CN106213675A - Far infrared health care adjusts shoe pad and preparation method thereof - Google Patents
Far infrared health care adjusts shoe pad and preparation method thereof Download PDFInfo
- Publication number
- CN106213675A CN106213675A CN201610751833.0A CN201610751833A CN106213675A CN 106213675 A CN106213675 A CN 106213675A CN 201610751833 A CN201610751833 A CN 201610751833A CN 106213675 A CN106213675 A CN 106213675A
- Authority
- CN
- China
- Prior art keywords
- layer
- shoe pad
- far infrared
- far
- health care
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of far infrared health care and adjust shoe pad, described insole body by five layer by layer structure constitute, ground floor is surface layer, the second layer is far IR fibre layer, third layer is buffer layer, and the 4th layer is adjustment structure sheaf, and layer 5 is skid resistant course, described surface layer, by soft nylon facing material, scratches 20 50g/M2Antibacterial latex, through cylinder heating, drying sizing form;Described far IR fibre layer uses far-infrared health-care fibre board;Described buffer layer uses the TPU expanded material of siliceous bath mud;Described adjustment structure sheaf uses low-temperature heat melting film;Described skid resistant course uses cotton yarn, through high temperature hot pressing in adjusting structure sheaf, the far infrared health care of the present invention adjusts shoe pad can be according to Foot-biomechanics designed, designed, it is suitable for self body weight and foot and health impetus thereof, adjust arch of foot and the balance of foot self, easy to adjust, to foot health promotion, increase walking time, kinergety have good effect.
Description
Technical field
The present invention relates to a kind of far infrared health care and adjust shoe pad and preparation method thereof.
Background technology
Now society, the physical condition of self is increasingly paid attention to by people, and acupoint, vola is the most, carry out vola by
Rub, health is had the biggest benefit.And in the winter time, cold weather, people need warming and heat insulation, attack with severe cold prevention,
Particularly foot protection becomes extremely important.But when people work long hours to the place not having warming installation and learn,
Foot is susceptible to cold injury, can significantly damage health;Moist due to the sweat gland above foot more Yi Shi foot again, not only can
Cause abnormal flavour, and make people feel the most uncomfortable;Furthermore the rainy day is due to vamp material reason sometimes, shoe pad also can soak.But
Traditional shoe pad typically utilizes cloth to make, and does not has and integrates heating, massaging point and ventilative degerming functional insole.
Summary of the invention
It is an object of the invention to solve the deficiencies in the prior art, it is provided that a kind of far infrared health care adjust shoe pad and
Preparation method, the far infrared health care of the present invention adjusts shoe pad, has self-heating structure, can perspire anticorrosion deodorization with warming moisture-absorbing,
And there is extremely strong antibacterial bacteriostatic and far infrared acupoint massage health-care effect.
The technical solution adopted for the present invention to solve the technical problems is:
Far infrared health care adjusts shoe pad, including insole body,
Described insole body by five layer by layer structure constitute, ground floor is surface layer, and the second layer is far IR fibre layer, third layer
For buffer layer, the 4th layer is adjustment structure sheaf, and layer 5 is skid resistant course,
Described surface layer, by soft nylon facing material, scratches 20-50g/M2Antibacterial latex, through cylinder heating, drying sizing and
Become;There is high ventilative moisture absorbing and sweat releasing, antibacterial sub-deodoriging properties,
Described far IR fibre layer uses far-infrared health-care fibre board;Its made of soft, have higher elasticity and, can connect
The far infrared wave of the 4um-14um useful to human body is gone out so that shoe temperature by the heat emission of body temperature between human body 25 DEG C-37 DEG C
Raising about 0.4 DEG C, this far infrared wave energy, by acupuncture point bottom human foot, the moisture in activating human body, enhances metabolism,
Increase cell viability.
Described buffer layer uses the TPU expanded material of siliceous bath mud;Diatom ooze tool is significantly improved TPU expanded material bullet
Property and the function of flexibility so that TPU expanded material has superpower elasticity and soft feel. good damping can be played
Buffering effect, and there is elimination formaldehyde, purify air, regulation humidity, sound-insulating, releasing negative oxygen ion, anti-deodorization and sterilization etc.
Effect.
