CN106319728A - Production method of high-strength plastic woven bag - Google Patents
Production method of high-strength plastic woven bag Download PDFInfo
- Publication number
- CN106319728A CN106319728A CN201610705496.1A CN201610705496A CN106319728A CN 106319728 A CN106319728 A CN 106319728A CN 201610705496 A CN201610705496 A CN 201610705496A CN 106319728 A CN106319728 A CN 106319728A
- Authority
- CN
- China
- Prior art keywords
- polypropylene
- flat filament
- polyethylene
- woven bag
- filament
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a production method of a high-strength plastic woven bag. The production method comprises the following steps: firstly, preparing polypropylene primary flat filaments, polypropylene primary flat filaments and polypropylene filament yarns; secondly, performing hot stretching and hot setting to obtain polypropylene finished flat filament and polypropylene finished flat filaments; weaving on a circular weaving machine to obtain woven drum fabric; thirdly, performing coextrusion and two-way stretching on special two-way stretching level polypropylene materials to obtain a cylindrical polypropylene inner coating film, and enabling the cylindrical polypropylene inner coating film to penetrate through and sleeve the inner part of the woven plastic woven drum fabric; enabling the woven plastic woven drum fabric to enter a heating baking oven; performing pressing fit, lifting and winding to obtain the plastic woven bag with the polypropylene inner coating film. According to the production method disclosed by the invention, the high-strength polypropylene finished flat filament, the polypropylene finished flat filament and polypropylene filament yarns are respectively adopted in a warp direction and a weft direction for weaving, so that the strength of woven base cloth is guaranteed; in addition, the inner part of the woven bag is coated with a polypropylene thin film, so that the strength of the plastic woven bag is improved; the plastic woven bag is suitable for packaging powdery small particle objects.
Description
Technical field
The present invention relates to woven bag field, particularly relate to the production method of a kind of high strength plastics woven bag.
Background technology
Polywoven Bag is the packaging bag of the plastic flat wire braided utilizing warp-wise and broadwise, is widely used in daily life
Live and in work, agricultural production.And existing Polywoven Bag uses the flat filament through broadwise to have certain degree of hardness, in braiding process
In, often there is phase mutual friction in the flat filament of warp-wise and broadwise so that produces shearing force between crossing flat filament, in weaving process
The intensity of flat filament is caused infringement, also allows for the strength decline of the plastic woven cloth knit out, it is impossible to be enough satisfied to packaging
The material that requirement of strength is higher.
Summary of the invention
Present invention seek to address that the deficiencies in the prior art, and the production method of a kind of high strength plastics woven bag is provided.
The present invention for achieving the above object, by the following technical solutions: the production method of a kind of high strength plastics woven bag, its
Being characterised by, its step is as follows:
(1) polypropylene plastics granule is extruded into thin film by plastic extruder, after cutting, makes polypropylene come into being flat
Silk;Polypropylene plastic grain is extruded into thin film by plastic extruder, after cutting, makes polypropylene come into being flat filament;By polypropylene plastics
Granule is extruded into polypropylene filament yarn by plastic extruder;
(2) respectively polypropylene is come into being flat filament and polypropylene flat filament of coming into being carries out hot gas spring and thermal finalization, prepare polypropylene
Finished product flat filament and polypropylene finished product flat filament;
(3) with polypropylene finished product flat filament as warp, with polypropylene finished product flat filament and polypropylene filament yarn collectively as parallel, knit at circle
Braiding cylinder cloth is woven on machine;
(4) biaxial tension level polyethylene special-purpose material is used to cover in coextrusion and the two-way polyethylene being drawn into cylindrical shape
Film;
(5) will blow out after drum by overlay film air-blast device in the cylindric polyethylene of preparation, and be set on and be woven into
Inside plastic weaving tube cloth, entering back into heated oven, temperature is set to 90 DEG C, and in the polyethylene of liner, overlay film occurs melted, laminating
Inside Polywoven Bag, then the Polywoven Bag of overlay film in pressing, lifting and rolling are produced with polyethylene.
Particularly, the line density of the polypropylene finished product flat filament in described step (2) is more than 1600D, polypropylene finished product flat filament
Line density is more than 1500D.
Particularly, in described step (4), when coextrusion, the extrusion temperature of polyethylene extrudes slab at 240 DEG C, with
20 DEG C of temperature chillings are solidified into sheet, then carry out longitudinal stretching after 100 DEG C of preheatings, carry out cross directional stretch after thermal finalization, system
Become overlay film in the polyethylene of cylindrical shape.
