The preparation method of Dustless writing board special coating
Technical field
The present invention relates to a kind of preparation method of Dustless writing board special coating.
Background technology
Present Dustless writing board is various in style, does not possess generally and writes and wipe for a long time, does not reach long-lived effect
Fruit
The content of the invention
In order to solve the above problems, the present invention provides a kind of making side of long-lived Dustless writing board special coating
Method.
To reach above-mentioned purpose, the preparation method of Dustless writing board special coating of the invention, described method is at least wrapped
Include making lower floor coating step:
One) No. 1 resin is prepared:
Take following raw materials:
Organic siliconresin XIAMETER RSN-6018:20-50 parts,
15-30 parts of silicone polyester resin Hypomer SPE-115,
Saturated polyester resin DYNAPOL-L658:25-50 parts and 5-25 parts of solvent.
(1) solvent part of above-mentioned formula ratio, is added under normal temperature in a kettle., with 1-5 DEG C per minute of speed after addition
Temperature is raised to 80 DEG C;
(2) organic siliconresin of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
XIAMETER RSN-6018 and silicone polyester resin Hypomer SPE-115;Raised after addition with 1-5 DEG C per minute of speed
To 100 DEG C, it is kept stirring for, thermostatic 60 minutes;
(3) the saturated polyester resin DYNAPOL-L658 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute, is added
Plus after be increased to 120 DEG C with 1-5 DEG C per minute of speed, be kept stirring for, thermostatic 3 hours;
(4) it is cooled to after normal temperature and discharges;
Two) No. 2 resins are prepared
Take following raw materials:
Organic siliconresin XIAMETER RSN-0805:5-50 parts,
Epoxy resin DER331:10-70 parts, 5-25 parts of solvent,
(1) solvent of above-mentioned formula ratio in a kettle. under normal temperature, temperature is raised after addition with 1-5 DEG C per minute of speed
To 80 DEG C;
(2) organic siliconresin of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute under stirring
XIAMETER RSN-0805,100 DEG C are increased to after addition with 1-5 DEG C per minute of speed;
(3) the epoxy resin DER331 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute, with every point after addition
The speed of 1-5 DEG C of clock raises temperature to 120 DEG C, is kept stirring for, thermostatic 3 hours,
(4) it is cooled to after normal temperature and discharges;
Three) mill base is prepared;
A, preparation white colorant
(1) raw material of following weight parts is taken:
No. 1 12-60 parts of resin, No. 2 8-50 parts of resins, Amino resin Resimene797:3-35 parts,
Titanium dioxide CR-828:10-65 parts, 0.5-5 parts of Disponer904S dispersants,
0.5-5 parts of Disponer9850 dispersants, 1-10 parts of Deurheo202 anti-settling agents, 5-25 parts of solvent;
(2) spice
First solvent part is added in agitator, stirring is opened, enclosed with 100-150/the speed stirring of minute in the case of with
The speed of 1-5 parts by weight/minute sequentially adds the Disponer904S dispersants of above-mentioned formula ratio, Disponer9850 dispersants
With Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
Titanium dioxide CR-828 and the Deurheo202 anti-settling agent for adding above-mentioned formula ratio continue to stir 20 minutes;
B, the blue mill base of preparation
(1) it is comprised the concrete steps that, takes the raw material of following weight parts:
