CN106381204A - Lubricating oil for installation of bolts - Google Patents
Lubricating oil for installation of bolts Download PDFInfo
- Publication number
- CN106381204A CN106381204A CN201610748228.8A CN201610748228A CN106381204A CN 106381204 A CN106381204 A CN 106381204A CN 201610748228 A CN201610748228 A CN 201610748228A CN 106381204 A CN106381204 A CN 106381204A
- Authority
- CN
- China
- Prior art keywords
- parts
- lubricating oil
- lubricating
- bolt
- bolt installation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to lubricating oil for installation of bolts. The lubricating oil is composed of the following components (by weight): 30-40 parts of oleic acid, 11-13 parts of imidazoline, 3-9 parts of polyaleneglycol, 4-6 parts of n-octyl alcohol, 6-9 parts of isopropanol, 3-12 parts of base oil, 5-7 parts of sulfurized calcium alkyl phenate, 2-5 parts of sodium sulfite, 3-6 parts of sodium dodecyl benzene sulfonate, 1-4 parts of triethanolamine, 1-3 parts of an anti-wear agent, 2-3 parts of an antirust agent and 1-2 parts of an anti-oxidant. The lubricating oil prepared by the above mode has advantages of less preparation component, simple preparation process and good lubricating property. After the prepared lubricating oil coats the surface of a bolt, the lubricating oil can maintain a long-term lubricating effect, and the surface of the bolt will not be rusted for a long time. The lubricating oil has a good fixation effect on workpieces, has a good lubricating effect, requires no frequent manual coating, and is simple to operate.
Description
Technical field
The present invention relates to a kind of lubricating oil, specifically a kind of bolt installation lubricating oil.
Background technology
It is various that hardware & tools refers to that the Physical Processing such as the process forging of the metals such as ferrum, steel, aluminum, calendering, cutting are fabricated by
The general name of metal device;Hardware & tools include various manually, electrically, pneumatic, cutting tool, vapour protect instrument, agricultural tools, lifting
Instrument, survey tool, machine tool, cutting element, clamping apparatus, cutter, mould, cutlery, emery wheel, drill bit, buffing machine, instrument are joined
Part, measuring and cutting tool, grinding tool abrasive material, screw, bolt, pad, gear etc.;Now in each field to bolt using widely,
Bolt needs periodically to apply lubricating oil after mounting, so that will not get rusty in bolt surface, if bolt surface oxidisation, it will serious
Impact the fixed effect to workpiece for the bolt, to ensure the normal work of workpiece, but the existing oil lubrication time is short, lubrication
Effect is poor, and rustless property is poor, needs manually constantly to apply lubricating oil, complex operation.
Content of the invention
For above-mentioned technical problem, the present invention provides a kind of bolt installation lubricating oil, and prepared composition is few, preparation technology letter
Single, greasy property is good, and the lubricating oil that the present invention is prepared can keep some time after being coated in bolt surface
Lubrication, the surface some time will not get rusty, the good fixing effect to workpiece, and high lubricating effect need not manually often apply, behaviour
Make easy.
The technical problem to be solved employs the following technical solutions to realize:
A kind of bolt installation lubricating oil, this lubricating oil is grouped into by the group of following weight portion:Oleic acid 30-40 part, imidazoles
Quinoline 11-13 part, poly- alkylene ethylene glycol 3-9 part, n-octyl alcohol 4-6 part, isopropanol 6-9 part, base oil 3-12 part, calcium sulfenyl phenolate
5-7 part, sodium sulfite 2-5 part, dodecylbenzene sodium sulfonate 3-6 part, triethanolamine 1-4 part, antiwear additive 1-3 part, antirust agent 2-3
Part and antioxidant 1-2 part.
A kind of bolt installation lubricating oil, this lubricating oil is grouped into by the group of following optimum weight part:35 parts of Oleic acid, imidazoles
12 parts of quinoline, 6 parts of poly- alkylene ethylene glycol, 5 parts of n-octyl alcohol, 7 parts of isopropanol, 8 parts of base oil, 6 parts of calcium sulfenyl phenolate, sodium sulfite
3 parts, 4 parts of dodecylbenzene sodium sulfonate, 3 parts of triethanolamine, 2 parts of antiwear additive, 2 parts of antirust agent and 1 part of antioxidant.
As a preferred technical solution of the present invention, described antiwear additive type is sulfur-bearing extreme pressure anti-wear additives.
As a preferred technical solution of the present invention, described antirust agent type is water-based antirust.
The invention has the beneficial effects as follows:Compared to existing technology, the lubricating oil preparing by the way, prepared composition
Few, preparation process is simple, greasy property is good, and the lubricating oil that the present invention is prepared can protected after being coated in bolt surface
Hold the lubrication of some time, the surface some time will not get rusty, the good fixing effect to workpiece, high lubricating effect need not
Manually often apply, easy and simple to handle.
