CN106396316A - Sludge curing agent as well as preparation method and use method thereof - Google Patents
Sludge curing agent as well as preparation method and use method thereof Download PDFInfo
- Publication number
- CN106396316A CN106396316A CN201611102162.1A CN201611102162A CN106396316A CN 106396316 A CN106396316 A CN 106396316A CN 201611102162 A CN201611102162 A CN 201611102162A CN 106396316 A CN106396316 A CN 106396316A
- Authority
- CN
- China
- Prior art keywords
- mud
- sludge
- solid
- calcium oxide
- composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a sludge curing agent as well as a preparation method and a use method thereof. The sludge curing agent comprises a liquid composition and a solid composition, wherein the dosage of the liquid composition accounts for 1-6% of the dosage of sludge; the dosage of the solid composition accounts for 1-6% of the dosage of sludge. The sludge curing agent provided by the invention can reduce the sludge water content from 75-85% to 45-60% via the synergistic effect of chemical modification and mechanical dehydration, reduces sludge size, lowers the transportation cost, and facilitates the disposal of the sludge in the later stage; toxic and side products cannot be introduced or generated in sludge dehydration-conditioning and dehydration processes in the invention, to avoid environmental pollution.
Description
Technical field
The present invention relates to technical field of sludge treatment, specifically disclose a kind of sludge solidifying agent and preparation method thereof and use
Method.
Background technology
Operation with large amount of sewage treatment plant runs, and sludge yield will significantly increase.According to the literature, 2011
China's total amount of sewage discharge reaches 482.4 hundred million tons, produces 8,470,000 tons of excess sludge (dry mass), and the remaining dirt discharged every year
Mud amount is with average annual about 10% speed increase.In addition, the Organic substance in biological wastewater treatment process, in micropopulation and sewage
Contact, picked-up organism in water decompose composition carry out growth and breeding, in this process hypertrophy glue plumage formed bacterium can with from status
Remaining suspension solid in the extracellular polymeric secreted, aqueous phase, filamentous bacteria, funguses, protozoacide and divalent calcium, magnesium ion, altogether
With assembling the mud glue plumage connecting to about hundreds of microns of size, its short texture, moisture content is high, and has huge surface area and height
Degree hydrophilic, with combining water in a large number, leads to Treatment of Sludge difficulty to increase.Therefore, the process of mud is examined with disposing day by day to become
Core sewage treatment plant runs the important indicator of performance.
Moisture in mud is divided into four kinds by its state:1) Interstitial Water, Interstitial Water is the free water that mud granule surrounds
Point, typically constitute from the 70% about of mud total moisture content;2) capillary water, capillary water be between mud granule or in particulate fractures due to
The moisture that capillarity and mud granule are combined together, accounts for the 20% about of total Water;3) adsorb water, absorption water is due to table
The moisture on mud granule surface for the effect absorption of face tension force, because mud granule is little, has extremely strong superficial attractive forces;4) tie
Heshui, is included in the intracellular moisture of sludge microbe in conjunction with water, and the internal structure only changing mud granule could will be tied
Heshui separates;Account for 10% about of total moisture content in mud in conjunction with water and absorption water altogether.
Sludge dewatering actually refers to remove the Interstitial Water in mud.Interstitial Water easily removes in theory, but due to
Mud is to be formed by cotton-shaped colloid set, and granule is very thin and very soft, because soft granule has certain compressibility, works as external force
During increase, granule can be very little " film " in one layer of space of filter media surface formation, so that water is difficult to pass through, dehydration is also
Seem abnormal difficult.
The modifier treatment of mud is key link and the core technology of sludge dewatering.Modifier treatment is exactly the glue destroying mud
State structure, reduces the affinity between muddy water, improves the dewatering of mud.
Chinese patent CN101955312B discloses a kind of sludge conditioner and its using method, and this conditioner is using interpolation
Enzyme the improvement for biochemical sludge, are destroyed the extracellular polymeric in mud, improve dehydrating effect, can make using acid and enzyme
Mud mass dryness fraction brings up to 40~50% from 20~30%.This invention conditioner needs cellulose and hemicellulase, conditioning time
Also up to 240 minutes, relatively costly, and content of organic matter height is it is impossible to avoid the problem of the easy compression of filter cake.