No. 1 12-60 parts of resin, No. 2 8-50 parts of resins, Amino resin Resimene797:3-35 parts,
0.5-4 parts of phthalocyanine blue BF401,0.5-5 parts of Disponer904S dispersants,
0.5-5 parts of Disponer9850 dispersants, 1-10 parts of Deurheo202 anti-settling agents, 5-25 parts of solvent;
(2) spice
First above-mentioned solvent is added in agitator, stirring is opened ,/speed the stirring at low speed of minute is enclosed with 100-150, and
Successively with the speed of 1-5 parts by weight/minute add the Disponer904S dispersants of formula ratio, Disponer9850 dispersants and
Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
The phthalocyanine blue BF401 and anti-settling agent of above-mentioned formula ratio are added, continues to stir 20 minutes;
C, green mill base preparation
It is comprised the concrete steps that:
(1) raw material of following weight parts is taken:
No. 1 12-60 parts of resin, No. 2 8-50 parts of resins, Amino resin Resimene797:3-35 parts,
0.5-2 parts of 0.5-4 parts of dark green 5339D, dark green 5309H, 0.5-5 parts of Disponer904S dispersants,
0.5-5 parts of Disponer9850 dispersants, 1-10 parts of Deurheo202 anti-settling agents, 5-25 parts of solvent;
(2) spice
First above-mentioned solvent is added in agitator, stirring is opened ,/speed the stirring at low speed of minute is enclosed with 100-150, and
Successively with the speed of 1-5 parts by weight/minute add the Disponer904S dispersants of formula ratio, Disponer9850 dispersants and
Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
After stirring, successively by formula ratio add after dark green 5339D and dark green 5309H stir 10 minutes after,
Again plus formula ratio anti-settling agent, continue stir 20 minutes;
D, black color paste preparation
It is comprised the concrete steps that:
(1) raw material of following weight parts is taken:
No. 1 12-60 parts of resin, No. 2 8-50 parts of resins, Amino resin Resimene797:3-35,
0.5-2.0 parts of carbon black FW-200,0.5-5 parts of Disponer904S dispersants,
0.5-5 parts of Disponer9850 dispersants, 1-10 parts of Deurheo202 anti-settling agents, 5-25 parts of solvent;
2) spice
First above-mentioned solvent is added in agitator, stirring is opened ,/speed the stirring at low speed of minute is enclosed with 100-150, and
Successively with the speed of 1-5 parts by weight/minute add the Disponer904S dispersants of formula ratio, Disponer9850 dispersants and
Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
After stirring, carbon black FW-200 is added by formula ratio successively, after stirring 10 minutes, the anti-settling of formula ratio is added
Agent, continues to stir 20 minutes;
Four) coating is allocated;
It is comprised the concrete steps that:
Take the raw material of following weight parts:
No. 1 12-60 parts of resin, No. 2 8-50 parts of resins, Amino resin Resimene797:3-35 parts,
20-60 parts of white colorant, 0-5 parts of black color paste, blue mill base 0-5 parts, green mill base 0-5 parts,
It is micronized wax DeuWax FA-115:5-30 parts, 0.1-5 parts of Levaslip876 levelling agents,
Levelling agent Levelol TSP:1-5 parts, Adherant1051 adhesion promoters:0.1-3 parts,
1-4 parts of curing accelerator Catacure KB;5-45 parts of solvent;
Wherein, black color paste, blue mill base and green mill base can not be zero simultaneously;
The raw material of above-mentioned formula ratio is distinguished in metered agitator in the case of stirring, after stirring about 60 minutes
For finished product coating.
