CN106278112A - Wear-resisting cement brick - Google Patents
Wear-resisting cement brick Download PDFInfo
- Publication number
- CN106278112A CN106278112A CN201610735161.4A CN201610735161A CN106278112A CN 106278112 A CN106278112 A CN 106278112A CN 201610735161 A CN201610735161 A CN 201610735161A CN 106278112 A CN106278112 A CN 106278112A
- Authority
- CN
- China
- Prior art keywords
- wear
- cement
- cement brick
- flyash
- clay
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wear-resisting cement brick, be made up of following weight parts composition: cement 20 30, flyash 50 70, aluminium oxide 10 14, magnesium sulfate 8 14, chitosan 10 20, clay 20 24, metallic fiber 10 12, Gypsum Fibrosum 15 20.The present invention closely bonds, and finished product occurs that the probability in crack is low；There is good water-fast acid resistance, stronger cracking resistance and rupture strength, indeformable, colour-fast.Its color, moulding, material can be designed as required, have the advantages such as low cost, environmental protection, the industrial policy meeting sustainable development.Can be widely applied to the decoration of metope, ground, furniture surface etc..
Description
Technical field
The present invention relates to cement brick technical field, a kind of wear-resisting cement brick.
Background technology
Along with the development of national economy life, the material that Outdoor Design is used has been directed to iron and steel, non-ferrous metal, change
The multiple industries such as work, weaving, timber, pottery, plastics, glass.People for Outdoor Design theme tone emphasizing with weight
Depending on, it is also desirable to the new material of great individual character moderate cost again realizes.Single with regard to wall, ground decoration one, available material
Huge number, such as glaze for glazed tile, marble, granite finishing brick etc., but above-mentioned material is difficult to have new on decorative effect
Breakthrough, and cost is higher.Develop the feature cheap, functional, there is environmental protection, meet the dress of national development policy
Decorations brick material is quite necessary.Patent CN101126271A discloses a kind of cement decorative plate including surface layer and bottom；But
The contract with dry rate gap being the surface layer of this cement decorative plate and bottom is relatively big, and crack easily occurs in its finished product.
Cement brick refer to utilize flyash, cinder, gangue, mine tailings, residue of chemical industry or natural sand, tidal land mud etc. (with
One or several of upper raw material) as primary raw material, do coagulator with cement, a kind of Novel wall manufactured without high-temperature calcination
Body material.
Summary of the invention
The present invention is directed to the deficiencies in the prior art, propose a kind of wear-resisting cement brick, form ingenious rationally, performance is good.
In order to realize foregoing invention purpose, the present invention provides techniques below scheme: a kind of wear-resisting cement brick, by following weight
Part composition is constituted: cement 20-30, flyash 50-70, aluminium oxide 10-14, magnesium sulfate 8-14, chitosan 10-20, clay 20-
24, metallic fiber 10-12, Gypsum Fibrosum 15-20.
Further, the weight portion of each composition is: cement 25, flyash 60, aluminium oxide 12, magnesium sulfate 11, chitosan 15,
Clay 22, metallic fiber 11, Gypsum Fibrosum 18.
Compared with prior art, the invention have the advantages that and closely bond, finished product occurs that the probability in crack is low；Have
Good water-fast acid resistance, stronger cracking resistance and rupture strength, indeformable, colour-fast.Its color, moulding, material can root
It is designed according to needs, there is the advantages such as low cost, environmental protection, the industrial policy meeting sustainable development.Can be widely applied to wall
The decoration of face, ground, furniture surface etc..
Detailed description of the invention
Describing the present invention below in conjunction with embodiment, the description of this part is only exemplary and explanatory, no
Reply protection scope of the present invention has any restriction effect.
Embodiment 1
A kind of wear-resisting cement brick, is made up of following weight parts composition: cement 25, flyash 60, aluminium oxide 12, magnesium sulfate 11, shell
Polysaccharide 15, clay 22, metallic fiber 11, Gypsum Fibrosum 18.
Embodiment 2
A kind of wear-resisting cement brick, is made up of following weight parts composition: cement 20, flyash 70, aluminium oxide 10, magnesium sulfate 14, shell
Polysaccharide 10, clay 24, metallic fiber 10, Gypsum Fibrosum 20.
Embodiment 3
A kind of wear-resisting cement brick, is made up of following weight parts composition: cement 30, flyash 50, aluminium oxide 14, magnesium sulfate 8, shell are poly-
Sugar 20, clay 20, metallic fiber 12, Gypsum Fibrosum 15.
The manufacture method of the said goods is, by proportioning, each composition is stirred mixing, adds suitable quantity of water slurrying, injects mould
Tool shakes flat, condenses maintenance 3 days, the demoulding, dries.
The cement brick that the present invention prepares has high abrasion, high anti-skidding function, easily slides after decreasing the wet water of floor tile
The danger of traumatic injury.After tested, every technological standards of this product reaches requirement.
The above is only the preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For Yuan, under the premise without departing from the principles of the invention, it is also possible to make some improvements and modifications, these improvements and modifications also should
It is considered as protection scope of the present invention.
Claims (2)
1. a wear-resisting cement brick, it is characterised in that: it is made up of following weight parts composition: cement 20-30, flyash 50-70, oxygen
Change aluminum 10-14, magnesium sulfate 8-14, chitosan 10-20, clay 20-24, metallic fiber 10-12, Gypsum Fibrosum 15-20.
Wear-resisting cement brick the most as claimed in claim 1, it is characterised in that: the weight portion of each composition is: cement 25, flyash 60,
Aluminium oxide 12, magnesium sulfate 11, chitosan 15, clay 22, metallic fiber 11, Gypsum Fibrosum 18.