CN106366449A - Transparent beverage straw and production technology thereof - Google Patents
Transparent beverage straw and production technology thereof Download PDFInfo
- Publication number
- CN106366449A CN106366449A CN201610859853.XA CN201610859853A CN106366449A CN 106366449 A CN106366449 A CN 106366449A CN 201610859853 A CN201610859853 A CN 201610859853A CN 106366449 A CN106366449 A CN 106366449A
- Authority
- CN
- China
- Prior art keywords
- parts
- raw material
- weight portion
- suction pipe
- plasticiser
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a transparent beverage straw and a production technology thereof, and belongs to the technical field of plastic production and manufacture. The transparent beverage straw is mainly processed from, by weight, 80-200 parts of degradable polypropylene particles, 5-14 parts of a transparent agent, 10-16 parts of a modifying material, 8-17 parts of a plasticizer and 1-3 parts of an antibacterial agent. The invention further provides the production technology of the transparent beverage straw. The production technology comprises the following steps of raw material drying, material mixing, modifying, feeding, extruding, drawing, slitting, disinfecting and casing. By adopting the degradable polypropylene particles as a base material and adding the homemade plasticizer and the modifying material, the straw is high in glossiness, transparent in surface and few in impurity, achieves both tenacity and high strength and still can keep the good using performance in a high temperature state; the production technology is simple and controllable in process and low in cost and pollution, straw waste generated after the straw is used is easily decomposed by microorganisms to be returned to nature, and green and environmental friendliness are achieved.
Description
[technical field]
The present invention relates to plastics-production manufacturing technology field is and in particular to a kind of transparent beverage suction pipe and its production technology.
[background technology]
With the quickening increasingly improving with rhythm of life of people's living standard, the various liquid of milk, beverage is eaten
The consumption of product gets more and more, and this based food typically can use suction pipe.Because cup will not be contacted with suction pipe compare health;In addition
Had a drink with suction pipe, contribute to the health of tooth, have effect to tooth-whitening;And suction pipe low price.Suction pipe is as once
Sex aids because it is convenient, healthy, cheap and favored by people.
Due to being widely used, in recent years, plastic suction pipe has also obtained developing faster, and transparent straw is due to it
Safety highest receives the favor of people, and the suction pipe on market also has and there is some problem following: one, transparency is not high, surface
There are some speckle impurity;2nd, the requirement of intensity and toughness can not be met, the suction pipe of general good toughness is all very soft simultaneously, use
Get up inconvenient;3rd, heat-resisting ability is uneven, if when sucking hot drink, the suction pipe heat water of heat-resisting ability difference
The composition of some can be dissolved, sucked by human body and certain harm is produced to human body;4th, often it is dropped after completing to use, become
Become white pollution, environmental pollution is very big.
[content of the invention]
For defect present in prior art, it is an object of the invention to provide a kind of transparent beverage suction pipe and its production
Technique, the transparent beverage suction pipe of the present invention adopts degradable polypropylene granule as base material, adds self-control plasticiser and modified material
Material, makes suction pipe glossiness high, the bright impurity in surface, and has toughness and high intensity concurrently, remains at high operating temperatures keep good
Serviceability, the production process of the present invention is simply controlled, low cost, and pollutes little, using rear suction pipe rubbish easily by micro- life
Thing decomposes, back to nature, environmental protection.
To achieve these goals, the technical solution used in the present invention is as follows:
A kind of transparent beverage suction pipe, is mainly obtained by the Raw material processing of following weight portion: degradable polypropylene granule 80-
200 parts, clarifier 5-14 part, material modified 10-16 part, plasticiser 8-17 part, antibacterial 1-3 part;
Described degradable polypropylene granule is mainly made up of the raw material of following weight portion: polypropylene 30-50 part, starch 2-10
Part, polylactic acid 10-30 part, antioxidant 2-6 part;
Described material modified mainly it is made up of the raw material of following weight portion: tas-2a dispersed lubricant 0.1-1.5 part, carbonization
Vanadium 5-9 part, pbs polymer 5-14 part, thermoplastic polyester elastomer 5-10 part, hydroxypropyl cellulose 2-4 part;
Described plasticiser is mainly made up of the raw material of following weight portion: Pulvis Talci 40-70 part, limestone 40-70 part, paraffin
10-22 part, methylcellulose 8-17 part, polycaprolactam 1-5 part.
