CN106283385A - A kind of ventilative, manufacture method of fireproof adhesion lining cloth - Google Patents
A kind of ventilative, manufacture method of fireproof adhesion lining cloth Download PDFInfo
- Publication number
- CN106283385A CN106283385A CN201610652423.0A CN201610652423A CN106283385A CN 106283385 A CN106283385 A CN 106283385A CN 201610652423 A CN201610652423 A CN 201610652423A CN 106283385 A CN106283385 A CN 106283385A
- Authority
- CN
- China
- Prior art keywords
- fiber
- binder fibre
- fireproof
- woven base
- base cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of ventilative, manufacture method of fireproof adhesion lining cloth, weigh the soybean fiber 60 95 parts according to parts by weight, silk fiber 40 70 parts, ES binder fibre 1 15 parts, then soybean fiber, silk fiber and ES binder fibre are stretched respectively, tatting, hot calendering bonding obtain non-woven base cloth layer;Use two-sided dipping mangle, the leaching of non-woven base cloth layer is processed in a liquid, use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer;Then it is wound through trimming meter length.The lining cloth ventilation and perspiration function that the present invention prepares is effective, also has grease proofing, fireproof function, can protect human-body safety, particularly in fire-fighting and oil field, can reduce the infringement to human body skin of human body extensive wound and oil.Processing technology process of the present invention simply, easily operate, is suitable to large-scale production.
Description
Technical field
The present invention relates to lining cloth production technical field, a kind of ventilative, manufacture method of fireproof adhesion lining cloth.
Background technology
Along with the reach of science and the raising of social desirability, textile garment fabric increasingly diversification and specialization, various
Garment material and Final finishing processing are arisen at the historic moment.Substantial amounts of functional fabric emerges in large numbers, and fabric is more and more smooth comfortable, various functions
More and more prominent, but the development of dress lining cloth just seems delayed simultaneously, does not catches up with the requirement that fabric matches.Reality according to market
Border demand, it is possible to the lining cloth of the problem that actually active solution part is brought because of particularity or the high demand of fabric, is called merit
Can property lining cloth.Existing capability lining cloth, although kind is a lot, but do not have a kind of lining cloth can relate to breathability, grease proofing, fire prevention simultaneously
Etc. effect.
Summary of the invention
It is an object of the invention to provide that a kind of ventilation and perspiration function is effective, grease proofing, the manufacture method of fireproof adhesion lining cloth,
With the problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
A kind of ventilative, manufacture method of fireproof adhesion lining cloth, comprises the steps:
1) stretching: claim according to parts by weight soybean fiber 60-95 part, silk fiber 40-70 part, ES binder fibre 1-15 part
Take soybean fiber, silk fiber and ES binder fibre, then soybean fiber, silk fiber and ES binder fibre are drawn respectively
Stretch;
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting;
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer;
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 0.3-2s, uses
The pressure of 6-10kg, in holding, liquid measure is 1.2-3g/m2;
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer;
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
As the further scheme of the present invention: step 1) in, according to parts by weight soybean fiber 65-90 part, silk fiber
45-65 part, ES binder fibre 3-12 part weigh soybean fiber, silk fiber and ES binder fibre.
As the further scheme of the present invention: step 1) in, according to parts by weight soybean fiber 73-85 part, silk fiber
50-60 part, ES binder fibre 5-8 part weigh soybean fiber, silk fiber and ES binder fibre.
As the further scheme of the present invention: step 4) in, liquid includes the composition of following percentage ratio: 10%-15%
Fluorine-containing silicone oil, the fire retardant of 10%-15% and the water of surplus.
As the further scheme of the present invention: step 4) in, the pH value of liquid is 6-7.
