CN106279875A - A kind of novel polyethylene floor heating pipe and preparation method - Google Patents
A kind of novel polyethylene floor heating pipe and preparation method Download PDFInfo
- Publication number
- CN106279875A CN106279875A CN201610650887.8A CN201610650887A CN106279875A CN 106279875 A CN106279875 A CN 106279875A CN 201610650887 A CN201610650887 A CN 201610650887A CN 106279875 A CN106279875 A CN 106279875A
- Authority
- CN
- China
- Prior art keywords
- polyethylene
- heating pipe
- floor heating
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of preparation method of novel polyethylene floor heating pipe, it is characterised in that: obtained outer layer polyethylene foamed, polyethylene 80 100 parts, modifying agent 15 parts, 0.1 0.5 parts of antioxidant, foaming agent 48 parts by the raw material Hybrid Heating of following parts by weight;Internal layer heat-proof polythene is obtained: heat-proof polythene 80 100 parts, 0.1 0.5 parts of antioxidant, black masterbatch 24 parts, coextrusion mold in double-layer coextrusion goes out machine obtains double-decker polyethylene floor heating pipe by above-mentioned outer layer polyethylene foamed and internal layer heat-proof polythene by the raw material Hybrid Heating of following parts by weight.The invention has the beneficial effects as follows: outer layer polyethylene foamed improves resisted shrinkage performance, ageing resistace, extends service life, improve the rigidity of floor heating pipe;Internal layer heat resistant polyethylene material has high temperature durability, improves durable, the heat resistance of floor heating pipe.
Description
Technical field
The present invention relates to polymeric material field, be specifically related to a kind of novel polyethylene floor heating pipe and preparation method.
Background technology
When cold winter arrives, " thermal insulation " day by day becomes the much-talked-about topic that people talk about.Floor heating full name is floor
Radiant heating, is a kind of accumulation of heat based on ground, heat transfer technology.Floor heating pipe is mainly formed by plastic processing, and floor heating pipe is embedded in ground
Under, the stability of pipeline, load performance, rigidity, intensity are had high requirements.Meanwhile, some plastic conduit outer surfaces are scratch-resistant, resistance to
Mill property is poor, it is easy to occur as soon as slight crack.Floor heating pipe is embedded in building building cement, and repair and replacement are extremely difficult, when product quality occur
Problem, will result in serious property safety accident.Therefore, national standard is the highest to the performance requirement of floor heating pipe, to ensure that it is pacified
Full use.
Polyethylene is typical thermoplastic, owing to PE tubing has nontoxic, tasteless, odorless, good cold-resistant, heat-resisting
Property and chemical stability, higher rigidity and toughness, and good mechanical property, the plurality of advantages such as easy for installation, widely should
Give for building, draining, the field such as buried drain pipe, appendix and telecommunications engineering.Common polyvinyl piping materials is as floor heating pipe
During use, scratch-resistant, wear no resistance, it is easy to occur as soon as slight crack, it is therefore desirable to floor heating pipe is improved.
Summary of the invention
The technical problem to be solved is to provide a kind of durable, heat-resisting novel polyethylene floor heating pipe and preparation
Method.
The present invention solves above-mentioned technical problem and be the technical scheme is that the preparation side of a kind of novel polyethylene floor heating pipe
Method, it is characterised in that: obtained outer layer polyethylene foamed by the raw material Hybrid Heating of following parts by weight, polyethylene 80-100 part,
Modifying agent 1-5 part, antioxidant 0.1-0.5 part, foaming agent 4-8 part;Internal layer is obtained by the raw material Hybrid Heating of following parts by weight
Heat-proof polythene: heat-proof polythene 80-100 part, antioxidant 0.1-0.5 part, black masterbatch 2-4 part, by poly-for above-mentioned outer layer foaming
Ethylene and internal layer heat-proof polythene coextrusion mold in double-layer coextrusion goes out machine obtain double-decker polyethylene floor heating pipe.
