CN106398402A - Corrosion-resistant marine paint - Google Patents
Corrosion-resistant marine paint Download PDFInfo
- Publication number
- CN106398402A CN106398402A CN201510487347.8A CN201510487347A CN106398402A CN 106398402 A CN106398402 A CN 106398402A CN 201510487347 A CN201510487347 A CN 201510487347A CN 106398402 A CN106398402 A CN 106398402A
- Authority
- CN
- China
- Prior art keywords
- parts
- marine paint
- corrosion
- base
- organobentonite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of marine paint and particularly discloses corrosion-resistant marine paint. The corrosion-resistant marine paint contains the following ingredients in parts by mass: 3-11 parts of polymerized o-p-toluidine, 15-23 parts of organobentonite, 3.5-5.6 parts of keto-aldehyde resin, 1.8-3.2 parts of polytrifluorochloroethylene, 5-14 parts of hydrogenated nitrile-butadiene rubber, 12-18 parts of dialkenyl diimide, 4.8-6.5 parts of alkylsuccinate imide and 4-10 parts of glass micro-beads. By adopting the formula, the corrosion-resistant marine paint disclosed by the invention has excellent hydrophobic and lipophobic properties, antifouling property and corrosion resistance, is not prone to marine-organism attachment and is applicable to marine operating environments; and furthermore, the ingredients of the corrosion-resistant marine paint are low in cost, so that popularization and application are facilitated.
Description
Technical field
The present invention relates to marine paint technical field, particularly a kind of anticorrosive marine paint.
Background technology
For ship and each position of ocean engineering structure, meet and prevent sea water, sea atmosphere corrosion and ocean life
The general designation of the coating of thing attachment and other particular/special requirements.Marine paint is ship priming paint, ship bottom anticorrosion paint, ship
Bottom anti-fouling paint, marine paint for boot toppings series, shell and superstructure paint, various ships cabin paint ballast
A series of paint composition such as water tank paint, oil tank paint, drinking water tank paint, dry cargo hold paint.
Content of the invention
The technical problem to be solved in the invention is to provide a kind of anticorrosive marine paint.
For solving above-mentioned technical problem, a kind of anticorrosive marine paint of the present invention, according to mass fraction meter bag
Include following components：Polymerization adjacency pair base toluidines 3-11 part, organobentonite 15-23 part, aldehyde ketone resin 3.5-5.6
Part, polytrifluorochloroethylene 1.8-3.2 part, hydrogenate nitrile rubber 5-14 part, diene base imidodicarbonic diamide 12-18
Part, alkyl acid imide 4.8-6.5 part, glass microballoon 4-10 part.
Further, include following components according to mass fraction meter：3 parts of adjacency pair base toluidines of polymerization, organic bentonite
15 parts of profit soil, 3.5 parts of aldehyde ketone resin, 1.8 parts of polytrifluorochloroethylene, hydrogenate 5 parts of nitrile rubber, diene
12 parts of base imidodicarbonic diamide, 4.8 parts of alkyl acid imide, 4 parts of glass microballoon.
Further, include following components according to mass fraction meter：11 parts of adjacency pair base toluidines of polymerization, organic
23 parts of bentonite, 5.6 parts of aldehyde ketone resin, 3.2 parts of polytrifluorochloroethylene, hydrogenate 14 parts of nitrile rubber,
18 parts of diene base imidodicarbonic diamide, 6.5 parts of alkyl acid imide, 10 parts of glass microballoon.
Further, include following components according to mass fraction meter：8 parts of adjacency pair base toluidines of polymerization, organic bentonite
20 parts of profit soil, 4.3 parts of aldehyde ketone resin, 2.3 parts of polytrifluorochloroethylene, hydrogenate 8 parts of nitrile rubber, diene
13 parts of base imidodicarbonic diamide, 5.4 parts of alkyl acid imide, 6 parts of glass microballoon.
Further, include following components according to mass fraction meter：9 parts of adjacency pair base toluidines of polymerization, organic bentonite
22 parts of profit soil, 4.9 parts of aldehyde ketone resin, 2.5 parts of polytrifluorochloroethylene, hydrogenate 12 parts of nitrile rubber, double
15 parts of thiazolinyl imidodicarbonic diamide, 6.2 parts of alkyl acid imide, 9 parts of glass microballoon.
After above-mentioned formula, the anticorrosive marine paint of the present invention, there is excellent hydrophobic and lyophobic property, antifouling
Property and corrosion resistance, marine organisms are difficult to adhere to, and are suitable to the use environment of ship；In addition, present component
Low cost, easy to utilize.