Preferably, the step of also including making investment precoat:
One) No. 3 resins are prepared:
Take following raw materials:
Organic siliconresin DOW CORNING TORAY AY42-151:25-65 parts,
15-30 parts of silicone polyester resin Hypomer SPE-115,
Saturated polyester resin DYNAPOL-L658:25-50 parts and 5-25 parts of solvent;
(1) above-mentioned formula ratio solvent, is added under normal temperature in a kettle., is raised after addition with 1-5 DEG C per minute of speed
Temperature is to 120 DEG C;
(2) the organic siliconresin DOW of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
CORNING TORAY AY42-151 and silicone polyester resin Hypomer SPE-115;With 1-5 DEG C per minute of speed after addition
140 DEG C are increased to, is kept stirring for, thermostatic 60 minutes;
(3) the saturated polyester resin DYNAPOL-L658 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute, is added
Plus after be kept stirring for, constant temperature 140 DEG C 3 hours;
(4) it is cooled to after normal temperature and discharges;
Two) No. 4 resins are prepared:
Take following raw materials:
Organic siliconresin DOW CORNING 840RESIN:25-65 parts,
Saturated polyester resin DYNAPOL-L658:25-65 parts and 5-25 parts of solvent;
(1) above-mentioned formula ratio solvent, is added under normal temperature in a kettle., is raised after addition with 1-5 DEG C per minute of speed
Temperature is to 120 DEG C;
(2) the organic siliconresin DOW of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
CORNING840RESIN and saturated polyester resin DYNAPOL-L658;After addition 140 are increased to 1-5 DEG C per minute of speed
DEG C, it is kept stirring for, thermostatic 3 hours;
(3) it is cooled to after normal temperature and discharges;
Three) coating is allocated;
It is comprised the concrete steps that:
Take the raw material of following weight parts:
No. 3 12-60 parts of resins, No. 4 8-50 parts of resins, Amino resin Resimene797:3-35 parts,
3033-35 parts of Amino resin CYMEL, micronizing wax DeuWax FA-115:5-30 parts,
0.1-5 parts of Levaslip876 levelling agents, levelling agent DOW CORNING 29RESIN:1-5 parts;5-45 parts of solvent;
Adherant1051 adhesion promoters:0.1-3 parts, 1-4 parts of curing accelerator Catacure KB.
To reach above-mentioned purpose, dust-free writing board manufacturing method of the invention, described method comprises the steps:
Brush on a metal plate under first pass after coating, drying;
Brush on a metal plate after second time lower coating, drying;
Brush on a metal plate after the 3rd time lower coating, drying;
Brush on a metal plate after first pass investment precoat, drying;
Brush on a metal plate after second time investment precoat, drying.
Product of the present invention has following advantage to existing projection writing plate:
1. hardness is high (being not less than 6H), lacquer painting is difficult to scratch the integrality that keeps writing surface when beneficial to writing, and city
Plate on face typically only has 1-3H hardness, and plate face has been easy to cut in long-term writing process, is unfavorable for writing
2. chemicals-resistant corrosivity is high, hardness is tested after being soaked 72 hours in butanone solvent immediately and is not less than 3H, this
Clipboard is conducive to be kept in being contacted for a long time with writing ink not by ink etch, so as to influence to wipe the writings of on the market
Plate is soaked after 2 hours in butanone solvent, and hardness only has 2B, and such clipboard one is easily to be written nib scuffing, and two are
Writing ink is easy to etch and enters clipboard, has a strong impact on wiping
3. weather resistance is excellent, pass through GB/T23987-2009《The artificial weathering aging of paint and varnish coating is exposed to the sun cruelly
It is exposed to fluorescent UV and water》Loss of gloss is 5% after 800 hours, no discoloration and other any anomalies;Do not influence to write and wipe
Wipe, this is beneficial to writing and wiping of the plate during long-term use;And clipboard on the market loses under similarity condition now
Light is 33%, and color xanthochromia has a strong impact on wiping, and such plate can gradually influence the wiping of ink during long-term use
Wipe
4. wearability is good, with being wiped 20,000 times under 1KG gravity with having soaked butanone solution absorbent cotton, film is complete, not shadow
Ring writing and wipe, this is beneficial to the long-term normal writing and wiping onboard of lettering pen;Plate on the market typically can wipe 1
Thousand times film just returns show-through
Embodiment
With reference to embodiment, the present invention is further illustrated.
Embodiment 1
One) No. 1 resin is prepared:
Take following raw materials:
Organic siliconresin XIAMETER RSN-6018:30 parts,
30 parts of silicone polyester resin Hypomer SPE-115,
Saturated polyester resin DYNAPOL-L658:50 parts and 20 parts of solvent.
