CN106242609A - A kind of preparation method of mine tailing flint clay water-permeable brick - Google Patents
A kind of preparation method of mine tailing flint clay water-permeable brick Download PDFInfo
- Publication number
- CN106242609A CN106242609A CN201610659047.8A CN201610659047A CN106242609A CN 106242609 A CN106242609 A CN 106242609A CN 201610659047 A CN201610659047 A CN 201610659047A CN 106242609 A CN106242609 A CN 106242609A
- Authority
- CN
- China
- Prior art keywords
- mine tailing
- flint clay
- permeable brick
- water
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the preparation method of a kind of mine tailing flint clay water-permeable brick, comprise the steps: that (1) crushes, discarded mine tailing flint clay pulverizer is crushed to 0 10mm;(2) screening, screens out the 30 above granules of mesh in step (1) pulverized particles stand-by, and wherein 30 mesh 1mm are as surface layer, and 1 3mm is as main part;(3) batch mixing, adds the close material formula of following mass percent by the raw material that filters out: aluminum phosphate solution 10% 20%, aluminum sulfate solution 15% 25%, carbamide 4 10%, clay 15 25%, sodium silicate 8 16%, binding agent 4 6%, sodium sulfate 4 6%;(4) stirring, fully stirs evenly with blender;(5) molding, adds mixture paste in mould, compressing with press;(6) high temperature sintering, kiln discharge chooses to install.It is short that the present invention has the firing time, and process is simple, and production cost is relatively low, and product water-permeable and air permeable performance is good, intensity is high, rough surface, and wearability is strong, and snow defence is anti-skidding, and salvage value is high, protection environment, saving natural resources.
Description
Technical field
The present invention relates to a kind of water-permeable brick preparing technical field, particularly relate to the preparation side of a kind of mine tailing flint clay water-permeable brick
Method.
Background technology
At present, mostly using the non-permeable materials such as cement, pitch, marble to lay ground in urban construction, these are hard
Changing road surface makes earth's surface and the heat of air, exchange of moisture highly difficult, the poor ability of Natural regulation urban ground temperature and humidity,
Earth's surface absorbs heat difficulty, retains a large amount of waste heat in causing city space, and ground also can be reflected in a large number, radiates solar thermal energy, from
And cause that the phenomenon that city nocturnal temperature is higher than countryside nocturnal temperature occurs.And, when the rainy day, hard surface can stop rainwater
Directly permeate the ground, cause hydrops everywhere, affect comfortableness and the safety of road, blocked simultaneously rainwater directly the most addedly under
The approach of water, makes Urban Underground water level be difficult to go up, and directly affects the healthy growth of urban surface vegetation, greening difficulty, increases the weight of
The drought and water shortage problem in city;And hydrops injects rivers after pouring in sewer, increase the weight of the row of sewerage system and rivers
Letting out burden, during fine day, ground is the most extremely dry, stirs up a cloud of dust, and environmental degree of comfort is substantially reduced.
To this end, those skilled in the art are by further investigation, develop the water penetration material of some water-permeable brick, porous pavements etc.
Material.Such as, CN 101528630A discloses a kind of composite water permeable brick, and this water-permeable brick includes permeable top layer and porous base course, permeable
Top layer and porous base course are closely as one;Permeable top layer and porous base course include aggregate and bonding aggregate viscous respectively
Knot agent;Including at least there being hydrophilic agglomerant in binding agent in described permeable top layer.But, in this patent application and be not disclosed
The preparation method of water-permeable brick.
In prior art, the Chinese patent of Patent No. CN200310115100 discloses one and has network-like hole knot
The steel slag pavement brick of structure.It is characterized in that adding in steel slag pavement brick slag, steel slag pavement brick divides up and down
Two-layer, steel slag particle particle diameter is 2.5~10mm, and in bottom raw material, steel slag particle accounts for 75~78wt%, No. 42.5 cement account for 13~
15wt%, slag mill fine powder accounts for 3~5wt%, and water reducer accounts for 0.5~0.8wt%, and water accounts for 3.5~6.0wt%;In the raw material of upper strata,
Steel slag particle accounts for 71~74wt%, and No. 42.5 cement account for 15~18wt%, and slag mill fine powder accounts for 3.5~5.5wt%, and water reducer accounts for
0.7~0.9wt%, water accounts for 3.5~6.0wt%.Compared with ceramic water-permeable brick, the present invention can be greatly lowered road surface water-permeable brick
Production cost, is not required to calcining simultaneously, can save the energy, protects environment.Compared with current existing common cement-base water-permeable brick, keep away
The shortcoming having exempted from freeze-thaw resistance difference.
