CN106275682B - A kind of dumbbell shape cup - Google Patents
A kind of dumbbell shape cup Download PDFInfo
- Publication number
- CN106275682B CN106275682B CN201610768061.1A CN201610768061A CN106275682B CN 106275682 B CN106275682 B CN 106275682B CN 201610768061 A CN201610768061 A CN 201610768061A CN 106275682 B CN106275682 B CN 106275682B
- Authority
- CN
- China
- Prior art keywords
- cup
- layer
- additive
- pan
- main body
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Dumbbell shape cup disclosed by the invention, including bottom of a cup, cup body and cup lid, the middle part of cup body is column construction and its both ends respectively has at least two pans stacked, column construction has accommodation space with composition in its at least pan of one end, cup body is enhancing PP materials, also has protective layer on cup body inner wall.The silastic-layer and rubber thin-bed with lower opening that the present invention passes through setting, pass through the suction-operated of the silastic-layer of bottom end opening, keep its placement property more preferable, it is not easily susceptible to slight vibration or touches and topple over, there is better safety in utilization, and the protective layer structure for passing through setting, effective insulating effect can be played, and the easy leaching composition in plastics is prevented to be leached in use, and be ingested in vivo, to improve the safety in utilization of plastic cup.
Description
Technical field
The present invention relates to a kind of plastic cup, especially a kind of dumbbell shape cup.
Background technology
Plastic products bring great convenience to our life, and but then, its appearance allows people to its peace again
Full property is half believing, half doubting.Plastic cup is used for the disposable container of dixie cup and tea.Disposal plastic cup usage amount is maximum to be usually
Liquor store, hot cold drink shop, milk tea shop, hotel, dining room and cafe, the tyre drink and scene for providing various plastics cups make
With.
Plastic cup belongs to nondegradable product, and many people conveniently just throw away cup after finishing off beverage, but also
This disposal plastic cup becomes the main source of " white pollution ".And the common soya-bean milk bottle of pp plastic cups, Yogurt bottle, fruit juice
Beverage bottle, micro-wave oven cutlery box, hot water cup etc..Fusing point is up to 167 DEG C, is the plastic casing that can uniquely put micro-wave oven into, can be small
It is reused after heart cleaning.It is noted that some micro-wave oven cutlery boxs, box body is manufactured with No. 5 pp, but box cover is manufactured with No. 1 PE,
Since PE cannot be supported by high temperature, therefore micro-wave oven cannot be put into together with box body.
Using polypropylene, there is pp plastic cups good heat resistance, product can be carried out in 100 DEG C of temperatures above for it
Sterilization, under conditions of not by external force, 150 DEG C also indeformable.Brittle temperature be -35 DEG C, can occur less than -35 DEG C it is crisp
Change, cold resistance is not so good as polyethylene.Polyacrylic melting temperature about improves 40 one 50% than polyethylene, about 164 1 170 DEG C,
100% grade polypropylene.
Although be by materials such as PE, PP of food-grade usually it is nontoxic, as synthesis high molecular material, modeling
The polymer that can have various auxiliary agents and oligomeric form in material, in routine use, as hot-water soak, oil, milk,
Wine, acid, fruit juice etc. can leach the substance of these in plastics, and as usage time is longer and leaching effect is better, from
And be ingested in human body, influence whether health by long-term accumulation.Meanwhile easily because of small collision in routine use
Or shake and topple over, content outflow influences the safety and efficiency of daily life, work.
Invention content
To solve the above problems, dumbbell shape cup disclosed by the invention, passes through the silicon rubber with lower opening of setting
Layer and rubber thin-bed keep its placement property more preferable, are not easily susceptible to slight vibration by the suction-operated of the silastic-layer of bottom end opening
Or touch and topple over, there is better safety in utilization, and by the protective layer structure of setting, can play effectively every
Effect absolutely, and the easy leaching composition in plastics is prevented to be leached in use, and be ingested in vivo, to improve plastic cup
Safety in utilization.
