CN106365466A - Temperable mirror and craftsmanship - Google Patents
Temperable mirror and craftsmanship Download PDFInfo
- Publication number
- CN106365466A CN106365466A CN201610859740.XA CN201610859740A CN106365466A CN 106365466 A CN106365466 A CN 106365466A CN 201610859740 A CN201610859740 A CN 201610859740A CN 106365466 A CN106365466 A CN 106365466A
- Authority
- CN
- China
- Prior art keywords
- layer
- mirror
- glass
- inorganic pigment
- tempering
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a temperable mirror. The temperable mirror comprises a glass body, one or multiple metal film layers and one inorganic pigment layer are arranged on one side of the glass body, and the metal film layers are arranged between the inorganic pigment layer and the glass body. The inorganic pigment layer comprises an inorganic glass base glaze layer, a varnish layer and a colorant layer, and the inorganic glass base glaze layer, the varnish layer and the colorant layer are welded into a whole. A glass mirror formed by combining the metal film layer and the inorganic pigment layer on the glass body achieves that the mirror is capable of being tempered, and the mirror has a good weather resistance, is uneasy to be oxidized, has strong stability in use, and expands the range of application of mirror decorations; in addition, other processes such as laminating and hollowing can be conducted after conducting cutting on the mirror so as to further improve the range of application and practicability of the mirror decorations. The temperable mirror has a wide range of application, is environment-friendly, safe and decoration resistant, has changeable and enduring esthetic effects, is suitable for indoor and outdoor decorations, simple in craftsmanship and low in cost, and is easy to realize industrial production.
Description
Technical field
The present invention relates to a kind of glass product technical field, particularly a kind of can tempering mirror.
Background technology
In building decoration engineering, glass is the class ornament materials being most widely used.With the development of building industry, glass
Architectural must use more and more extensive.Glass decoration functions till now from initially single daylighting function, gradually develop
The main flow of non-line generation building.And architectural decorative glass is to be leading with design concept and function, using glass material and artistic skill
Ingeniously, become unified harmonious entirety with decorated building, both enriched art of architecture image, and also can improve utilitarian function,
Economic worth and social value, mirror is the conventional article of everyday use that glass processing is made, for reaching certain decorative effect, glass now
Glass mirror is widely used in finishing field, and because mirror processing is limited, the mirror of existing use is all to be unable to tempering, fragile
Split, safety is low, cause the limitation that fitting-up uses.
Content of the invention
The present invention be directed to prior art exist problem, provide a kind of any cutting, can tempering mirror, be that one kind was both suitable
Indoor and outdoor ambetti mirror, can realize again energy-saving and environmental protection, will not fade, resistance to decoration, aesthetic is changeable persistently, can be
What outdoor or interior carried out decorative processing installation can tempering mirror.
In order to solve the above problems, the technical solution adopted in the present invention is:
One kind can tempering mirror, including glass body it is characterised in that: described glass body one side is provided with one or more layers
Metallic diaphragm and one layer of inorganic pigment layer, described metallic diaphragm is located between inorganic pigment layer and glass body.
Described inorganic pigment layer includes unorganic glass base glaze layer, inking oil reservoir, coloring agent layer, described unorganic glass base
Glaze layer, inking oil reservoir, coloring agent layer welding are integral.
Described metallic diaphragm is a kind of titanium, titanium oxide, titanium dioxide, chromium or zirconium refractory metal material film layer.
Described unorganic glass base glaze layer is a kind of boron oxide, boron oxide, aluminium oxide, titanium oxide, zirconium oxide, silicic acid mixing
Heat the unorganic glass base glaze layer of formation.
Described inking oil reservoir is that one kind is added by Oleum Terebinthinae, Lignum Pini Nodi alcohol, resin, ethyl cellulose, the mixing of organic flux
The inking oil reservoir that temperature is formed.
Described coloring agent layer be a kind of take on a red color, yellow, blueness, black, white, green, brown or many mixture of colours
Colorant layer.
Described metallic diaphragm is 50nm 90nm for thickness.
Described inorganic pigment layer is 110nm 150nm for thickness.
