CN106240115A - A kind of long-acting optics antifog film and preparation method thereof - Google Patents
A kind of long-acting optics antifog film and preparation method thereof Download PDFInfo
- Publication number
- CN106240115A CN106240115A CN201610606342.7A CN201610606342A CN106240115A CN 106240115 A CN106240115 A CN 106240115A CN 201610606342 A CN201610606342 A CN 201610606342A CN 106240115 A CN106240115 A CN 106240115A
- Authority
- CN
- China
- Prior art keywords
- antifog film
- long
- layer
- acting
- optics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of long-acting optics antifog film, described antifog film includes high transparency PET base material, described high transparency PET base material upper surface scribbles anti-fog layer, described anti-fog layer is that hydrophilic nano polymer solution prepares after 60~100 DEG C of solidifications, lower surface scribbles water white transparency acrylate glue adhesion coating, described adhesive layer laminating mould release membrance peel ply.The invention also discloses a kind of method preparing above-mentioned antifog film.The antifog film of the present invention has good anti-fog performance, tack and good optical transmission, glass article surface of easily fitting, and does not interferes with original optical transmission, and glass breaking also can be avoided to hurt sb.'s feelings, and safety is good.
Description
Technical field
The present invention relates to relate to a kind of long-acting optics antifog film and preparation method thereof.
Background technology
Glass and transparent plastic film are the transparent materials being widely used in industrial and agricultural production and daily life.Vehicle, builds
Build thing window-glass and mirror, bathroom mirror, the lens of instrument and the display mirror etc. of electronic product and often can run into surface atomizing
Phenomenon, the steam in air forms droplet on its surface, and the surface blur making otherwise transparent is unclear, makes to production and life
Become adverse influence, cause observability impaired, bring a lot of potential safety hazard.Anti-fog method and antifog article are weighed widely
Depending on, current anti-fog method mainly has electrical heating method and sprays anti-fog coating at substrate surface, and electrical heating uses in the car except mist
More, it is antifog respond well, but its energy consumption is big, expensive, and spraying anti-fog coating has the most anti-fog properties in a short time, but
Coating uncured, continues anti-fog properties poor, uses environment to be restricted.
Summary of the invention
It is an object of the invention to provide a kind of long-acting optics antifog film, it is possible to be widely used in glass article surface, tool
There is good long timeliness anti-fog properties, and the light transmission of glass will not be reduced, material surface is shielded, reduce mill
Damage.
Further object is that the preparation method that above-mentioned long-acting optics antifog film is provided.
In order to solve the problem of above-mentioned technology, the technical solution used in the present invention is: a kind of long-acting optics antifog film, described
Antifog film includes that high transparency PET base material, described high transparency PET base material upper surface scribble anti-fog layer, and described anti-fog layer is hydrophilic
Nanometer polymer solution layer, lower surface scribbles water white transparency acrylate glue adhesion coating, described adhesive layer laminating mould release membrance peel ply.
The antifog film of the present invention is by being coated with one layer of hydrophilic nano polymer solution at substrate upper surface, through high-temperature baking
Solidification, making substrate surface is hydrophiling, when it is in the environment of easy fogging, steam can carry out automatic affine absorption, and
Reduce the surface tension of water, reduce the contact angle of hydrone and substrate surface, make steam also not be agglomerated into carefully at substrate surface
Before droplet, moistening will spread, or be adsorbed in substrate surface one layer of ultra-thin transparent moisture film of formation, no longer to incident illumination
Learn the effect producing scattering, do not disturb the sight line of people thus reach antifog purpose.
Preferably, the one during described anti-fog layer is polyurethane, diethanolamine, polyhydric alcohol, surfactant solution layer
Or several mixture, it being attached to substrate surface through heat cure, form nano-high molecule film, preferred thickness is 0.5-1um, to water
Molecule energy automatic absorbing, has superior resistance to wiping due to the intrinsic elasticity of polyurethane, it is thus possible to continuing of long timeliness
Antifog.
Preferably, the thickness of described high transparency PET base material at 50-75um, light transmittance polyester PET more than 90%, its
There is good processing of cutting so that it is prepared products application, when other materials surface, does not affect applied material
Original light transmittance.
