniae essence, changes
Kind plastic gear grease taste.
5. plastic gear grease according to claim 2 it is characterised in that:Described inorganic thickening agent is amination swelling
Soil.
6. a kind of described plastic gear preparation of greases method as arbitrary in claim 1-5, it comprises the steps:
Described chlorinated paraffin, amination bentonite and dehydrated alcohol are added in reactive tank and is stirred with 400-600 rev/min of speed
Mix, add diethanolamine, polyisobutylene succinamide, sulfur phosphorus fourth octyl group zinc salt, aluminum isopropylate. stirring 20-60 minute
Afterwards, Fructus Citri Limoniae essence, 300-500 rev/min of speed stirring of speed governing are added, after one hour to one and a half hours, standing completes cream-coloured moulding
Material gear grease finished product.