Dumbbell shape cup disclosed by the invention, including bottom of a cup, cup body and cup lid, the middle part of cup body be column construction and its
Respectively there are at least two pans stacked, column construction to have appearance with composition in its at least pan of one end at both ends
Receive space, cup body is enhancing PP materials, also has protective layer on cup body inner wall.The protective layer of this programme setting can be to PP materials
Isolated protection is carried out, the leaching probability of the small-molecule substance in plastics in a state of use is reduced, to promote the safety used
Property, while the cup of the structure conveniently prevents and by holding so that the use of cup place it is more convenient.
A kind of improvement of dumbbell shape cup disclosed by the invention, the outer diameter of pan are more than the maximum outside diameter of column construction.
A kind of improvement of dumbbell shape cup disclosed by the invention, state the column construction of cup body and the junction of pan and/
Or the junction of pan and pan has groove structure and/or projective structure.
A kind of improvement of dumbbell shape cup disclosed by the invention, when junction has projective structure comprising silicon rubber material
The main body of matter.The main body of silicone rubber material makes the bulge-structure have good elasticity and buffering recovery capability in this programme,
To make it when being held or being collided, good flexible buffer is provided.
A kind of improvement of dumbbell shape cup disclosed by the invention, hard cap is additionally provided in main body, and hard cap is arranged in master
It body end portion and is matched with body end.
The hard cap being arranged in this programme while providing protection for the main body of silicone rubber material, makes it be not easy using
In be destroyed, while wearability can be improved again, prevent from wearing.Hard cap can be ceramic cap, which can be ceramics
Sheet type has good compatibility with silicon rubber main body, while having the characteristic light, rigidity is good, wearability is strong again, makes
It provides adequately protection to bulge-structure.The hard cap of ceramic sheet type, using ceramic high intensity high rigidity characteristic and
In conjunction with its relatively thin thickness, and when cup is by greater impact, the preferential rigidity that occurs is broken, and stress is then transmitted to master again
Body and cup body, to implement rigid-flexible double protection, to promote the ability of protecting against shock damage.Ceramics can in the program
Think, raw material composition includes, in terms of parts by weight:00 part of silica 1;Alumina particle and magnesium oxide particle 0.3-1.2
Part;3-10 parts of boric acid.Preferably, the granularity of silica is D50≤0.5 micron.It is furthermore preferred that alumina particle and oxidation
The granularity of magnesium granules is D50≤3.0 micron.It is highly preferred that raw material is prepared through water base ball milling, wherein addition accounts for original when water base ball milling
Expect the PVA aqueous solutions of gross mass percentage 16-20%, a concentration of 10wt.% of PVA aqueous solutions.It is highly preferred that when water base ball milling
Also addition accounts for the dispersant of raw material gross mass percentage 0.05-0.5%.
A kind of improvement of dumbbell shape cup disclosed by the invention, is additionally provided with silastic-layer under bottom of a cup, under silastic-layer
End is provided at least one groove, and groove only has at least one opening in lower section.
The silastic-layer is set by the way that the position outside bottom outside i.e. vial bottom is arranged in this programme, by setting
The opening of the groove set and setting thereunder --- the setting to be open in the bottom of groove and towards down-set,
The silica gel material for coordinating quality softer simultaneously, to place in use, it can be made to be oppressed, thus by the air in groove
It is emptied from bottom and forms negative pressure, suction-operated is generated to cup, and adsorbed on the table, to be not easy because touching vibration
And topple over, occur damaged.
A kind of improvement of dumbbell shape cup disclosed by the invention is provided with folded slot, folded slot in the groove of silastic-layer
It is parallel with bottom lower surface.The folded slot on groove inner wall is arranged in this programme so that cup is when placing, the silicon rubber of bottom
Glue-line is more easy to be folded, and oppresses groove, to be more easy to fully exclude the air in groove, and maximally forms negative-pressure adsorption power,
To promote stability and the safety of placement.
A kind of improvement of dumbbell shape cup disclosed by the invention, enhancing PP are the outer skin in the main body of PP materials to add
Agent is added to be doped, additive is at least one of carbon fiber, ceramic fibre, titanium nitride, calcium carbonate, and it is total that additive accounts for main body
The 0.1-0.3wt% of quality.PP materials are that common food grade cup is molded PP raw materials in this programme.This programme is added by addition
Add agent part, as the protective layer and mechanical performance of PP materials, the enhancing tissue of wear-resisting property, to change it from microscopic pattern
Abrasiveness and mechanical performance, and achieve the purpose that enhancing and improve service life.By the specific use of additive, overcome
The harmful effect in terms of structure and intensity such as impurity element and crystal defect.