Further, the preferred formula of described transparent beverage suction pipe consists of, by weight, by following Raw material processing
Obtain: 150 parts of degradable polypropylene granule, 10 parts of clarifier, material modified 12 parts, 13 parts of plasticiser, 2 parts of antibacterial;
Described degradable polypropylene granule is mainly made up of the raw material of following weight portion: 40 parts of polypropylene, 6 parts of starch, gathers
20 parts of lactic acid, 4 parts of antioxidant;
Described material modified mainly it is made up of the raw material of following weight portion: 1 part of tas-2a dispersed lubricant, 7 parts of vanadium carbide,
10 parts of pbs polymer, 7 parts of thermoplastic polyester elastomer, 3 parts of hydroxypropyl cellulose;
Described plasticiser is mainly made up of the raw material of following weight portion: 55 parts of Pulvis Talci, 55 parts of limestone, 16 parts of paraffin,
12 parts of methylcellulose, 3 parts of polycaprolactam.
Further, described degradable polypropylene granule mainly obtains by the following method:
A. pre-treatment of raw material: the polypropylene of described weight portion and polylactic acid are added in deionized water cleanout fluid and carry out
Cleaning, and by cleaning after dry materials;
B. raw material screening: the starch of described weight portion is mixed with through pretreated material, selects by 100-
The raw materials particles of 150 eye mesh screens, obtain mixture a;
C. plus antioxidant: step b gained mixture a is put in high-speed mixer, adds antioxidant, with 800-
The rotating speed stirring 10-30min of 1100r/min, obtains mixture b;
D. pelletize: mixture b is added carry out melt blending in double screw extruder, extrusion, cooling, pelletize must be combined grain
Son.
Further, the preparation method of described plasticiser is by formula proportion, above-mentioned each material to be put into mulser revolve at a high speed
Turn agitating heating 10-20 minute, then become the raw material of paste to extrude, cool down in bulk through air-cooler, place in pulverizer
It is ground into powder, powder material is inputted modified machine inlet, after IR Catalysis cracking and puffing, raw material is entered by pipeline and makes
Grain tower crane molding, gets product.
The present invention also provides a kind of production technology of above-mentioned transparent beverage suction pipe, comprises the following steps:
(1) drying of raw material: the degradable polypropylene granule of corresponding weight portion is dried at 80-110 DEG C 3-8 hour, water
Point content controls below 0.1%;
(2) batch mixing: the degradable polypropylene granule through step (1) and plasticiser, antibacterial, clarifier mixing are added anti-
Answer in device, purpose granule, at 175-185 DEG C, is melted into molten condition under conditions of stirring by the temperature control of reactor;
(3) modified: by the material modified fused solution adding in step (2), and vacuum stirring, mix homogeneously;
(4) feed: the raw material mixing is put in extruder, starts extruder heating function, extruder one area is arrived
The heating-up temperature in 6th area all controls at 200-240 DEG C, and heat time heating time is 40-65 minute;
(5) extrude: open extruder main frame, suction pipe blank is extruded, and opens air pump, the pressure of air pump is set as 5-
7mpa;
(6) stretching, cooling: the material that step (5) is extruded is stretched to bosh, and the water temperature of bosh controls
At 12-42 DEG C, cool time is 2-8s;
(7) cut: the material after cooling is cut;
(8) sterilize: the material through step (7) is carried out disinfection by ultraviolet light, disinfecting time is 15-20 minute, ambient temperature
It is controlled to 20-40 DEG C;
(9) case: automatically packed with platoon automatic packaging machine, then cased, being entered with ozone again after vanning
Row is sterilized.
Further, the suction pipe blank diameter of described step (5) extruder extrusion is 3-8mm.
The features such as pbs polymer has cheap, excellent in mechanical performance, compared with the pla of close prices, pbs has
Easy to process, it is suitable for plastic processing conventional at present, the good feature of heat resistance, its heat distortion temperature can exceed
100 DEG C (heat resisting temperature of pla only has 60 DEG C about), and the raw material sources of pbs synthesis are extensively, both can be petroleum resources,
Can also be obtained by biomass resource fermentation.