Further, the preparation process of described outer layer polyethylene foamed:
Step 1: by weight by polyethylene and 1~5 part of modifying agent mixed melting at 170~190 DEG C of 80-100 part
Prepare a material;
Step 2: by weight by the polyethylene of 5~10 parts and 0.1~0.5 part of antioxidant at 170~190 DEG C of mixed meltings
Prepare b material;
Step 3: a material and b material are mixed and added into 4~8 parts of foaming agent and obtain outer layer polyethylene foamed.
Further, described internal layer heat-proof polythene presses heat-proof polythene 80-100 part, antioxidant 0.1-0.5 part, black masterbatch
2-4 part carries out proportioning, is sequentially placed in blender, and mixture temperature 80 DEG C, mixing time is 20 30min, obtains internal layer heat-resisting
Polyethylene;
Further, the barrel zone temperature of described extruder is 180 DEG C 210 DEG C, and the temperature of die orifice is 210 DEG C 230 DEG C;Squeeze
Go out tubing through vacuum sizing, cool down molding, obtain double-decker polyethylene floor heating pipe.
Further, any one during described modifying agent is titanate coupling agent, aluminate coupling agent;Described antioxidant is
Any one in phenols main antioxygen TCA, oxygen agent 1010;Described foaming agent is in azodicarbonamide, azodiisobutyronitrile
Any one.
A kind of novel polyethylene floor heating pipe, it is characterised in that: prepared by the preparation method described in above-mentioned any one.
The invention has the beneficial effects as follows: outer layer polyethylene foamed improves resisted shrinkage performance, ageing resistace, extends and makes
With the life-span, improve the rigidity of floor heating pipe;Internal layer heat resistant polyethylene material has high temperature durability, improves the resistance to of floor heating pipe
For a long time, heat resistance.
Detailed description of the invention
Technical scheme will be clearly and completely described below, it is clear that described embodiment is this
Bright a part of embodiment rather than whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art are not having
Have and make the every other embodiment obtained under creative work premise, broadly fall into the scope of protection of the invention.
Embodiment 1
By weight polyethylene and 3 parts of titanate coupling agent mixed meltings at 170~190 DEG C of 90 parts are prepared a material;
By weight polyethylene and 0.3 part of antioxygen TCA of 10 parts are prepared b material at 170~190 DEG C of mixed meltings;By mixed to a material and b material
Merge 5 parts of azodicarbonamides of addition and add in extruder stand-by.
By weight heat-proof polythene (PE-RT) 100 parts, antioxygen TCA 0.3 part, black masterbatch 2 parts are sequentially placed into blender
In, mixture temperature 80 DEG C, mixing time is 20 30min, obtains internal layer heat resistant polyethylene material;
Internal layer heat resistant polyethylene material is joined coextrusion mold in above-mentioned extruder, and barrel zone temperature is 180 DEG C 210
DEG C, the temperature of die orifice is 210 DEG C 230 DEG C;Extruding pipe material, through vacuum sizing, cools down molding.
Embodiment 2
By weight polyethylene and 3 parts of titanate coupling agent mixed meltings at 170~190 DEG C of 90 parts are prepared a material;
By weight polyethylene and 0.2 part of antioxygen TCA of 10 parts are prepared b material at 170~190 DEG C of mixed meltings;By mixed to a material and b material
Merge 4 parts of azodiisobutyronitriles of addition and add in extruder stand-by.
By weight heat-proof polythene (PE-RT) 100 parts, antioxygen TCA 0.3 part, black masterbatch 2 parts are sequentially placed into blender
In, mixture temperature 80 DEG C, mixing time is 20 30min, obtains internal layer heat resistant polyethylene material;
Internal layer heat resistant polyethylene material is joined coextrusion mold in above-mentioned extruder, and barrel zone temperature is 180 DEG C 210
DEG C, the temperature of die orifice is 210 DEG C 230 DEG C;Extruding pipe material, through vacuum sizing, cools down molding.