As the further scheme of the present invention: step 4) in, non-woven base cloth layer to be soaked in a liquid, the time of staying is 0.5-
1s, uses the pressure of 7-8kg, and in holding, liquid measure is 1.5-2g/m2。
Compared with prior art, the invention has the beneficial effects as follows:
The lining cloth ventilation and perspiration function that the present invention prepares is effective, also has grease proofing, fireproof function, and human body can be protected to pacify
Entirely, particularly in fire-fighting and oil field, the infringement to human body skin of human body extensive wound and oil can be reduced.System of the present invention
Make technical process simply, easily operate, be suitable to large-scale production.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of ventilative, manufacture method of fireproof adhesion lining cloth, comprise the steps:
1) stretching: weigh Semen sojae atricolor fibre according to parts by weight soybean fiber 60 parts, silk fiber 40 parts, ES binder fibre 1 part
Dimension, silk fiber and ES binder fibre, then stretch respectively to soybean fiber, silk fiber and ES binder fibre.
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting.
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer.
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 0.3s, uses 6kg
Pressure, in holding, liquid measure is 1.2g/m2, spraying equipment installs air accumulator, it is ensured that stablizing of pressure additional, to keep upper liquid measure
Stablize.Liquid includes the composition of following percentage ratio: fluorine-containing silicone oil, the fire retardant of 10% and the water of surplus, the liquid of 10%
The pH value of body is 6.
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer.
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
Embodiment 2
In the embodiment of the present invention, a kind of ventilative, manufacture method of fireproof adhesion lining cloth, comprise the steps:
1) stretching: weigh Semen sojae atricolor fibre according to parts by weight soybean fiber 95 parts, silk fiber 70 parts, ES binder fibre 15 parts
Dimension, silk fiber and ES binder fibre, then stretch respectively to soybean fiber, silk fiber and ES binder fibre.
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting.
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer.
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 2s, uses 10kg
Pressure, in holding, liquid measure is 3g/m2, spraying equipment installs air accumulator, it is ensured that stablizing of pressure additional, to keep upper liquid measure
Stable.Liquid includes the composition of following percentage ratio: fluorine-containing silicone oil, the fire retardant of 15% and the water of surplus, the liquid of 15%
PH value be 7.
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer.
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
Embodiment 3
In the embodiment of the present invention, a kind of ventilative, manufacture method of fireproof adhesion lining cloth, comprise the steps:
1) stretching: weigh Semen sojae atricolor fibre according to parts by weight soybean fiber 65 parts, silk fiber 45 parts, ES binder fibre 3 parts
Dimension, silk fiber and ES binder fibre, then stretch respectively to soybean fiber, silk fiber and ES binder fibre.
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting.
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer.
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 0.5s, uses 7kg
Pressure, in holding, liquid measure is 1.5g/m2, spraying equipment installs air accumulator, it is ensured that stablizing of pressure additional, to keep upper liquid measure
Stablize.Liquid includes the composition of following percentage ratio: fluorine-containing silicone oil, the fire retardant of 13% and the water of surplus, the liquid of 12%
The pH value of body is 7.
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer.
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
Embodiment 4
In the embodiment of the present invention, a kind of ventilative, manufacture method of fireproof adhesion lining cloth, comprise the steps:
1) stretching: weigh Semen sojae atricolor fibre according to parts by weight soybean fiber 90 parts, silk fiber 65 parts, ES binder fibre 12 parts
Dimension, silk fiber and ES binder fibre, then stretch respectively to soybean fiber, silk fiber and ES binder fibre.
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting.
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer.
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 1s, uses 8kg's
Pressure, in holding, liquid measure is 2g/m2, spraying equipment installs air accumulator, it is ensured that stablizing of pressure additional, to keep the steady of upper liquid measure
Fixed.Liquid includes the composition of following percentage ratio: fluorine-containing silicone oil, the fire retardant of 15% and the water of surplus of 15%, liquid
PH value is 6.
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer.
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
Embodiment 5
In the embodiment of the present invention, a kind of ventilative, manufacture method of fireproof adhesion lining cloth, comprise the steps:
1) stretching: weigh Semen sojae atricolor fibre according to parts by weight soybean fiber 73 parts, silk fiber 50 parts, ES binder fibre 5 parts
Dimension, silk fiber and ES binder fibre, then stretch respectively to soybean fiber, silk fiber and ES binder fibre.