Polypropylene is polymer nontoxic, that odorless, tasteless milky are highly crystalline, and polyacrylic degree of crystallinity is high, and structure is advised
Whole, thus there is excellent mechanical property, wherein, polypropylene performance the most prominent is exactly flexural fatigue resistance, is commonly called as polypropylene (PP).
Polylactic acid is to be the polymer that main polymerizable raw material obtains with lactic acid, belongs to polyester family, and polylactic acid raw material is originated
Fully renewable, production process is pollution-free, and product can be realized the circulation in nature, be preferable green with biodegradation
Macromolecular material.Polylactic acid is a kind of new biodegradation material, and it has good biodegradability, can quilt after use
In nature, microorganism is degradable, ultimately generates carbon dioxide and water, free from environmental pollution, this is highly beneficial to environmental protection,
The environment-friendly material being well recognized as.
Vanadium carbide has very high density, in the present invention as the density filler making straw, makes plastic
There is high density, high rigidity, the feature of high intensity.
Thermoplastic polyester body is the block copolymer containing polyester hard section and polyester soft segment, wherein polyester soft segment and not
The polyester of crystallization forms amorphous phase polyester hard section partially crystallizable and forms crystalline domains, plays the effect of physical crosslinking point, it has
The elasticity of rubber and the intensity of engineering plastics;Soft section gives its elasticity, makes it as rubber;Hard section gives its processing characteristics, makes it
As plastics;Compared with rubber, it has more preferable processing characteristics and longer service life;Compared with engineering material, equally have
The high feature of intensity, and pliability and dynamic mechanical are more preferable.
A kind of transparent beverage suction pipe provided by the present invention and its production technology, compared with prior art, having following has
Beneficial effect:
1st, the transparent beverage suction pipe of the present invention is as base material using degradable polypropylene granule, add self-control plasticiser and
Material modified and prepared, wherein, add self-control plasticiser and so that the material of suction pipe is become soft and increase viscosity, improve intermolecular
Adhesion, thus improving the intensity of suction pipe product, in addition, the raw material composition of plasticiser to obtain channel simple, with low cost;Add
Plus material modified imparting suction pipe high mechanical properties, it is provided simultaneously with high tenacity, and heat distortion temperature is high, is heated and is unlikely to deform, use
Safer.
2nd, the degradable polypropylene granule of the present invention is with polypropylene as primary raw material, adds polylactic acid and starch, gathers breast
Acid has a good biodegradability, and cooperation starch makes the straw of the present invention after a procedure can be by life micro- in nature
Thing is degradable, ultimately generates carbon dioxide and water, free from environmental pollution, highly beneficial to environmental protection.
3rd, the simple science of transparent beverage suction pipe production process of the present invention, controllability is high, low cost, is easy to promote life
Produce, either degradable polypropylene granule, plasticiser or transparent beverage suction pipe production process, all to machine and production
Environmental nonpollution.
[specific embodiment]
The following examples can help those skilled in the art to be more completely understood by the present invention, but cannot be with any
Mode limits the present invention.
Embodiment 1
A kind of transparent beverage suction pipe, is mainly obtained by the raw material of following weight portion: 80 parts of degradable polypropylene granule, transparent
5 parts of agent dimethylbenzene, 0.1 part of tas-2a dispersed lubricant, 3 parts of vanadium carbide, 3 parts of pbs polymer, 3 parts of thermoplastic polyester elastomer,
1 part of hydroxypropyl cellulose, 2 parts of Pulvis Talci, 2 parts of limestone, 1 part of paraffin, 0.5 part of methylcellulose, 0.1 part of polycaprolactam,
1 part of antibacterial nano-titanium oxide;Degradable polypropylene granule is mainly made up of the raw material of following weight portion: 30 parts of polypropylene, forms sediment
2 parts of powder, 10 parts of polylactic acid, 2 parts of antioxidant 1076 consumption.
