CN106351417A - Waterproof wear-resistant floor and preparing method thereof - Google Patents
Waterproof wear-resistant floor and preparing method thereof Download PDFInfo
- Publication number
- CN106351417A CN106351417A CN201610733676.0A CN201610733676A CN106351417A CN 106351417 A CN106351417 A CN 106351417A CN 201610733676 A CN201610733676 A CN 201610733676A CN 106351417 A CN106351417 A CN 106351417A
- Authority
- CN
- China
- Prior art keywords
- parts
- proof
- floor
- coatings
- abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof wearing floor, comprising base materials, a coating layer and a surface layer, wherein the base materials are formed by adhering two layers of double-layer composite plates; the surface layer is covered by the coating layer; the coating layer is prepared from, by weight, 40-80 parts of polyvinyl chloride resin, 20-40 parts of epoxy resin, 10-20 parts of chloroprene rubber, 5-10 parts of ethylene-propylene-diene monomer rubber, 20-40 parts of talcum powder, 15-30 parts of sericite powder, 10-20 parts of glass fibers, 3-6 parts of titanium dioxide, 5-10 parts of simethicone, 3-5 parts of surface active agent, 2-8 parts of chlorinated paraffin, 3-6 parts of liquid silicon rubber,10-15 parts of glycerol, 2-6 parts of aluminium oxide, 1-4 parts of brightener,1-4 parts of coupling agent, 2-4 parts of dispersing agent, 0.5-2 parts of light stabilizer and 2-4 parts of vulcanizing agent. The floor is firm, wearable and excellent in waterproof performance, and the floor has low manufacturing cost and convenient preparation process.
Description
Technical field
The present invention relates to decorative materials technology, more particularly, to a kind of water-proof and abrasion-proof floor and preparation method thereof.
Background technology
Floor is a kind of ornament materials, has beautifying functions.Its species is various, is broadly divided into solid wooden floor board and compound ground
Plate, due to solid wooden floor board price costly, so the usage amount of composite floor board is larger.Existing composite floor board is mainly by one
Veneer is bonded by glue layer by layer, the long-time phenomenon using, sheet material disengaging often.Due to the special characteristic in floor,
Often it is layed on ground, is therefore not fee from the friction with article or shoes, rub for a long time, floor surface can produce to be drawn
Trace, have even can expose inner sheet, affect aesthetics.And because floor is different by weight situation, traditional floor exists
Floor surface can be recessed after experiencing long-term weight extruding, make floor surface uneven.In addition, floor surface has
Shi Huiyu water contacts, and water penetration can make the sheet material of inside mouldy or even rotten after entering floor, shorten the service life on floor, also can
Accelerate the disengaging of sheet material.
Content of the invention
The invention aims to shortcoming present in solution prior art, and a kind of water-proof and abrasion-proof floor proposing and
Its preparation method.
A kind of water-proof and abrasion-proof floor, including base material and coatings, top layer, described base material bonded by two-layer double layer composite board and
Become, described composite plate is made up of folder polyurethane in the middle of two-layer solid wood board, and described top layer is plant epidermis, and by described coatings bag
Wrap up in, described coatings include the raw material of following weight portion: 40～80 parts of Corvic, 20～40 parts of epoxy resin, neoprene
10～20 parts of rubber, 5～10 parts of ethylene propylene diene rubber, 20～40 parts of Pulvis Talci, 15～30 parts of sericite in powder, glass fibre 10～
20 parts, 3～6 parts of titanium dioxide, 5～10 parts of dimethicone, 3～5 parts of surfactant, 2～8 parts of chlorinated paraffin, liquid silica gel 3
～6 parts, 10～15 parts of glycerol, 2～6 parts of aluminium sesquioxide, 1～4 part of brightener, 1～4 part of coupling agent, 2～4 parts of dispersant,
0.5～2 part of light stabilizer, 2～4 parts of vulcanizing agent.
