CN106283405A - 一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法 - Google Patents

一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法 Download PDF

Info

Publication number
CN106283405A
CN106283405A CN201610709444.1A CN201610709444A CN106283405A CN 106283405 A CN106283405 A CN 106283405A CN 201610709444 A CN201610709444 A CN 201610709444A CN 106283405 A CN106283405 A CN 106283405A
Authority
CN
China
Prior art keywords
woven fabrics
anticorrosive
fire retardant
negative oxygen
powder
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610709444.1A
Other languages
English (en)
Inventor
张泽成
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Province Taihu Ze Hong Plastic Co Ltd
Original Assignee
Anhui Province Taihu Ze Hong Plastic Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Province Taihu Ze Hong Plastic Co Ltd filed Critical Anhui Province Taihu Ze Hong Plastic Co Ltd
Priority to CN201610709444.1A priority Critical patent/CN106283405A/zh
Publication of CN106283405A publication Critical patent/CN106283405A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法，其特征在于，是由以下重量份的原料制成：生石膏2‑4，竹丝纤维粉3‑7，滑石粉2‑3，纳米电气石粉4‑8，PAMAM溶液4‑9，聚乳酸5‑10，聚乙二醇200 1‑2，微晶蜡2‑5，活性炭3‑5，薄荷香精4‑8，高碘酸钠溶液10‑15，等规聚丙烯50‑70，硅藻土3‑6，十二烷基磺酸钠1‑2，羟甲基纤维素钠适量，水适量；在无纺布中添加纳米电气石粉，可以达到连续释放负氧离子的效果，应用于服装内衬时，具有镇静、镇痛、镇咳、止痒、增食欲、降血压之效；配合添加了生石膏和滑石粉，赋予目标材料阻燃防腐的特点。