The production technology of above-mentioned transparent beverage suction pipe, comprises the steps:
(1) prepare degradable polypropylene granule
A. pre-treatment of raw material: by the polypropylene of described weight portion, tas-2a dispersed lubricant, starch and polylactic acid addition
Be carried out in deionized water cleanout fluid, and by cleaning after dry materials;
B. raw material screening: the starch of described weight portion is mixed with through pretreated material, selects by 100 mesh
The raw materials particles of screen cloth, obtain mixture a;
Plus antioxidant c.: step b gained mixture a is put in high-speed mixer, adds antioxidant 1076, with
The rotating speed stirring 10-30min of 800-1100r/min, obtains mixture b;
D. pelletize: mixture c is added carry out melt blending in double screw extruder, extrusion, cooling, pelletize must be combined grain
Son, double screw extruder is divided into five temperature subregions, and wherein, each area temperature control is: an area: 178 DEG C, 2nd area: 188 DEG C, three
Area: 198 DEG C, 4th area: 208 DEG C, 5th area: 219 DEG C, head: 219 DEG C;Screw speed is 120r/min.
(2) prepare plasticiser
By 2 parts of Pulvis Talci, 2 parts of limestone, 1 part of paraffin, 0.5 part of methylcellulose, 0.1 part of polycaprolactam puts into emulsifying
Machine high-speed rotation agitating heating 10 minutes, has then been become the raw material of paste to extrude, cools down in bulk through air-cooler, places into pulverizing
It is ground into powder in machine, powder material is inputted modified machine inlet, after IR Catalysis cracking and puffing, raw material passes through special pipe
Road enters pelletize tower crane molding, gets product.
(3) prepare transparent beverage suction pipe
(1) drying of raw material: the degradable polypropylene granule of corresponding weight portion is dried 3 hours at 80 DEG C, moisture
Control below 0.1%;
(2) batch mixing: the degradable polypropylene granule through step (1) and plasticiser, antibacterial, clarifier mixing are added anti-
Answer in device, purpose granule, at 175 DEG C, is melted into molten condition under conditions of stirring by the temperature control of reactor;
(3) modified: by the material modified fused solution adding in step (2), and vacuum stirring, mix homogeneously;
(4) feed: the raw material mixing is put in extruder, starts extruder heating function, extruder one area is arrived
The heating-up temperature in 6th area all controls at 200 DEG C, and heat time heating time is 40 minutes;
(5) extrude: open extruder main frame, suction pipe blank is extruded, and opens air pump, the pressure of air pump is set as
5mpa;
(6) stretching, cooling: the material that step (5) is extruded is stretched to bosh, and the water temperature of bosh controls 12
At DEG C, cool time is 2s;
(7) cut: the material after cooling is cut;
(8) sterilize: the material through step (7) is carried out disinfection by ultraviolet light, disinfecting time is 15 minutes, and ambient temperature controls
For 20-40 DEG C;
(9) case: automatically packed with platoon automatic packaging machine, then cased, being entered with ozone again after vanning
Row is sterilized.
Embodiment 2
A kind of transparent beverage suction pipe, is mainly obtained by the raw material of following weight portion: 120 parts of degradable polypropylene granule, thoroughly
8 parts of bright dose of chloroform, 1 part of tas-2a dispersed lubricant, 4 parts of vanadium carbide, 3 parts of pbs polymer, 3 parts of thermoplastic polyester elastomer, hydroxyl
2 parts of propyl cellulose, 4 parts of Pulvis Talci, 4 parts of limestone, 2 parts of paraffin, 1 part of methylcellulose, 0.3 part of polycaprolactam, antibacterial
2 parts of agent nano-titanium oxide;Degradable polypropylene granule is mainly made up of the raw material of following weight portion: 40 parts of polypropylene, starch 7
Part, 20 parts of polylactic acid, 4 parts of antioxidant 164 consumption.
The production technology of above-mentioned transparent beverage suction pipe, comprises the steps:
(1) prepare degradable polypropylene granule
A. pre-treatment of raw material: by the polypropylene of described weight portion, tas-2a dispersed lubricant, starch and polylactic acid addition
Be carried out in deionized water cleanout fluid, and by cleaning after dry materials;
B. raw material screening: the starch of described weight portion is mixed with through pretreated material, selects by 120 mesh
The raw materials particles of screen cloth, obtain mixture a;
Plus antioxidant c.: step b gained mixture a is put in high-speed mixer, adds antioxidant 164, with
The rotating speed stirring 20min of 950r/min, obtains mixture b;
D. pelletize: mixture c is added carry out melt blending in double screw extruder, extrusion, cooling, pelletize must be combined grain
Son, double screw extruder is divided into five temperature subregions, and wherein, each area temperature control is: an area: 178 DEG C, 2nd area: 188 DEG C, three
Area: 198 DEG C, 4th area: 208 DEG C, 5th area: 219 DEG C, head: 219 DEG C;Screw speed is 120r/min.
