CN106221528A - A kind of have the most smooth PU matte white finish of gloss and preparation method thereof - Google Patents
A kind of have the most smooth PU matte white finish of gloss and preparation method thereof Download PDFInfo
- Publication number
- CN106221528A CN106221528A CN201610736223.3A CN201610736223A CN106221528A CN 106221528 A CN106221528 A CN 106221528A CN 201610736223 A CN201610736223 A CN 201610736223A CN 106221528 A CN106221528 A CN 106221528A
- Authority
- CN
- China
- Prior art keywords
- component
- slurry
- gloss
- smooth
- solid content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of have the most smooth PU matte white finish of gloss and preparation method thereof, this PU matte white finish is the white slurry with 60% solid content, short oil alkyd resin, PE delustring wax is starched, the 6900 anti-settling waxes of 20X, anti-settling slurry, wetting dispersing agent, levelling agent, defoamer, MIBK, the vinyl chloride-vinyl acetate resin liquid of 20% solid content, the mute powder of ED 30, polytetrafluoroethylwax wax powder etc. makes first component, with 1451 light trimer curing agents, TDI addition product firming agent, HDI trimer firming agent, MIBK, MEK and n-butyl acetate are made into component B, with toluene, n-butyl acetate, ethyl acetate, MEK and propylene glycol methyl ether acetate are made into the third component, again by first, second, third component mixes in proportion.The PU matte white finish of the present invention, after testing and probationary certificate, paint film good leveling property after its spraying, resist sagging ability are strong, scumbling without growing dim, can keep the most smooth, gloss is stable, is suitable for the application of the woodworks such as top-grade furniture.
Description
Technical field
The invention belongs to woodwork coating manufacturing industry, be specifically related to a kind of there is the PU dumb light flour that gloss is the most smooth
Paint research and development.
Background technology
Common PU matte white finish is when spraying, and all coating technology practitioners both know about gloss paint film delustring mainly
Use aerosil, but due to the self character of aerosil, thus, it is by construction technology, drying time, ring
The impact of the factor such as environmental temperature and humidity, result of prevention is big, particularly when producing the white finish paint of low gloss, if aerosil is used
Amount is big, and lustre lacking uniformity easily occurs in paint film, the film defect such as grow dim；Organosilicon and wax powder is used to be suspended in paint film top layer and provide
Feel, paint film on furniture as time went on, use during constantly friction, after paint film abrasion is old, organosilicon and wax
The silk wiping sense of the given film of powder will disappear.Along with top-grade furniture is increasingly liked by consumer, coating specification the most constantly carries
Rising, common PU dumb light can not meet the most far away clearly high-grade application demand.
The present invention is to utilize the easy delustring of high molecular short oil alkyd resin, the feature of fast drying, spells with 1451 light trimerizations
Body firming agent, HDI trimer firming agent, make paint film have excellent lifting in rate of drying, flexibility, by adding
The vinyl chloride-vinyl acetate resin solution of 20% solid content improves the resistance to of paint and opens dilute performance, helps delustering agent arrangement uniformly, utilizes PE delustring
Wax self the smooth feature that suspends of slurry, collocation is a small amount of containing the flatting silica of Lasaxing Oilfield, polytetrafluoroethylwax wax, the making of organosilicon auxiliary agent
With, in raising, powder anti-settling, mute is evenly distributed, give the paint film smooth effect from surface to nexine simultaneously, will not be because of paint film top layer
Rub and lose smooth effect, prepare and there is the PU matte white finish finish paint product that gloss is the most smooth.
Summary of the invention
It is an object of the invention to: for above-mentioned the deficiencies in the prior art, it is provided that a kind of to have gloss the most smooth
PU matte white finish and preparation method thereof, this PU matte white finish has instant good leveling property, gloss is stable, permanent retention is refreshing
Cunning, no sag, without the feature such as growing dim, adapt to the application demand of the stable wooden articles in light requirement pool.