One kind can tempering mirror production technology, comprise the following steps:
Choose one block of suitable plate glass, plate glass one side carries out plating one layer or many using vacuum coating equipment
Layer metallic diaphragm, gets ready inorganic with unorganic glass base glaze layer, inking oil reservoir, dyed layer welding all-in-one-piece according to necessary requirement
Material, uniformly applies and is added on the glass of metal-plated membrane layer, then carry out high-temperature heating, until surface slowly softens, its painting is located at
The inorganic material on surface also melts, and till adhesion metal film surface, finally cools down, and making one kind can tempering mirror.
The temperature of described high-temperature heating is 550 DEG C -720 DEG C, and warm-up time is 10~20 minutes.
The invention has the beneficial effects as follows:
The glass mirror that metallic diaphragm and inorganic pigment layer are formed is combined on vitreous body, realize mirror can tempering, weatherability
Good, not oxidizable, stability in use is strong, expands mirror decoration range, carry out after also can carrying out clipping doubling, hollow etc. its
It is processed, and improves range and the practicality of decoration further.
Can tempering mirror range is wide, environmental protection, safety, resistance to decoration, aesthetic is changeable persistently, suitably indoor, outdoor
Decoration, and processing technology is simple, with low cost, it is easy to accomplish industrialized production.
Brief description
Fig. 1 is the structural reference figure of the present invention.
Specific embodiment
One kind can tempering mirror, including glass body 1, described glass body 1 one side is provided with one or more layers metallic diaphragm 2
With one layer of inorganic pigment layer 3, described metallic diaphragm 2 is located between inorganic pigment layer 3 and glass body 1.
Described inorganic pigment layer 3 includes unorganic glass base glaze layer, inking oil reservoir, coloring agent layer, described unorganic glass
Base glaze layer, inking oil reservoir, coloring agent layer welding are integral.
Metallic diaphragm 1 is a kind of titanium, titanium oxide, titanium dioxide, chromium or zirconium refractory metal material film layer.
Unorganic glass base glaze layer is that a kind of boron oxide, boron oxide, aluminium oxide, titanium oxide, zirconium oxide, silicic acid mixing are heated shape
The unorganic glass base glaze layer becoming
Inking oil reservoir is that one kind is heated and formed by Oleum Terebinthinae, Lignum Pini Nodi alcohol, resin, ethyl cellulose, the mixing of organic flux
Inking oil reservoir.
Coloring agent layer be a kind of take on a red color, the coloring agent of yellow, blueness, black, white, green, brown or many mixture of colours
Layer.
When preparing coloring agent, when preparation takes on a red color, can be obtained using cadmium red and cadmium sulfide;When preparation is in yellow, can adopt
Uranium salt, cadmium sulfide and chromate are obtained;When preparation is in blueness, can be obtained using cobalt aluminate;When preparation is in black, can be using oxidation
Iridium, C.I. Pigment Yellow 45 and cobalt salt, the mixture of manganese salt are obtained;When preparing white, stannum oxide, calcium oxide, zirconium oxide, kaolinite can be adopted
Soil is obtained;When preparation is in green, can be obtained using chromium oxide;When preparing brown, can be obtained using ferrum oxide, manganese salt.
Metallic diaphragm 2 is 50nm 90nm for thickness.
Inorganic pigment layer 3 is 110nm 150nm for thickness.
One kind can tempering mirror production technology, comprise the following steps:
Choose one block of suitable plate glass, plate glass one side carries out plating one layer or many using vacuum coating equipment
Layer metallic diaphragm, gets ready inorganic with unorganic glass base glaze layer, inking oil reservoir, dyed layer welding all-in-one-piece according to necessary requirement
Material, uniformly applies and is added on the glass of metal-plated membrane layer, then carry out high-temperature heating, until surface slowly softens, its painting is located at
The inorganic material on surface also melts, and till adhesion metal film surface, finally cools down, and making one kind can tempering mirror.
The temperature of described high-temperature heating is 550 DEG C -720 DEG C, and warm-up time is 10~20 minutes.
The glass mirror that metallic diaphragm and inorganic pigment layer are formed is combined on vitreous body, realize mirror can tempering, weatherability
Good, not oxidizable, stability in use is strong, expands mirror decoration range, carry out after also can carrying out clipping doubling, hollow etc. its
It is processed, and improves range and the practicality of decoration further.