Chinese patent CN101967035A discloses a kind of dewatering conditioner of municipal sludge, and conditioner adopts anionic
PAM is prepared with shitosan, effectively reduces anionic PAM consumption, improves dewatering performance of sludge.This invention conditioner is organic
Composition, high expensive, difficult degradation and have bio-toxicity, additionally, there is no inorganic conditioner difficult to form strong mesh skeleton structure,
The Incoercibility of mud can not be improved it is impossible to improve efficiency of press filtering.
Chinese patent CN104926075A discloses a kind of excess sludge deep dehydration conditioner, and this conditioner adopts rice husk
Powder, as sludge dehydration conditioner, can overcome current FeCl3With CaO can corrode burning facility, organic minimizing is unfavorable for burning
The defects such as burning.The used conditioner of this invention can not improve the dehydration property of mud, improve mud comprcssive strength, deeply dehydrating sludge
Moisture content can not substantially be reduced afterwards.
Content of the invention
It is an object of the invention to overcoming existing defect, provide a kind of sludge solidifying agent and preparation method thereof and user
Method, this sludge solidifying agent and mechanical dewatering equipment are used in combination, and by 75~85%, moisture percentage in sewage sludge can be down to 45~60%, with
When reduce process time, improve treatment effeciency.
In order to realize object above, the present invention passes through to include technical scheme below realization:A kind of sludge solidifying agent, including
Fluid composition and solid-state composition, the dosage of described fluid composition accounts for the 1-6% of mud dosage, described solid-state composition
The dosage of thing accounts for the 1-6% of mud dosage.
Preferably, described fluid composition includes the component of following weight portion:2~8 parts of sodium silicate, magnesium chloride 20~40
Part, 20~40 parts of ferrous sulfate, 1~2 part of organic flocculant, 2~8 parts of water reducer, 90~392 parts of water.
Preferably, described solid-state composition includes calcium oxide.
It is further preferred that described solid-state composition also includes skeleton agent, the weight of described skeleton agent and described calcium oxide
Than for (0.1~3):1, described skeleton agent is made up of one or more of plant ash, flyash and kieselguhr.
Preferably, described organic flocculant is octadecyl trimethyl ammonium chloride.
Preferably, described water reducer is made up of ligninsulfonate and naphthalene sulphonate formaldehyde polymer, described ligninsulfonate
With the weight of described naphthalene sulphonate formaldehyde polymer than for 1:(2~3).
Preferably, described calcium oxide, described plant ash, described flyash and described diatomaceous moisture content are respectively less than 2%.
Preferably, described calcium oxide, described plant ash, described flyash and described kieselguhr are powder, and particle diameter is equal
For 200-500 mesh.Take calcium oxide, plant ash, flyash and the kieselguhr of powder, be conducive to solid-state composition fast with mud
Speed reacts, and shortens the response time, improves sludge modification effect.
Plant ash, flyash and kieselguhr whether add with required process mud mud and required up to standard require relevant
System:
It is less than 45% when processing the content of organic matter (VSS/TSS) in mud, and up to standard when requiring as moisture content 55~60%,
Described solid-state composition is calcium oxide;
It is less than 45% when processing the mud content of organic matter (VSS/TSS), and up to standard when requiring as moisture content 45~55%, institute
State the component that solid-state composition includes following weight portion:1~3 part of calcium oxide, 1~4 part of plant ash;
It is higher than 45% when processing the mud content of organic matter (VSS/TSS), and up to standard when requiring as moisture content 55~60%, institute
State the component that solid-state composition includes following weight portion:3~5 parts of calcium oxide, 1~4 part of plant ash, 1~2 part of kieselguhr;
It is higher than 45% when processing the mud content of organic matter (VSS/TSS), and up to standard when requiring as moisture content 45~55%, institute
State the component that solid-state composition includes following weight portion:3~5 parts of calcium oxide, 1~2 part of plant ash, 1~2 part of flyash, diatom
1~2 part of soil;Wherein, the volatilizable organic matter of mud that the content of organic matter (VSS/TSS) refers to accounts for the weight of sewage sludge solid material total amount
Amount percentage ratio.