For reaching above-mentioned purpose, the technical solution used in the present invention is: a kind of have the PU dumb light that gloss is the most smooth
White finish paint, this PU matte white finish is formed by weight 1:0.4:0.3～0.7 mixing by first component, component B and the third component；
Wherein, first component is by weight percentage by the white slurry 45%～60% of 60% solid content, short oil alkyd resin 10%
～13%, the anti-settling wax of 6900-20X 3.5%～5%, anti-settling slurry 1.5%～2%, wetting dispersing agent 1%～1.7%, levelling agent
0.2%～0.5%, defoamer 0.3%～0.5%, MIBK 1%～1.5%, polytetrafluoroethylwax wax powder 0.3%～0.5%,
The vinyl chloride-vinyl acetate resin solution 8%～12% of the mute powder of ED-30 0.5%～1%, 20% solid content, PE delustring wax slurry 8%～13% and vinegar
Acid butyl ester 3%～7% forms；
Starching by weight percentage by short oil alkyd resin 34.6%, aerosil in vain of above-mentioned 60% solid content
0.2%, dispersant 1.2%, Rutile type titanium dioxide 60% and dimethylbenzene 4% form；
Component B is by weight percentage by 1451 light trimer curing agents 25%～35%, TDI addition product firming agent 6%
～13%, HDI trimer firming agent 8%～18%, MIBK 12%, MEK 10% and n-butyl acetate 22%～29% composition；
Third component is by weight percentage by toluene 40%～45%, n-butyl acetate 20%～25%, ethyl acetate 10%
～15%, MEK 10% and propylene glycol methyl ether acetate 5%～20% composition.
Described first component fineness≤25um, viscosity is 300～800mpa.s/25 DEG C.
The vinyl chloride-vinyl acetate resin solution of described 20% solid content is by weight percentage by dimethylbenzene 25%, MIBK 55% and chlorine vinegar
Resin 20% forms (for prior art).
Described anti-settling slurry is by weight percentage by dimethylbenzene 68.5%, high molecular short oil alkyd resin 20% (macromolecule
Amount short oil alkyd resin is purchased from Zhuhai Sa Bisi chemical company), EFCONA 5054 dispersant 1.5% and BENTONE 34 swelling
Soil 10% composition.
Wetting dispersing agent in described first component is modified polyurethane polymeric dispersant.
Described levelling agent is silicone levelling agent (Di Gao auxiliary agent company limited) or organosilicon levelling agent.
Described defoamer is broken to steep polymer and the solution of polysiloxanes.
Dispersant in the white slurry of described 60% solid content is the copolymer solution containing acidic-group.
Present invention simultaneously provides the above-mentioned preparation method with the most smooth PU matte white finish of gloss, the method
Step is as follows:
Prepare first, second, the third component the most respectively:
Preparation first component: be sequentially added into the white slurry of 60% solid content, short oil alkyd resin, 6900-20X in dispersion cylinder anti-
Heavy wax, anti-settling slurry, wetting dispersing agent, levelling agent, defoamer and MIBK, be stirred until homogeneous with 600～800r/min, add poly-
Tetrafluoroethene wax powder and the mute powder of ED-30, with 1200～1500r/min dispersed with stirring 10～15min to fineness≤25um, then depend on
The vinyl chloride-vinyl acetate resin solution of secondary addition 20% solid content, PE delustring wax slurry and a small amount of ethyl acetate, with 800～1000r/min stirrings
To uniformly, finally adjust viscosity to 300～800mpa.s/25 DEG C with remaining butyl acetate；
The white slurry of above-mentioned 60% solid content mentioned is first to take short oil alkyd resin, aerosil, dimethylbenzene and divide
Powder mixes, and disperses 3～7 minutes with the rotating speeds of 800～1000 revs/min, then adds under the rotating speed of 600～800 revs/min
Enter Rutile type titanium dioxide, with 1200～1500 revs/min of dispersed with stirring 12～18 minutes, be finally ground to fineness≤20um；
Prepare component B: in 1451 light trimer curing agents, be sequentially added into TDI addition product firming agent, HDI trimer
Firming agent, MIBK, MEK and n-butyl acetate, stir, and seals, standby；
Prepare the third component: take toluene, n-butyl acetate, ethyl acetate, MEK and propylene glycol methyl ether acetate mixing, stirring
Uniformly, standby；
B. by first component, component B and the third component by weight 1:0.4:0.3～0.7 mixing, stir.
The vinyl chloride-vinyl acetate resin solution of above-mentioned 20% solid content mentioned be take dimethylbenzene and MIBK mixing, 400～600 turns/
Minute rotating speed under add vinyl chloride-vinyl acetate resin, then be stirred until homogeneous to fineness≤10um with 800～1000 revs/min.