Description

一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法
技术领域
本发明涉及一种无纺布及其制备方法，具体涉及一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法。
背景技术
无纺布是一种非织造布，它是直接利用高聚物切片、短纤维或长丝将纤维通过气流或机械成网，然后经过水刺，针刺，或热轧加固，最后经过后整理形成的无编织的布料。具有柔软、透气和平面结构的新型纤维制品，优点是不产生纤维屑，强韧、耐用、丝般柔软，而且还有棉质的感觉，已被广泛用于服装领域。随着人们对“生态、健康、环保”理念的不断追求，纺织品和时尚、健康环保已紧密联系在一起，这种时尚折射出的是人类对自身的关爱和对生存环境的关注，同时由于生态纺织品概念在全球范围内的推广，以及人们追求天然舒适、回归自然、返璞归真的心理，绿色纺织品已经成为未来纺织品发展的主要趋向。
蒋颖刚在《含竹炭粉内衬布制备与吸附性能研究》中，利用竹炭粉和非织造布，通过涂层、浸轧等方法，制成多种含竹炭粉非织造衬布。然而，还存在着不能提供负氧离子、不能释放提神清凉的芳香等有利于人的身体健康、提神抗疲劳的不足之处。
发明内容
综合以上的考虑，本发明提供一种无纺布及其配方，目的在于解决当无纺布应用于汽车内饰时，不能连续释放负氧离子，提供更好的车内空间的缺陷。
为实现上述目的， 本发明的技术方案如下：
一种阻燃防腐、可连续释放负氧离子的无纺布，其特征在于，由以下重量份的原料制成：
生石膏2-4，竹丝纤维粉3-7，滑石粉2-3，纳米电气石粉4-8，PAMAM溶液4-9，聚乳酸5-10，聚乙二醇200 1-2，微晶蜡2-5，活性炭3-5，薄荷香精4-8，高碘酸钠溶液10-15，等规聚丙烯50-70，硅藻土3-6，十二烷基磺酸钠1-2，羟甲基纤维素钠适量，水适量；
所述高碘酸钠溶液的浓度为0.1-10g/L；PAMAM溶液浓度为1-10g/L。
所述的一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法，其特征在于，由以下步骤制成：
a. 在150-200℃下，将纳米电气石粉、滑石粉加入到聚乳酸中，再加入聚乙二醇200，搅拌均匀，使纳米电气石粉和滑石粉均匀分散到聚乳酸中，形成微球，过滤并烘干；
b. 将活性炭、生石膏添加到水中分散均匀，然后向其中添加薄荷香精，继续分散，分散均匀后转入抽真空条件下静置3-5h，后经离心、干燥、研磨处理得到负载有薄荷香精的活性炭粉和生石膏混合物；
c. 将竹丝纤维粉置于高碘酸钠溶液中避光氧化反应3-5h，反应温度为40-110℃，过滤、水洗、烘干，得到氧化竹纤维；将氧化竹纤维浸渍在PAMAM 溶液中3-6h，反应温度25-85℃，过滤烘干并研磨，得到PAMAM 接枝竹丝纤维粉；
d. 将等规聚丙烯、步骤a所得微球、步骤b所得混合物、步骤c所得PAMAM接枝竹丝纤维、微晶蜡粉添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得无纺布；
e. 将硅藻土加入到水中，搅拌均匀后加入十二烷基磺酸钠，搅拌均匀后加入羟甲基纤维素钠，调整粘度适中，制得浆液；将步骤d所得无纺布完全浸没于浆液，并放入超声波振荡器中超声 5-10min，取出，采用“二浸二轧”的方法，即充分浸没，用浸轧机轧液，再一次浸没，然后用浸轧机轧液后，放入焙烘机，烘焙2-5min，取出。
所述的一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法，其特征在于，步骤b中所述烘焙机烘焙温度为70-110℃。
本发明的有益效果是：在无纺布中添加纳米电气石粉，可以达到连续释放负氧离子的效果，应用于服装内衬时，具有镇静、镇痛、镇咳、止痒、增食欲、降血压之效，搭配薄荷香精，可以使人神清气爽，抗疲劳；利用聚乳酸来包裹纳米电气石粉，不仅防止了纳米电气石粉的破碎和脱落，并且促进了电气石粉与聚丙烯基底的容合与分散，同时聚乳酸具有优良的透气性、透氧性，以及抑菌及抗霉特性，提高了无纺布的抗霉性，延长使用年限；用活性炭来负载薄荷香精，增加了薄荷香精的载入量及空气接触面积，达到更加持久的释放效果，同时引入了活性炭的吸附特性，增加无纺布吸附异味的功能；竹丝纤维经高碘酸钠氧化后，其表面的羟基基团被氧化为醛基甚至羧基，与PAMAM 表面的氨基发生交联反应，从而将PAMAM 接枝到竹丝纤维上，不仅可以使竹丝纤维更加柔软蓬松，而且增强了竹丝纤维与等规聚丙烯基底的融合；配合添加了生石膏和滑石粉，赋予目标材料阻燃防腐的特点。
具体实施方式
下面结合实施例， 对本发明的具体实施方式作进一步描述。
实施例
一种阻燃防腐、可连续释放负氧离子的无纺布，其特征在于，由以下重量份的原料制成：
生石膏4，竹丝纤维粉7，滑石粉3，纳米电气石粉8，PAMAM溶液9，聚乳酸10，聚乙二醇2002，微晶蜡5，活性炭5，薄荷香精8，高碘酸钠溶液15，等规聚丙烯70，硅藻土6，十二烷基磺酸钠2，羟甲基纤维素钠适量，水适量；
所述高碘酸钠溶液的浓度为0.1-10g/L；PAMAM溶液浓度为1-10g/L。
所述的一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法，其特征在于，由以下步骤制成：
a. 在150-200℃下，将纳米电气石粉、滑石粉加入到聚乳酸中，再加入聚乙二醇200，搅拌均匀，使纳米电气石粉和滑石粉均匀分散到聚乳酸中，形成微球，过滤并烘干；
b. 将活性炭、生石膏添加到水中分散均匀，然后向其中添加薄荷香精，继续分散，分散均匀后转入抽真空条件下静置3-5h，后经离心、干燥、研磨处理得到负载有薄荷香精的活性炭粉和生石膏混合物；
c. 将竹丝纤维粉置于高碘酸钠溶液中避光氧化反应3-5h，反应温度为40-110℃，过滤、水洗、烘干，得到氧化竹纤维；将氧化竹纤维浸渍在PAMAM 溶液中3-6h，反应温度25-85℃，过滤烘干并研磨，得到PAMAM 接枝竹丝纤维粉；
d. 将等规聚丙烯、步骤a所得微球、步骤b所得混合物、步骤c所得PAMAM接枝竹丝纤维、微晶蜡粉添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得无纺布；
e. 将硅藻土加入到水中，搅拌均匀后加入十二烷基磺酸钠，搅拌均匀后加入羟甲基纤维素钠，调整粘度适中，制得浆液；将步骤d所得无纺布完全浸没于浆液，并放入超声波振荡器中超声 5-10min，取出，采用“二浸二轧”的方法，即充分浸没，用浸轧机轧液，再一次浸没，然后用浸轧机轧液后，放入焙烘机，烘焙2-5min，取出。
所述的一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法，其特征在于，步骤b中所述烘焙机烘焙温度为70-110℃。
本发明的技术参数为：
单位重量无纺布的甲醛吸附率≥11.09%，苯吸附率≥14.83%，TVOC吸附率≥13.42%。