(1) solvent, is added under normal temperature in a kettle., temperature is raised to 80 DEG C with 1-5 DEG C of speed after addition;
(2) organic siliconresin of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
XIAMETER RSN-6018 and silicone polyester resin Hypomer SPE-115;After addition 100 are increased to 1-5 DEG C of speed
DEG C, it is kept stirring for, thermostatic 60 minutes;
(3) the saturated polyester resin DYNAPOL-L658 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute, is added
Plus after be increased to 120 DEG C with 1-5 DEG C of speed, be kept stirring for, thermostatic 3 hours;
(4) it is cooled to after normal temperature and discharges;
In No. 1 above-mentioned resin, by utilizing organic siliconresin XIAMETER to saturated polyester resin DYNAPOL-L658
After RSN-6018 and silicone polyester resin Hypomer SPE-115 progress is high temperature modified, increase molecular resin amount, introduce silicon member
Element, can be with the anti-soil of reinforced resin, wearability and hardness.
Two) No. 2 resins are prepared
Take following raw materials:
Organic siliconresin XIAMETER RSN-0805:20 parts,
Epoxy resin DER331:40 parts, 20 parts of solvent.
(1) 20 parts of solvent is added under normal temperature in a kettle., temperature is raised to 80 DEG C with 1-5 DEG C of speed after addition;
(2) organic siliconresin of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
XIAMETER RSN-0805,100 DEG C are increased to after addition with 1-5 DEG C of speed;
(3) the epoxy resin DER331 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute, with 1-5 DEG C after addition
Speed raise temperature to 120 DEG C, be kept stirring for, thermostatic 3 hours.
(4) it is cooled to after normal temperature and discharges;
By utilizing organic siliconresin XIAMETER RSN-0805 rows to epoxy resin DER331 in No. 2 above-mentioned resins
After high temperature modified, increase molecular resin amount, introduce element silicon, can be with the adhesive force of reinforced resin, corrosion resistance, wearability and hard
Degree.
Three) mill base is prepared;
A white colorant) is prepared
1) raw material of following weight parts is taken:
No. 1 50 parts of resin, No. 2 40 parts of resins;Amino resin Resimene797:30 parts;Titanium dioxide CR-828:
50 parts, 5 parts of Disponer904S dispersants, 5 parts of Disponer9850 dispersants, 10 parts of Deurheo202 anti-settling agents, solvent 25
Part;
2) spice
First solvent part is added in agitator, stirring is opened, enclosed with 100-150/the speed stirring of minute in the case of with
The speed of 1-5 parts by weight/minute sequentially adds the Disponer904S dispersants of above-mentioned formula ratio, Disponer9850 dispersants
With Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
Titanium dioxide CR-828 and the Deurheo202 anti-settling agent for adding above-mentioned formula ratio continue to stir 20 minutes;
B blue mill base) is prepared
1) it is comprised the concrete steps that, takes the raw material of following weight parts:
No. 1 12-60 parts of resin, No. 2 8-50 parts of resins;Amino resin Resimene797:35 parts;Phthalocyanine blue
BF4011 parts, 2 parts of Disponer904S dispersants, 2 parts of Disponer9850 dispersants, 10 parts of Deurheo202 anti-settling agents are molten
25 parts of agent;
2) spice
First above-mentioned solvent is added in agitator, stirring is opened ,/speed the stirring at low speed of minute is enclosed with 100-150, and
Successively with the speed of 1-5 parts by weight/minute add the Disponer904S dispersants of formula ratio, Disponer9850 dispersants and
Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
The phthalocyanine blue BF401 and anti-settling agent of above-mentioned formula ratio are added, continues to stir 20 minutes;
C) the preparation of green mill base
It is comprised the concrete steps that:
1) raw material of following weight parts is taken:
No. 1 20 parts of resin, No. 2 20 parts of resins;Amino resin Resimene797:20 parts;