Preferably, described water white transparency acrylate glue adhesion coating thickness is at 15-20um, for acrylic type sticker, acrylic acid
Adhesive layer has high viscous automatic absorbing function, can be affixed on application material surface easily, moreover it is possible to increase its printing opacity during use
Rate, hurts sb.'s feelings even if damage of material does not breaks up yet, and security performance is good.
Preferably, described peel ply mould release membrance is polyester PET mould release membrance, and thickness, at 20-30um, is easily peeled off during use.
Present invention also offers a kind of preparation method preparing above-mentioned long-acting optics antifog film, comprise the following steps:
(1) it is coated with hydrophilic nano polymer solution anti-fog layer at high transparency PET base material upper surface, after entering curing oven
Rolling;
(2) it is coated with acrylate glue adhesion coating at high transparency PET base material lower surface;
(3) in acrylate glue paste layer laminating peel ply mould release membrance, rolling.
Further, after step (2), also include entering curing oven.
Further, said method also includes carrying out base material in advance wind pouring, removes foreign body and the dust of substrate surface, then
The electrostatic entrained by material surface is removed through ionotron;It is coated with anti-fog solutions, through floated baking oven by intaglio plate coating head
Rolling after solidification;Solidification temperature 60-100 DEG C, 30 seconds to 1 minute hardening time.
Further, the coating process of described acrylate glue adhesion coating is to be coated with acrylic acid glue by slit type coating head,
After floated curing oven, fit mould release membrance, rolling, wherein, solidification temperature is 60~120 DEG C, hardening time be 30 seconds to 1
Minute.
The preparation method of the present invention uses multi-layer coated complex technique, utilizes the advantage of different coating method to prepare accordingly
The coating of thickness, makes required function combine, the corresponding time and at a temperature of, it is possible to completion of cure, make the performance of coating obtain
With stable, and the described floated baking oven smart metastable control temperature of energy, it is internal without deflector roll, reduces material scratch, it is ensured that
The optical property of material is not damaged.
A kind of long-acting optics antifog film of the present invention has good long timeliness anti-fog performance, and it is by antifogging coating, height
Transparent PET substrate layer, acrylic acid adhesive layer and mould release membrance are composited by multi-layer coated, existing good anti-fog performance,
Also have good tack and good optical transmission, glass article surface of easily fitting, do not interfere with original optical lens
The property crossed, also can avoid glass breaking to hurt sb.'s feelings, and safety is good.
Accompanying drawing explanation
Accompanying drawing described herein is used for providing a further understanding of the present invention, constitutes the part of the application, not
Constitute inappropriate limitation of the present invention, in the accompanying drawings:
Fig. 1 is the structural representation of the present invention long-acting optics antifog film.
Detailed description of the invention
The present invention is described in detail, in the illustrative examples of this present invention below in conjunction with accompanying drawing and specific embodiment
And explanation is used for explaining the present invention, but not as a limitation of the invention.
Example is raw materials used, unless otherwise indicated, is city's pin industrial goods, commercially available by commercial channel.
As it is shown in figure 1, a kind of long-acting optics antifog film of the present invention, including four layers, the 1st layer is anti-fog layer, is mainly composed of
One or several mixture in polyurethane, diethanolamine, polyhydric alcohol, surfactant solution, the 2nd layer is high transparency
PET base material layer, light transmittance is the polyester PET of 92%, and the 3rd layer is acrylate glue adhesion coating, and the 4th layer is peel ply, polyester release film;
Wherein, the heat cure of described anti-fog layer 1 is combined in the upper surface of high PET base material 2 thoroughly, and acrylate glue adhesion coating 3 heat cure is combined in height
PET base material 2 lower surface thoroughly, mould release membrance 4 is compounded in acrylate glue adhesion coating 3 surface.
Concrete, in the present embodiment, antifog film thickness is 85.5-126um, and wherein the thickness of antifogging coating 1 is 0.5-
1um;High transparency PET polyester base material 2 thickness is 50-75um;Acrylate glue adhesion coating 3 thickness is 15-20um;Peel ply 4 mould release membrance
Thickness is 20-30um.