The above-mentioned anti-settling slurry mentioned is first to take dimethylbenzene, high molecular short oil alkyd resin and EFCONA 5054 dispersant
Mixing, with the rotating speed dispersed with stirring 3 of 800～100 revs/min～7 minutes, then puts under the rotating speed of 600～800 revs/min
BENTONE 34 bentonite, with the rotating speed dispersed with stirring 8 of 1200～1500 revs/min～12 minutes, be finally ground to fineness≤
20um。
The first component of the present invention, component B and the third component separately store after producing, and during use, allotment generation PU is mute in proportion
Light white finish paint, the third component is not involved in chemical reaction, only plays latting drown construction action.(performance indications can refer to GB/23997-after testing
2009, limits of harmful substances is with reference to GB18581-2009), each performance indications of PU matte white finish of the present invention see table 1, this
Bright PU matte white finish, as a example by three light splitting, with the Performance comparision of existing three commercially available light splitting matte white finish, see table 2.
It follows that PU matte white finish gloss of the present invention is stable, can keep smooth coating, good leveling property, not sagging, gloss is stable,
Keep smooth, be the first-selection of top-grade furniture spraying.
Each performance indications table of table 1 PU of the present invention matte white finish
Table 2 product of the present invention and prior art products Performance comparision table
Compared with prior art, the invention have the advantage that the PU matte white finish of the present invention after testing and probationary certificate, its
There is the features such as instant good leveling property, gloss is stable, permanent retention is smooth, no sag, nothing are grown dim, to adapt to be sprayed at high-grade family
The application of tool.
Detailed description of the invention
Prepare the vinyl chloride-vinyl acetate resin solution of 20% solid content: take dimethylbenzene 25% and MIBK 55% by weight percentage and mix,
Under the rotating speed of 400～600 revs/min, add vinyl chloride-vinyl acetate resin 20%, then be stirred until homogeneous to carefully with 800～1000 revs/min
Degree≤10um.
Prepare anti-settling slurry: the most first take dimethylbenzene 68.5%, high molecular short oil alkyd resin 20% and
EFCONA 5054 dispersant 1.5% mixes, with the rotating speed dispersed with stirring 5 minutes of 800～100 revs/min, then 600～800
Rev/min rotating speed under put into BENTONE 34 bentonite 10%, with the rotating speed dispersed with stirring 10 points of 1200～1500 revs/min
Clock, is finally ground to fineness≤20um.
Embodiment 1
Prepare the white slurry of 60% solid content: the most first take short oil alkyd resin 34.6%, aerosil
0.2%, dimethylbenzene 4% and dispersant (copolymer solution containing acidic-group) 1.2% mixing, divide with the rotating speed of 800 revs/min
Dissipate 7 minutes, under the rotating speed of 600 revs/min, then add Rutile type titanium dioxide 60%, with 1200 revs/min of dispersed with stirring
18 minutes, finally it is ground to fineness≤20um.
Preparation first component: be sequentially added into the white slurry 45% of 60% solid content, short oil alcohol in dispersion cylinder by weight percentage
The anti-settling wax of acid resin 13%, 6900-20X 5%, anti-settling slurry 2%, modified polyurethane polymeric dispersant 1.7%, silicone stream
Flat agent 0.2%, defoamer (broken bubble polymer and the solution of polysiloxanes) 0.3% and MIBK 1.5%, stir with 600r/min
To uniformly, add the mute powder 1% of polytetrafluoroethylwax wax powder 0.3% and ED-30, with 1200r/min dispersed with stirring 15min to fineness
≤ 25um, is then sequentially added into the vinyl chloride-vinyl acetate resin solution 10% of 20% solid content, PE delustring wax slurry 13% and ethyl acetate 3%,
It is stirred until homogeneous with 800r/min, finally adjusts viscosity to 800mpa.s/25 DEG C with butyl acetate 4%.
Prepare component B: be sequentially added into 1451 light trimer curing agents 25%, the solidification of TDI addition product by weight percentage
Agent 13%, HDI trimer firming agent 18%, MIBK 12%, MEK 10% and n-butyl acetate 22%, stir, and seals.
Prepare the third component: take toluene 40%, n-butyl acetate 20%, ethyl acetate 10%, MEK by weight percentage
10% and propylene glycol methyl ether acetate 20% mix, stir.
First component, component B and the third component are mixed by weight 1:0.4:0.3, obtains the PU dumb light flour of the present invention
Paint.
