CN106280102A - A kind of Plant fiber strengthens composite plastic - Google Patents
A kind of Plant fiber strengthens composite plastic Download PDFInfo
- Publication number
- CN106280102A CN106280102A CN201610688620.8A CN201610688620A CN106280102A CN 106280102 A CN106280102 A CN 106280102A CN 201610688620 A CN201610688620 A CN 201610688620A CN 106280102 A CN106280102 A CN 106280102A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- composite plastic
- wood
- plant fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe open a kind of Plant fiber of the present invention strengthens composite plastic,By weight,Including following raw material components: Corvic 50 60 parts、40 65 parts of arghan base、Calcium carbonate 8 15 parts、Carboxyethyl cellulose 10 20 parts、Nano imvite 79 parts、Basalt fibre 35 45 parts、The wood fiber 60 65 parts、Methylisothiazolinone 3.5 4.5 parts、Camphorwood powder 24 parts、Spine stem wood powder 24 parts、Eaglewood powder 0.1 0.2 parts、Melamine cyanurate salt 9 13 parts、Carborundum powder 8 10 parts、Sodium carboxymethyl cellulose 14 20 parts、Meerschaum 37 parts、10 20 parts of asbestos powder、Tributyl 2-acetylcitrate 13 15 parts、Diethylene glycol ether acetate alone 23 parts、Magnesium stearate 12 parts、3 hydroxy benzoic acids 46 parts、Diethylenetriamine 46 parts、Palladous nitrate. 0.2 0.4 parts、Yttrium oxide 0.2 0.4 parts、23 parts of gelatin.The advantages such as it is higher that the composite plastic of the present invention has environmental protection, dimensionally stable, hot strength and impact strength, with low cost.
Description
Technical field
The present invention relates to field of material technology, specifically a kind of Plant fiber strengthens composite plastic.
Background technology
Igelite is formed by polymerization of vinyl choride monomer, is one of conventional thermoplastic.Its commodity
Referred to as " chlorine is moulded ", english abbreviation is PVC to title.
Pure Corvic is hard thermoplastic, and its decomposition temperature is very close to plasticization temperature, Er Qieji
Tool intensity is poor.Therefore, it is impossible to mould product processed with Corvic, it is necessary to add plasticizer, stabilizer, filler etc. to change
Kind performance, makes igelite, is then reprocessed into various product.
Natural plant fibre resource is extensive, of a great variety, the master related at composite material of plant fiber area research at present
The stem stalk fiber etc. of bast-fibre to be had, bamboo fiber, bagasse fibre, coir and other plant, and the wood fiber
Application in field of compound material is still in blank out, and therefore, exploitation Wood Fiber Composites has the most wide answering
Use prospect.
In recent years, owing to waste plastic " white pollution " brought that be difficult to degrade is on the rise, cause global extensively
General concern, countries in the world have put into effect the relevant laws and regulations limiting or prohibitting the use of non-degradable plastic packing article successively.On the other hand, by
Non-renewable resources in manufacturing the raw material oil of conventional plastic, along with a large amount of use of the mankind will be exhausted, thus development with
Renewable resource is that raw material, degradable environmental friendliness plastic are extremely urgent.
Summary of the invention
It is an object of the invention to provide a kind of Plant fiber and strengthen composite plastic.
The purpose of the present invention can be achieved through the following technical solutions:
A kind of Plant fiber strengthens composite plastic, by weight, including following raw material components: Corvic 50-
60 parts, arghan base 40-65 part, calcium carbonate 8-15 part, carboxyethyl cellulose 10-20 part, nano imvite 7-9 part, profound
Military rock fiber 35-45 part, wood fiber 60-65 part, Methylisothiazolinone 3.5-4.5 part, camphorwood powder 2-4 part, spine stem wood powder
2-4 part, eaglewood powder 0.1-0.2 part, melamine cyanurate salt 9-13 part, carborundum powder 8-10 part, sodium carboxymethyl cellulose
14-20 part, meerschaum 3-7 part, asbestos powder 10-20 part, tributyl 2-acetylcitrate 13-15 part, diethylene glycol monoethyl ether acetic acid
Ester 2-3 part, magnesium stearate 1-2 part, 3-hydroxy benzoic acid 4-6 part, diethylenetriamine 4-6 part, Palladous nitrate. 0.2-0.4 part, three oxygen
Change two yttrium 0.2-0.4 parts, gelatin 2-3 part.
Preferably, described a kind of Plant fiber strengthens composite plastic, by weight, including following raw material components: poly-
Vinyl chloride resin 50 parts, 40 parts of arghan base, calcium carbonate 8 parts, carboxyethyl cellulose 10 parts, nano imvite 7 parts, the Black Warrior
Rock fiber 35 parts, the wood fiber 60 parts, Methylisothiazolinone 3.5 parts, camphorwood powder 2 parts, spine stem wood powder 2 parts, eaglewood powder 0.1
Part, melamine cyanurate salt 9 parts, carborundum powder 8 parts, sodium carboxymethyl cellulose 14 parts, meerschaum 3 parts, 10 parts of asbestos powder, second
Acyl tributyl citrate 13 parts, diethylene glycol ether acetate alone 2 parts, magnesium stearate 1 part, 3-hydroxy benzoic acid 4 parts, divinyl
Triamine 4 parts, Palladous nitrate. 0.2 part, yttrium oxide 0.2 part, 2 parts of gelatin.