(2) prepare plasticiser
By 4 parts of Pulvis Talci, 4 parts of limestone, 2 parts of paraffin, 1 part of methylcellulose, 0.3 part of polycaprolactam puts into mulser
High-speed rotation agitating heating 15 minutes, has then been become the raw material of paste to extrude, cools down in bulk through air-cooler, places into pulverizer
Inside it is ground into powder, powder material is inputted modified machine inlet, after IR Catalysis cracking and puffing, raw material passes through special pipeline
Enter pelletize tower crane molding, get product.
(3) prepare transparent beverage suction pipe
(1) drying of raw material: the degradable polypropylene granule of corresponding weight portion is dried 5 hours at 95 DEG C, moisture
Control below 0.1%;
(2) batch mixing: the degradable polypropylene granule through step (1) and plasticiser, antibacterial, clarifier mixing are added anti-
Answer in device, purpose granule, at 180 DEG C, is melted into molten condition under conditions of stirring by the temperature control of reactor;
(3) modified: by the material modified fused solution adding in step (2), and vacuum stirring, mix homogeneously;
(4) feed: the raw material mixing is put in extruder, starts extruder heating function, extruder one area is arrived
The heating-up temperature in 6th area all controls at 220 DEG C, and heat time heating time is 55 minutes;
(5) extrude: open extruder main frame, suction pipe blank is extruded, and opens air pump, the pressure of air pump is set as
6mpa;
(6) stretching, cooling: the material that step (5) is extruded is stretched to bosh, and the water temperature of bosh controls 30
At DEG C, cool time is 5s;
(7) cut: the material after cooling is cut;
(8) sterilize: the material through step (7) is carried out disinfection by ultraviolet light, disinfecting time is 18 minutes, and ambient temperature controls
For 30 DEG C;
(9) case: automatically packed with platoon automatic packaging machine, then cased, being entered with ozone again after vanning
Row is sterilized.
Embodiment 3
A kind of transparent beverage suction pipe, is mainly obtained by the raw material of following weight portion: 200 parts of degradable polypropylene granule, thoroughly
14 parts of bright dose of dimethylbenzene, 1.5 parts of tas-2a dispersed lubricant, 5 parts of vanadium carbide, 4 parts of pbs polymer, thermoplastic polyester elastomer 4
Part, 3 parts of hydroxypropyl cellulose, 6 parts of Pulvis Talci, 5 parts of limestone, 3 parts of paraffin, 1.5 parts of methylcellulose, polycaprolactam 0.5
Part, 3 parts of antibacterial nano-titanium oxide;Degradable polypropylene granule is mainly made up of the raw material of following weight portion: 50 parts of polypropylene,
10 parts of starch, 30 parts of polylactic acid, antioxidant tnp6 part.
The production technology of above-mentioned transparent beverage suction pipe, comprises the steps:
(1) prepare degradable polypropylene granule
A. pre-treatment of raw material: by the polypropylene of described weight portion, tas-2a dispersed lubricant, starch and polylactic acid addition
Be carried out in deionized water cleanout fluid, and by cleaning after dry materials;
B. raw material screening: the starch of described weight portion is mixed with through pretreated material, selects by 150 mesh
The raw materials particles of screen cloth, obtain mixture a;
Plus antioxidant c.: step b gained mixture a is put in high-speed mixer, adds antioxidant tnp, with
The rotating speed stirring 30min of 1100r/min, obtains mixture b;
D. pelletize: mixture c is added carry out melt blending in double screw extruder, extrusion, cooling, pelletize must be combined grain
Son, double screw extruder is divided into five temperature subregions, and wherein, each area temperature control is: an area: 182 DEG C, 2nd area: 192 DEG C, three
Area: 202 DEG C, 4th area: 212 DEG C, 5th area: 221 DEG C, head: 221 DEG C;Screw speed is 180r/min.