2 parts of 4 parts of dark green 5339D, dark green 5309H, 5 parts of Disponer904S dispersants, Disponer9850 points
5 parts of powder, 10 parts of Deurheo202 anti-settling agents, 25 parts of solvent;
2) spice
First above-mentioned solvent is added in agitator, stirring is opened ,/speed the stirring at low speed of minute is enclosed with 100-150, and
Successively with the speed of 1-5 parts by weight/minute add the Disponer904S dispersants of formula ratio, Disponer9850 dispersants and
Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
After stirring, successively by formula ratio add after dark green 5339D and dark green 5309H stir 10 minutes after,
Again plus formula ratio anti-settling agent, continue stir 20 minutes;
D) the preparation of black color paste
It is comprised the concrete steps that:
1) raw material of following weight parts is taken:
No. 1 20 parts of resin, No. 2 20 parts of resins;Amino resin Resimene797:20;Carbon black FW-200 2.0
Part, 5 parts of Disponer904S dispersants, 5 parts of Disponer9850 dispersants, 5 parts of Deurheo202 anti-settling agents, 5 parts of solvent;
2) spice
First above-mentioned solvent is added in agitator, stirring is opened ,/speed the stirring at low speed of minute is enclosed with 100-150, and
Successively with the speed of 1-5 parts by weight/minute add the Disponer904S dispersants of formula ratio, Disponer9850 dispersants and
Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
After stirring, carbon black FW-200 is added by formula ratio successively, after stirring 10 minutes, the anti-settling of formula ratio is added
Agent, continues to stir 20 minutes;
Four) coating is allocated;
It is comprised the concrete steps that:
Take the raw material of following weight parts:
No. 1 60 parts of resin, No. 2 50 parts of resins;Amino resin Resimene797:35 parts;
20 parts of white colorant;1 part of black color paste;Blue 1 part of mill base;Green 5 parts of mill base;
It is micronized wax DeuWax FA-115:5 parts, 0.1 part of Levaslip876 levelling agents,
Levelling agent Levelol TSP:1 part;Adherant1051 adhesion promoters:0.1 part,
1 part of curing accelerator Catacure KB;45 parts of solvent;
The raw material of above-mentioned formula ratio is distinguished in metered agitator in the case of stirring, stirred about 60 minutes,
Finished product coating can be turned into.
Embodiment 1 is finished.
Embodiment 2
One) No. 1 resin is prepared:
Take following raw materials:
Organic siliconresin XIAMETER RSN-6018:50 parts,
15 parts of silicone polyester resin Hypomer SPE-115,
Saturated polyester resin DYNAPOL-L658:25 parts and 25 parts of solvent.
(1) 25 parts of solvent, is added under normal temperature in a kettle., temperature is raised to 80 DEG C with 1-5 DEG C of speed after addition;
(2) organic siliconresin of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
XIAMETER RSN-6018 and silicone polyester resin Hypomer SPE-115;After addition 100 are increased to 1-5 DEG C of speed
DEG C, it is kept stirring for, thermostatic 60 minutes;
(3) the saturated polyester resin DYNAPOL-L658 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute, is added
Plus after be increased to 120 DEG C with 1-5 DEG C of speed, be kept stirring for, thermostatic 3 hours;
(4) it is cooled to after normal temperature and discharges;
Two) No. 2 resins are prepared
Take following raw materials:
Organic siliconresin XIAMETER RSN-0805:50 parts,
Epoxy resin DER331:70 parts, 25 parts of solvent.
(1) 25 parts of solvent is added under normal temperature in a kettle., temperature is raised to 80 DEG C with 1-5 DEG C of speed after addition;
(2) organic siliconresin of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
XIAMETER RSN-0805,100 DEG C are increased to after addition with 1-5 DEG C of speed;
(3) the epoxy resin DER331 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute, with 1-5 DEG C after addition
Speed raise temperature to 120 DEG C, be kept stirring for, thermostatic 3 hours.