The present invention discloses a kind of method preparing sludge solidifying agent described above, comprises the following steps:
1) it is dried:Carried out using following A1 or B1 mode:
A1, take described calcium oxide to carry out heating, drying under the conditions of 105-110 DEG C, moisture content is down to less than 2%;
B1, described calcium oxide and described skeleton agent is taken to carry out heating, drying under the conditions of 105-110 DEG C, by moisture content
It is down to less than 2%;
2) prepare solid-state composition:Carried out using following A2 or B2 mode:
A2, described calcium oxide is crushed to respectively step by step by below 1mm using pulverizer, ball is carried out respectively using ball mill
By the size controlling of described calcium oxide in 200~500 mesh after mill, broken, ball milling, form solid-state composition;
B2, described calcium oxide and described skeleton agent are crushed to step by step respectively by below 1mm using pulverizer, using ball mill
Carry out respectively ball milling, after broken, ball milling by the size controlling of described calcium oxide and described skeleton agent in 200~500 mesh;To pass through
The described calcium oxide processing and described skeleton agent, according to weight proportion mix homogeneously, form solid-state composition;
3) prepare fluid composition:Carried out using A3 mode:
A3, described sodium silicate, described magnesium chloride, described ferrous sulfate, described organic flocculant and described water reducer are pressed
It is dissolved in described water according to weight proportion, mix homogeneously, form fluid composition.
Invention additionally discloses a kind of method using sludge solidifying agent described above, it comprises the steps:
1) mud and described fluid composition are added to mixing arrangement, stir 30-120s at normal temperatures, mixed
Thing;Wherein, described fluid composition and the weight ratio of described mud are (1~6):100;
2) add described solid-state composition in described mixture, at normal temperatures stirring 2-5min, then mechanical dehydration, real
The solidification minimizing of existing mud;Wherein, described solid-state composition and the weight ratio of described mud are (1~6):100.
Preferably, described mud comes from sludge of sewage treatment plant, riverway sludge, anaerobism biogas residue and dangerous solid waste
Middle one kind, its water content is 75~85%.
Preferably, in described step 2) in, add at dot spacing 0.8-1.2m with liquid, add in described mixture
Enter described solid-state composition.Add at dot spacing 0.8-1.2m with liquid, primarily to making fluid composition and dirt
Mud fully reacts, and changes mud internal structure, is conducive to the uniformity that solid-state composition is mixed with mud, can improve dirt simultaneously
Mud modified effect, reduces firming agent dosage.
In general, it is in sticky fluidised form moisture content 75~85% mud, mud internal void is few, the main position of pore-size more
Between 10~150 μm;Mud granule is connected with each other, and how in the form of sheets, particle size is predominantly located between 20~150 μm;No net
Shape or column crystallization body.The fluid composition that the present invention adds makes mud internal void increasing number, pore-size increase, hole
Gap size is predominantly located between 30~80 μm;Mud granule is relatively independent, granular in the majority, and particle size is predominantly located at 40~80 μm
Between.After adding solid-state composition, mud internal void quantity, pore-size and particle size remain unchanged, in mud substantially
Portion's cell wall cracks, and produces netted and column crystallization body, and dewatering performance of sludge and comprcssive strength improve further.Through mechanical dehydration
Mud solid-state in the form of sheets afterwards, mud internal void quantity has reduced compared with modified sewage sludge, pore-size reduces, and pore-size is main
Between 15~40 μm;Mud granule is relatively independent, granular in the majority, and particle size is predominantly located between 40~80 μm;Exist
Netted and column crystallization body.
In sum, the present invention provides a kind of sludge solidifying agent and preparation method thereof and using method, and the present invention's is beneficial
Effect:
A kind of sludge solidifying agent that the present invention provides, using the medicament being easier to acquisition, and medicament dry dosage is only
The 2~6% of moisture content 75~85% sludge quality, have greatly saved operating cost.The present invention passes through fluid composition and consolidates
State compositionss are used in combination, and improve mud comprcssive strength and dewatering, beneficial to follow-up mechanical sludge dewatering.
Further, the present invention, can be by the mud of moisture content 75~85% by medicament modification and mechanical dehydration synergism
It is dehydrated to moisture content 45~60%, decreases sludge volume, reduce cost of transportation, beneficial to the disposal of later stage mud.
Further, the present invention will not introduce in sludge dewatering conditioning and dehydration or produce malicious side-product, it is to avoid
Pollute environment again.
Specific embodiment
The present invention is expanded on further with reference to embodiment.It should be understood that embodiment is merely to illustrate the present invention, and unrestricted
The scope of the present invention.
Embodiment 1
A kind of sludge solidifying agent, including fluid composition and solid-state composition, be 100 tons by mud dosage based on, liquid
The dosage of compositionss is 4 tons, and wherein, fluid composition includes the component of following weight portion:6 parts of sodium silicate, 40 parts of magnesium chloride,
30 parts of ferrous sulfate, 2 parts of organic flocculant, 6 parts of water reducer, 252 parts of water;Organic flocculant is octadecyl trimethyl chlorination
Ammonium.The dosage of solid-state composition is 5 tons, and solid-state composition includes the component of following weight portion:3 parts of calcium oxide, plant ash 1
Part, 1 part of flyash, 2 parts of kieselguhr.