Specific embodiment
In order that the technological means of present invention realization and creation characteristic are easy to understand, below the present invention is explained further
State.
Embodiment one:
A kind of bolt installation lubricating oil, this lubricating oil is grouped into by the group of following weight portion:30 parts of Oleic acid, imidazoline 11
Part, 3 parts of poly- alkylene ethylene glycol, 4 parts of n-octyl alcohol, 6 parts of isopropanol, 3 parts of base oil, 5 parts of calcium sulfenyl phenolate, 2 parts of sodium sulfite,
3 parts of dodecylbenzene sodium sulfonate, 1 part of triethanolamine, 1 part of antiwear additive, 2 parts of antirust agent and 1 part of antioxidant.
Described antiwear additive type is sulfur-bearing extreme pressure anti-wear additives.
Described antirust agent type is water-based antirust.
Embodiment two:
A kind of bolt installation lubricating oil, this lubricating oil is grouped into by the group of following weight portion:35 parts of Oleic acid, imidazoline 12
Part, 6 parts of poly- alkylene ethylene glycol, 5 parts of n-octyl alcohol, 7 parts of isopropanol, 8 parts of base oil, 6 parts of calcium sulfenyl phenolate, 3 parts of sodium sulfite,
4 parts of dodecylbenzene sodium sulfonate, 3 parts of triethanolamine, 2 parts of antiwear additive, 2 parts of antirust agent and 1 part of antioxidant.
Described antiwear additive type is sulfur-bearing extreme pressure anti-wear additives.
Described antirust agent type is water-based antirust.
Embodiment three:
A kind of bolt installation lubricating oil, this lubricating oil is grouped into by the group of following weight portion:40 parts of Oleic acid, imidazoline 13
Part, 9 parts of poly- alkylene ethylene glycol, 6 parts of n-octyl alcohol, 9 parts of isopropanol, 12 parts of base oil, 7 parts of calcium sulfenyl phenolate, sodium sulfite 5
Part, 6 parts of dodecylbenzene sodium sulfonate, 4 parts of triethanolamine, 3 parts of antiwear additive, 3 parts of antirust agent and 2 parts of antioxidant.
Described antiwear additive type is sulfur-bearing extreme pressure anti-wear additives.
Described antirust agent type is water-based antirust.
By implementing one, implementing two and implementing three lubricating oil that prepare, compared to existing technology in plain oil,
The lubricating oil that the present invention is prepared by above-described embodiment, prepared composition is few, preparation process is simple, and greasy property is good, incite somebody to action this
Invent after the lubricating oil for preparing is coated in bolt surface in the lubrication that can keep some time, when surface is very long
Between will not get rusty, the good fixing effect to workpiece, high lubricating effect, need not manually often apply, easy and simple to handle.
Ultimate principle, principal character and the advantages of the present invention of the present invention have been shown and described above.The technology of the industry
The simply present invention it should be appreciated that the present invention is not restricted to the described embodiments, described in above-described embodiment and description for the personnel
Principle, without departing from the spirit and scope of the present invention, the present invention also has various changes and modifications, these change and
Improvement both falls within scope of the claimed invention.Claimed scope is by appending claims and its equivalent
Thing defines.
Claims (4)
1. a kind of bolt installation lubricating oil it is characterised in that:This lubricating oil is grouped into by the group of following weight portion:Oleic acid 30-
40 parts, imidazoline 11-13 part, poly- alkylene ethylene glycol 3-9 part, n-octyl alcohol 4-6 part, isopropanol 6-9 part, base oil 3-12 part, sulfur
Change alkyl phenol calcium 5-7 part, sodium sulfite 2-5 part, dodecylbenzene sodium sulfonate 3-6 part, triethanolamine 1-4 part, antiwear additive 1-3
Part, antirust agent 2-3 part and antioxidant 1-2 part.
2. a kind of bolt installation lubricating oil according to claim 1 it is characterised in that:This lubricating oil is by following optimal weight
The group of amount part is grouped into:35 parts of Oleic acid, 12 parts of imidazoline, 6 parts of poly- alkylene ethylene glycol, 5 parts of n-octyl alcohol, 7 parts of isopropanol, base oil
8 parts, 6 parts of calcium sulfenyl phenolate, 3 parts of sodium sulfite, 4 parts of dodecylbenzene sodium sulfonate, 3 parts of triethanolamine, 2 parts of antiwear additive, anti-
2 parts of rust agent and 1 part of antioxidant.
3. a kind of bolt installation lubricating oil according to claim 1 and 2 it is characterised in that:Described antiwear additive type
For sulfur-bearing extreme pressure anti-wear additives.
4. a kind of bolt installation lubricating oil according to claim 1 and 2 it is characterised in that:Described antirust agent type
For water-based antirust.