Preferably, described coatings include the raw material of following weight portion: 50～70 parts of Corvic, epoxy resin 25
～35 parts, 10～20 parts of neoprene, 8～10 parts of ethylene propylene diene rubber, 30～40 parts of Pulvis Talci, 20～30 parts of sericite in powder,
12～18 parts of glass fibre, 4～6 parts of titanium dioxide, 6～10 parts of dimethicone, 3～5 parts of surfactant, chlorinated paraffin 4～6
Part, 3～6 parts of liquid silica gel, 12～15 parts of glycerol, 2～6 parts of aluminium sesquioxide, 2～4 parts of brightener, 1～3 part of coupling agent,
2～4 parts of dispersant, 1～2 part of light stabilizer, 2～4 parts of vulcanizing agent.
Preferably, described coatings include the raw material of following weight portion: 60 parts of Corvic, 30 parts of epoxy resin,
15 parts of neoprene, 9 parts of ethylene propylene diene rubber, 35 parts of Pulvis Talci, 25 parts of sericite in powder, 15 parts of glass fibre, 5 parts of titanium dioxide,
8 parts of dimethicone, 4 parts of surfactant, 5 parts of chlorinated paraffin, 5 parts of liquid silica gel, 14 parts of glycerol, 4 parts of aluminium sesquioxide,
3 parts of brightener, 2 parts of coupling agent, 3 parts of dispersant, 1.5 parts of light stabilizer, 3 parts of vulcanizing agent.
Preferably, the weight part ratio of described Corvic and epoxy resin is 1～4:1.
Preferably, described surfactant is dodecylbenzene sodium sulfonate, tween, one of castor oil hydrogenated and Pyrusussuriensiss
The mixture of alcohol, and dodecylbenzene sodium sulfonate, tween, castor oil hydrogenated is 1～4:1 with the weight part ratio of Sorbitol.
The invention allows for a kind of preparation method of water-proof and abrasion-proof floor, comprise the following steps:
S1: solid wood board is placed in cutting machine and is cut according to drawing requirement, be prepared into satisfactory solid wood board, then will
Two block specifications identical solid wood boards are placed in compounding machine, then add polyurethane in compounding machine, by two pieces of solid wood boards and polyurethane
It is combined with each other, prepared composite plate, then by the composite plate of two pieces of above-mentioned preparations with adhesive bonding together, it is placed in 40～60
DEG C baking oven in carry out consolidation process, obtain final product the base material on floor；
S2: by the Corvic of corresponding weight portion, epoxy resin, neoprene and ethylene propylene diene rubber are placed in kneader
In, and carry out mixing 4～8min at 120～140 DEG C, then add other coatings of corresponding weight portion former in kneader
Material, continues mixing 5～10 minutes, obtains final product coatings mixed slurry, then it is enterprising that coatings mixed slurry is coated on floor surface
Row pressurize, cooling and stripping operation；
S3: obtain final product water-proof and abrasion-proof floor by compressed together with the ground top layer having coated coatings for the base material on the floor of preparation.
Floor proposed by the present invention, with double layer composite board as base material, and every layer of composite plate is by folder in the middle of two-layer solid wood board
Polyurethane forms, and carries out cured after composite plate bonding, strengthens fastness and the anti-pressure ability of floor base material；Cover with paint, lacquer, colour wash, etc.
The good Corvic of layer choosing wearability is major ingredient, with the good epoxy resin of pliability as adjuvant, makes coatings have one
Fixed abrasive resistance and pliability, add neoprene to strengthen water resistance and the ageing resistace of coatings, add simultaneously
Ethylene propylene diene rubber can improve the impact resistance of coatings, thus extending the service life on floor, Pulvis Talci, sericite
The addition of powder and glass fibre makes the abrasive resistance of coatings and shock resistance significantly increase, it is to avoid plate face after the life-time service of floor
Rough phenomenon occurs, and reduces the production cost of coatings simultaneously again, and the addition of aluminium sesquioxide can be further
Improve the abrasive resistance of coatings, the floor after making to be combined has high-strength abrasion-proof performance, and the addition of surfactant can carry
The dirty performance of the overall Water-proof and oil-proof in high floor, the addition of titanium dioxide can improve the weatherability of ornament materials, extend floor
The addition of service life, and dimethicone, chlorinated paraffin, liquid silica gel and glycerol can make the preparation process of coatings
More easy to operate, faster, effect is more preferable for mixing velocity.