The preparation method of sludge solidifying agent, comprises the following steps:
1) by calcium oxide, plant ash, flyash and kieselguhr, heating, drying 9 hours under the conditions of 105 DEG C, by moisture content
It is down to less than 2%;
2) calcium oxide, plant ash, flyash and kieselguhr are crushed to respectively step by step by below 1mm using pulverizer, adopt
Ball mill carry out respectively ball milling, after broken, ball milling by calcium oxide, plant ash, flyash and diatomaceous size controlling 200~
500 mesh;
3) at normal temperatures, by treated calcium oxide, plant ash, flyash and kieselguhr according to solid in sludge solidifying agent
The proportioning mix homogeneously of state compositionss, forms solid-state composition;
4) sodium silicate, magnesium chloride, ferrous sulfate, organic flocculant, water reducer are dissolved in water according to weight proportion, mix
Close uniformly, form fluid composition.
The using method of sludge solidifying agent, it comprises the steps:
1) by moisture content be 76%, the content of organic matter be 49% mud and fluid composition be added in mixing arrangement,
Stir 40s at normal temperatures, stir, obtain mixture;Wherein, fluid composition dosage is the 4% of the weight of mud.
2) add at 1 meter of dot spacing with fluid composition, add solid-state composition in mixture, stir at normal temperatures
3min, mechanical dehydration, realize the solidification of mud;Solid-state composition dosage is the 5% of the weight of mud.
3) moisture percentage in sewage sludge after detection process.
Embodiment 2
A kind of sludge solidifying agent, including fluid composition and solid-state composition, be 100 tons by mud dosage based on, liquid
The dosage of compositionss is 4 tons, and wherein, fluid composition includes the component of following weight portion:4 parts of sodium silicate, 40 parts of magnesium chloride,
30 parts of ferrous sulfate, 2 parts of organic flocculant, 2 parts of water reducer, 200 parts of water;And the dosage of solid-state composition is 5 tons, solid-state group
Compound includes the component of following weight portion:4 parts of calcium oxide, 2 parts of plant ash, 1 part of kieselguhr.
The preparation method of sludge solidifying agent, comprises the following steps:
1) by calcium oxide, plant ash and kieselguhr, under the conditions of 105 DEG C, heating, drying more than 8 hours, moisture content is down to
Less than 2%;
2) calcium oxide, plant ash and kieselguhr are crushed to step by step respectively by below 1mm using pulverizer, are divided using ball mill
Do not carry out ball milling, after broken, ball milling by calcium oxide, plant ash and diatomaceous size controlling in 200~500 mesh;At normal temperatures,
By treated calcium oxide, plant ash and kieselguhr according to weight proportion mix homogeneously, form solid-state composition;
3) sodium silicate, magnesium chloride, ferrous sulfate, organic flocculant, water reducer are dissolved in water according to weight proportion, mix
Close uniformly, form fluid composition.
The using method of sludge solidifying agent, it comprises the steps:
1) by moisture content be the 83%, content of organic matter be that 49% mud and fluid composition are added in mixing arrangement,
Stir 50s under room temperature, stir, obtain mixture;Wherein, fluid composition dosage is the 4% of the weight of mud.
2) add at 1 meter of dot spacing with fluid composition, add solid-state composition in mixture, stir at normal temperatures
3min, mechanical dehydration, realize the solidification of mud;Wherein, solid-state composition dosage is the 5% of the weight of mud.
3) moisture percentage in sewage sludge after detection process.
Embodiment 3
A kind of sludge solidifying agent, including fluid composition and solid-state composition, be 100 tons by mud dosage based on, liquid
The dosage of compositionss is 4 tons, and wherein, fluid composition includes the component of following weight portion:4 parts of sodium silicate, 30 parts of magnesium chloride,
20 parts of ferrous sulfate, 1 part of organic flocculant, 4 parts of water reducer, 220 parts of water;The dosage of solid-state composition is 5 tons, solid-state composition
Thing includes the component of following weight portion:4 parts of calcium oxide, 2 parts of plant ash.