Embodiment 1 and embodiment 2 are carried out performance experiment test with conventional floor heating pipe, result such as following table:
Table 1: tubing senile experiment result
Table 2: mechanical properties of tubular goods is tested
Performance | Heating coil routinely | Embodiment 1 | Embodiment 2 |
Hot strength MPa | 22.5 | 37.8 | 38.6 |
Elongation at break % | 578.3 | 543.8 | 580.9 |
Impact strength KJ/m2 | 28.5 (breach) | 47.9 (breach) | 45.4 (breach) |
Last it is noted that various embodiments above is only in order to illustrate technical scheme, it is not intended to limit;To the greatest extent
The present invention has been described in detail by pipe with reference to foregoing embodiments, it will be understood by those within the art that: it depends on
So the technical scheme described in foregoing embodiments can be modified, or the most some or all of technical characteristic is entered
Row equivalent;And these amendments or replacement, do not make the essence of appropriate technical solution depart from various embodiments of the present invention technology
The scope of scheme.
Claims (7)
1. the preparation method of a novel polyethylene floor heating pipe, it is characterised in that: by the raw material Hybrid Heating of following parts by weight
Obtain outer layer polyethylene foamed, polyethylene 80-100 part, modifying agent 1-5 part, antioxidant 0.1-0.5 part, foaming agent 4-8 part;By
The raw material Hybrid Heating of following parts by weight obtains internal layer heat-proof polythene: heat-proof polythene 80-100 part, antioxidant 0.1-0.5
Part, black masterbatch 2-4 part, become above-mentioned outer layer polyethylene foamed with internal layer heat-proof polythene co-extrusion in double-layer coextrusion goes out machine
Type obtains double-decker polyethylene floor heating pipe.
The preparation method of a kind of novel polyethylene floor heating pipe the most according to claim 1, it is characterised in that: described outer layer is sent out
The preparation process of bubble polyethylene:
Step 1: by weight polyethylene and 1~5 part of modifying agent mixed melting at 170~190 DEG C of 80-100 part are prepared a
Material;
Step 2: by weight polyethylene and 0.1~0.5 part of antioxidant of 5~10 parts are prepared at 170~190 DEG C of mixed meltings
B expects;
Step 3: a material and b material are mixed and added into 4~8 parts of foaming agent and obtain outer layer polyethylene foamed.
The preparation method of a kind of novel polyethylene floor heating pipe the most according to claim 1, it is characterised in that: described internal layer is resistance to
Hot polymerization ethylene carries out proportioning by heat-proof polythene 80-100 part, antioxidant 0.1-0.5 part, black masterbatch 2-4 part, is sequentially placed into stirring
In machine, mixture temperature 80 DEG C, mixing time is 20 30min, obtains internal layer heat-proof polythene.
The preparation method of a kind of novel polyethylene floor heating pipe the most according to claim 1, it is characterised in that: described extruder
Barrel zone temperature be 180 DEG C 210 DEG C, the temperature of die orifice is 210 DEG C 230 DEG C;Extruding pipe material, through vacuum sizing, is cooled to
Type, obtains double-decker polyethylene floor heating pipe.
5. according to the preparation method of a kind of novel polyethylene floor heating pipe described in claim 1 ~ 4 any one, it is characterised in that:
Described modifying agent is any one in titanate coupling agent, aluminate coupling agent;Described antioxidant be phenols main antioxygen TCA,
Any one in oxygen agent 1010;Described foaming agent is any one in azodicarbonamide, azodiisobutyronitrile.
6. a novel polyethylene floor heating pipe, it is characterised in that: by the preparation method system described in claim 1 ~ 4 any one
?.
A kind of novel polyethylene floor heating pipe the most according to claim 6, it is characterised in that: described modifying agent is that titanate esters is even
Connection agent, aluminate coupling agent in any one;Described antioxidant is any one in phenols main antioxygen TCA, oxygen agent 1010;
Described foaming agent is any one in azodicarbonamide, azodiisobutyronitrile.