CN106319927A - 珊瑚绒面料的后整理工艺 - Google Patents

珊瑚绒面料的后整理工艺 Download PDF

Info

Publication number
CN106319927A
CN106319927A CN201610692754.7A CN201610692754A CN106319927A CN 106319927 A CN106319927 A CN 106319927A CN 201610692754 A CN201610692754 A CN 201610692754A CN 106319927 A CN106319927 A CN 106319927A
Authority
CN
China
Prior art keywords
weight
weight portion
parts
successively
fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610692754.7A
Other languages
English (en)
Inventor
张金龙
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshou City Golden Needle Textile Co Ltd
Original Assignee
Changshou City Golden Needle Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshou City Golden Needle Textile Co Ltd filed Critical Changshou City Golden Needle Textile Co Ltd
Priority to CN201610692754.7A priority Critical patent/CN106319927A/zh
Publication of CN106319927A publication Critical patent/CN106319927A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种珊瑚绒面料的后整理工艺，包括如下步骤：1)将1～2重量份纳米氧化锌、3.1重量份聚(α‑烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；3)再将面料在整理液中浸轧处理，取出后恒温烘干。本发明整理后的面料性能好，且手感柔软。

Description

珊瑚绒面料的后整理工艺
技术领域
本发明涉及珊瑚绒面料的后整理工艺。
背景技术
现有面料的防霉、防蛀、抗菌、阻燃、抗静电、耐洗、防缩、抗皱、耐磨性能都有待提高，且手感不够柔软。
发明内容
本发明的目的在于提供一种珊瑚绒面料的后整理工艺，其整理后的面料具有优异的防霉、防蛀、抗菌、阻燃、抗静电、耐洗、防缩、抗皱、耐磨性能，且手感柔软。
为实现上述目的，本发明的技术方案是设计一种珊瑚绒面料的后整理工艺，包括如下步骤：
1)将1～2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
优选的，珊瑚绒面料的后整理工艺，包括如下步骤：
1)将1重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
优选的，珊瑚绒面料的后整理工艺，包括如下步骤：
1)将2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
优选的，珊瑚绒面料的后整理工艺，包括如下步骤：
1)将1.2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
本发明的优点和有益效果在于：提供一种珊瑚绒面料的后整理工艺，其整理后的面料具有优异的防霉、防蛀、抗菌、阻燃、抗静电、耐洗、防缩、抗皱、耐磨性能，且手感柔软。
“整理液”的性能和用途是由其组分及配比所决定的，且“整理液”中的不同组分会相互影响，组分及其配比会决定“整理液”的最终性能，如果组分及其配比不相互协调，单个组分所带来的有益效果，会被其他组分消减甚至消除，严重的时候，不同组分相互抵触，起不到整体综合作用，产生负作用和次品。本发明通过大量创造性劳动、反复验证，得到“整理液”的最优组分及配比，使得多个组分综合在一起、相互协调、并产生正向综合效应。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
珊瑚绒面料的后整理工艺，包括如下步骤：
1)将1～2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
实施例2
珊瑚绒面料的后整理工艺，包括如下步骤：
1)将1重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
实施例3
珊瑚绒面料的后整理工艺，包括如下步骤：
1)将2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
实施例4
珊瑚绒面料的后整理工艺，包括如下步骤：
1)将1.2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
经上述各实施例整理后的面料，具有优异的防霉、防蛀、抗菌、阻燃、抗静电、耐洗、防缩、抗皱、耐磨性能，且手感柔软。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。

Claims (4)

1.珊瑚绒面料的后整理工艺，其特征在于，包括如下步骤：
1)将1～2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
2.根据权利要求1所述的珊瑚绒面料的后整理工艺，其特征在于，包括如下步骤：
1)将1重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
3.根据权利要求1所述的珊瑚绒面料的后整理工艺，其特征在于，包括如下步骤：
1)将2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
4.根据权利要求1所述的珊瑚绒面料的后整理工艺，其特征在于，包括如下步骤：
1)将1.2重量份纳米氧化锌、3.1重量份聚(α-烷基脂肪烯砜)类化合物、1.4重量份磷酸氢二铵、2.3重量份聚二甲基硅氧烷二季胺盐、1.1重量份脂肪胺聚氧乙烯醚依次投入45重量份去离子水中，搅拌均匀；
2)再依次投入2.6重量份乙二醇、0.9重量份醇乙氧化物羧酸盐、1.9重量份柠檬酸、2.9重量份二苯醚四酸二酐、0.7重量份海藻酸钠，继续搅拌，至充分混合均匀，制得整理液；
3)再将面料在整理液中浸轧处理，取出后恒温烘干。
CN201610692754.7A 2016-08-19 2016-08-19 珊瑚绒面料的后整理工艺 Pending CN106319927A (zh)