The preparation method of sludge solidifying agent, comprises the following steps:
1) heating, drying 10 hours under the conditions of 110 DEG C by calcium oxide and plant ash, moisture content is down to less than 2%;
2) calcium oxide, plant ash are crushed to respectively step by step by below 1mm using pulverizer, ball is carried out respectively using ball mill
After mill, broken, ball milling by calcium oxide, plant ash size controlling in 200~500 mesh;At normal temperatures, by treated oxidation
Calcium, plant ash, according to weight proportion mix homogeneously, form solid-state composition;
4) sodium silicate, magnesium chloride, ferrous sulfate, organic flocculant, water reducer are dissolved in water according to weight proportion, mix
Close uniformly, form fluid composition.
The using method of sludge solidifying agent, it comprises the steps:
1) by moisture content be the 83%, content of organic matter be that 43% mud and fluid composition are added in mixing arrangement,
Stir 50s under room temperature, stir, obtain mixture;Fluid composition dosage is the 4% of the weight of mud.
2) add at 1 meter of dot spacing with fluid composition, add solid-state composition in mixture, stir at normal temperatures
4min, mechanical dehydration, realize the solidification of mud.Solid-state composition dosage is the 5% of the weight of mud.
3) moisture percentage in sewage sludge after detection process.
Embodiment 4
A kind of sludge solidifying agent, including fluid composition and solid-state composition, be 100 tons by mud dosage based on, liquid
The dosage of compositionss is 4 tons, and wherein, fluid composition includes the component of following weight portion:7 parts of sodium silicate, 36 parts of magnesium chloride,
32 parts of ferrous sulfate, 2 parts of organic flocculant, 5 parts of water reducer, 280 parts of water;The dosage of solid-state composition is 4 tons, solid-state composition
Thing is calcium oxide.
The preparation method of sludge solidifying agent, comprises the following steps:
1) by calcium oxide under the conditions of 110 DEG C heating, drying 9 hours, moisture content is down to less than 2%;
2) calcium oxide is crushed to respectively step by step by below 1mm using pulverizer, carries out ball milling respectively, break using ball mill
By the size controlling of calcium oxide in 200~500 mesh after broken, ball milling, form solid-state composition;
3) sodium silicate, magnesium chloride, ferrous sulfate, organic flocculant, water reducer are dissolved in water according to weight proportion, mix
Close uniformly, form fluid composition.
The using method of sludge solidifying agent, it comprises the steps:
1) by moisture content be the 83%, content of organic matter be that 42% mud and fluid composition are added in mixing arrangement,
Stir 60s under room temperature, stir, obtain mixture;Fluid composition dosage is the 4% of the weight of mud.
2) add at 1 meter of dot spacing with fluid composition, add solid-state composition in mixture, stir at normal temperatures
4min, mechanical dehydration, realize the solidification of mud.Solid-state composition dosage is the 4% of the weight of mud.
3) moisture percentage in sewage sludge after detection process.
Test result
Table 1 embodiment 1 to 4 uses the water-cut variation result of mud after sludge solidifying agent process
As can be seen from Table 1:Embodiment 1 to 4 all by medicament modification and mechanical dehydration synergism, can substantially reduce dirt
The moisture content of mud, reduces sludge volume;Embodiment 1 is aqueous by mud (former moisture content is the 76%, content of organic matter is 49%)
Rate is reduced to 45%, and the moisture content of mud (former moisture content is the 83%, content of organic matter is 49%) is reduced to by embodiment 2
56%, the moisture content of mud (former moisture content is the 83%, content of organic matter is 43%) is reduced to 47% by embodiment 3, embodiment 4
The moisture content of mud (former moisture content is the 83%, content of organic matter is 42%) is reduced to 57%.So, in actual Treatment of Sludge
In, according to the content of organic matter in mud and moisture content requirement up to standard, judge whether to add skeleton agent, it is to avoid unnecessary economy
Cost.
To sum up, the mud of moisture content 75~85%, by medicament modification and mechanical dehydration synergism, can be taken off by the present invention
Water, to moisture content 45~60%, decreases sludge volume, reduces cost of transportation, and beneficial to the disposal of later stage mud, the present invention exists
Will not introduce in sludge dewatering conditioning and dehydration or produce malicious side-product, it is to avoid environmental pollution.So, the present invention is effective
Overcome various shortcoming of the prior art and have high industrial utilization.