Specific embodiment
With reference to specific embodiment, the present invention is explained further.
Embodiment one
A kind of water-proof and abrasion-proof floor proposed by the present invention, including base material and coatings, top layer, described base material is by two-layer two-layer compound
Plate is bonded, and described composite plate is made up of folder polyurethane in the middle of two-layer solid wood board, and described top layer is plant epidermis, and described
Coatings wrap up, and described coatings include the raw material of following weight portion: 60 parts of Corvic, 30 parts of epoxy resin, neoprene
15 parts of rubber, 9 parts of ethylene propylene diene rubber, 35 parts of Pulvis Talci, 25 parts of sericite in powder, 15 parts of glass fibre, 5 parts of titanium dioxide, diformazan
8 parts of base silicone oil, 3 parts of dodecylbenzene sodium sulfonate, 1 part of Sorbitol, 5 parts of chlorinated paraffin, 5 parts of liquid silica gel, 14 parts of glycerol, three
4 parts of Al 2 O, 3 parts of brightener, 2 parts of coupling agent, 3 parts of dispersant, 1.5 parts of light stabilizer, 3 parts of vulcanizing agent.
Its preparation method, comprises the following steps:
S1: solid wood board is placed in cutting machine and is cut according to drawing requirement, be prepared into satisfactory solid wood board, then will
Two block specifications identical solid wood boards are placed in compounding machine, then add polyurethane in compounding machine, by two pieces of solid wood boards and polyurethane
It is combined with each other, prepared composite plate, then by the composite plate of two pieces of above-mentioned preparations with adhesive bonding together, it is placed in 50 DEG C
Carry out consolidation process in baking oven, obtain final product the base material on floor；
S2: by the Corvic of corresponding weight portion, epoxy resin, neoprene and ethylene propylene diene rubber are placed in kneader
In, and carry out mixing 6min at 130 DEG C, in kneader, then add other coatings raw materials of corresponding weight portion, continue mixed
Close 8 minutes, obtain final product coatings mixed slurry, then coatings mixed slurry is coated on floor surface carry out pressurize, cooling and
Stripping operation；
S3: obtain final product water-proof and abrasion-proof floor by compressed together with the ground top layer having coated coatings for the base material on the floor of preparation.
Embodiment two
A kind of water-proof and abrasion-proof floor proposed by the present invention, including base material and coatings, top layer, described base material is by two-layer two-layer compound
Plate is bonded, and described composite plate is made up of folder polyurethane in the middle of two-layer solid wood board, and described top layer is plant epidermis, and described
Coatings wrap up, and described coatings include the raw material of following weight portion: 40 parts of Corvic, 40 parts of epoxy resin, neoprene
10 parts of rubber, 9 parts of ethylene propylene diene rubber, 20 parts of Pulvis Talci, 15 parts of sericite in powder, 10 parts of glass fibre, 6 parts of titanium dioxide, diformazan
5 parts of base silicone oil, 4 parts of tween, 1 part of Sorbitol, 2 parts of chlorinated paraffin, 5 parts of liquid silica gel, 10 parts of glycerol, 4 parts of aluminium sesquioxide,
1 part of brightener, 2 parts of coupling agent, 3 parts of dispersant, 1.5 parts of light stabilizer, 3 parts of vulcanizing agent.