Described adjustment structure sheaf uses low-temperature heat melting film;User can design according to Foot-biomechanics, in conjunction with certainly
The body weight of body and foot and health impetus thereof, adjust arch of foot and the balance of foot self, easy to adjust, protects foot
Strong, increase walking time, kinergety have good effect,
Described skid resistant course uses cotton yarn, through high temperature hot pressing in adjusting structure sheaf;
Described antibacterial latex is formed by the Raw material processing of following weight portion: PUR 50-80 part, carbon fiber 10-20 part, electricity
Gas stone 5-15 part, far infrared ceramic powder 5-10 part, magnetic ordered mesoporous carbon 5-8 part;
The described TPU expanded material containing diatom ooze refers to add appropriate diatom ooze, diatom in the TPU expanded material course of processing
The addition of mud is the 5-8% of other raw material gross mass of TPU expanded material.
Consumer is when using far infrared health care of the present invention to adjust shoe pad, it is possible to use 60-70 DEG C of temperature is softened also
Place footwear chamber, put on the shoes about 3-5 second, i.e. can according to Foot-biomechanics, in conjunction with self body weight and foot and
Health impetus, is shaped into the entirely appropriate Special shoe pad wearing own characteristic, and then room temperature cooling can normally make for 2-4 hour
With.
Preferably, described antibacterial latex is formed by the Raw material processing of following weight portion: PUR 75 parts, 15 parts of carbon fiber,
10 parts of tourmaline, far infrared ceramic powder 8 parts, magnetic ordered mesoporous carbon 6 parts.
Magnetic ordered mesoporous carbon of the present invention possesses huge specific surface area and abundant three dimensional pore structures, high
Specific surface area is conducive to the adsorption storage of carbon fiber;Regular orderly open duct, the aperture of size adjustable are the antibacterial factor
Produce with anion and provide path, be conducive to slowly persistently producing for a long time for the antibacterial factor and anion, improve far infrared
Health care adjusts the using effect of shoe pad, extends its service life.
Preferably, in the described TPU expanded material containing diatom ooze, the addition of diatom ooze is other raw material of TPU expanded material
The 6% of gross mass.Diatom ooze tool is significantly improved the elastic function with flexibility of TPU expanded material so that TPU expanded material
There is superpower elasticity and soft feel. good damping, buffering effect can be played, TPU expanded material under this addition
Performance optimal.
A kind of far infrared health care adjusts the preparation method of shoe pad, and described preparation method step is as follows:
(1) first between surface layer and far IR fibre layer, breathed freely hot-melt adhesive film by 0.3-0.75UM thermoplastics type, warp,
Plane abutted equipment is heated to 130-150 DEG C of laminating, requires to cut the footwear that size shape is consistent further according to prepared insole design
Pad top semifinished material;
(2), when preparing low-temperature heat melting film, low-temperature heat melting film is directly tied by temperature when being cast by die head with adjusting
Structure layer bonding fits to together, and the design prepared further according to shoe pad requires to cut, and forms later half slotting material;
(3) according to shoe pad preparation design requirement, successively shoe pad top semifinished material, buffer layer and later half slotting material are divided
Other located coincident is placed on thermocompression forming mould and carries out softening heat pressure adhesive sizing, places it in chill the most again and colds pressing
Molding;
(4) require automatically to prune to cut molding according to shoe pad preparation design, it is thus achieved that far infrared health care adjusts shoe pad finished product.
Preferably, hot pressing pressure is set as that 2.5-3Mpa, temperature are set as 80-110 DEG C, and hot pressing time is the 8-12 second, cold
Molding pressure is set as that 2.5-3Mpa, temperature are set as 0-5 DEG C. the time of colding pressing is the 8-12 second.
The invention has the beneficial effects as follows:
(1) present invention far infrared health care adjust shoe pad can accept the heat emission of body temperature between human body 25 DEG C-37 DEG C go out right
The far infrared wave of the 4um-14um that human body is useful so that shoe temperature raises about 0.4 DEG C, superpower far infrared wavelength is launched
Function, the moisture in activating human body, enhance metabolism, increase cell viability, the acupuncture point of sole can be stimulated to carry out sole acupoint
Massage effect, improves blood circulation and strengthens health-care effect;
(2) the far infrared health care adjustment shoe pad of the present invention has the performance of good anti-freezing and heat-insulating at arctic weather;
(3) the far infrared health care adjustment shoe pad of the present invention has the superpower efficacy of adsorption of uniqueness, can human body natural be got rid of
Perspiration absorb completely, be allowed to be excluded in outside footwear by the permeability of material, substantially improve shoes internal medium, thus have
Imitate prevents the various disease of foot;
(4) the far infrared health care adjustment shoe pad of the present invention has the permanent various harmful gas of anion releasing adsorption-decomposition function
Function;
(5) the far infrared health care adjustment shoe pad of the present invention has self-heating structure, can perspire anticorrosion deodorization with warming moisture-absorbing,
And there is extremely strong antibacterial bacteriostatic performance;
(6) the far infrared health care adjustment shoe pad of the present invention can be suitable for self according to Foot-biomechanics designed, designed
Body weight and foot and health impetus thereof, adjust arch of foot and the balance of foot self, easy to adjust, to foot health promotion,
Increase the walking time, kinergety has good effect.
