CN106319761A - Production process of ET non-woven fabric - Google Patents
Production process of ET non-woven fabric Download PDFInfo
- Publication number
- CN106319761A CN106319761A CN201610714602.2A CN201610714602A CN106319761A CN 106319761 A CN106319761 A CN 106319761A CN 201610714602 A CN201610714602 A CN 201610714602A CN 106319761 A CN106319761 A CN 106319761A
- Authority
- CN
- China
- Prior art keywords
- hot
- woven fabrics
- composite fibre
- pet
- rolling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production process of an ET non-woven fabric. The production process comprises the steps of opening carding, hot rolling, hardening treatment and winding splitting. The production process is characterized in that the ET non-woven fabric with the low oil agent content is used as raw materials; the hardening treatment is performed after the hot rolling, so that the ET non-woven fabric capable of being subjected to hot sealing directly is obtained; the proportion of the PE fiber and the PET fiber is regulated according to different requirements on the ventilation performance and the filtering efficiency to obtain the required product. The production process can be used for drying agent package, ice bag package, medical material package or lavipeditum bag package.
Description
Technical field
The present invention relates to the production technology of a kind of ET non-woven fabrics.
Background technology
Non-woven fabrics is to use the natural plant fibre warps such as textile raw material, such as terylene, acrylon, nylon, polyvinyl chloride fibre, cotton, fiber crops
Cross nonwoven molding, the product the most referred to as non-woven fabrics i.e. produced by nonwoven fabric production technology.Desiccant package, ice bag bag
Dress, medical material packaging, foot bath bag packaging etc. are required for adding the heat-sealing of material laggard row within a package, and at present, common non-woven fabrics exists
After adding material, it usually needs be coated with last layer glue at opening part and seal, the heat-sealing of such non-woven fabrics is got up the most numerous
Trivial, complex process, efficiency is low, and easily affects the quality of product.
Summary of the invention
For the problems referred to above, the invention provides the production technology of a kind of ET non-woven fabrics, use the PE/PET of low oil preparation multiple
Condensating fiber is as raw material, and processes through stiffened after hot rolling, obtains harder ET non-woven fabrics, and can directly carry out heat
Envelope, thus simplify the ET non-woven fabrics production technology when heat-sealing, improve production efficiency.
The technical solution used in the present invention is:
The production technology of a kind of ET non-woven fabrics, comprises the following steps:
(1) shredding combing: PE/PET composite fibre feeding opener is carried out shredding, the PE/PET composite fibre after shredding
Enter carding machine and carry out combing；
(2) hot rolling: the PE/PET composite fibre after combing is entered hot-rolling mill hot rolling；
(3) stiffened processes: will carry out stiffened process from hot-rolling mill product out；
(4) winding is cut: the product after being processed by stiffened is wound into a roll through trimming meter length, carries out point after rolling again
Cut, obtain the ET non-woven fabrics of finished product.
As preferably, in described PE/PET composite fibre, PE fiber is 1:1 or 1:2 or 2 with the mass ratio of PET:
1。
As preferably, in step (2), the hot-rolled temperature of hot-rolling mill is 150-180 DEG C.
As preferably, the PE/PET composite fibre that step (1) is selected is low oil preparation PE/PET composite fibre.
The present invention, by using the PE/PET composite fibre of low oil preparation as raw material, carries out stiffened process after hot rolling, thus
Obtain the ET non-woven fabrics that can directly seal, and according to the different demands to breathability and filter efficiency, adjust PE fiber with
The ratio of PET, obtains required product, can be used for desiccant package, ice bag packaging, medical material packaging or foot bath bag packaging.
Detailed description of the invention
Below by specific embodiment, the present invention is described in further detail.
Embodiment 1
The production technology of a kind of ET non-woven fabrics, comprises the following steps:
(1) shredding combing: the PE/PET composite fibre of the low oil preparation that PE fiber and the mass ratio of PET are 1:1 is sent
Entering opener and carry out shredding, the PE/PET composite fibre after shredding enters carding machine and carries out combing；
(2) hot rolling: the PE/PET composite fibre after combing is entered hot-rolling mill hot rolling, and hot-rolled temperature is 150-180 DEG C；
(3) stiffened processes: will carry out stiffened process from hot-rolling mill product out；
(4) winding is cut: the product after being processed by stiffened is wound into a roll through trimming meter length, carries out point after rolling again
Cut, obtain the ET non-woven fabrics of finished product.
Embodiment 2
The production technology of a kind of ET non-woven fabrics, comprises the following steps:
(1) shredding combing: the PE/PET composite fibre of the low oil preparation that PE fiber and the mass ratio of PET are 1:2 is sent
Entering opener and carry out shredding, the PE/PET composite fibre after shredding enters carding machine and carries out combing；
(2) hot rolling: the PE/PET composite fibre after combing is entered hot-rolling mill hot rolling, and hot-rolled temperature is 150-180 DEG C；
(3) stiffened processes: will carry out stiffened process from hot-rolling mill product out；
(4) winding is cut: the product after being processed by stiffened is wound into a roll through trimming meter length, carries out point after rolling again
Cut, obtain the ET non-woven fabrics of finished product.
Embodiment 3
The production technology of a kind of ET non-woven fabrics, comprises the following steps:
(1) shredding combing: the PE/PET composite fibre of the low oil preparation that PE fiber and the mass ratio of PET are 2:1 is sent
Entering opener and carry out shredding, the PE/PET composite fibre after shredding enters carding machine and carries out combing；
(2) hot rolling: the PE/PET composite fibre after combing is entered hot-rolling mill hot rolling, and hot-rolled temperature is 150-180 DEG C；
(3) stiffened processes: will carry out stiffened process from hot-rolling mill product out；
(4) winding is cut: the product after being processed by stiffened is wound into a roll through trimming meter length, carries out point after rolling again
Cut, obtain the ET non-woven fabrics of finished product.
The present invention, according to the different demands to breathability and filter efficiency, adjusts the ratio of PE fiber and PET, obtains
Required product, can be used for desiccant package, ice bag packaging, medical material packaging or foot bath bag packaging.
Claims (4)
1. the production technology of an ET non-woven fabrics, it is characterised in that comprise the following steps:
(1) shredding combing: PE/PET composite fibre feeding opener is carried out shredding, and the PE/PET composite fibre after shredding enters
Carding machine carries out combing；
(2) hot rolling: the PE/PET composite fibre after combing is entered hot-rolling mill hot rolling；
(3) stiffened processes: will carry out stiffened process from hot-rolling mill product out；
(4) winding is cut: the product after being processed by stiffened is wound into a roll through trimming meter length, cuts after rolling again,
ET non-woven fabrics to finished product.
The production technology of a kind of ET non-woven fabrics the most according to claim 1, it is characterised in that the compound fibre of described PE/PET
In dimension, PE fiber is 1:1 or 1:2 or 2:1 with the mass ratio of PET.
The production technology of a kind of ET non-woven fabrics the most according to claim 1 and 2, it is characterised in that hot-rolling mill in step (2)
Hot-rolled temperature be 150-180 DEG C.
The production technology of a kind of ET non-woven fabrics the most according to claim 3, it is characterised in that the PE/ that step (1) is selected
PET composite fibre is low oil preparation PE/PET composite fibre.