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting.
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer.
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 0.5s, uses 7kg
Pressure, in holding, liquid measure is 1.5g/m2, spraying equipment installs air accumulator, it is ensured that stablizing of pressure additional, to keep upper liquid measure
Stablize.Liquid includes the composition of following percentage ratio: fluorine-containing silicone oil, the fire retardant of 10% and the water of surplus, the liquid of 10%
The pH value of body is 6.
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer.
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
Embodiment 6
In the embodiment of the present invention, a kind of ventilative, manufacture method of fireproof adhesion lining cloth, comprise the steps:
1) stretching: weigh Semen sojae atricolor fibre according to parts by weight soybean fiber 85 parts, silk fiber 60 parts, ES binder fibre 8 parts
Dimension, silk fiber and ES binder fibre, then stretch respectively to soybean fiber, silk fiber and ES binder fibre.
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting.
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer.
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 1s, uses 8kg's
Pressure, in holding, liquid measure is 2g/m2, spraying equipment installs air accumulator, it is ensured that stablizing of pressure additional, to keep the steady of upper liquid measure
Fixed.Liquid includes the composition of following percentage ratio: fluorine-containing silicone oil, the fire retardant of 12% and the water of surplus of 11%, liquid
PH value is 6.
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer.
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (6)
1. ventilative, the manufacture method of fireproof adhesion lining cloth, it is characterised in that comprise the steps:
1) stretching: weigh greatly according to parts by weight soybean fiber 60-95 part, silk fiber 40-70 part, ES binder fibre 1-15 part
Bean fiber, silk fiber and ES binder fibre, then stretch respectively to soybean fiber, silk fiber and ES binder fibre;
2) tatting: by step 1) soybean fiber, silk fiber and the ES binder fibre that stretch carry out tatting;
3) hot calendering bonding: to step 2) fleece that weaves carries out hot calendering bonding, thus obtains non-woven base cloth layer;
4) processing: use two-sided dipping mangle, soaked in a liquid by non-woven base cloth layer, the time of staying is 0.3-2s, uses 6-
The pressure of 10kg, in holding, liquid measure is 1.2-3g/m2;
5) coating: use silicone oil neutral emulsion to make prime cement after drying, and sprinkle PA rubber powder on the surface of non-woven base cloth layer;
6) winding: by step 5) coating after non-woven base cloth layer, be then wound through trimming meter length.
Ventilative, the manufacture method of fireproof adhesion lining cloth the most according to claim 1, it is characterised in that step 1) in, press
Soybean fiber, silk fibroin is weighed according to parts by weight soybean fiber 65-90 part, silk fiber 45-65 part, ES binder fibre 3-12 part
Peacekeeping ES binder fibre.
Ventilative, the manufacture method of fireproof adhesion lining cloth the most according to claim 1, it is characterised in that step 1) in, press
Soybean fiber, silk fibroin is weighed according to parts by weight soybean fiber 73-85 part, silk fiber 50-60 part, ES binder fibre 5-8 part
Peacekeeping ES binder fibre.
Ventilative, the manufacture method of fireproof adhesion lining cloth the most according to claim 1, it is characterised in that step 4) in, liquid
Body includes the fluorine-containing silicone oil of the composition of following percentage ratio: 10%-15%, the fire retardant of 10%-15% and the water of surplus.
Ventilative, the manufacture method of fireproof adhesion lining cloth the most according to claim 1, it is characterised in that step 4) in, liquid
The pH value of body is 6-7.
Ventilative, the manufacture method of fireproof adhesion lining cloth the most according to claim 1, it is characterised in that step 4) in, will
Non-woven base cloth layer soaks in a liquid, and the time of staying is 0.5-1s, uses the pressure of 7-8kg, and in holding, liquid measure is 1.5-2g/m2。