The Chinese patent of Patent No. CN200410039203 discloses a kind of environmental protection water permeable brick structure and preparation method thereof, and this is saturating
Water brick includes the upper brick layer integrally fired and lower brick layer, and the thickness of this lower brick layer accounts for the 75~95% of water-permeable brick gross thickness,
On this, brick layer and lower brick layer are formed by the ceramic fine particle and coarse grain being mixed with additive and bonding agent respectively, and composition after saturating
The comprcssive strength of water brick is more than specification value 300kgf/cm2, and rupture strength is at more than 50kgf/cm2, and permeability rate is more than
0.035ml·cm/mm2/sec.Above-mentioned water-permeable brick according to setting procedure by waste ceramic processed, through high temperature sintering molding, can
Make the increase of water-permeable brick intensity, easy coloring, can back washing and may filter that impurity and tool breathability;Be applicable to pavement, ramp, from
Runway and the water-permeable brick of edge of pool.
The Chinese patent of Patent No. CN200610159648 discloses the production method of a kind of composite ceramic water-permeable brick, should
Method with include combustible industrial residue for bottom aggregate, with waste ceramic particle for surface layer aggregate, its grain composition is all: cross 10~
The material of 20 mesh sieves accounts for 55~65, and the material crossing 20~30 mesh sieves accounts for 35~45;By additional appropriate high-temperature agglomerant and organic viscous
Knot agent CMC, through dispensing, old, molding, be dried, calcining process and obtain product.Said method is mainly by optimizing grain composition
Utilizing combustible that industrial residue itself contains as pore former dexterously, and two-layer uses different the most former up and down
Material, makes that the product not only water penetration that obtained by the method is strong, good water-retaining property, intensity are high, but also simplifies the technique mistake of brickmaking
Journey, reduces production cost.This product is a kind of reason for laying the public places such as footpath, parking lot, airport, square
Think product.
The Chinese patent of Patent No. CN03222998.4 discloses a kind of molding pressure producing ultra-thin large size ceramic tile
Machine, can produce thickness 3~5 millimeters, width 1 meter, the Ceramic Tiles of length 3 meters, is ceramic machinery field.It includes main frame frame
Frame, decompressor and Belt Conveying distribution device, main machine frame hollow forming has the punching press chamber running through overall, and decompressor is located at
Punching press intracavity, decompressor includes top board, the oil cylinder of a plurality of band piston, dynamic beam and base plate, and top board is located at bottom punching press chamber, dynamic
Beam is positioned at above top board, and oil cylinder and piston are between dynamic beam and top board, and base plate is fixed on punching press top of chamber and is positioned on dynamic beam
Side, Belt Conveying distribution device includes carrying club and belt, passes between the driven beam of belt and base plate.This utility model structure
Advantages of simple, does not use mould, can produce super large-scale ornament materials easily, saves ceramic powder and the energy.
The Chinese patent of Patent No. CN200510020723.9 discloses a kind of process producing ultrathin ceramic bricks,
Including: use ultra-fine equipment to carry out micronization process the raw material producing Ceramic Tiles;It is dried the powder body after micronization;Will be dry
Burn till after pressed by powder molding after dry, polish and obtain finished product.Superfine powder machine is taked in useful the having the technical effect that of the present invention
Ceramic Material is processed by tool, replaces original ball mill and technique thereof, can fundamentally solve ceramic industry powder
High energy consumption problem in terms of preparation, meanwhile, superfine powder raw material will bring revolution for subsequent technique and final ceramic product quality
The progress of property.
But major part is all with pottery as raw material in prior art disclosed above, does not has and use mine tailing flint clay next life
Produce water-permeable brick, the most both solved the secondary Utilizing question of mine tailing flint clay, and can well complete water-permeable brick again, permeable,
Moisturizing, compressive property.
Summary of the invention
For in above prior art, the problem existed, the invention provides the preparation of a kind of mine tailing flint clay water-permeable brick
Method, can well complete permeable, the moisturizing of water-permeable brick, compressive property, can make full use of again mine tailing flint clay.
