CN106279899A - A kind of heat insulation antibacterial food packaging material and preparation method thereof - Google Patents
A kind of heat insulation antibacterial food packaging material and preparation method thereof Download PDFInfo
- Publication number
- CN106279899A CN106279899A CN201610682072.8A CN201610682072A CN106279899A CN 106279899 A CN106279899 A CN 106279899A CN 201610682072 A CN201610682072 A CN 201610682072A CN 106279899 A CN106279899 A CN 106279899A
- Authority
- CN
- China
- Prior art keywords
- packaging material
- organobentonite
- food packaging
- antibacterial
- heat insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat insulation antibacterial food packaging material, it is prepared by the raw materials in: Low Density Polyethylene 100, nano zine oxide 3.5 3.7, Basil Essential 6.5 6.7, glycerol 24, calcium alginate 0.2 0.4, di-2-ethylhexyl maleate 34, organobentonite 12, bamboo powder 68, polyacrylonitrile fibre 79, vinyl three (β methoxy ethoxy) silane 7.5 7.7, suitable quantity of water, with Low Density Polyethylene as base material, using the nano zine oxide after silane coupler activation processing as photocatalysis antibacterial agent, and compound Basil Essential, even if still having stronger antibiotic property under conditions of unglazed, broad-spectrum antibacterial property is high;Adding modified organobentonite as filler, absorption heat-proof quality strengthens simultaneously, and the antibacterial food packaging material prepared can effectively suppress staphylococcus aureus, the growing of escherichia coli rate, and oozes out without composition at 150 DEG C, uses safety.
Description
Technical field
The present invention relates to Food Packaging technology field, particularly relate to a kind of heat insulation antibacterial food packaging material and making side thereof
Method.
Background technology
Microorganism volume is small, of a great variety, breeding rapidly and adapts to the ability of environment by force, the widest in distributed in nature
General.Major part food nutritious, moisture is high, it is easy to caused putrid and deteriorated by the pollution of microorganism, significantly
Shorten the shelf-life of food.The microorganism how preventing food is polluted, and the shelf-life of prolongation food is always the whole world and is correlated with
Scientist's research and the problem paid close attention to.Along with the development of science and technology, utilize packaging material for food prepared by antimicrobial technology
The most more can become a kind of practical and reliable antibacterial scheme.
In the last few years, along with going deep into and the expansion of Application of micron of nanotechnology research, application nano material realized
Antibacterial functions has become current current research focus." nano-ZnO/LDPE antibacterial food packaging material are developed " literary composition is with low close
The strong antibacterial action Nano-class zinc oxide that has of activation processing, as the base material of packaging for foodstuff, is passed through melting blending by degree polyethylene
Method is added in base material, then through single screw extrusion machine and inflation film manufacturing machine, the pellet of gained is blow molded into thin film, i.e. prepares and provides
Having the packaging material of antibacterial functions, result of the test shows: the packaging material prepared can not only extend the shelf-life of food, improves
The safety of food, and the antibacterial that can be effectively prevented between person to person, people and thing, people and food, thing and food is intersected
Infect, give the new implication of packaging for foodstuff and function.
But nano zine oxide Antibacterial Mechanism is photocatalysis antibacterial in literary composition, under there is no light catalysis, effect of food preservation
Difference, shelf life is short, and condition is harsh and broad-spectrum antibacterial property is narrow, needs a kind of nontoxic, durable antibacterial effect of interpolation badly and urges without light
The antibacterial compatibility therewith changed;Only have obstruct and defencive function with packaging material for food in eight-legged essay, structure is single, along with food
The importance of packaging material safety constantly rises, and the requirement of packaging material for food is continuously increased by market, it is desirable to can be fresh
Extend the shelf life with the food of high-quality, especially the demand to Active Packaging Materials because it can pass through deoxygenation, antibacterial,
Dehumidifying, the pack environment of material internal of changing package except modes such as ethylene, release ethanol, prevent the growth of microorganism, Jin Erti
The shelf-life of high food, thus be necessary prior art is modified.
Summary of the invention
The object of the invention is contemplated to make up the defect of prior art, it is provided that a kind of heat insulation antibacterial food packaging material and
Manufacture method.
The present invention is achieved by the following technical solutions:
A kind of heat insulation antibacterial food packaging material, are prepared by the raw materials in: Low Density Polyethylene 100, nano oxidized
Zinc 3.5-3.7, Basil Essential 6.5-6.7, glycerol 2-4, calcium alginate 0.2-0.4, di-2-ethylhexyl maleate 3-4, organobentonite
1-2, bamboo powder 6-8, polyacrylonitrile fibre 7-9, vinyl three ('beta '-methoxy ethyoxyl) silane 7.5-7.7, suitable quantity of water.