Detailed description of the invention
Below by specific embodiment, technical scheme is described in further detail.
Embodiment 1
Far infrared health care adjusts shoe pad, including insole body,
Described insole body by five layer by layer structure constitute, ground floor is surface layer, and the second layer is far IR fibre layer, third layer
For buffer layer, the 4th layer is adjustment structure sheaf, and layer 5 is skid resistant course,
Described surface layer, by soft nylon facing material, scratches 50g/M2Antibacterial latex, through cylinder heating, drying sizing form;
Described far IR fibre layer uses far-infrared health-care fibre board;
Described buffer layer uses the TPU expanded material of siliceous bath mud;
Described adjustment structure sheaf uses low-temperature heat melting film;
Described skid resistant course uses cotton yarn, through high temperature hot pressing in adjusting structure sheaf;
Described antibacterial latex is formed by the Raw material processing of following weight portion: PUR 50 parts, 10 parts of carbon fiber, tourmaline 5
Part, far infrared ceramic powder 5 parts, magnetic ordered mesoporous carbon 5 parts;
The described TPU expanded material containing diatom ooze refers to add appropriate diatom ooze, diatom in the TPU expanded material course of processing
The addition of mud is the 5% of other raw material gross mass of TPU expanded material, and described far infrared health care adjusts the preparation method step of shoe pad
Rapid as follows:
(1) first between surface layer and far IR fibre layer, being breathed freely hot-melt adhesive film by 0.3UM thermoplastics type, warp, plane is pasted
Conjunction equipment is heated to 130 DEG C of laminatings, requires to cut shoe pad top half one-tenth that size shape is consistent further according to prepared insole design
Product material;
(2), when preparing low-temperature heat melting film, low-temperature heat melting film is directly tied by temperature when being cast by die head with adjusting
Structure layer bonding fits to together, and the design prepared further according to shoe pad requires to cut, and forms later half slotting material;
(3) according to shoe pad preparation design requirement, successively shoe pad top semifinished material, buffer layer and later half slotting material are divided
Other located coincident is placed on thermocompression forming mould and carries out softening heat pressure adhesive sizing, places it in chill the most again and colds pressing
Molding;
(4) require automatically to prune to cut molding according to shoe pad preparation design, it is thus achieved that far infrared health care adjusts shoe pad finished product, heat
Pressure pressure is set as that 2.5Mpa, temperature are set as 110 DEG C, and hot pressing time is 8 seconds, and chill pressure is set as that 2.5Mpa, temperature set
It being set to 5 DEG C. the time of colding pressing is 12 seconds.