The technical solution used in the present invention is: the preparation method of a kind of mine tailing flint clay water-permeable brick, it is characterised in that: include
Following steps: (1) crushes, pulverize mine tailing flint clay pulverizer;(2) screening, screen out in step (1) pulverized particles 30 mesh with
Upper granule is stand-by, and 30 mesh-1mm are as surface layer, and 1-3mm is as main part;(3) batch mixing, adds as follows by the raw material filtered out
The close material formula of mass percent: aluminum phosphate solution 10%-20%, aluminum sulfate solution 15%-25%, carbamide 4-10%, clay
15-25%, sodium silicate 8-16%, binding agent 4-6%, sodium sulfate 4-6%;(4) stirring, fully stirs evenly with blender;(5) become
Type, adds mixture paste in mould, compressing with press;(6) high temperature sintering, kiln discharge chooses to install.
Preferably, in described step (1), mine tailing flint clay pulverizer is crushed to 0-10mm.
Preferably, the press selected in described step (5) is hydraulic press or friction press.
Preferably, in described step (6), the temperature of high temperature sintering is 1200 DEG C-1300 DEG C
Preferably, in described step (5), the mine tailing flint clay water brick specification of compacting is 200 × 100mm, and thickness is 40mm-
60mm。
The invention has the beneficial effects as follows: the inventive method can make mine tailing Jiao produced precious plus close material formula in the present invention
Stone water-permeable brick, intensity is high, and the porosity that goes out of water-permeable brick can reach 20%, has good water permeability, and water-permeable brick is micro-
Shape capillary tube through hole structure is instigateed in hole, absorbable noise, serves the effect of noise reduction, the mine tailing flint clay that additionally present invention produces
Water-permeable brick can absorb vehicle exhaust to a certain extent, serves the effect purifying air, decreases vehicle exhaust to urban air
Pollution;Water-permeable brick compressive property prepared by the inventive method is good, and intensity is high, anti-skidding, noise reduction.
Detailed description of the invention
The invention provides the preparation method of a kind of mine tailing flint clay water-permeable brick, comprise the steps: that (1) crushes, by tail
Ore deposit flint clay pulverizer is crushed to 0-10mm;(2) screening, screens out the 30 above granules of mesh in step (1) pulverized particles stand-by,
30 mesh-1mm are as surface layer, and 1-3mm is as main part;(3) batch mixing, adds following mass percent by the raw material filtered out
Close material formula: aluminum phosphate solution 10%-20%, aluminum sulfate solution 15%-25%, carbamide 4-10%, clay 15-25%, silicic acid
Sodium 8-16%, binding agent 4-6%, sodium sulfate 4-6%;(4) stirring, fully stirs evenly with blender;(5) molding, starches mixture
Material adds in mould, compressing with hydraulic press or friction press, and the specification of compacting water-permeable brick is 200 × 100mm, thickness
For 40mm-60mm;(6) high temperature sintering, sintering temperature is 1200 DEG C-1300 DEG C, and kiln discharge chooses to install.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although with reference to aforementioned reality
Executing example to be described in detail the present invention, for a person skilled in the art, it still can be to aforementioned each enforcement
Technical scheme described in example is modified, or wherein portion of techniques feature is carried out equivalent.All essences in the present invention
Within god and principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.
Claims (5)
1. the preparation method of a mine tailing flint clay water-permeable brick, it is characterised in that: comprise the steps:
(1) broken, mine tailing flint clay pulverizer is pulverized;
(2) screening, screens out the 30 above granules of mesh in step (1) pulverized particles stand-by, and 30 mesh-1mm make as surface layer, 1-3mm
For main part;
(3) batch mixing, adds the close material formula of following mass percent by the raw material that filters out: aluminum phosphate solution 10%-20%, sulfur
Acid aluminum solutions 15%-25%, carbamide 4-10%, clay 15-25%, sodium silicate 8-16%, binding agent 4-6%, sodium sulfate 4-
6%;
(4) stirring, fully stirs evenly with blender;
(5) molding, adds mixture paste in mould, compressing with press;
(6) high temperature sintering, kiln discharge chooses to install.
The preparation method of mine tailing flint clay water-permeable brick the most according to claim 1, it is characterised in that: in described step (1)
Mine tailing flint clay pulverizer is crushed to 0-10mm.
The preparation method of mine tailing flint clay water-permeable brick the most according to claim 1, it is characterised in that: in described step (5)
The press selected is hydraulic press or friction press.
The preparation method of mine tailing flint clay water-permeable brick the most according to claim 1, it is characterised in that: in described step (6)
The temperature of high temperature sintering is 1200 DEG C-1300 DEG C.
The preparation method of mine tailing flint clay water-permeable brick the most according to claim 1, it is characterised in that: in described step (5)
The mine tailing flint clay water-permeable brick specification of compacting is 200 × 100mm, and thickness is 40mm-60mm.