The above, only presently preferred embodiments of the present invention, not any to the present invention formal and substantial restriction,
It should be pointed out that for those skilled in the art, on the premise of without departing from the inventive method, also can make
Some improvement and supplement, these improve and supplement also should be regarded as protection scope of the present invention.All those skilled in the art,
Without departing from the spirit and scope of the present invention, when available disclosed above technology contents make a little more
Equivalent variations that are dynamic, modifying and develop, are the Equivalent embodiments of the present invention;Meanwhile, all substantial technological pair according to the present invention
The change of any equivalent variations, modification and differentiation that above-described embodiment is made, all still fall within the scope of technical scheme
Interior.
Claims (10)
1. a kind of sludge solidifying agent it is characterised in that:Including fluid composition and solid-state composition, the throwing of described fluid composition
Dosage accounts for the 1~6% of mud dosage, and the dosage of described solid-state composition accounts for the 1~6% of mud dosage.
2. sludge solidifying agent according to claim 1 is it is characterised in that described fluid composition includes following weight portion
Component:2~8 parts of sodium silicate, 20~40 parts of magnesium chloride, 20~40 parts of ferrous sulfate, 1~2 part of organic flocculant, water reducer 2~8
Part, 90~392 parts of water.
3. sludge solidifying agent according to claim 1 is it is characterised in that described solid-state composition includes calcium oxide.
4. sludge solidifying agent as claimed in claim 3 it is characterised in that:Described solid-state composition also includes skeleton agent, described
Skeleton agent is (0.1~3) with the weight ratio of described calcium oxide:1, described skeleton agent is by plant ash, flyash and kieselguhr
One or more composition.
5. sludge solidifying agent as claimed in claim 2 it is characterised in that:Described organic flocculant is octadecyl trimethyl chlorine
Change ammonium.
6. sludge solidifying agent as claimed in claim 2 it is characterised in that:Described water reducer is by ligninsulfonate and naphthalene sulfonate
Yuban forms, and the weight of described ligninsulfonate and described naphthalene sulphonate formaldehyde polymer ratio is for 1:(2~3).
7. sludge solidifying agent as claimed in claim 4 it is characterised in that:Described calcium oxide, described plant ash, described flyash
It is respectively less than 2% with described diatomaceous moisture content;
And/or, described calcium oxide, described plant ash, described flyash and described kieselguhr are powder.
8. a kind of method preparing the arbitrary described sludge solidifying agent of claim 1 to 7 is it is characterised in that comprise the following steps:
1) it is dried:Carried out using following A1 or B1 mode:
A1, take described calcium oxide to carry out heating, drying under the conditions of 105-110 DEG C, moisture content is down to less than 2%;
B1, take described calcium oxide and described skeleton agent to carry out heating, drying under the conditions of 105-110 DEG C, moisture content is down to
Less than 2%;
2) prepare solid-state composition:Carried out using following A2 or B2 mode:
A2, described calcium oxide is crushed to respectively step by step by below 1mm using pulverizer, ball milling, broken is carried out respectively using ball mill
By the size controlling of described calcium oxide in 200~500 mesh after broken, ball milling, form solid-state composition;
B2, described calcium oxide and described skeleton agent are crushed to respectively step by step by below 1mm using pulverizer, using ball mill respectively
Carry out ball milling, after broken, ball milling by the size controlling of described calcium oxide and described skeleton agent in 200~500 mesh;Will be through processing
Described calcium oxide and described skeleton agent according to weight proportion mix homogeneously, form solid-state composition;
3) prepare fluid composition:Carried out using A3 mode:
A3, by described sodium silicate, described magnesium chloride, described ferrous sulfate, described organic flocculant and described water reducer according to weight
Amount proportioning is dissolved in described water, and mix homogeneously forms fluid composition.
9. a kind of method using described sludge solidifying agent as arbitrary in claim 1 to 7 it is characterised in that it include as follows
Step:
1) mud and described fluid composition are added to mixing arrangement, stir 30-120s at normal temperatures, obtain mixture;
Wherein, described fluid composition and the weight ratio of described mud are (1~6):100;
2) add described solid-state composition in described mixture, stir 2-5min, then mechanical dehydration at normal temperatures, realize dirty
The solidification minimizing of mud;Wherein, described solid-state composition and the weight ratio of described mud are (1~6):100.
10. sludge solidifying agent as claimed in claim 9 using method it is characterised in that:Described mud comes from sewage
A kind of in reason factory mud, riverway sludge, anaerobism biogas residue and dangerous solid waste, its water content is 75~85%;
And/or, in described step 2) in, add at dot spacing 0.8-1.2m with liquid, add institute in described mixture
State solid-state composition.