Can tempering mirror range is wide, environmental protection, resistance to decoration, aesthetic is changeable persistently, suitably indoor, outdoor decoration,
And processing technology is simple, with low cost, it is easy to accomplish industrialized production.
Embodiment 1
One kind can tempering mirror, including glass body 1, described glass body 1 one side is provided with layer of metal film layer 2 and one layer
Inorganic pigment layer 3, described metallic diaphragm 2 is located between inorganic pigment layer 3 and glass body 1.
Inorganic pigment layer 3 includes unorganic glass base glaze layer, inking oil reservoir, coloring agent layer, its unorganic glass base glaze layer, inking
Oil reservoir, coloring agent layer welding are integral.
Metallic diaphragm 1 is titanium oxide refractory metal material film layer.
Unorganic glass base glaze layer is that a kind of boron oxide, boron oxide, aluminium oxide, titanium oxide, zirconium oxide, silicic acid mixing are heated shape
The unorganic glass base glaze layer becoming.
Inking oil reservoir is that one kind is heated and formed by Oleum Terebinthinae, Lignum Pini Nodi alcohol, resin, ethyl cellulose, the mixing of organic flux
Inking oil reservoir.
Coloring agent layer is a kind of white coloring agent layer.
When preparing white, can be obtained using stannum oxide, calcium oxide, zirconium oxide, Kaolin;
Metallic diaphragm 2 is 90nm for thickness, and inorganic pigment layer 3 is 110nm for thickness.
One kind can tempering mirror production technology, comprise the following steps:
Choose one block of suitable plate glass, plate glass one side carries out plating one layer of 90nm using vacuum coating equipment
The metallic diaphragm of thickness, gets ready with unorganic glass base glaze layer, inking oil reservoir, dyed layer welding all-in-one-piece according to necessary requirement
Inorganic material, penetrates uniform painting with vacuum magnetic control line and is added on the vitreous body of metal-plated membrane layer, then carry out 720 DEG C of high-temperature heatings 10
Minute, until glass surface slowly softens, the inorganic material that its painting is located at surface also melts, till glassivation surface, finally cold
But, making one kind can tempering mirror.
Embodiment 2
One kind can tempering mirror, including glass body 1, described glass body 1 one side is provided with double layer of metal film layer 2 and one layer
Inorganic pigment layer 3, described metallic diaphragm 2 is located between inorganic pigment layer 3 and glass body 1.
Inorganic pigment layer 3 includes unorganic glass base glaze layer, inking oil reservoir, coloring agent layer, its unorganic glass base glaze layer, inking
Oil reservoir, coloring agent layer welding are integral.
Metallic diaphragm 1 is titanium oxide refractory metal material film layer.
Unorganic glass base glaze layer is that a kind of boron oxide, boron oxide, aluminium oxide, titanium oxide, zirconium oxide, silicic acid mixing are heated shape
The unorganic glass base glaze layer becoming.
Inking oil reservoir is that one kind is heated and formed by Oleum Terebinthinae, Lignum Pini Nodi alcohol, resin, ethyl cellulose, the mixing of organic flux
Inking oil reservoir.
Coloring agent layer is that one kind takes on a red color coloring agent layer.
When preparing coloring agent, when preparation takes on a red color, it is obtained using cadmium red and cadmium sulfide.
Metallic diaphragm 2 is 50nm for thickness, and inorganic pigment layer 3 is 150nm for thickness.
One kind can tempering mirror production technology, comprise the following steps:
Choose one block of suitable plate glass, plate glass one side carries out plating one layer of 50nm using vacuum coating equipment
The metallic diaphragm of thickness, gets ready with unorganic glass base glaze layer, inking oil reservoir, dyed layer welding all-in-one-piece according to necessary requirement
Inorganic material, penetrates uniform painting with vacuum magnetic control line and is added on the vitreous body of metal-plated membrane layer, then carry out 550 DEG C of high-temperature heatings 20
Minute, until glass surface slowly softens, the inorganic material that its painting is located at surface also melts, till glassivation surface, finally cold
But, making one kind can tempering mirror.
Embodiment 3
One kind can tempering mirror, including glass body 1, described glass body 1 one side is provided with three-layer metal film layer 2 and one layer
Inorganic pigment layer 3, described metallic diaphragm 2 is located between inorganic pigment layer 3 and glass body 1.