Preferably, described a kind of Plant fiber strengthens composite plastic, by weight, including following raw material components: poly-
Vinyl chloride resin 60 parts, 65 parts of arghan base, calcium carbonate 15 parts, carboxyethyl cellulose 20 parts, nano imvite 9 parts, profound
Military rock fiber 45 parts, the wood fiber 65 parts, Methylisothiazolinone 4.5 parts, camphorwood powder 4 parts, spine stem wood powder 4 parts, eaglewood powder
0.2 part, melamine cyanurate salt 13 parts, carborundum powder 10 parts, sodium carboxymethyl cellulose 20 parts, meerschaum 7 parts, asbestos powder 20
Part, tributyl 2-acetylcitrate 15 parts, diethylene glycol ether acetate alone 3 parts, magnesium stearate 2 parts, 3-hydroxy benzoic acid 6 parts,
Diethylenetriamine 6 parts, Palladous nitrate. 0.4 part, yttrium oxide 0.4 part, 3 parts of gelatin.
Preferably, described a kind of Plant fiber strengthens composite plastic, by weight, including following raw material components: poly-
Vinyl chloride resin 55 parts, 50 parts of arghan base, calcium carbonate 10 parts, carboxyethyl cellulose 15 parts, nano imvite 8 parts, profound
Military rock fiber 35 parts, the wood fiber 60 parts, Methylisothiazolinone 4 parts, camphorwood powder 3 parts, spine stem wood powder 3 parts, eaglewood powder 0.2
Part, melamine cyanurate salt 12 parts, carborundum powder 9 parts, sodium carboxymethyl cellulose 15 parts, meerschaum 4 parts, 15 parts of asbestos powder,
Tributyl 2-acetylcitrate 14 parts, diethylene glycol ether acetate alone 2 parts, magnesium stearate 1 part, 3-hydroxy benzoic acid 5 parts, diethyl
Alkene triamine 5 parts, Palladous nitrate. 0.4 part, yttrium oxide 0.4 part, 3 parts of gelatin.
Beneficial effects of the present invention: the composite plastic of the present invention has environmental protection, dimensionally stable, hot strength and impact strength
Higher, the advantage such as with low cost.
Detailed description of the invention
Below in conjunction with specific embodiment, the present invention is described in further detail.
Embodiment 1
A kind of Plant fiber strengthens composite plastic, by weight, including following raw material components: Corvic 50
Part, 40 parts of arghan base, calcium carbonate 8 parts, carboxyethyl cellulose 10 parts, nano imvite 7 parts, basalt fibre 35 parts,
The wood fiber 60 parts, Methylisothiazolinone 3.5 parts, camphorwood powder 2 parts, spine stem wood powder 2 parts, eaglewood powder 0.1 part, cyanuric acid three
9 parts of paracyanogen amine salt, carborundum powder 8 parts, sodium carboxymethyl cellulose 14 parts, meerschaum 3 parts, 10 parts of asbestos powder, acetyl tributyl citrate three
Butyl ester 13 parts, diethylene glycol ether acetate alone 2 parts, magnesium stearate 1 part, 3-hydroxy benzoic acid 4 parts, diethylenetriamine 4 parts, nitre
Acid palladium 0.2 part, yttrium oxide 0.2 part, 2 parts of gelatin.
The preparation method of the present invention is same as the prior art.
Embodiment 2
A kind of Plant fiber strengthens composite plastic, by weight, including following raw material components: Corvic 60
Part, 65 parts of arghan base, calcium carbonate 15 parts, carboxyethyl cellulose 20 parts, nano imvite 9 parts, basalt fibre 45 parts,
The wood fiber 65 parts, Methylisothiazolinone 4.5 parts, camphorwood powder 4 parts, spine stem wood powder 4 parts, eaglewood powder 0.2 part, cyanuric acid three
13 parts of paracyanogen amine salt, carborundum powder 10 parts, sodium carboxymethyl cellulose 20 parts, meerschaum 7 parts, 20 parts of asbestos powder, acetyl tributyl citrate
Tributyl 15 parts, diethylene glycol ether acetate alone 3 parts, magnesium stearate 2 parts, 3-hydroxy benzoic acid 6 parts, diethylenetriamine 6 parts,
Palladous nitrate. 0.4 part, yttrium oxide 0.4 part, 3 parts of gelatin.
The preparation method of the present invention is same as the prior art.