(4) it is cooled to after normal temperature and discharges;
Three) mill base is prepared;
A white colorant) is prepared
1) raw material of following weight parts is taken:
No. 1 60 parts of resin, No. 2 50 parts of resins;Amino resin Resimene797:35 parts;Titanium dioxide CR-828:
65 parts, 5 parts of Disponer904S dispersants, 5 parts of Disponer9850 dispersants, 10 parts of Deurheo202 anti-settling agents, solvent 25
Part;
2) spice
First the solvent of formula ratio is added in agitator, stirring is opened ,/the feelings of the speed stirring of minute are enclosed with 100-150
Disponer904S dispersants, the Disponer9850 of above-mentioned formula ratio are sequentially added under condition with the speed of 1-5 parts by weight/minute
Dispersant and Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
Titanium dioxide CR-828 and the Deurheo202 anti-settling agent for adding above-mentioned formula ratio continue to stir 20 minutes;
B blue mill base) is prepared
1) it is comprised the concrete steps that, takes the raw material of following weight parts:
No. 1 12 parts of resin, No. 28 parts of resins;Amino resin Resimene797:3 parts;Phthalocyanine blue BF401 0.5
Part, 0.5 part of Disponer904S dispersants, 0.5 part of Disponer9850 dispersants, 1 part of Deurheo202 anti-settling agents, solvent 10
Part;
2) spice
First the solvent of above-mentioned formula ratio is added in agitator, stirring is opened ,/speed the low speed of minute is enclosed with 100-150
Stirring, and Disponer904S dispersants, the Disponer9850 of formula ratio are added with the speed of 1-5 parts by weight/minute successively
Dispersant and Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
The phthalocyanine blue BF401 and anti-settling agent of above-mentioned formula ratio are added, continues to stir 20 minutes;
C) the preparation of green mill base
It is comprised the concrete steps that:
1) raw material of following weight parts is taken:
No. 1 60 parts of resin, No. 2 50 parts of resins;Amino resin Resimene797:35 parts;
2 parts of 4 parts of dark green 5339D, dark green 5309H, 5 parts of Disponer904S dispersants, Disponer9850 points
5 parts of powder, 10 parts of Deurheo202 anti-settling agents, 20 parts of solvent;
2) spice
First the solvent of above-mentioned formula ratio is added in agitator, stirring is opened ,/speed the low speed of minute is enclosed with 100-150
Stirring, and Disponer904S dispersants, the Disponer9850 of formula ratio are added with the speed of 1-5 parts by weight/minute successively
Dispersant and Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
After stirring, successively by formula ratio add after dark green 5339D and dark green 5309H stir 10 minutes after,
Again plus formula ratio anti-settling agent, continue stir 20 minutes;
D) the preparation of black color paste
It is comprised the concrete steps that:
1) raw material of following weight parts is taken:
No. 1 12 parts of resin, No. 28 parts of resins;Amino resin Resimene797:3 parts;2 parts of carbon black FW-200,
5 parts of Disponer904S dispersants, 2 parts of Disponer9850 dispersants, 10 parts of Deurheo202 anti-settling agents, 20 parts of solvent;
2) spice
First above-mentioned solvent is added in agitator, stirring is opened ,/speed the stirring at low speed of minute is enclosed with 100-150, and
Successively with the speed of 1-5 parts by weight/minute add the Disponer904S dispersants of formula ratio, Disponer9850 dispersants and
Deurheo202 anti-settling agents;
After stirring evenly, then enclosed with 500-600/speed of minute stirs, and sequentially adds No. 1 resin of formula ratio, No. 2 trees
Fat and Amino resin Resimene797, while opening cooling water, temperature control stirs less than 40 DEG C;
After stirring, carbon black FW-200 is added by formula ratio successively, after stirring 10 minutes, the anti-settling of formula ratio is added
Agent, continues to stir 20 minutes;
Four) coating is allocated;
It is comprised the concrete steps that:
Take the raw material of following weight parts:
No. 1 60 parts of resin, No. 2 50 parts of resins;Amino resin Resimene797:35 parts;
60 parts of white colorant;5 parts of black color paste;Blue 1 part of mill base;Green 5 parts of mill base;
It is micronized wax DeuWax FA-115:5 parts, 0.1 part of Levaslip876 levelling agents,
Levelling agent Levelol TSP:5 parts;Adherant1051 adhesion promoters:3 parts,
4 parts of curing accelerator Catacure KB;45 parts of solvent;
The raw material of above-mentioned formula ratio is distinguished in metered agitator in the case of stirring, stirred about 60 minutes,
Finished product coating can be turned into.