Embodiment 2
Prepare the white slurry of 60% solid content: the most first take short oil alkyd resin 34.6%, aerosil
0.2%, dimethylbenzene 4% and dispersant (copolymer solution containing acidic-group) 1.2% mixing, with the rotating speed of 1000 revs/min
Disperse 3 minutes, under the rotating speed of 800 revs/min, then add Rutile type titanium dioxide 60%, with 1500 revs/min of stirrings point
Dissipate 12 minutes, be finally ground to fineness≤20um.
Preparation first component: be sequentially added into the white slurry 52.6% of 60% solid content, short oil in dispersion cylinder by weight percentage
The anti-settling wax of alkyd resin 12%, 6900-20X 4%, anti-settling slurry 1.8%, modified polyurethane polymeric dispersant 1.5%, organosilicon
Levelling agent 0.3%, defoamer (broken bubble polymer and the solution of polysiloxanes) 0.4% and MIBK 1.2%, stir with 700r/min
Mix to uniformly, add the mute powder 0.8% of polytetrafluoroethylwax wax powder 0.4% and ED-30, with 1300r/min dispersed with stirring 13min extremely
Fineness≤25um, is then sequentially added into the vinyl chloride-vinyl acetate resin solution 12% of 20% solid content, PE delustring wax slurry 10% and ethyl acetate
1.2%, it is stirred until homogeneous with 900r/min, finally adjusts viscosity to 500mpa.s/25 DEG C with butyl acetate 1.8%.
Prepare component B: be sequentially added into 1451 light trimer curing agents 31%, the solidification of TDI addition product by weight percentage
Agent 10%, HDI trimer firming agent 8%, MIBK 12%, MEK 10% and n-butyl acetate 29%, stir, and seals.
Prepare the third component: take toluene 43%, n-butyl acetate 22%, ethyl acetate 12%, MEK by weight percentage
10% and propylene glycol methyl ether acetate 13% mix, stir.
First component, component B and the third component are mixed by weight 1:0.4:0.5, obtains the PU dumb light flour of the present invention
Paint.
Embodiment 3
Prepare the white slurry of 60% solid content: the most first take short oil alkyd resin 34.6%, aerosil
0.2%, dimethylbenzene 4% and dispersant (copolymer solution containing acidic-group) 1.2% mixing, divide with the rotating speed of 900 revs/min
Dissipate 5 minutes, under the rotating speed of 700 revs/min, then add Rutile type titanium dioxide 60%, with 1300 revs/min of dispersed with stirring
15 minutes, finally it is ground to fineness≤20um.
Preparation first component: be sequentially added into the white slurry 60% of 60% solid content, short oil alcohol in dispersion cylinder by weight percentage
The anti-settling wax of acid resin 10%, 6900-20X 3.5%, anti-settling slurry 1.5%, modified polyurethane polymeric dispersant 1%, organosilicon stream
Flat agent 0.5%, defoamer (broken bubble polymer and the solution of polysiloxanes) 0.5% and MIBK 1.0%, stir with 800r/min
To uniformly, add the mute powder 0.5% of polytetrafluoroethylwax wax powder 0.5% and ED-30, with 1500r/min dispersed with stirring 10min to carefully
Degree≤25um, is then sequentially added into the vinyl chloride-vinyl acetate resin solution 8% of 20% solid content, PE delustring wax slurry 8% and ethyl acetate
1.7%, it is stirred until homogeneous with 1000r/min, finally adjusts viscosity to 300mpa.s/25 DEG C with butyl acetate 3.3%.
Prepare component B: be sequentially added into 1451 light trimer curing agents 35%, the solidification of TDI addition product by weight percentage
Agent 6%, HDI trimer firming agent 12%, MIBK 12%, MEK 10% and n-butyl acetate 25%, stir, and seals.
Prepare the third component: take toluene 45%, n-butyl acetate 25%, ethyl acetate 15%, MEK by weight percentage
10% and propylene glycol methyl ether acetate 5% mix, stir.
First component, component B and the third component are mixed by weight 1:0.4:0.7, obtains the PU dumb light flour of the present invention
Paint.