The manufacture method of described a kind of heat insulation antibacterial food packaging material, comprises the following steps:
(1) nano zine oxide, calcium alginate, Basil Essential stirring and evenly mixing are put in mixer, turning with 10000r/min
Speed high-speed stirred obtains modified nano zinc oxide in 30 seconds;
(2) by organobentonite, bamboo powder, di-2-ethylhexyl maleate stirring and evenly mixing, activation processing 20-30 minute at 570-620 DEG C,
Be cooled to room temperature addition polyacrylonitrile fibre, vinyl three ('beta '-methoxy ethyoxyl) silane ultrasonic disperse must change for 40-50 minute
Property organobentonite;
(3) by step (1), (2) reaction mass stirring and evenly mixing, add Low Density Polyethylene ultrasonic grinding 10-15 minute, put into double
Melt blending, pelletize in screw extruder, obtain packaging pellet;
(4) the packaging pellet blowing obtained in step (3) is made the thin film of thickness about 70-90 μm, discharging.
The invention have the advantage that the present invention with Low Density Polyethylene as base material, by receiving after silane coupler activation processing
Rice zinc oxide, as photocatalysis antibacterial agent, makes the organic principle such as antibacterial, moisture be decomposed, thus kills or bacteria growing inhibiting,
And compound Basil Essential, even if still having stronger antibiotic property under conditions of unglazed, broad-spectrum antibacterial property is high;Add simultaneously and change
Organobentonite after property is as filler, and absorption heat-proof quality strengthens, and by deoxygenation, dehumidifies, changes package except modes such as ethylene
The pack environment of material internal, prevents the growth of microorganism, degradable low cost, and antibacterial effect is notable, utilizes the present invention to prepare
Antibacterial food packaging material can effectively suppress staphylococcus aureus, the growing of escherichia coli rate, and without composition at 150 DEG C
Ooze out, use safety.
Detailed description of the invention
A kind of heat insulation antibacterial food packaging material, are prepared by the raw materials in: Low Density Polyethylene 100, nanometer
Zinc oxide 3.5, Basil Essential 6.5, glycerol 2, calcium alginate 0.2, di-2-ethylhexyl maleate 3, organobentonite 1, bamboo powder 6, poly-third
Alkene nitrile fiber 7, vinyl three ('beta '-methoxy ethyoxyl) silane 7.5, suitable quantity of water.
The manufacture method of described a kind of heat insulation antibacterial food packaging material, comprises the following steps:
(1) nano zine oxide, calcium alginate, Basil Essential stirring and evenly mixing are put in mixer, turning with 10000r/min
Speed high-speed stirred obtains modified nano zinc oxide in 30 seconds;
(2) by organobentonite, bamboo powder, di-2-ethylhexyl maleate stirring and evenly mixing, activation processing 20-30 minute at 570-620 DEG C,
Be cooled to room temperature addition polyacrylonitrile fibre, vinyl three ('beta '-methoxy ethyoxyl) silane ultrasonic disperse must change for 40-50 minute
Property organobentonite;
(3) by step (1), (2) reaction mass stirring and evenly mixing, add Low Density Polyethylene ultrasonic grinding 10-15 minute, put into double
Melt blending, pelletize in screw extruder, obtain packaging pellet;
(4) the packaging pellet blowing obtained in step (3) is made the thin film of thickness about 70-90 μm, discharging.
Utilizing antibacterial food packaging material smooth in appearance that the present invention prepares, transparent, material color tends to constant, close to
The color of blank low density polyethylene films and outward appearance, to escherichia coli, bacillus subtilis, staphylococcus aureus, mouse typhus
The antibiotic rate of contaminated bacteria common in Salmonella, Listeria monocytogenes, 6 kinds of food of Pseudomonas aeruginosa is in room temperature
And have under conditions of natural light irradiation up to 99.73%, 37 DEG C, unglazed according under conditions of minimum 94.93%.
Claims (2)
1. heat insulation antibacterial food packaging material, it is characterised in that be prepared by the raw materials in: Low Density Polyethylene
100, nano zine oxide 3.5-3.7, Basil Essential 6.5-6.7, glycerol 2-4, calcium alginate 0.2-0.4, di-2-ethylhexyl maleate 3-
4, organobentonite 1-2, bamboo powder 6-8, polyacrylonitrile fibre 7-9, vinyl three ('beta '-methoxy ethyoxyl) silane 7.5-7.7,
Suitable quantity of water.
The manufacture method of a kind of heat insulation antibacterial food packaging material the most according to claim 1, it is characterised in that include with
Lower step:
(1) nano zine oxide, calcium alginate, Basil Essential stirring and evenly mixing are put in mixer, turning with 10000r/min
Speed high-speed stirred obtains modified nano zinc oxide in 30 seconds;
(2) by organobentonite, bamboo powder, di-2-ethylhexyl maleate stirring and evenly mixing, activation processing 20-30 minute at 570-620 DEG C,
Be cooled to room temperature addition polyacrylonitrile fibre, vinyl three ('beta '-methoxy ethyoxyl) silane ultrasonic disperse must change for 40-50 minute
Property organobentonite;
(3) by step (1), (2) reaction mass stirring and evenly mixing, add Low Density Polyethylene ultrasonic grinding 10-15 minute, put into double
Melt blending, pelletize in screw extruder, obtain packaging pellet;
(4) the packaging pellet blowing obtained in step (3) is made the thin film of thickness about 70-90 μm, discharging.