Prepare investment precoat:
One) No. 3 resins are prepared:
Take following raw materials:
Organic siliconresin DOW CORNING TORAY AY42-151:30 parts,
25 parts of silicone polyester resin Hypomer SPE-115,
Saturated polyester resin DYNAPOL-L658:30 parts and 15 parts of solvent.
(1) 15 parts of solvent, is added under normal temperature in a kettle., after addition with 1-5 DEG C per minute of speed rise temperature extremely
120℃;
(2) the organic siliconresin DOW of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
CORNING TORAY AY42-151:30 parts and silicone polyester resin Hypomer SPE-115:25 parts;With per minute after addition
1-5 DEG C of speed is increased to 140 DEG C, is kept stirring for, thermostatic 60 minutes;
(3) the saturated polyester resin DYNAPOL-L658 of above-mentioned formula ratio is added with the speed of 1-5 parts by weight/minute:30
Part, it is kept stirring for after addition, constant temperature 140 DEG C/3 hours;
(4) it is cooled to after normal temperature and discharges;
Two) No. 4 resins are prepared:
Take following raw materials:
Organic siliconresin DOW CORNING 840RESIN:45 parts,
Saturated polyester resin DYNAPOL-L658:45 parts and 10 parts of solvent.
(1) 10 parts of solvent, is added under normal temperature in a kettle., after addition with 1-5 DEG C per minute of speed rise temperature extremely
120℃;
(2) the organic siliconresin DOW of above-mentioned formula ratio, is added with the speed of 1-5 parts by weight/minute under stirring
CORNING840RESIN:45 parts and saturated polyester resin DYNAPOL-L658:45 parts;With 1-5 DEG C per minute of speed after addition
140 DEG C are increased to, is kept stirring for, thermostatic 3 hours;
(3) it is cooled to after normal temperature and discharges;
Three) coating is allocated;
It is comprised the concrete steps that:
Take the raw material of following weight parts:
No. 3 25 parts of resins, No. 4 25 parts of resins;Amino resin Resimene797:3 parts;High methyl-etherified amino tree
Fat
CYMEL303:7 parts;It is micronized wax DeuWax FA-115:20 parts, 2 parts of Levaslip876 levelling agents, levelling agent
DOW CORNING 29RESIN:2 parts;Adherant1051 adhesion promoters:3 parts,
3 parts of curing accelerator Catacure KB;5 parts of solvent;
The raw material of above-mentioned formula ratio is distinguished in metered agitator in the case of stirring, stirred about 60 minutes,
Upper strata transparent suboptical coating can be turned into.The upper coating, which is coated in high-temperature baking on the colored paint of lower floor, can turn into matt book
Write plate.Writing board manufacturing method comprises the steps:
Brush on a metal plate under first pass after coating, drying;
Brush on a metal plate after second time lower coating, drying;
Brush on a metal plate after the 3rd time lower coating, drying;
Brush on a metal plate after first pass investment precoat, drying;
Brush on a metal plate after second time investment precoat, drying.
In summary, coating of the invention can be used for steel blackboard, and the clipboard of making can be write and wipe for a long time, reach
To long-lived effect
Obviously, those skilled in the art can carry out essence of the various changes without departing from the present invention to the formula of the present invention
Refreshing scope.So if these changes belong in the range of claims of the present invention and its equivalent technologies, then the present invention is also intended to
Cover these changes.