(2) prepare plasticiser
6 parts of Pulvis Talci, 5 parts of limestone, 3 parts of paraffin, 1.5 parts of methylcellulose, 0.5 part of polycaprolactam puts into mulser
High-speed rotation agitating heating 20 minutes, has then been become the raw material of paste to extrude, cools down in bulk through air-cooler, places into pulverizer
Inside it is ground into powder, powder material is inputted modified machine inlet, after IR Catalysis cracking and puffing, raw material is entered by pipeline
Pelletize tower crane molding, gets product.
(3) prepare transparent beverage suction pipe
(1) drying of raw material: the degradable polypropylene granule of corresponding weight portion is dried 8 hours at 110 DEG C, moisture
Control below 0.1%;
(2) batch mixing: the degradable polypropylene granule through step (1) and plasticiser, antibacterial, clarifier mixing are added anti-
Answer in device, purpose granule, at 185 DEG C, is melted into molten condition under conditions of stirring by the temperature control of reactor;
(3) modified: by the material modified fused solution adding in step (2), and vacuum stirring, mix homogeneously;
(4) feed: the raw material mixing is put in extruder, starts extruder heating function, extruder one area is arrived
The heating-up temperature in 6th area all controls at 240 DEG C, and heat time heating time is 65 minutes;
(5) extrude: open extruder main frame, suction pipe blank is extruded, and opens air pump, the pressure of air pump is set as
7mpa;
(6) stretching, cooling: the material that step (5) is extruded is stretched to bosh, and the water temperature of bosh controls 42
At DEG C, cool time is 8s;
(7) cut: the material after cooling is cut;
(8) sterilize: the material through step (7) is carried out disinfection by ultraviolet light, disinfecting time is 20 minutes, and ambient temperature controls
For 20-40 DEG C;
(9) case: automatically packed with platoon automatic packaging machine, then cased, being entered with ozone again after vanning
Row is sterilized.
For the feature of the clearer explanation present invention, it is following contrast experiment:
Contrast groups 1: degradable polypropylene granule is changed to simple polypropylene, removes the step producing PP GRANULES,
Other are carried out in strict accordance with embodiment 2.
Contrast groups 2: plasticiser is changed to plasticiser dehp, removes production plasticiser step, other are in strict accordance with embodiment 2
Carry out.
Contrast groups 3: remove material modified, remove modified step in vacuum, other enter in strict accordance with embodiment 2 simultaneously
OK.
The present invention: carry out in strict accordance with embodiment 2.
Can be seen that from the above, compare 3 contrast groups, using the formula of the present invention and the straw of technique productions,
With respect to the contrast groups 1 being not added with degradable polypropylene granule, there is advantage capable of being fast degraded, it is to avoid pollution to environment,
With respect to the contrast groups 2 that self-control plasticiser is changed into plasticiser dehp, there is the high clear superiority of bending strength;Relatively remove and change
Property material contrast groups 3 have that intensity is high, heat distortion temperature is high, and mist degree is low, the high clear superiority of transparency;The present invention's is transparent
The straw not only bright beauty of outward appearance, and function admirable, using degradable after complete discarding, it is to avoid the pollution to environment.
Described above is the detailed description for the preferable possible embodiments of the present invention, but embodiment is not limited to this
Bright patent claim, the equal change being completed under the technical spirit suggested by all present invention or modification change, all should belong to
In the covered the scope of the claims of the present invention.
Claims (6)
1. a kind of transparent beverage suction pipe is it is characterised in that mainly obtained by the Raw material processing of following weight portion: degradable polypropylene
Granule 80-200 part, clarifier 5-14 part, material modified 10-16 part, plasticiser 8-17 part, antibacterial 1-3 part;
Described degradable polypropylene granule is mainly made up of the raw material of following weight portion: polypropylene 30-50 part, starch 2-10 part,
Polylactic acid 10-30 part, antioxidant 2-6 part;
Described material modified mainly it is made up of the raw material of following weight portion: tas-2a dispersed lubricant 0.1-1.5 part, vanadium carbide 5-
9 parts, pbs polymer 5-14 part, thermoplastic polyester elastomer 5-10 part, hydroxypropyl cellulose 2-4 part;
Described plasticiser is mainly made up of the raw material of following weight portion: Pulvis Talci 40-70 part, limestone 40-70 part, paraffin 10-
22 parts, methylcellulose 8-17 part, polycaprolactam 1-5 part.