Its preparation method, comprises the following steps:
S1: solid wood board is placed in cutting machine and is cut according to drawing requirement, be prepared into satisfactory solid wood board, then will
Two block specifications identical solid wood boards are placed in compounding machine, then add polyurethane in compounding machine, by two pieces of solid wood boards and polyurethane
It is combined with each other, prepared composite plate, then by the composite plate of two pieces of above-mentioned preparations with adhesive bonding together, it is placed in 40 DEG C
Carry out consolidation process in baking oven, obtain final product the base material on floor；
S2: by the Corvic of corresponding weight portion, epoxy resin, neoprene and ethylene propylene diene rubber are placed in kneader
In, and carry out mixing 8min at 120 DEG C, in kneader, then add other coatings raw materials of corresponding weight portion, continue mixed
Close 5 minutes, obtain final product coatings mixed slurry, then coatings mixed slurry is coated on floor surface carry out pressurize, cooling and
Stripping operation；
S3: obtain final product water-proof and abrasion-proof floor by compressed together with the ground top layer having coated coatings for the base material on the floor of preparation.
Embodiment three
A kind of water-proof and abrasion-proof floor proposed by the present invention, including base material and coatings, top layer, described base material is by two-layer two-layer compound
Plate is bonded, and described composite plate is made up of folder polyurethane in the middle of two-layer solid wood board, and described top layer is plant epidermis, and described
Coatings wrap up, and described coatings include the raw material of following weight portion: 80 parts of Corvic, 20 parts of epoxy resin, neoprene
15 parts of rubber, 10 parts of ethylene propylene diene rubber, 40 parts of Pulvis Talci, 30 parts of sericite in powder, 20 parts of glass fibre, 5 parts of titanium dioxide, diformazan
8 parts of base silicone oil, 2 parts of dodecylbenzene sodium sulfonate, 1 part of Sorbitol, 5 parts of chlorinated paraffin, 6 parts of liquid silica gel, 14 parts of glycerol, three
6 parts of Al 2 O, 3 parts of brightener, 1 part of coupling agent, 3 parts of dispersant, 2 parts of light stabilizer, 4 parts of vulcanizing agent.
Its preparation method, comprises the following steps:
S1: solid wood board is placed in cutting machine and is cut according to drawing requirement, be prepared into satisfactory solid wood board, then will
Two block specifications identical solid wood boards are placed in compounding machine, then add polyurethane in compounding machine, by two pieces of solid wood boards and polyurethane
It is combined with each other, prepared composite plate, then by the composite plate of two pieces of above-mentioned preparations with adhesive bonding together, it is placed in 60 DEG C
Carry out consolidation process in baking oven, obtain final product the base material on floor；
S2: by the Corvic of corresponding weight portion, epoxy resin, neoprene and ethylene propylene diene rubber are placed in kneader
In, and carry out mixing 4min at 140 DEG C, in kneader, then add other coatings raw materials of corresponding weight portion, continue mixed
Close 10 minutes, obtain final product coatings mixed slurry, then coatings mixed slurry is coated on floor surface carry out pressurize, cooling and
Stripping operation；
S3: obtain final product water-proof and abrasion-proof floor by compressed together with the ground top layer having coated coatings for the base material on the floor of preparation.
Example IV
A kind of water-proof and abrasion-proof floor proposed by the present invention, including base material and coatings, top layer, described base material is by two-layer two-layer compound
Plate is bonded, and described composite plate is made up of folder polyurethane in the middle of two-layer solid wood board, and described top layer is plant epidermis, and described
Coatings wrap up, and described coatings include the raw material of following weight portion: 60 parts of Corvic, 30 parts of epoxy resin, neoprene
20 parts of rubber, 5 parts of ethylene propylene diene rubber, 35 parts of Pulvis Talci, 15 parts of sericite in powder, 20 parts of glass fibre, 3 parts of titanium dioxide, diformazan
10 parts of base silicone oil, 2 parts of tween, 2 parts of Sorbitol, 8 parts of chlorinated paraffin, 3 parts of liquid silica gel, 15 parts of glycerol, aluminium sesquioxide 4
Part, 2 parts of brightener, 3 parts of coupling agent, 2 parts of dispersant, 0.5 part of light stabilizer, 3 parts of vulcanizing agent.
