CN106381069A - A method of preparing a grinding lubricant used for a hyperfine polishing machine tool - Google Patents
A method of preparing a grinding lubricant used for a hyperfine polishing machine tool Download PDFInfo
- Publication number
- CN106381069A CN106381069A CN201610706529.4A CN201610706529A CN106381069A CN 106381069 A CN106381069 A CN 106381069A CN 201610706529 A CN201610706529 A CN 201610706529A CN 106381069 A CN106381069 A CN 106381069A
- Authority
- CN
- China
- Prior art keywords
- machine tool
- stirring
- minute
- hydroxypropyl cellulose
- mixing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A method of preparing a grinding lubricant used for a hyperfine polishing machine tool is disclosed. The method includes (1) mixing dimethyl siloxane, carboxymethyl hydroxypropyl cellulose, glyceryl triacetate and triethanolamine, heating and stirring, (2) mixing butadienyl triethoxysilane and dimethylolurea, stirring, heating and performing ultrasonic treatment, and (3) mixing the materials treated in the step (1) and the step (2), adding tetrasodium EDTA, performing ultrasonic treatment, fully stirring, adding water, and stirring again to obtain the grinding lubricant. Beneficial effects of the method are that the carboxymethyl hydroxypropyl cellulose and the dimethylolurea are added so that the grinding lubricant is more uniform in dispersion, higher in cooling speed during grinding and capable of effectively increasing the hyperfine polishing efficiency of the machine tool.
Description
Technical field
The present invention relates to lapping liquid technical field, the preparation method of particularly a kind of lapping liquid for superfinishing casting machine tool.
Background technology
During Machine Manufacture, in order to process the precision of workpiece, the required precision of lathe itself is also very high.Usual lathe
Plane or vital part typically require and reach micron-sized degree of accuracy, and the roughness on its surface needs to reach the level of minute surface level.
Want to reach the plane of minute surface level, lathe needs a series of polishing grinding operations just can complete, especially the most in process
Need the support of superfinishing glossing afterwards.
But in lathe in the technical process that superfinishing polishes, generally require very high technical requirements and equipment requirements, and
And very time-consuming take a lot of work, also there is very big risk of failure.
Content of the invention
The purpose of the present invention is for solving the problems of the prior art, disclosing a kind of lapping liquid for superfinishing casting machine tool
Preparation method.
For achieving the above object, the invention discloses a kind of preparation method of the lapping liquid for superfinishing casting machine tool, by weight
Amount number takes dimethyl siloxane 2-4, carboxymethyl hydroxypropyl cellulose 2-4, tetrasodium ethylenediamine tetraacetate 1-3, triacetic acid glycerol
Ester 2-4, triethanolamine 1-3, butadienyl triethoxysilane 1-3, dimethylol urea 1-3, water 100-150, it is specifically prepared
Step is：
（1）Dimethyl siloxane, carboxymethyl hydroxypropyl cellulose, glyceryl triacetate, triethanolamine mixing post-heating to 60-80
DEG C, stir 30-40 minute；
（2）Again by after butadienyl triethoxysilane, dimethylol urea mix and blend 20-30 minute, it is again heated to 60-80 DEG C
Ultrasonic 15-20 minute；
（3）By step（1）With（2）In handle well material mixing, add tetrasodium ethylenediamine tetraacetate, after ultrasonic 10-15 minute
It is sufficiently stirred for 4-5 hour again, be eventually adding water and be again stirring for 2-3 hour and obtain lapping liquid.
Advantages of the present invention and good effect are：
Present invention adds carboxymethyl hydroxypropyl cellulose, dimethylol urea, so that lapping liquid is disperseed more uniform, cool down during grinding
Speed faster, can effectively improve the efficiency of lathe superfinishing throwing.