Specific embodiment
A kind of anticorrosive marine paint of the present invention, includes following components according to mass fraction meter：Polymerization adjacency pair base
Toluidines 3-11 part, organobentonite 15-23 part, aldehyde ketone resin 3.5-5.6 part, polytrifluorochloroethylene
1.8-3.2 part, hydrogenates nitrile rubber 5-14 part, diene base imidodicarbonic diamide 12-18 part, alkyl succinic acid acyl
Imines 4.8-6.5 part, glass microballoon 4-10 part.
Embodiment one：
Include following components according to mass fraction meter：3 parts of adjacency pair base toluidines of polymerization, 15 parts of organobentonite,
3.5 parts of aldehyde ketone resin, 1.8 parts of polytrifluorochloroethylene, hydrogenate 5 parts of nitrile rubber, diene base imidodicarbonic diamide
12 parts, 4.8 parts of alkyl acid imide, 4 parts of glass microballoon.
Embodiment two：
Include following components according to mass fraction meter：11 parts of adjacency pair base toluidines of polymerization, 23 parts of organobentonite,
5.6 parts of aldehyde ketone resin, 3.2 parts of polytrifluorochloroethylene, hydrogenate 14 parts of nitrile rubber, diene base imidodicarbonic diamide
18 parts, 6.5 parts of alkyl acid imide, 10 parts of glass microballoon.
Embodiment three：
Include following components according to mass fraction meter：8 parts of adjacency pair base toluidines of polymerization, 20 parts of organobentonite,
4.3 parts of aldehyde ketone resin, 2.3 parts of polytrifluorochloroethylene, hydrogenate 8 parts of nitrile rubber, diene base imidodicarbonic diamide
13 parts, 5.4 parts of alkyl acid imide, 6 parts of glass microballoon.
Embodiment four：
Include following components according to mass fraction meter：9 parts of adjacency pair base toluidines of polymerization, 22 parts of organobentonite,
4.9 parts of aldehyde ketone resin, 2.5 parts of polytrifluorochloroethylene, hydrogenate 12 parts of nitrile rubber, diene base imidodicarbonic diamide
15 parts, 6.2 parts of alkyl acid imide, 9 parts of glass microballoon.
Although the foregoing describing the specific embodiment of the present invention, those skilled in the art should manage
Solution, these are merely illustrative of, and can make various changes or modifications to present embodiment, without departing from send out
Bright principle and essence, protection scope of the present invention is only limited by the claims that follow.
Claims (5)
1. a kind of anticorrosive marine paint is it is characterised in that include following components according to mass fraction meter：Polymerization is adjacent
To base toluidines 3-11 part, organobentonite 15-23 part, aldehyde ketone resin 3.5-5.6 part, poly- trifluoro chloroethene
Alkene 1.8-3.2 part, hydrogenates nitrile rubber 5-14 part, diene base imidodicarbonic diamide 12-18 part, alkyl succinic acid
Acid imide 4.8-6.5 part, glass microballoon 4-10 part.
2. according to a kind of anticorrosive marine paint described in claim 1 it is characterised in that according to mass fraction meter
Including following components：3 parts of adjacency pair base toluidines of polymerization, 15 parts of organobentonite, 3.5 parts of aldehyde ketone resin,
1.8 parts of polytrifluorochloroethylene, hydrogenates 5 parts of nitrile rubber, 12 parts of diene base imidodicarbonic diamide, alkyl succinic acid
4.8 parts of acid imide, 4 parts of glass microballoon.
3. according to a kind of anticorrosive marine paint described in claim 1 it is characterised in that according to mass fraction meter
Including following components：11 parts of adjacency pair base toluidines of polymerization, 23 parts of organobentonite, 5.6 parts of aldehyde ketone resin,
3.2 parts of polytrifluorochloroethylene, hydrogenates 14 parts of nitrile rubber, 18 parts of diene base imidodicarbonic diamide, alkyl
6.5 parts of acid imide, 10 parts of glass microballoon.
4. according to a kind of anticorrosive marine paint described in claim 1 it is characterised in that according to mass fraction meter
Including following components：8 parts of adjacency pair base toluidines of polymerization, 20 parts of organobentonite, 4.3 parts of aldehyde ketone resin,
2.3 parts of polytrifluorochloroethylene, hydrogenates 8 parts of nitrile rubber, 13 parts of diene base imidodicarbonic diamide, alkyl succinic acid
5.4 parts of acid imide, 6 parts of glass microballoon.
5. according to a kind of anticorrosive marine paint described in claim 1 it is characterised in that according to mass fraction meter
Including following components：9 parts of adjacency pair base toluidines of polymerization, 22 parts of organobentonite, 4.9 parts of aldehyde ketone resin,
2.5 parts of polytrifluorochloroethylene, hydrogenates 12 parts of nitrile rubber, 15 parts of diene base imidodicarbonic diamide, alkyl
6.2 parts of acid imide, 9 parts of glass microballoon.