Claims (9)
1. one kind has the PU matte white finish that gloss is the most smooth, it is characterised in that this PU matte white finish is by first group
Part, component B and the third component form by weight 1:0.4:0.3～0.7 mixing；
Wherein, first component by weight percentage by the white slurry 45%～60% of 60% solid content, short oil alkyd resin 10%～
13%, the anti-settling wax of 6900-20X 3.5%～5%, anti-settling slurry 1.5%～2%, wetting dispersing agent 1%～1.7%, levelling agent
0.2%～0.5%, defoamer 0.3%～0.5%, MIBK 1%～1.5%, polytetrafluoroethylwax wax powder 0.3%～0.5%,
The vinyl chloride-vinyl acetate resin solution 8%～12% of the mute powder of ED-30 0.5%～1%, 20% solid content, PE delustring wax slurry 8%～13% and vinegar
Acid butyl ester 3%～7% forms；
The white slurry of above-mentioned 60% solid content by weight percentage by short oil alkyd resin 34.6%, aerosil 0.2%, point
Powder 1.2%, Rutile type titanium dioxide 60% and dimethylbenzene 4% form；
Component B by weight percentage by 1451 light trimer curing agents 25%～35%, TDI addition product firming agent 6%～
13%, HDI trimer firming agent 8%～18%, MIBK 12%, MEK 10% and n-butyl acetate 22%～29% composition；
Third component by weight percentage by toluene 40%～45%, n-butyl acetate 20%～25%, ethyl acetate 10%～
15%, MEK 10% and propylene glycol methyl ether acetate 5%～20% composition.
A kind of have the PU matte white finish that gloss is the most smooth, it is characterised in that described
First component fineness≤25um, viscosity is 300～800mpa.s/25 DEG C.
A kind of have the PU matte white finish that gloss is the most smooth, it is characterised in that described
Anti-settling slurry is by weight percentage by dimethylbenzene 68.5%, high molecular short oil alkyd resin 20%, EFCONA 5054 dispersant
1.5% and BENTONE 34 bentonite 10% forms.
A kind of have the PU matte white finish that gloss is the most smooth, it is characterised in that described
Wetting dispersing agent in first component is modified polyurethane polymeric dispersant.
A kind of have the PU matte white finish that gloss is the most smooth, it is characterised in that described
Levelling agent is silicone levelling agent or organosilicon levelling agent.
A kind of have the PU matte white finish that gloss is the most smooth, it is characterised in that described
Defoamer is broken to steep polymer and the solution of polysiloxanes.
A kind of have the PU matte white finish that gloss is the most smooth, it is characterised in that described
Dispersant in the white slurry of 60% solid content is the copolymer solution containing acidic-group.
8. a kind of preparation side with the most smooth PU matte white finish of gloss according to any one of claim 1-7
Method, it is characterised in that the method step is as follows:
Prepare first, second, the third component the most respectively:
Preparation first component: be sequentially added into the white slurry of 60% solid content, short oil alkyd resin, 6900-20X in dispersion cylinder anti-settling
Wax, anti-settling slurry, wetting dispersing agent, levelling agent, defoamer and MIBK, be stirred until homogeneous with 600～800r/min, adds poly-four
Fluorothene wax powder and the mute powder of ED-30, with 1200～1500r/min dispersed with stirring 10～15min to fineness≤25um, the most successively
Add the vinyl chloride-vinyl acetate resin solution of 20% solid content, PE delustring wax slurry and a small amount of ethyl acetate, with 800～1000r/min stirrings extremely
Uniformly, finally adjust viscosity to 300～800mpa.s/25 DEG C with remaining butyl acetate；
Wherein, the white slurry of 60% solid content is first to take short oil alkyd resin, aerosil, dimethylbenzene and dispersant,
Disperse 3～7 minutes with the rotating speeds of 800～1000 revs/min, under the rotating speed of 600～800 revs/min, then add rutile
Type titanium dioxide, with 1200～1500 revs/min of dispersed with stirring 12～18 minutes, is finally ground to fineness≤20um；
Prepare component B: in 1451 light trimer curing agents, be sequentially added into TDI addition product firming agent, HDI trimer solidification
Agent, MIBK, MEK and n-butyl acetate, stir, and seals, standby；
Prepare the third component: take toluene, n-butyl acetate, ethyl acetate, MEK and propylene glycol methyl ether acetate mixing, stir,
Standby；
B. by first component, component B and the third component by weight 1:0.4:0.3～0.7 mixing, stir.
9. preparation method as claimed in claim 8, it is characterised in that described anti-settling slurry is that first to take dimethylbenzene, high molecular short
Oil alkyd resin and EFCONA 5054 dispersant, with the rotating speed dispersed with stirring 3 of 800～100 revs/min～7 minutes, then
Under the rotating speed of 600～800 revs/min, put into BENTONE 34 bentonite, stir with the rotating speeds of 1200～1500 revs/min and divide
Dissipate 8～12 minutes, be finally ground to fineness≤20um.