CN106398481A - Oil contamination-preventing paint for frame of electric appliance - Google Patents
Oil contamination-preventing paint for frame of electric appliance Download PDFInfo
- Publication number
- CN106398481A CN106398481A CN201610376973.4A CN201610376973A CN106398481A CN 106398481 A CN106398481 A CN 106398481A CN 201610376973 A CN201610376973 A CN 201610376973A CN 106398481 A CN106398481 A CN 106398481A
- Authority
- CN
- China
- Prior art keywords
- parts
- barium
- iron oxide
- polyester resin
- precipitation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an oil contamination-preventing paint for a frame of an electric appliance. The oil contamination-preventing paint comprises, by weight, 125.56 to 127.56 parts of epoxy resin E-12, 187 to 189 parts of polyester resin, 5 to 6 parts of a leveling agent, 5 to 6 parts of a brightening agent, 2.15 to 2.35 parts of benzoin, 3 to 3.4 parts of sumatriptan, 74.04 to 76.04 parts of precipitated barium sulfate, 89.05 to 91.05 part of titanium dioxide, 44.02 to 46.02 parts of high-light barium sulfate, 0.12 to 0.32 part of black, 0.018 to 0.020 part of iron oxide red, 0.48 to 0.50 part of iron oxide yellow, 0.01 to 0.03 part of ultramarine and 0.05 to 0.07 part of color black. The paint provided by the invention has strong bonding force on the frame of the electric appliance, enables the frame not to prone to tarnishing and shedding, and has good oil contamination resistance and aging resistance.
Description
Technical field
The present invention relates to chemical field, particularly to a kind of electrical equipment frame oil-stain-preventing paint.
Background technology
Because electrical equipment frame can not often clean, of long duration greasy dirt situation occurs, market low-quality goods occurs and paints for the attainment of one's purpose, employ chemical composition against regulation in a large number and participate.Electrical equipment frame mainly can be made good in dark moist local time long non-corrosive, acidproof, alkali resistance, oil-stain-preventing performance.
Content of the invention
For the deficiencies in the prior art, it is an object of the invention to provide a kind of electrical equipment frame oil-stain-preventing paint, good cleaning, cohesive force is strong, has oil-stain-preventing effect moreover it is possible to extend the life-span.
Technical scheme is as follows：
A kind of electrical equipment frame oil-stain-preventing paint, is made up of following component in parts by weight：E-12 epoxy resin 125.56-127.56 part, polyester resin 187-189 part, levelling agent 5-6 part, brightener 5-6 part, styrax 2.15-2.35 part, cured powder 3-3.4 part, precipitation barium 74.04-76.04 part, titanium dioxide 89.05-91.05 part, bloom barium 44.02-46.02 part, mineral black 0.12-0.32 part, iron oxide red pigment 0.018-0.020 part, iron oxide yellow pigments 0.48-0.50 part, ultramarine 0.01-0.03 part, colour carbon black 0.05-0.07 part；Its preparation method comprises the steps：
（1）Precipitation barium, cured powder, titanium dioxide, precipitation barium, bloom barium, colour carbon black are mixed rear 120-150 DEG C of process 0.5-0.8h, grinds to form superfine powder after cooling, obtain mixed powder, standby；
（2）E-12 epoxy resin, polyester resin, SJ5#C polyester resin are mixed with styrax, 1200-1600rpm stirs 8-12min, at 350-450 DEG C, calcine 0.5-0.7h, after cooling, add brightener, levelling agent, 1500-1800rpm stirs 15-22min, standby；
（3）By step（1）、（2）In the product that obtains and other surplus stocks mix, stir, be again heated to 85-95 DEG C of stirring 25-35min, drop to normal temperature and pour out, you can.
A kind of electrical equipment frame oil-stain-preventing paint, is composed of the following components in parts by weight：126.56 parts of E-12 epoxy resin, 187.6 parts of polyester resin, 5.5 parts of levelling agent, 5.5 parts of brightener, 2.25 parts of styrax, 3.25 parts of cured powder, 75.04 parts of barium of precipitation, 90.05 parts of titanium dioxide, 45.02 parts of bloom barium, 0.22 part of mineral black, 0.019 part of iron oxide red pigment, 0.49 part of iron oxide yellow pigments, 0.02 part of ultramarine, 0.06 part of colour carbon black.