2. a kind of transparent beverage suction pipe according to claim 1 is it is characterised in that mainly added by the raw material of following weight portion
Work obtains: 150 parts of degradable polypropylene granule, 10 parts of clarifier, material modified 12 parts, 13 parts of plasticiser, 2 parts of antibacterial;
Described degradable polypropylene granule is mainly made up of the raw material of following weight portion: 40 parts of polypropylene, 6 parts of starch, polylactic acid
20 parts, 4 parts of antioxidant;
Described material modified mainly it is made up of the raw material of following weight portion: 1 part of tas-2a dispersed lubricant, 7 parts of vanadium carbide, pbs
10 parts of polymer, 7 parts of thermoplastic polyester elastomer, 3 parts of hydroxypropyl cellulose;
Described plasticiser is mainly made up of the raw material of following weight portion: 55 parts of Pulvis Talci, 55 parts of limestone, 16 parts of paraffin, methyl
12 parts of cellulose, 3 parts of polycaprolactam.
3. a kind of transparent beverage suction pipe according to claim 1 is it is characterised in that described degradable polypropylene granule is main
Obtain by the following method:
A. pre-treatment of raw material: the polypropylene of described weight portion and polylactic acid are added in deionized water cleanout fluid and carry out clearly
Wash, and by cleaning after dry materials;
B. raw material screening: the starch of described weight portion is mixed with through pretreated material, selects by 100-150 mesh
The raw materials particles of screen cloth, obtain mixture a;
C. plus antioxidant: step b gained mixture a is put in high-speed mixer, adds antioxidant, with 800-
The rotating speed stirring 10-30min of 1100r/min, obtains mixture b;
D. pelletize: mixture b is added carry out melt blending in double screw extruder, extrusion, cooling, pelletize obtain compound particle.
4. a kind of transparent beverage suction pipe according to claim 1 it is characterised in that the preparation method of described plasticiser be by
Above-mentioned each material puts into mulser high-speed rotation agitating heating 10-20 minute by formula proportion, has then been become the raw material of paste
Extrusion, cools down in bulk through air-cooler, places into crusher for crushing and become powder, powder material is inputted modified machine inlet, passes through
After IR Catalysis cracking and puffing, raw material enters pelletize tower crane molding by pipeline, gets product.
5. the production technology according to a kind of arbitrary described transparent beverage suction pipe of claim 1-4 is it is characterised in that include as follows
Step:
(1) drying of raw material: the degradable polypropylene granule of corresponding weight portion is dried at 80-110 DEG C 3-8 hour, moisture contains
Amount controls below 0.1%;
(2) batch mixing: the degradable polypropylene granule through step (1) and plasticiser, antibacterial, clarifier mixing are added reactor
In, purpose granule, at 175-185 DEG C, is melted into molten condition under conditions of stirring by the temperature control of reactor;
(3) modified: by the material modified fused solution adding in step (2), and vacuum stirring, mix homogeneously;
(4) feed: the raw material mixing is put in extruder, starts extruder heating function, by extruder one area to 6th area
Heating-up temperature all control at 200-240 DEG C, heat time heating time be 40-65 minute;
(5) extrude: open extruder main frame, suction pipe blank is extruded, and opens air pump, the pressure of air pump is set as 5-7mpa;
(6) stretching, cooling: the material that step (5) is extruded is stretched to bosh, and the water temperature of bosh controls in 12-42
At DEG C, cool time is 2-8s;
(7) cut: the material after cooling is cut;
(8) sterilize: the material through step (7) is carried out disinfection by ultraviolet light, disinfecting time is 15-20 minute, ambient temperature controls
For 20-40 DEG C;
(9) case: automatically packed with platoon automatic packaging machine, then cased, being disappeared with ozone again after vanning
Poison.
6. according to claim 5 a kind of production technology of transparent beverage suction pipe it is characterised in that described step (5) extrusion
The suction pipe blank diameter of machine extrusion is 3-8mm.