Present invention also offers the preparation method of a kind of long-acting optics antifog film, specifically include following steps:
Step one: base material carries out wind pouring in advance, removes foreign body and the dust of substrate surface, then removes through ionotron
Electrostatic entrained by material surface, then carries out anti-fog layer coating;
Step 2: be diluted anti-fog layer coating, range of viscosities is at 10-300mpa.s/25 DEG C;Antifoggant composition includes
Polyacrylic acid, diethanolamine, polyhydric alcohol, surfactant solution;
Step 3: the antifoggant coating after being diluted by intaglio plate coating head is uniformly applied to high PET base material upper surface thoroughly;
Step 4: the product obtained by step 3 is solidified as the suspension drying in oven of 60-100 DEG C, hardening time
30s-1 minute, more rolling device rolling;
Step 5: the mixed material of configuration acrylate glue adhesion coating, by acrylic acid adhesive, firming agent and ethyl acetate by not
With component mix and blend, range of viscosities is at 100-500mpa.s/25 DEG C;
Step 6: mixed material step 5 configured by slit type coating head is uniformly applied under high PET base material thoroughly
Surface;
Step 7: the product obtained by step 6 is placed in the suspension drying in oven solidification of 60-120 DEG C, hardening time
30 seconds to 1 minute;
Step 8: being combined with mould release membrance through laminating apparatus, long-acting optics antifog film is made in rolling again.
Below in conjunction with specific embodiment, the present invention is described in further detail:
Embodiment 1
Step one: select 75um, light transmittance is the high PET base material thoroughly of more than 90%, in advance base material is carried out wind pouring.Remove
The foreign body of substrate surface and dust, then remove the electrostatic entrained by material surface through ionotron, then carry out anti-fog layer painting
Cloth;
Step 2: anti-fog layer is commercially available ELECUT C-043 antifoggant, adds deionized water, carries out 7 times of dilutions;
Step 3: the antifoggant coating after being diluted by intaglio plate coating head is uniformly applied to high PET base material upper surface thoroughly;
Step 4: product obtained by step 3 is placed in 2m*6 joint suspension baking oven in, temperature be set as 60 DEG C, 80 DEG C,
100 DEG C, 100 DEG C, 80 DEG C, 70 DEG C, speed is 20m/min, and hardening time is 36s, more rolling device rolling;
Step 5: select commercially available Co., Ltd. C T-3850 acrylic acid sticker, by sticker: ethyl acetate: firming agent is
100:60:1.5 carries out mix and blend, and solid content is about 27.5%;
Step 6: mixed material step 5 configured by slit type coating head is uniformly applied under high PET base material thoroughly
Surface;
Step 7: product obtained by step 6 is placed in 2m*6 joint suspension baking oven in, temperature be set as 60 DEG C, 80 DEG C,
100 DEG C, 120 DEG C, 100 DEG C, 70 DEG C, speed is 20m/min, and hardening time is 36s;
Step 8: being combined with mould release membrance through laminating apparatus, long-acting optics antifog film is made in rolling again.
As follows the performance of the long-acting optics antifog film of embodiment 1 is detected:
A) water contact angle: use contact angle instrument to test at the anti-fog surface of long-acting optics antifog film;
B) peel strength: with reference to standard GB/T/T 2792;
C) light transmittance: use Ai Seli spectrophotometer to test;
D) anti-fog properties: the antifogging coating face of optics antifog film to be placed in above the water container of 60-100 DEG C at 5cm stifling 1 little
Time, observe the anti-fog surface whether fogging of optics antifog film,
E) erasibility: dip in full water with pure cotton cloth, wraps in and (wraps rear test area about 1.5cm on the counterweight of 500g2) with 50-
The speed of 60 beats/min, the stroke of 20mm, in the anti-fog layer surface wipe cycle back and forth of optics antifog film, after circulating 500 times,
Observing the anti-fog performance of anti-fog layer again, if anti-fog performance is good, then its coating erasibility is preferable;
F) resistance to water: optics antifog film antifogging coating face is covered in the water surface of 23 degrees centigrade, after standing 1 day, then
Observe damaged condition and the anti-fog performance of anti-fog layer;
G) weatherability: optics antifog film is placed in the climatic chamber 7 days of 85% humidity, 85 DEG C of temperature, then surveys antifog painting
The anti-fog performance of aspect and peel strength;
H) hardness: with reference to standard GB/T/T 6739.