A kind of improvement of dumbbell shape cup disclosed by the invention, additive doping depth in main body are not more than 0.5mm.
A kind of improvement of dumbbell shape cup disclosed by the invention, additive are uniformly distributed or from outward appearance to inner essence in main body surface layer
Successively decrease (i.e. with the increase of doping depth, the content of additive is reduced in same depth) on ground.
In the present invention program, the extexine structure of the cup of PP materials is only entrained in using the additive of low-doped amount,
The surface enhanced of the cup under low-doped amount is realized, while reducing the content in material internal additive, and is reduced internal
The content of " impurity " form substance of institutional framework is influenced, the influence to microstructures such as crystallizations is reduced, reduces boundary stress, from
And reduce the influence to Fine Texture of Material stability and uniformity.
A kind of improvement of dumbbell shape cup disclosed by the invention, protective layer be glass protecting layer either ceramic protection layer or
Stainless steel protective cover.
A kind of improvement of dumbbell shape cup disclosed by the invention, protective layer have porous structure.
Cup disclosed by the invention has simple in structure, production and application convenience, with better safety in utilization and gripping
Convenience, while material has good wear resistance and stability, in use since the negative-pressure adsorption of bottom acts on,
It is not susceptible to topple over, and is not susceptible to small-molecule substance leaching, to have more good safety in utilization.
Description of the drawings
The structural schematic diagram of a kind of embodiment of Fig. 1, dumbbell shape cup disclosed by the invention.
Reference numerals list:1, column construction;2, pan.
Specific implementation mode
With reference to the accompanying drawings and detailed description, the present invention is furture elucidated, it should be understood that following specific implementation modes are only
For illustrating the present invention rather than limiting the scope of the invention.It should be noted that word " preceding " used in the following description,
" rear ", "left", "right", "up" and "down" refer to that the direction in attached drawing, word "inner" and "outside" refer respectively to direction or remote
Direction from geometric center of specific component.
Embodiment 1
As shown in Figure 1, dumbbell shape cup in the present embodiment, including bottom of a cup, cup body and cup lid, the middle part of cup body is cylindricality knot
Structure 1 and its both ends respectively have there are two the pan 2 that stacks, column construction 1 in its at least pan 2 of one end
It is enhancing PP materials that composition, which has accommodation space, cup body, and protective layer is provided on cup body inner wall.
Embodiment 2
Dumbbell shape cup in the present embodiment, including bottom of a cup, cup body and cup lid cup body middle part be column construction and its two
End respectively has there are three the pan stacked, and column construction has receiving empty with composition in its at least pan of one end
Between, cup body is enhancing PP materials, and protective layer is provided on cup body inner wall.
Embodiment 3
Dumbbell shape cup in the present embodiment, including bottom of a cup, cup body and cup lid, the middle part of cup body be column construction and its two
End respectively have there are two, three pans stacked, column construction, which is constituted with it at least in the pan of one end, appearance
Receive space, cup body is enhancing PP materials, and protective layer is provided on cup body inner wall.
Embodiment 4
Dumbbell shape cup in the present embodiment, including bottom of a cup, cup body and cup lid, the middle part of cup body be column construction and its two
End respectively have there are three, four pans stacked, column construction, which is constituted with it at least in the pan of one end, appearance
Receive space, cup body is enhancing PP materials, and protective layer is provided on cup body inner wall.
With include but not limited to what above-described embodiment distinguished, the quantity for the pan of cup body end stacked can also be
Five, six, seven it is even more, and the quantity at both ends can be the same or different.
With include but not limited to what above-described embodiment distinguished, the outer diameter of pan is more than the maximum outside diameter of column construction.
The outer diameter of the pan of the same end may be the same or different;The outer diameter of the maximum pan at both ends can be identical, also may be used
With difference.