The invention has the beneficial effects as follows: a kind of high strength plastics woven bag prepared by the present invention, warp-wise and broadwise are respectively adopted
High-strength polypropylene finished product flat filament and polypropylene finished product flat filament and polypropylene filament yarn carry out the braiding of base fabric, it is ensured that braiding base fabric
Strength, and be covered with polyethylene film in the inside of woven bag, not only increase the strength of Polywoven Bag, and be applicable to
The packaging of powdery small particle body.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described:
The production method of a kind of high strength plastics woven bag, it is characterised in that its step is as follows:
(1) polypropylene plastics granule is extruded into thin film by plastic extruder, after cutting, makes polypropylene come into being flat
Silk;Polypropylene plastic grain is extruded into thin film by plastic extruder, after cutting, makes polypropylene come into being flat filament;By polypropylene plastics
Granule is extruded into polypropylene filament yarn by plastic extruder;
(2) respectively polypropylene is come into being flat filament and polypropylene flat filament of coming into being carries out hot gas spring and thermal finalization, prepare polypropylene
Finished product flat filament and polypropylene finished product flat filament, the line density of polypropylene finished product flat filament is 1700D, and the line density of polypropylene finished product flat filament is
1550D。
(3) with polypropylene finished product flat filament as warp, with polypropylene finished product flat filament and polypropylene filament yarn collectively as parallel, knit at circle
Braiding cylinder cloth is woven on machine;
(4) biaxial tension level polyethylene special-purpose material is used to cover in the polyethylene of cylindrical shape is made in coextrusion and biaxial tension
Film, when coextrusion, the extrusion temperature of polyethylene extrudes slab at 240 DEG C, is solidified into sheet, then warp with 20 DEG C of temperature chillings
Carry out longitudinal stretching after 100 DEG C of preheatings, after thermal finalization, carry out cross directional stretch, make overlay film in the polyethylene of cylindrical shape;
(5) will blow out after drum by overlay film air-blast device in the cylindric polyethylene of preparation, and be set on and be woven into
Inside plastic weaving tube cloth, entering back into heated oven, temperature is set to 90 DEG C, and in the polyethylene of liner, overlay film occurs melted, laminating
Inside Polywoven Bag, then the Polywoven Bag of overlay film in pressing, lifting and rolling are produced with polyethylene.
Above the present invention is exemplarily described, it is clear that the present invention implements and is not subject to the restrictions described above,
As long as have employed method design and the various improvement that carry out of technical scheme of the present invention, or the most improved directly apply to other
Close, all within protection scope of the present invention.
Claims (3)
1. the production method of a high strength plastics woven bag, it is characterised in that its step is as follows:
(1) polypropylene plastics granule is extruded into thin film by plastic extruder, after cutting, makes polypropylene come into being flat filament;Will
Polypropylene plastic grain is extruded into thin film by plastic extruder, makes polypropylene and come into being flat filament after cutting;By polypropylene plastic grain
It is extruded into polypropylene filament yarn by plastic extruder;
(2) respectively polypropylene is come into being flat filament and polypropylene flat filament of coming into being carries out hot gas spring and thermal finalization, prepare polypropylene finished product
Flat filament and polypropylene finished product flat filament;
(3) with polypropylene finished product flat filament as warp, with polypropylene finished product flat filament and polypropylene filament yarn collectively as parallel, on circular weaving machine
Weave braiding cylinder cloth;
(4) biaxial tension level polyethylene special-purpose material overlay film in the polyethylene of cylindrical shape is made in coextrusion and biaxial tension is used;
(5), after overlay film air-blast device in the cylindric polyethylene of preparation being blown out drum, it is set on the plastics being woven into
Inside braiding cylinder cloth, entering back into heated oven, temperature is set to 90 DEG C, and in the polyethylene of liner, overlay film occurs melted, is fitted in and moulds
Inside material woven bag, then the Polywoven Bag of overlay film in pressing, lifting and rolling are produced with polyethylene.
The production method of a kind of high strength plastics woven bag the most according to claim 1, it is characterised in that particularly, described
The line density of the polypropylene finished product flat filament in step (2) is more than 1600D, and the line density of polypropylene finished product flat filament is more than 1500D.
The production method of a kind of high strength plastics woven bag the most according to claim 1, it is characterised in that described step (4)
In, when coextrusion, the extrusion temperature of polyethylene extrudes slab at 240 DEG C, is solidified into sheet, then warp with 20 DEG C of temperature chillings
Carry out longitudinal stretching after 100 DEG C of preheatings, after thermal finalization, carry out cross directional stretch, make overlay film in the polyethylene of cylindrical shape.