Its preparation method, comprises the following steps:
S1: solid wood board is placed in cutting machine and is cut according to drawing requirement, be prepared into satisfactory solid wood board, then will
Two block specifications identical solid wood boards are placed in compounding machine, then add polyurethane in compounding machine, by two pieces of solid wood boards and polyurethane
It is combined with each other, prepared composite plate, then by the composite plate of two pieces of above-mentioned preparations with adhesive bonding together, it is placed in 50 DEG C
Carry out consolidation process in baking oven, obtain final product the base material on floor；
S2: by the Corvic of corresponding weight portion, epoxy resin, neoprene and ethylene propylene diene rubber are placed in kneader
In, and carry out mixing 6min at 120 DEG C, in kneader, then add other coatings raw materials of corresponding weight portion, continue mixed
Close 7 minutes, obtain final product coatings mixed slurry, then coatings mixed slurry is coated on floor surface carry out pressurize, cooling and
Stripping operation；
S3: obtain final product water-proof and abrasion-proof floor by compressed together with the ground top layer having coated coatings for the base material on the floor of preparation.
Embodiment five
A kind of water-proof and abrasion-proof floor proposed by the present invention, including base material and coatings, top layer, described base material is by two-layer two-layer compound
Plate is bonded, and described composite plate is made up of folder polyurethane in the middle of two-layer solid wood board, and described top layer is plant epidermis, and described
Coatings wrap up, and described coatings include the raw material of following weight portion: 60 parts of Corvic, 30 parts of epoxy resin, neoprene
15 parts of rubber, 8 parts of ethylene propylene diene rubber, 30 parts of Pulvis Talci, 20 parts of sericite in powder, 15 parts of glass fibre, 5 parts of titanium dioxide, diformazan
8 parts of base silicone oil, 3 parts of castor oil hydrogenated, 1 part of Sorbitol, 4 parts of chlorinated paraffin, 5 parts of liquid silica gel, 14 parts of glycerol, three oxidations two
2 parts of aluminum, 4 parts of brightener, 4 parts of coupling agent, 4 parts of dispersant, 1 part of light stabilizer, 2 parts of vulcanizing agent.
Its preparation method, comprises the following steps:
S1: solid wood board is placed in cutting machine and is cut according to drawing requirement, be prepared into satisfactory solid wood board, then will
Two block specifications identical solid wood boards are placed in compounding machine, then add polyurethane in compounding machine, by two pieces of solid wood boards and polyurethane
It is combined with each other, prepared composite plate, then by the composite plate of two pieces of above-mentioned preparations with adhesive bonding together, it is placed in 40 DEG C
Carry out consolidation process in baking oven, obtain final product the base material on floor；
S2: by the Corvic of corresponding weight portion, epoxy resin, neoprene and ethylene propylene diene rubber are placed in kneader
In, and carry out mixing 8min at 140 DEG C, in kneader, then add other coatings raw materials of corresponding weight portion, continue mixed
Close 6 minutes, obtain final product coatings mixed slurry, then coatings mixed slurry is coated on floor surface carry out pressurize, cooling and
Stripping operation；
S3: obtain final product water-proof and abrasion-proof floor by compressed together with the ground top layer having coated coatings for the base material on the floor of preparation.
Wear-resisting test and waterproof test are carried out to the floor of above-described embodiment one～five preparation, result of the test shows basis
The water resistance of floor entirety of preparation method preparation and anti-wear performance are all relatively strong, and the wearability on the floor of embodiment three preparation
Can be the strongest, and the floor water resistance of embodiment two preparation is preferably, and the floor of embodiment one preparation, from preparation cost, was prepared
Journey and overall performance evaluation are best.
The above, the only present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto,
Any those familiar with the art the invention discloses technical scope in, technology according to the present invention scheme and its
Inventive concept equivalent or change in addition, all should be included within the scope of the present invention.