Embodiment 2
Far infrared health care adjusts shoe pad, including insole body,
Described insole body by five layer by layer structure constitute, ground floor is surface layer, and the second layer is far IR fibre layer, third layer
For buffer layer, the 4th layer is adjustment structure sheaf, and layer 5 is skid resistant course,
Described surface layer, by soft nylon facing material, scratches 20g/M2Antibacterial latex, through cylinder heating, drying sizing form;
Described far IR fibre layer uses far-infrared health-care fibre board;
Described buffer layer uses the TPU expanded material of siliceous bath mud;
Described adjustment structure sheaf uses low-temperature heat melting film;
Described skid resistant course uses cotton yarn, through high temperature hot pressing in adjusting structure sheaf;
Described antibacterial latex is formed by the Raw material processing of following weight portion: PUR 80 parts, 20 parts of carbon fiber, tourmaline 15
Part, far infrared ceramic powder 10 parts, magnetic ordered mesoporous carbon 8 parts;
The described TPU expanded material containing diatom ooze refers to add appropriate diatom ooze, diatom in the TPU expanded material course of processing
The addition of mud is the 8% of other raw material gross mass of TPU expanded material;
Preparation method step is as follows:
(1) first between surface layer and far IR fibre layer, breathed freely hot-melt adhesive film by 0.75UM thermoplastics type, warp, plane
Abutted equipment is heated to 150 DEG C of laminatings, requires to cut the shoe pad top half that size shape is consistent further according to prepared insole design
Finished-product material;
(2), when preparing low-temperature heat melting film, low-temperature heat melting film is directly tied by temperature when being cast by die head with adjusting
Structure layer bonding fits to together, and the design prepared further according to shoe pad requires to cut, and forms later half slotting material;
(3) according to shoe pad preparation design requirement, successively shoe pad top semifinished material, buffer layer and later half slotting material are divided
Other located coincident is placed on thermocompression forming mould and carries out softening heat pressure adhesive sizing, places it in chill the most again and colds pressing
Molding;
(4) require automatically to prune to cut molding according to shoe pad preparation design, it is thus achieved that far infrared health care adjusts shoe pad finished product, heat
Pressure pressure is set as that 3Mpa, temperature are set as 80 DEG C, and hot pressing time is 8 seconds, and chill pressure is set as that 3Mpa, temperature are set as 0
DEG C. the time of colding pressing is 8 seconds.
Embodiment 3
Far infrared health care adjusts shoe pad, including insole body,
Described insole body by five layer by layer structure constitute, ground floor is surface layer, and the second layer is far IR fibre layer, third layer
For buffer layer, the 4th layer is adjustment structure sheaf, and layer 5 is skid resistant course,
Described surface layer, by soft nylon facing material, scratches 30g/M2Antibacterial latex, through cylinder heating, drying sizing form;
Described far IR fibre layer uses far-infrared health-care fibre board;
Described buffer layer uses the TPU expanded material of siliceous bath mud;
Described adjustment structure sheaf uses low-temperature heat melting film;
Described skid resistant course uses cotton yarn, through high temperature hot pressing in adjusting structure sheaf;
Described antibacterial latex is formed by the Raw material processing of following weight portion: PUR 65 parts, 15 parts of carbon fiber, tourmaline 10
Part, far infrared ceramic powder 8 parts, magnetic ordered mesoporous carbon 6 parts;
The described TPU expanded material containing diatom ooze refers to add appropriate diatom ooze, diatom in the TPU expanded material course of processing
The addition of mud is the 6% of other raw material gross mass of TPU expanded material;
Preparation method step is as follows:
(1) first between surface layer and far IR fibre layer, being breathed freely hot-melt adhesive film by 0.5UM thermoplastics type, warp, plane is pasted
Conjunction equipment is heated to 140 DEG C of laminatings, requires to cut shoe pad top half one-tenth that size shape is consistent further according to prepared insole design
Product material;
(2), when preparing low-temperature heat melting film, low-temperature heat melting film is directly tied by temperature when being cast by die head with adjusting
Structure layer bonding fits to together, and the design prepared further according to shoe pad requires to cut, and forms later half slotting material;
(3) according to shoe pad preparation design requirement, successively shoe pad top semifinished material, buffer layer and later half slotting material are divided
Other located coincident is placed on thermocompression forming mould and carries out softening heat pressure adhesive sizing, places it in chill the most again and colds pressing
Molding;
(4) require automatically to prune to cut molding according to shoe pad preparation design, it is thus achieved that far infrared health care adjusts shoe pad finished product, heat
Pressure pressure is set as that 2.8Mpa, temperature are set as 100 DEG C, and hot pressing time is 10 seconds, and chill pressure is set as that 2.8Mpa, temperature set
It being set to 2 DEG C. the time of colding pressing is 10 seconds.