Inorganic pigment layer 3 includes unorganic glass base glaze layer, inking oil reservoir, coloring agent layer, its unorganic glass base glaze layer, inking
Oil reservoir, coloring agent layer welding are integral.
Metallic diaphragm 1 is titanium oxide refractory metal material film layer.
Unorganic glass base glaze layer is that a kind of boron oxide, boron oxide, aluminium oxide, titanium oxide, zirconium oxide, silicic acid mixing are heated shape
The unorganic glass base glaze layer becoming.
Inking oil reservoir is that one kind is heated and formed by Oleum Terebinthinae, Lignum Pini Nodi alcohol, resin, ethyl cellulose, the mixing of organic flux
Inking oil reservoir.
Coloring agent layer is one kind is in blue-colored oxidant layer, when preparing coloring agent, when preparation is in blueness, can adopt cobalt aluminate system
?;
Metallic diaphragm 2 is 70nm for thickness, and inorganic pigment layer 3 is 130nm for thickness.
One kind can tempering mirror production technology, comprise the following steps:
Choose one block of suitable plate glass, plate glass one side carries out plating one layer of 70nm using vacuum coating equipment
The metallic diaphragm of thickness, gets ready with unorganic glass base glaze layer, inking oil reservoir, dyed layer welding all-in-one-piece according to necessary requirement
Inorganic material, penetrates uniform painting with vacuum magnetic control line and is added on the vitreous body of metal-plated membrane layer, then carry out 650 DEG C of high-temperature heatings 15
Minute, until glass surface slowly softens, the inorganic material that its painting is located at surface also melts, till glassivation surface, finally cold
But, making one kind can tempering mirror.
Claims (10)
1. one kind can tempering mirror, including glass body (1) it is characterised in that: described glass body (1) one side be provided with one layer or
Multiple layer metal film layer (2) and one layer of inorganic pigment layer (3), described metallic diaphragm (2) is located at inorganic pigment layer (3) with glass originally
Between body (1).
2. one kind according to claim 1 can tempering mirror it is characterised in that: described inorganic pigment layer (3) includes inorganic
Glass base glaze layer, inking oil reservoir, coloring agent layer, described unorganic glass base glaze layer, inking oil reservoir, coloring agent layer are fused into one
Body.
3. one kind according to claim 1 can tempering mirror it is characterised in that: described metallic diaphragm (1) is a kind of titanium, oxygen
Change titanium, titanium dioxide, chromium or zirconium refractory metal material film layer.
4. one kind according to claim 2 can tempering mirror it is characterised in that: described unorganic glass base glaze layer is a kind of oxygen
Change boron, boron oxide, aluminium oxide, titanium oxide, zirconium oxide, silicic acid mix the unorganic glass base glaze layer of formation of heating.
5. one kind according to claim 2 can tempering mirror it is characterised in that: described inking oil reservoir is a kind of by Lignum Pini Nodi
Oil, Lignum Pini Nodi alcohol, resin, ethyl cellulose, organic flux mix the inking oil reservoir of formation of heating.
6. one kind according to claim 2 can tempering mirror it is characterised in that: described coloring agent layer be one kind take on a red color, yellow
Color, blueness, black, white, the coloring agent layer of green, brown or many mixture of colours.
7. one kind according to claim 1 can tempering mirror it is characterised in that: described metallic diaphragm (2) for thickness is
50nm—90nm.
8. one kind according to claim 1 can tempering mirror it is characterised in that: described inorganic pigment layer (3) for thickness is
110nm—150nm.
9. one kind of arbitrary the claims can tempering mirror it is characterised in that: production technology, comprise the following steps:
Choose one block of suitable plate glass, plate glass one side carries out plating one or more layers gold using vacuum coating equipment
Belong to film layer, get ready with unorganic glass base glaze layer, inking oil reservoir, dyed layer welding all-in-one-piece inorganic material according to necessary requirement,
Uniformly apply and be added on the glass of metal-plated membrane layer, then carry out high-temperature heating, until surface slowly softens, its painting is located at surface
Inorganic material also melt, till adhesion metal film surface, finally cool down, making one kind can tempering mirror.
10. one kind according to claim 7 can tempering mirror it is characterised in that: the temperature of described high-temperature heating be 550
DEG C -720 DEG C, warm-up time is 10~20 minutes.