Compared with prior art, the present invention has the advantages that：
Whitewashing in the present invention washing away through the highly corrosive industrial chemicals of 1.5 months in electrical equipment frame, still complete be set in electrical equipment frame, this formula paint is suitable for using in adverse circumstances such as countrysides.Paint is used in cohesive force in electrical equipment frame and by force, is difficult to get rusty and comes off, and good to oil-stain-preventing, ageing-resistant performance.
Specific embodiment
A kind of electrical equipment frame oil-stain-preventing paint, is composed of the following components in parts by weight：126.56 parts of E-12 epoxy resin, 187.6 parts of polyester resin, 5.5 parts of levelling agent, 5.5 parts of brightener, 2.25 parts of styrax, 3.25 parts of cured powder, 75.04 parts of barium of precipitation, 90.05 parts of titanium dioxide, 45.02 parts of bloom barium, 0.22 part of mineral black, 0.019 part of iron oxide red pigment, 0.49 part of iron oxide yellow pigments, 0.02 part of ultramarine, 0.06 part of colour carbon black；Its preparation method comprises the steps：
（1）Precipitation barium, cured powder, titanium dioxide, precipitation barium, bloom barium, colour carbon black are mixed rear 120-150 DEG C of process 0.5-0.8h, grinds to form superfine powder after cooling, obtain mixed powder, standby；
（2）E-12 epoxy resin, polyester resin, SJ5#C polyester resin are mixed with styrax, 1200-1600rpm stirs 8-12min, at 350-450 DEG C, calcine 0.5-0.7h, after cooling, add brightener, levelling agent, 1500-1800rpm stirs 15-22min, standby；
（3）By step（1）、（2）In the product that obtains and other surplus stocks mix, stir, be again heated to 85-95 DEG C of stirring 25-35min, drop to normal temperature and pour out, you can.
Claims (2)
1. a kind of electrical equipment frame oil-stain-preventing paints it is characterised in that being made up of following component in parts by weight：E-12 epoxy resin 125.56-127.56 part, polyester resin 187-189 part, levelling agent 5-6 part, brightener 5-6 part, styrax 2.15-2.35 part, cured powder 3-3.4 part, precipitation barium 74.04-76.04 part, titanium dioxide 89.05-91.05 part, bloom barium 44.02-46.02 part, mineral black 0.12-0.32 part, iron oxide red pigment 0.018-0.020 part, iron oxide yellow pigments 0.48-0.50 part, ultramarine 0.01-0.03 part, colour carbon black 0.05-0.07 part；Its preparation method comprises the steps：
（1）Precipitation barium, cured powder, titanium dioxide, precipitation barium, bloom barium, colour carbon black are mixed rear 120-150 DEG C of process 0.5-0.8h, grinds to form superfine powder after cooling, obtain mixed powder, standby；
（2）E-12 epoxy resin, polyester resin, SJ5#C polyester resin are mixed with styrax, 1200-1600rpm stirs 8-12min, at 350-450 DEG C, calcine 0.5-0.7h, after cooling, add brightener, levelling agent, 1500-1800rpm stirs 15-22min, standby；
（3）By step（1）、（2）In the product that obtains and other surplus stocks mix, stir, be again heated to 85-95 DEG C of stirring 25-35min, drop to normal temperature and pour out, you can.
2. electrical equipment frame oil-stain-preventing according to claim 1 paints it is characterised in that being composed of the following components in parts by weight：126.56 parts of E-12 epoxy resin, 187.6 parts of polyester resin, 5.5 parts of levelling agent, 5.5 parts of brightener, 2.25 parts of styrax, 3.25 parts of cured powder, 75.04 parts of barium of precipitation, 90.05 parts of titanium dioxide, 45.02 parts of bloom barium, 0.22 part of mineral black, 0.019 part of iron oxide red pigment, 0.49 part of iron oxide yellow pigments, 0.02 part of ultramarine, 0.06 part of colour carbon black.