Claims (6)
1. a kind of water-proof and abrasion-proof floor, including base material and coatings, top layer it is characterised in that described base material is double-deck multiple by two-layer
Plywood is bonded, and described composite plate is made up of folder polyurethane in the middle of two-layer solid wood board, and described top layer is plant epidermis, and by institute
State coatings parcel, and described coatings include the raw material of following weight portion: 40～80 parts of Corvic, epoxy resin 20
～40 parts, 10～20 parts of neoprene, 5～10 parts of ethylene propylene diene rubber, 20～40 parts of Pulvis Talci, 15～30 parts of sericite in powder,
10～20 parts of glass fibre, 3～6 parts of titanium dioxide, 5～10 parts of dimethicone, 3～5 parts of surfactant, chlorinated paraffin 2～8
Part, 3～6 parts of liquid silica gel, 10～15 parts of glycerol, 2～6 parts of aluminium sesquioxide, 1～4 part of brightener, 1～4 part of coupling agent,
2～4 parts of dispersant, 0.5～2 part of light stabilizer, 2～4 parts of vulcanizing agent.
2. a kind of water-proof and abrasion-proof floor according to claim 1 is it is characterised in that described coatings include following weight portion
Raw material: 50～70 parts of Corvic, 25～35 parts of epoxy resin, 10～20 parts of neoprene, ethylene propylene diene rubber 8～
10 parts, 30～40 parts of Pulvis Talci, 20～30 parts of sericite in powder, 12～18 parts of glass fibre, 4～6 parts of titanium dioxide, dimethicone
6～10 parts, 3～5 parts of surfactant, 4～6 parts of chlorinated paraffin, 3～6 parts of liquid silica gel, 12～15 parts of glycerol, three oxidations
Two 2～6 parts of aluminum, 2～4 parts of brightener, 1～3 part of coupling agent, 2～4 parts of dispersant, 1～2 part of light stabilizer, vulcanizing agent 2～4
Part.
3. a kind of water-proof and abrasion-proof floor according to claim 1 is it is characterised in that described coatings include following weight portion
Raw material: 60 parts of Corvic, 30 parts of epoxy resin, 15 parts of neoprene, 9 parts of ethylene propylene diene rubber, 35 parts of Pulvis Talci,
25 parts of sericite in powder, 15 parts of glass fibre, 5 parts of titanium dioxide, 8 parts of dimethicone, 4 parts of surfactant, 5 parts of chlorinated paraffin,
5 parts of liquid silica gel, 14 parts of glycerol, 4 parts of aluminium sesquioxide, 3 parts of brightener, 2 parts of coupling agent, 3 parts of dispersant, light stabilizer
1.5 parts, 3 parts of vulcanizing agent.
4. a kind of water-proof and abrasion-proof floor according to claim 1 is it is characterised in that described Corvic and asphalt mixtures modified by epoxy resin
The weight part ratio of fat is 1～4:1.
5. a kind of water-proof and abrasion-proof floor according to claim 1 is it is characterised in that described surfactant is dodecyl
Benzene sulfonic acid sodium salt, tween, the mixture of one of castor oil hydrogenated and Sorbitol, and dodecylbenzene sodium sulfonate, tween, hydrogenation
Oleum Ricini is 1～4:1 with the weight part ratio of Sorbitol.
6. a kind of preparation method of water-proof and abrasion-proof floor is it is characterised in that comprise the following steps:
S1: solid wood board is placed in cutting machine and is cut according to drawing requirement, be prepared into satisfactory solid wood board, then will
Two block specifications identical solid wood boards are placed in compounding machine, then add polyurethane in compounding machine, by two pieces of solid wood boards and polyurethane
It is combined with each other, prepared composite plate, then by the composite plate of two pieces of above-mentioned preparations with adhesive bonding together, it is placed in 40～60
DEG C baking oven in carry out consolidation process, obtain final product the base material on floor；
S2: by the Corvic of corresponding weight portion, epoxy resin, neoprene and ethylene propylene diene rubber are placed in kneader
In, and carry out mixing 4～8min at 120～140 DEG C, then add other coatings of corresponding weight portion former in kneader
Material, continues mixing 5～10 minutes, obtains final product coatings mixed slurry, then it is enterprising that coatings mixed slurry is coated on floor surface
Row pressurize, cooling and stripping operation；
S3: obtain final product water-proof and abrasion-proof floor by compressed together with the ground top layer having coated coatings for the base material on the floor of preparation.