Test result
Performance test | Testing standard | Measured value | Remarks |
Water droplet contact angle | ≤10° | 7.5° | -- |
Peel strength | 1400-1600gf/in | 1560gf/in | GB/T 2792 |
Light transmittance | >=85% | 90% | -- |
Anti-fog properties | 1h is without exception | 1h is without exception | -- |
Erasibility | 500 times without exception | 500 times without exception | -- |
Resistance to water | 24h is without exception | 24h is without exception | -- |
Weatherability | 7 days without exception | 7 days without exception | -- |
Hardness | ≥2H | 2H | Rhizoma Sparganii pencil hardometer |
Above-mentioned testing result show the present invention antifog film can long timeliness antifog, also there is good resistance to water, attachment
Property, optical transmission.The antifog film of the present invention uses the simplest, after concrete size cutting, is shelled by mould release membrance peel ply
It is pasted onto glass after to show, at vehicle, building window glass and mirror, bathroom mirror, the lens of instrument and electricity
After the long-acting optics antifog film of the surface mount present invention such as the display mirror of sub-product, it is possible to well play the antifog effect of long timeliness
Really, original light transmission is not interfered with, moreover it is possible to glass article surface is shielded, it is to avoid hurt sb.'s feelings after glass breaking.
The technical scheme provided the embodiment of the present invention above is described in detail, specific case used herein
Principle and embodiment to the embodiment of the present invention are set forth, and the explanation of above example is only applicable to help to understand this
The principle of inventive embodiments;Simultaneously for one of ordinary skill in the art, according to the embodiment of the present invention, in specific embodiment party
All will change in formula and range of application, in sum, this specification content should not be construed as limitation of the present invention.
Claims (10)
1. a long-acting optics antifog film, it is characterised in that: described antifog film includes high transparency PET base material, described high transparency PET
Substrate upper surface scribbles anti-fog layer, and described anti-fog layer is hydrophilic nano layer of polymer solution, and lower surface scribbles water white transparency third
Olefin(e) acid adhesive layer, described adhesive layer laminating mould release membrance peel ply.
One the most according to claim 1 this antifog film of long-acting light, it is characterised in that: described anti-fog layer be polyurethane,
The mixture of one or more in diethanolamine, polyhydric alcohol, surfactant solution layer.
One the most according to claim 2 long-acting optics antifog film, it is characterised in that: described anti-fog layer thickness is at 0.5-
1um。
One the most according to claim 1 long-acting optics antifog film, it is characterised in that: the thickness of described high transparency PET base material
Spend at 50-75um, light transmittance polyester PET more than 90%.
One the most according to claim 1 long-acting optics antifog film, it is characterised in that: described water white transparency acrylic acid is gluing
Layer thickness is at 15-20um, for acrylic type sticker.
One the most according to claim 1 long-acting optics antifog film, it is characterised in that: described peel ply mould release membrance thickness exists
20-30um。
7. preparing a preparation method for long-acting optics antifog film as described in claim 1~6 any one, its feature exists
In, comprise the following steps:
(1) it is coated with hydrophilic nano polymer solution anti-fog layer at high transparency PET base material upper surface, receives after entering curing oven
Volume;
(2) it is coated with acrylate glue adhesion coating at high transparency PET base material lower surface;
(3) in acrylate glue paste layer laminating peel ply mould release membrance, rolling.
The preparation method of a kind of long-acting optics antifog film the most according to claim 6, it is characterised in that: step (2) it
After, also include entering curing oven.
9. according to the preparation method of a kind of long-acting optics antifog film described in claim 6 or 7, it is characterised in that: also include pre-
First base material is carried out wind pouring, removes foreign body and the dust of substrate surface, then remove entrained by material surface through ionotron
Electrostatic;It is coated with anti-fog solutions, rolling after floated curing oven by intaglio plate coating head;Solidification temperature 60-100 DEG C, solidification
30 seconds to 1 minute time.
The preparation method of a kind of long-acting optics antifog film the most according to claim 8, it is characterised in that: described acrylic acid
The coating process of adhesive layer is to be coated with acrylic acid glue by slit type coating head, after floated curing oven, fits release
Film, rolling, wherein, solidification temperature is 60~120 DEG C, and hardening time is 30 seconds to 1 minute.