Embodiment 3
A kind of Plant fiber strengthens composite plastic, by weight, including following raw material components: Corvic 55
Part, 50 parts of arghan base, calcium carbonate 10 parts, carboxyethyl cellulose 15 parts, nano imvite 8 parts, basalt fibre 35 parts,
The wood fiber 60 parts, Methylisothiazolinone 4 parts, camphorwood powder 3 parts, spine stem wood powder 3 parts, eaglewood powder 0.2 part, cyanuric acid trimerization
Cyanamide salt 12 parts, carborundum powder 9 parts, sodium carboxymethyl cellulose 15 parts, meerschaum 4 parts, 15 parts of asbestos powder, acetyl tributyl citrate three fourth
Ester 14 parts, diethylene glycol ether acetate alone 2 parts, magnesium stearate 1 part, 3-hydroxy benzoic acid 5 parts, diethylenetriamine 5 parts, nitric acid
Palladium 0.4 part, yttrium oxide 0.4 part, 3 parts of gelatin.
The preparation method of the present invention is same as the prior art.
Claims (4)
1. a Plant fiber strengthens composite plastic, it is characterised in that by weight, including following raw material components: polychlorostyrene second
Olefine resin 50-60 part, arghan base 40-65 part, calcium carbonate 8-15 part, carboxyethyl cellulose 10-20 part, nano imvite
7-9 part, basalt fibre 35-45 part, wood fiber 60-65 part, Methylisothiazolinone 3.5-4.5 part, camphorwood powder 2-4 part, spine
Stem wood powder 2-4 part, eaglewood powder 0.1-0.2 part, melamine cyanurate salt 9-13 part, carborundum powder 8-10 part, carboxymethyl
Sodium cellulosate 14-20 part, meerschaum 3-7 part, asbestos powder 10-20 part, tributyl 2-acetylcitrate 13-15 part, diethylene glycol list
Ethyl ether acetate ester 2-3 part, magnesium stearate 1-2 part, 3-hydroxy benzoic acid 4-6 part, diethylenetriamine 4-6 part, Palladous nitrate. 0.2-0.4
Part, yttrium oxide 0.2-0.4 part, gelatin 2-3 part.
A kind of Plant fiber the most according to claim 1 strengthens composite plastic, it is characterised in that by weight, including
Following raw material components: Corvic 50 parts, 40 parts of arghan base, calcium carbonate 8 parts, carboxyethyl cellulose 10 parts, receive
Rice montmorillonite 7 parts, basalt fibre 35 parts, the wood fiber 60 parts, Methylisothiazolinone 3.5 parts, camphorwood powder 2 parts, spine stem wood
2 parts of powder, eaglewood powder 0.1 part, melamine cyanurate salt 9 parts, carborundum powder 8 parts, sodium carboxymethyl cellulose 14 parts, meerschaum
3 parts, 10 parts of asbestos powder, tributyl 2-acetylcitrate 13 parts, diethylene glycol ether acetate alone 2 parts, magnesium stearate 1 part, 3-hydroxyl
Yl benzoic acid 4 parts, diethylenetriamine 4 parts, Palladous nitrate. 0.2 part, yttrium oxide 0.2 part, 2 parts of gelatin.
A kind of Plant fiber the most according to claim 1 strengthens composite plastic, it is characterised in that by weight, including
Following raw material components: Corvic 60 parts, 65 parts of arghan base, calcium carbonate 15 parts, carboxyethyl cellulose 20 parts, receive
Rice montmorillonite 9 parts, basalt fibre 45 parts, the wood fiber 65 parts, Methylisothiazolinone 4.5 parts, camphorwood powder 4 parts, spine stem wood
4 parts of powder, eaglewood powder 0.2 part, melamine cyanurate salt 13 parts, carborundum powder 10 parts, sodium carboxymethyl cellulose 20 parts, Hai Pao
7 parts of stone, 20 parts of asbestos powder, tributyl 2-acetylcitrate 15 parts, diethylene glycol ether acetate alone 3 parts, magnesium stearate 2 parts, 3-
Hydroxy benzoic acid 6 parts, diethylenetriamine 6 parts, Palladous nitrate. 0.4 part, yttrium oxide 0.4 part, 3 parts of gelatin.
A kind of Plant fiber the most according to claim 1 strengthens composite plastic, it is characterised in that by weight, including
Following raw material components: Corvic 55 parts, 50 parts of arghan base, calcium carbonate 10 parts, carboxyethyl cellulose 15 parts, receive
Rice montmorillonite 8 parts, basalt fibre 35 parts, the wood fiber 60 parts, Methylisothiazolinone 4 parts, camphorwood powder 3 parts, spine stem wood powder 3
Part, eaglewood powder 0.2 part, melamine cyanurate salt 12 parts, carborundum powder 9 parts, sodium carboxymethyl cellulose 15 parts, meerschaum 4
Part, 15 parts of asbestos powder, tributyl 2-acetylcitrate 14 parts, diethylene glycol ether acetate alone 2 parts, magnesium stearate 1 part, 3-hydroxyl
5 parts of benzoic acid, diethylenetriamine 5 parts, Palladous nitrate. 0.4 part, yttrium oxide 0.4 part, 3 parts of gelatin.