With include but not limited to what above-described embodiment distinguished, the column construction of cup body and the junction of pan have recessed
Slot structure and/or projective structure.The pan of cup body and the junction of pan have groove structure and/or projective structure.Cup
There is groove structure and/or protrusion to tie for the column construction of body and the junction of pan and the junction of pan and pan
Structure.Refer to following any case with groove structure and/or projective structure:With groove structure;With projective structure;Simultaneously
With groove structure and projective structure.
With include but not limited to what above-described embodiment distinguished, junction have projective structure when comprising silicon rubber material
The main body of matter.
With include but not limited to what above-described embodiment distinguished, be additionally provided with hard cap in main body, the hard cap setting
It is matched in body end and with body end.
With include but not limited to what above-described embodiment distinguished, hard cap be ceramic sheet type.
With include but not limited to what above-described embodiment distinguished, ceramic hard cap can be by including but not limited to as follows
The preparation embodiment obtains:
Prepare embodiment 1
In this preparation embodiment, ceramic raw material group becomes 00 part of silica 1;Alumina particle and magnesium oxide particle
0.3 part;5 parts of boric acid, it is hard that above-mentioned raw materials obtain sintering ceramics after the techniques such as batch mixing ball milling, spray drying, dry-pressing formed, sintering
Matter cap,
It is wherein sintered to and is sintered under argon gas protection in vacuum high temperature furnace, sintering temperature is 1875 DEG C, and in-furnace temperature reaches
The heat preservation sintering time is 1.3h after sintering temperature, and argon gas is filled with when vacuum high temperature furnace is preheated to 1500 DEG C.
This preparation embodiment prepares ceramics sample 100, and sintering finished qualification rate 99%, sample is by detection, average densification
> 98% is spent, fracture toughness is less than 4.5MPA.
Prepare embodiment 2
In this preparation embodiment, ceramic raw material group becomes 00 part of silica 1;Alumina particle and magnesium oxide particle
0.7 part;3 parts of boric acid, it is hard that above-mentioned raw materials obtain sintering ceramics after the techniques such as batch mixing ball milling, spray drying, dry-pressing formed, sintering
Matter cap,
It is wherein sintered to and is sintered under argon gas protection in vacuum high temperature furnace, sintering temperature is 1860 DEG C, and in-furnace temperature reaches
The heat preservation sintering time is 1.8h after sintering temperature, and argon gas is filled with when vacuum high temperature furnace is preheated to 1500 DEG C.
This preparation embodiment prepares ceramics sample 100, and sintering finished qualification rate 99%, sample is by detection, average densification
> 98% is spent, fracture toughness is less than 4.5MPA.
Prepare embodiment 3
In this preparation embodiment, ceramic raw material group becomes 00 part of silica 1;Alumina particle and magnesium oxide particle
1.0 part;10 parts of boric acid, above-mentioned raw materials obtain sintering ceramics after the techniques such as batch mixing ball milling, spray drying, dry-pressing formed, sintering
Hard cap,
It is wherein sintered to and is sintered under argon gas protection in vacuum high temperature furnace, sintering temperature is 1870 DEG C, and in-furnace temperature reaches
The heat preservation sintering time is 1.3h after sintering temperature, and argon gas is filled with when vacuum high temperature furnace is preheated to 1500 DEG C.
This preparation embodiment prepares ceramics sample 100, and sintering finished qualification rate 99%, sample is by detection, average densification
> 98% is spent, fracture toughness is less than 4.5MPA.
Prepare embodiment 4
In this preparation embodiment, ceramic raw material group becomes 00 part of silica 1;Alumina particle and magnesium oxide particle
1.2 part;7 parts of boric acid, it is hard that above-mentioned raw materials obtain sintering ceramics after the techniques such as batch mixing ball milling, spray drying, dry-pressing formed, sintering
Matter cap,
It is wherein sintered to and is sintered under argon gas protection in vacuum high temperature furnace, sintering temperature is 1900 DEG C, and in-furnace temperature reaches
The heat preservation sintering time is 2h after sintering temperature, and argon gas is filled with when vacuum high temperature furnace is preheated to 1500 DEG C.