Claims (3)

1.一种阻燃防腐、可连续释放负氧离子的无纺布，其特征在于，由以下重量份的原料制成：
生石膏2-4，竹丝纤维粉3-7，滑石粉2-3，纳米电气石粉4-8，PAMAM溶液4-9，聚乳酸5-10，聚乙二醇200 1-2，微晶蜡2-5，活性炭3-5，薄荷香精4-8，高碘酸钠溶液10-15，等规聚丙烯50-70，硅藻土3-6，十二烷基磺酸钠1-2，羟甲基纤维素钠适量，水适量；
所述高碘酸钠溶液的浓度为0.1-10g/L；PAMAM溶液浓度为1-10g/L。
2.根据权利要求1所述的一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法，其特征在于，由以下步骤制成：
a. 在150-200℃下，将纳米电气石粉、滑石粉加入到聚乳酸中，再加入聚乙二醇200，搅拌均匀，使纳米电气石粉和滑石粉均匀分散到聚乳酸中，形成微球，过滤并烘干；
b. 将活性炭、生石膏添加到水中分散均匀，然后向其中添加薄荷香精，继续分散，分散均匀后转入抽真空条件下静置3-5h，后经离心、干燥、研磨处理得到负载有薄荷香精的活性炭粉和生石膏混合物；
c. 将竹丝纤维粉置于高碘酸钠溶液中避光氧化反应3-5h，反应温度为40-110℃，过滤、水洗、烘干，得到氧化竹纤维；将氧化竹纤维浸渍在PAMAM 溶液中3-6h，反应温度25-85℃，过滤烘干并研磨，得到PAMAM 接枝竹丝纤维粉；
d. 将等规聚丙烯、步骤a所得微球、步骤b所得混合物、步骤c所得PAMAM接枝竹丝纤维、微晶蜡粉添加到螺杆挤压机进行熔融，再经纺丝、牵伸、成网、热轧后制得无纺布；
e. 将硅藻土加入到水中，搅拌均匀后加入十二烷基磺酸钠，搅拌均匀后加入羟甲基纤维素钠，调整粘度适中，制得浆液；将步骤d所得无纺布完全浸没于浆液，并放入超声波振荡器中超声 5-10min，取出，采用“二浸二轧”的方法，即充分浸没，用浸轧机轧液，再一次浸没，然后用浸轧机轧液后，放入焙烘机，烘焙2-5min，取出。
3.根据权利要求2所述的一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法，其特征在于，步骤b中所述烘焙机烘焙温度为70-110℃。
CN201610709444.1A 2016-08-24 2016-08-24 一种阻燃防腐、可连续释放负氧离子的无纺布及其制备方法 Pending CN106283405A (zh)