Specific embodiment
Specific embodiment one：
A kind of preparation method of the lapping liquid for superfinishing casting machine tool, takes dimethyl siloxane 2, carboxymethyl hydroxypropyl by weight
Base cellulose 2, tetrasodium ethylenediamine tetraacetate 1, glyceryl triacetate 2, triethanolamine 1, butadienyl triethoxysilane 1, two
Methylolurea 1, water 100, its concrete preparation process is：
（1）Dimethyl siloxane, carboxymethyl hydroxypropyl cellulose, glyceryl triacetate, triethanolamine mixing post-heating to 60 DEG C,
Stirring 30 minutes；
（2）Again by after butadienyl triethoxysilane, dimethylol urea mix and blend 20 minutes, it is again heated to 60 DEG C ultrasonic 15
Minute；
（3）By step（1）With（2）In handle well material mixing, add tetrasodium ethylenediamine tetraacetate, fill again after ultrasonic 10 minutes
Divide stirring 4 hours, be eventually adding water and be again stirring for 2 hours obtaining lapping liquid.
Specific embodiment two：
A kind of preparation method of the lapping liquid for superfinishing casting machine tool, takes dimethyl siloxane 4, carboxymethyl hydroxypropyl by weight
Base cellulose 4, tetrasodium ethylenediamine tetraacetate 3, glyceryl triacetate 4, triethanolamine 3, butadienyl triethoxysilane 3, two
Methylolurea 3, water 150, its concrete preparation process is：
（1）Dimethyl siloxane, carboxymethyl hydroxypropyl cellulose, glyceryl triacetate, triethanolamine mixing post-heating to 80 DEG C,
Stirring 40 minutes；
（2）Again by after butadienyl triethoxysilane, dimethylol urea mix and blend 30 minutes, it is again heated to 80 DEG C ultrasonic 20
Minute；
（3）By step（1）With（2）In handle well material mixing, add tetrasodium ethylenediamine tetraacetate, fill again after ultrasonic 15 minutes
Divide stirring 5 hours, be eventually adding water and be again stirring for 3 hours obtaining lapping liquid.
Specific embodiment three：
A kind of preparation method of the lapping liquid for superfinishing casting machine tool, takes dimethyl siloxane 3, carboxymethyl hydroxypropyl by weight
Base cellulose 3, tetrasodium ethylenediamine tetraacetate 2, glyceryl triacetate 3, triethanolamine 2, butadienyl triethoxysilane 2, two
Methylolurea 2, water 120, its concrete preparation process is：
（1）Dimethyl siloxane, carboxymethyl hydroxypropyl cellulose, glyceryl triacetate, triethanolamine mixing post-heating to 70 DEG C,
Stirring 35 minutes；
（2）Again by after butadienyl triethoxysilane, dimethylol urea mix and blend 25 minutes, it is again heated to 70 DEG C ultrasonic 18
Minute；
（3）By step（1）With（2）In handle well material mixing, add tetrasodium ethylenediamine tetraacetate, fill again after ultrasonic 13 minutes
Divide stirring 4.5 hours, be eventually adding water and be again stirring for 2.5 hours obtaining lapping liquid.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any those familiar with the art the invention discloses technical scope in, technology according to the present invention scheme and its
Inventive concept equivalent or change in addition, all should be included within the scope of the present invention.
Claims (1)
1. a kind of preparation method of the lapping liquid for superfinishing casting machine tool, takes dimethyl siloxane 2-4, carboxymethyl by weight
Hydroxypropyl cellulose 2-4, tetrasodium ethylenediamine tetraacetate 1-3, glyceryl triacetate 2-4, triethanolamine 1-3, butadienyl three second
TMOS 1-3, dimethylol urea 1-3, water 100-150 are it is characterised in that its concrete preparation process is：
（1）Dimethyl siloxane, carboxymethyl hydroxypropyl cellulose, glyceryl triacetate, triethanolamine mixing post-heating to 60-80
DEG C, stir 30-40 minute；
（2）Again by after butadienyl triethoxysilane, dimethylol urea mix and blend 20-30 minute, it is again heated to 60-80 DEG C
Ultrasonic 15-20 minute；
（3）By step（1）With（2）In handle well material mixing, add tetrasodium ethylenediamine tetraacetate, after ultrasonic 10-15 minute
It is sufficiently stirred for 4-5 hour again, be eventually adding water and be again stirring for 2-3 hour and obtain lapping liquid.