This preparation embodiment prepares ceramics sample 100, and sintering finished qualification rate 99%, sample is by detection, average densification
> 98% is spent, fracture toughness is less than 4.5MPA.
Prepare embodiment 5
In this preparation embodiment, ceramic raw material group becomes 00 part of silica 1;Alumina particle and magnesium oxide particle
0.8 part;9 parts of boric acid, it is hard that above-mentioned raw materials obtain sintering ceramics after the techniques such as batch mixing ball milling, spray drying, dry-pressing formed, sintering
Matter cap,
It is wherein sintered to and is sintered under argon gas protection in vacuum high temperature furnace, sintering temperature is 1890 DEG C, and in-furnace temperature reaches
The heat preservation sintering time is 1.5h after sintering temperature, and argon gas is filled with when vacuum high temperature furnace is preheated to 1500 DEG C.
This preparation embodiment prepares ceramics sample 100, and sintering finished qualification rate 99%, sample is by detection, average densification
> 98% is spent, fracture toughness is less than 4.5MPA.
Prepare embodiment 6
In this preparation embodiment, ceramic raw material group becomes 00 part of silica 1;Alumina particle and magnesium oxide particle
0.5 part;8 parts of boric acid, it is hard that above-mentioned raw materials obtain sintering ceramics after the techniques such as batch mixing ball milling, spray drying, dry-pressing formed, sintering
Matter cap,
It is wherein sintered to and is sintered under argon gas protection in vacuum high temperature furnace, sintering temperature is 1850 DEG C, and in-furnace temperature reaches
The heat preservation sintering time is 1.2h after sintering temperature, and argon gas is filled with when vacuum high temperature furnace is preheated to 1500 DEG C.
This preparation embodiment prepares ceramics sample 100, and sintering finished qualification rate 99%, sample is by detection, average densification
> 98% is spent, fracture toughness is less than 4.5MPA.
It prepares embodiment 7-12 and prepares differing only in for embodiment 1-6, the granularity of silica is that D50≤0.5 is micro-
Rice (this place value can also for less than or equal to 0.3 micron, less than or equal to 0.15 micron, less than or equal to 0.4 micron, be less than or equal to
0.25 micron, be less than or equal to 0.37 micron, be less than or equal to 0.13 micron).Each preparation embodiment in this place prepares ceramics sample 100,
Sintering finished qualification rate 99%, sample is by detection, average density > 98.5%, fracture toughness 4.3-5.0MPA.
Embodiment 13-24 and preparation embodiment 1-12 is prepared to differ only in, alumina particle and magnesium oxide particle
Granularity be D50≤3.0 micron (this place value can also be less than or equal to 2.3 microns, less than or equal to 1.5 microns, be less than or equal to
1.4 microns, be less than or equal to 2.25 microns, be less than or equal to 2.7 microns, be less than or equal to 1.13 microns).Each preparation embodiment system in this place
Standby ceramics sample 100, sintering finished qualification rate 99%, sample is by detection, and average density > 98.5%, fracture toughness (takes
Average value ranges, similarly hereinafter) 4.8-5.3MPA.
It prepares embodiment 25-48 and prepares differing only in for embodiment 1-24, raw material is prepared through water base ball milling, wherein water
Addition accounts for the PVA aqueous solutions of raw material gross mass percentage 16%, a concentration of 10wt.% of PVA aqueous solutions when base ball milling.This place is each
It prepares embodiment and prepares ceramics sample 100, sintering finished qualification rate 99%, sample breaks by detection, average density > 98%
It splits toughness and is more than 7.4MPA.Here when water base ball milling PVA aqueous solutions addition account for raw material gross mass percentage can also be 17%,
17.5%, 18%, 18.5%, 19%, 19.5%, 20%, 18.3%, 17.2%, 16.7%, 19.4%, 16.1%, 18.8%
And other arbitrary values within the scope of 16-20%, and product quality is satisfied by the sintering finished qualification rate 99% of aforementioned claim, sample
Product are by detection, average density > 98%, fracture toughness 5.3-5.8MPA.