Far infrared health care that embodiment 1-3 prepares adjusts shoe pad and has a following excellent function:
(1) present invention far infrared health care adjust shoe pad can accept the heat emission of body temperature between human body 25 DEG C-37 DEG C go out right
The far infrared wave of the 4um-14um that human body is useful so that shoe temperature raises about 0.4 DEG C, superpower far infrared wavelength is launched
Function, the moisture in activating human body, enhance metabolism, increase cell viability, the acupuncture point of sole can be stimulated to carry out sole acupoint
Massage effect, improves blood circulation and strengthens health-care effect;
(2) the far infrared health care adjustment shoe pad of the present invention has the performance of good anti-freezing and heat-insulating at arctic weather;
(3) the far infrared health care adjustment shoe pad of the present invention has the superpower efficacy of adsorption of uniqueness, can human body natural be got rid of
Perspiration absorb completely, be allowed to be excluded in outside footwear by the permeability of material, substantially improve shoes internal medium, thus have
Imitate prevents the various disease of foot;
(4) the far infrared health care adjustment shoe pad of the present invention has the permanent various harmful gas of anion releasing adsorption-decomposition function
Function;
(5) the far infrared health care adjustment shoe pad of the present invention has self-heating structure, can perspire anticorrosion deodorization with warming moisture-absorbing,
And there is extremely strong antibacterial bacteriostatic performance;
(6) the far infrared health care adjustment shoe pad of the present invention can be suitable for self according to Foot-biomechanics designed, designed
Body weight and foot and health impetus thereof, adjust arch of foot and the balance of foot self, easy to adjust, to foot health promotion,
Increase the walking time, kinergety has good effect.
Embodiment described above is the one preferably scheme of the present invention, not makees the present invention any pro forma
Limit, on the premise of without departing from the technical scheme described in claim, also have other variant and remodeling.
Claims (5)
1. far infrared health care adjusts shoe pad, including insole body, it is characterised in that:
Described insole body by five layer by layer structure constitute, ground floor is surface layer, and the second layer is far IR fibre layer, and third layer is for subtracting
Shake layer, the 4th layer is adjustment structure sheaf, and layer 5 is skid resistant course,
Described surface layer, by soft nylon facing material, scratches 20-50g/M2Antibacterial latex, through cylinder heating, drying sizing form;
Described far IR fibre layer uses far-infrared health-care fibre board;
Described buffer layer uses the TPU expanded material of siliceous bath mud;
Described adjustment structure sheaf uses low-temperature heat melting film;
Described skid resistant course uses cotton yarn, through high temperature hot pressing in adjusting structure sheaf;
Described antibacterial latex is formed by the Raw material processing of following weight portion: PUR 50-80 part, carbon fiber 10-20 part, tourmaline
5-15 part, far infrared ceramic powder 5-10 part, magnetic ordered mesoporous carbon 5-8 part;
The described TPU expanded material containing diatom ooze refers to add appropriate diatom ooze in the TPU expanded material course of processing, diatom ooze
Addition is the 5-8% of other raw material gross mass of TPU expanded material.
Far infrared health care the most according to claim 1 adjusts shoe pad, it is characterised in that: described antibacterial latex is by following weight
The Raw material processing of part forms: PUR 75 parts, 15 parts of carbon fiber, 10 parts of tourmaline, far infrared ceramic powder 8 parts, magnetic is situated between in order
Hole charcoal 6 parts.
Far infrared health care the most according to claim 1 adjusts shoe pad, it is characterised in that: the described TPU foaming containing diatom ooze
In material, the addition of diatom ooze is the 6% of other raw material gross mass of TPU expanded material.
4. far infrared health care described in a claim 1-3 any one adjusts the preparation method of shoe pad, it is characterised in that described
Preparation method step is as follows:
(1) first between surface layer and far IR fibre layer, breathed freely hot-melt adhesive film by 0.3-0.75UM thermoplastics type, warp, plane
Abutted equipment is heated to 130-150 DEG C of laminating, requires to cut on the shoe pad that size shape is consistent further according to prepared insole design
Portion's semifinished material;
(2), when preparing low-temperature heat melting film, temperature when being cast by die head is directly by low-temperature heat melting film and adjustment structure sheaf
Bonding fits to together, and the design prepared further according to shoe pad requires to cut, and forms later half slotting material;
(3) according to shoe pad preparation design requirement, successively that shoe pad top semifinished material, buffer layer and later half slotting material is fixed respectively
Position overlaps to be placed on thermocompression forming mould and carries out softening heat pressure adhesive sizing, places it in chill the most again and is cold-pressed into
Type;
(4) require automatically to prune to cut molding according to shoe pad preparation design, it is thus achieved that far infrared health care adjusts shoe pad finished product.
The most according to claim 4, far infrared health care adjusts the preparation method of shoe pad, it is characterised in that hot pressing pressure is set as
2.5-3Mpa, temperature is set as 80-110 DEG C, and hot pressing time is the 8-12 second, and chill pressure is set as 2.5-3Mpa, and temperature sets
For 0-5 DEG C. the time of colding pressing is the 8-12 second.