It prepares embodiment 47-96 and prepares differing only in for embodiment 1-48, when carrying out water base ball milling, ball milling slurry is dense
Degree is (in terms of solid quality percentage) 45%, Ball-milling Time 3h.This place ball milling slurry concentration can also be 46%, 47%,
48%, any other value within the scope of 49%, 50% or 45-50%;Ball-milling Time can also be 1h, 2h, 1.5h or 1-3h
Other arbitrary values in range.Each preparation embodiment product quality in this place is satisfied by the sintering finished qualification rate 99% of aforementioned claim, sample
Product are by detection, average density > 98%, fracture toughness 5.5-6.2MPA.
It prepares embodiment 47-96 and prepares differing only in for embodiment 1-48, obtain spray drying when dry-pressing formed
Granularity D50 be 0.10mm granulation material, it is dry-pressing formed in 150MPA pressure.The granularity D50 that this place is dried to obtain can also be
0.15, any other value within the scope of 0.2,0.17,0.12,0.14 or 0.10-0.20mm;Dry-pressing formed pressure can also be
170, other arbitrary values within the scope of 200,175 or 150-200MPA.Each preparation embodiment product quality in this place is satisfied by aforementioned
It is required that sintering finished qualification rate 99%, sample is by detection, average density > 98%, fracture toughness 6.3-6.5MPA.
With include but not limited to what above-described embodiment distinguished, silastic-layer is additionally provided under bottom of a cup, under silastic-layer
End is provided at least one groove, and groove only has at least one opening in lower section, and it includes but not limited to as follows to be specifically as follows
It is any:The lower end setting of silastic-layer is there are one groove, and only in lower section tool, there are one openings for groove;The lower end of silastic-layer is arranged
There are one groove, only in lower section tool, there are two mutually independent openings for groove;There are one grooves for the lower end setting of silastic-layer, recessed
Only in lower section tool, there are three mutually independent openings for slot;There are two mutually independent grooves for the lower end setting of silastic-layer, wherein
Only in lower section tool, there are one openings for one groove, and another groove is only in lower section tool there are two mutually independent opening;Silicon rubber
The lower end setting of glue-line is there are three mutual groove, and only in lower section tool, there are one openings for one of groove, and another groove is only
In lower section, tool is there are two mutually opening, and only in lower section tool, there are three mutually independent openings for third groove;Under silastic-layer
End setting is there are three mutual groove, and two of which groove only all have in lower section there are one being open, and another groove is only in lower section
There are two mutually independent openings for tool;There are three mutual grooves for the lower end setting of silastic-layer, and two of which groove is only in lower section
Tool is there are two mutually independent opening, and another groove is only in lower section tool that there are three mutually independent openings.
With include but not limited to what above-described embodiment distinguished, folded slot, folded slot are provided in the groove of silastic-layer
It is parallel with bottom lower surface.
With include but not limited to what above-described embodiment distinguished, enhancing PP be PP materials main body outer skin to add
Agent is added to be doped, additive is at least one of carbon fiber, ceramic fibre, titanium nitride, calcium carbonate, and it is total that additive accounts for main body
The 0.1-0.3wt% of quality.
Include but not limited to the following specific embodiment for enhancing PP and is satisfied by the range limit of technical solution of the present invention
It is fixed.
Enhance PP embodiments 1
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber content in main body is 0.13wt%.
Enhance PP embodiments 2
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive ceramic fibre content in main body is 0.3wt%.
Enhance PP embodiments 3
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive titanium nitride content in main body is 0.2wt%.
Enhance PP embodiments 4
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive calcium carbonate content in main body is 0.1wt%.
Enhance PP embodiments 5
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber, the ceramic fibre content in main body are respectively 0.1wt%, 0.13wt%.
Enhance PP embodiments 6
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber, the calcium carbonate content in main body are respectively 0.01wt%, 0.16wt%wt%.
Enhance PP embodiments 7
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber, the titanium nitride content in main body are respectively 0.15wt%, 0.13wt%.
Enhance PP embodiments 8
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive ceramic fibre, the titanium nitride content in main body are respectively 0.1wt%, 0.18wt%.
Enhance PP embodiments 9
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive ceramic fibre, the calcium carbonate content in main body are respectively 0.05wt%, 0.05wt%.
Enhance PP embodiments 10
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive titanium nitride, the calcium carbonate content in main body are respectively 0.01wt%, 0.23wt%.
Enhance PP embodiments 11
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber, ceramic fibre, the titanium nitride content in main body are respectively 0.1wt%, 0.03wt%, 0.13wt%.
Enhance PP embodiments 12
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber, ceramic fibre, the calcium carbonate content in main body are respectively 0.04wt%, 0.08wt%, 0.12wt%.
Enhance PP embodiments 13
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber, titanium nitride, the calcium carbonate content in main body are respectively 0.15wt%, 0.07wt%, 0.04wt%.
Enhance PP embodiments 14
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive ceramic fibre, titanium nitride, the calcium carbonate content in main body are respectively 0.01wt%, 0.23wt%, 0.03wt%.
Enhance PP embodiments 15
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
It is miscellaneous, additive carbon fiber, ceramic fibre, titanium nitride, the calcium carbonate content in main body be respectively 0.11wt%, 0.03wt%,
0.05wt%, 0.11wt%.
Enhance PP embodiments 16
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
Miscellaneous, additive carbon fiber, the calcium carbonate content in main body are respectively 0.08wt%, 0.03wt%.
Enhance PP embodiments 17
The main part of the enhancing PP of the present embodiment is injection molding food-grade PP particulate materials, and surface layer is mixed with additive
It is miscellaneous, additive carbon fiber, ceramic fibre, titanium nitride, the calcium carbonate content in main body be respectively 0.08wt%, 0.03wt%,
0.05wt%, 0.10wt%.
It is distinguished with above-described embodiment, additive doping depth in main body is that 0.5mm (in main body mix by additive
Miscellaneous depth can also be 0.17mm, 0.29mm, 0.36mm, 0.48mm, 0.32mm, 0.4mm, 0.24mm, 0.25mm, 0.21mm,
0.18mm、0.30mm、0.33mm、0.14mm、0.22mm、0.103mm、0.02mm、0.05mm、0.07mm、0.08mm、0.1mm、
0.2mm, 0.15mm, 0.25mm, 0.35mm, 0.45mm and other values no more than 0.5mm).It is very small when being agglomerated into one
Thickness be that material surface forms one and mainly forms shell using PP as bonding agent by additive, have at this time good
Wearability and mechanical performance.At this point, additive can be uniformly distributed in the surface layer in main body in doping depth;It can also content
From outward appearance to inner essence successively decrease, i.e., with the increase of doping depth, the content of additive is reduced in same depth.
It is distinguished with above-described embodiment, protective layer is glass protecting layer.The thickness of glass protecting layer is 0.5mm (glass
The thickness of glass protective layer can also be 0.17mm, 0.29mm, 0.36mm, 0.48mm, 0.32mm, 0.4mm, 0.24mm, 0.25mm,
0.21mm、0.18mm、0.30mm、0.33mm、0.14mm、0.22mm、0.103mm、0.02mm、0.05mm、0.07mm、
0.08mm, 0.1mm, 0.2mm, 0.15mm, 0.25mm, 0.35mm, 0.45mm and other values no more than 0.5mm).
It is distinguished with above-described embodiment, protective layer is ceramic protection layer.The thickness of ceramic protection layer is 0.5mm (potteries
The thickness of porcelain protective layer can also be 0.17mm, 0.29mm, 0.36mm, 0.48mm, 0.32mm, 0.4mm, 0.24mm, 0.25mm,
0.21mm、0.18mm、0.30mm、0.33mm、0.14mm、0.22mm、0.103mm、0.02mm、0.05mm、0.07mm、
0.08mm, 0.1mm, 0.2mm, 0.15mm, 0.25mm, 0.35mm, 0.45mm and other values no more than 0.5mm).
It is distinguished with above-described embodiment, protective layer is stainless steel protective cover, is food-grade stainless steel.Stainless steel protects
Layer thickness be 0.5mm (thickness of stainless steel protective cover can also be 0.17mm, 0.29mm, 0.36mm, 0.48mm, 0.32mm,
0.4mm、0.24mm、0.25mm、0.21mm、0.18mm、0.30mm、0.33mm、0.14mm、0.22mm、0.103mm、0.02mm、
0.05mm, 0.07mm, 0.08mm, 0.1mm, 0.2mm, 0.15mm, 0.25mm, 0.35mm, 0.45mm and other it is not more than
The value of 0.5mm).
It is distinguished with above-described embodiment, protective layer has porous structure.The average pore size of porous structure is 10 μm (more
The average pore size of pore structure can also be 10.5 μm, 20 μm, 25.4 μm, 30 μm, 33.7 μm, 40 μm, 49.9 μm, 50 μm, 56.2 μ
M, its in 60 μm, 66.4 μm, 70 μm, 78.3 μm, 80 μm, 88.1 μm, 90 μm, 92.9 μm, 100 μm and 10-100 μ ms
Its arbitrary value).Preferably, it is that (hole of porous structure is evenly distributed 80/square inch that the hole of porous structure, which is evenly distributed density,
Density can also be 82/square inch, 90/square inch, 93/square inch, 100/square inch, 101/flat
Square inch, 110/square inch, 115/square inch, 120/square inch, 124/square inch, 130/square
Inch, 137/square inch, 140/square inch, 146/square inch, 150/square inch, 159/square English
Very little, 160/square inch, 168/square inch, 170/square inch, 177/square inch, 180/square English
Very little, 189/square inch, 290/square inch, 196/square inch, 200/square inch and 80-200/flat
Other arbitrary values in square inch range).Preferably, the depth in the hole of porous structure is 1/5 (porous structure of overcoat thickness
Hole depth can also be overcoat thickness 1/4,1/3,1/2,0.3,0.35,0.4,0.45 and 1/5-1/2 within the scope of
Other arbitrary values).
This place embodiment is in place of the claimed non-limit of technical scope midrange and in embodiment technology
In scheme to single or multiple technical characteristics it is same replacement be formed by new technical solution, equally all the present invention claims
In the range of protection;Simultaneously the present invention program it is all enumerate or unrequited embodiment in, in the same embodiment each
Parameter is merely representative of an example (i.e. a kind of feasible scheme) for its technical solution, and between parameters and is not present stringent
Cooperation and qualified relation, wherein each parameter can be replaced mutually stating the when asked without prejudice to axiom and the present invention, special declaration
Except.
The technical means disclosed in the embodiments of the present invention is not limited to the technical means disclosed in the above technical means, and further includes
By the above technical characteristic arbitrarily the formed technical solution of combination.The above is the specific implementation mode of the present invention, should be referred to
Go out, for those skilled in the art, without departing from the principle of the present invention, can also make several
Improvements and modifications, these improvements and modifications are also considered as protection scope of the present invention.
Claims (4)
1. a kind of dumbbell shape cup, including bottom of a cup, cup body and cup lid, which is characterized in that the middle part of the cup body is column construction
And its both ends respectively has at least two pans stacked, the pan of the column construction and its at least one end
Middle composition has accommodation space, the junction and/or pan of the column construction and pan and the junction of pan to have
Projective structure, and include the main body of silicone rubber material, ceramic sheet type hard cap is additionally provided in main body, the cup body is enhancing
PP materials, the enhancing PP are doped for the outer skin of the main body in PP materials with additive, and the additive is carbon fiber
At least one of dimension, ceramic fibre, titanium nitride, calcium carbonate, additive account for the 0.1-0.3wt% of main body gross mass, additive
Doping depth is not more than 0.5mm in main body, also has protective layer on the cup body inner wall, protective layer be glass protecting layer or
Ceramic protection layer or stainless steel protective cover.
2. dumbbell shape cup according to claim 1, which is characterized in that the outer diameter of the pan is more than column construction
Maximum outside diameter.
3. dumbbell shape cup according to claim 1, which is characterized in that be additionally provided with silastic-layer, institute under the bottom of a cup
The lower end for stating silastic-layer is provided at least one groove, and the groove only has at least one opening in lower section.
4. dumbbell shape cup according to claim 3, which is characterized in that be provided with folding in the groove of the silastic-layer
Slot, the folded slot are parallel with bottom lower surface.