CN106213635A - Polyester-cotton blend adhered by double sided plaster lining and production method thereof - Google Patents
Polyester-cotton blend adhered by double sided plaster lining and production method thereof Download PDFInfo
- Publication number
- CN106213635A CN106213635A CN201610618104.8A CN201610618104A CN106213635A CN 106213635 A CN106213635 A CN 106213635A CN 201610618104 A CN201610618104 A CN 201610618104A CN 106213635 A CN106213635 A CN 106213635A
- Authority
- CN
- China
- Prior art keywords
- polyester
- cotton blend
- double sided
- lining
- sided plaster
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The open a kind of polyester-cotton blend adhered by double sided plaster lining of the present invention and production method thereof, production procedure includes turning over seam → pre-treatment → heat setting → chemical shrinkproof hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized.Adhesive lining tow sides have adhesive layer, two pieces of fabrics of the same race or the most of the same race can be bonded together, it is thus achieved that harder feel, higher separation strength and other performances.Through the xeothermic size changing rate of broadwise 0.8%～+0.5%；Dissociate and hydrolysis formaldehyde≤40mg/kg；It is 1.0%～+0.5% through broadwise washing size changing rate.Production technology processing ease of the present invention, to eco-friendly, excellent product performance.
Description
Technical field
The present invention relates to a kind of polyester-cotton blend adhered by double sided plaster lining and production method thereof.
Background technology
There is adhesive layer in one face of conventional binder lining, can be bonded together with one piece of fabric.There are some special kinds clothing
Or have particular/special requirement clothing, it is desirable to adhesive lining can be bonded together two pieces of fabrics, it is thus achieved that harder feel, higher separation strength and
Other performances.To this end, research and development and production tow sides have the polyester-cotton blend adhered by double sided plaster of adhesive layer to serve as a contrast, meet apparel industry need
Ask.
Summary of the invention
Present invention aim at polyester-cotton blend adhered by double sided plaster lining and the producer thereof providing a kind of excellent performance, preparation easy
Method.
The technical solution of the present invention is:
A kind of polyester-cotton blend adhered by double sided plaster lining, is characterized in that: the tow sides in polyester-cotton blend base fabric have adhesive layer；Through the xeothermic chi of broadwise
Very little rate of change-0.8%～+0.5%；Dissociate and hydrolysis formaldehyde≤40mg/kg；Through broadwise washing size changing rate be-1.0%～+
0.5%。
The grey cloth specification of polyester-cotton blend lining cloth is the one in following two kinds: the first width is 48.5 inches, yarn count is
21s × 21s, density are 60 × 58 pieces/inch, and the second door width is 48.5 inches, yarn count is 16 s × 16s, density is
50 × 45 pieces/inch.
The production method of a kind of polyester-cotton blend adhered by double sided plaster lining, includes that turning over seam → pre-treatment → heat setting → chemistry prevents successively
Contracting hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized.It is characterized in that: heat is fixed
During shape, entering cloth, needle plate on overfeeding-0.5%～0% by open width, eight lattice hot blasts shape, wherein first and second lattice temperature 180 DEG C,
Third and fourth lattice temperature 190 DEG C, the 5th～eight lattice temperature 200 DEG C, two cylinder cooling cropping steps, speed is 30～35m/
min。
During the shrinkproof hard finishing of chemistry, consisting of of shrinkproof hard finishing liquid:
Fabric resin finishing agent KH-1 60～80 g/L
Auxiliary agent STN 150～200 g/L
MgCl2·6H2O 9～12 g/L
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8～4.2 with citric acid.
During applying coating, HDPE PUR is after the melted tank of temperature 155-160 DEG C is melted, by spout liquid hot melt adhesive
It is coated on cloth cover, coated weight 70～90 g/L.
Polyester-cotton blend adhered by double sided plaster of the present invention serves as a contrast, and two pieces of fabrics can be bonded together, to obtain harder feel, higher stripping
Strength and other performances, adhesive lining xeothermic dimensional contraction rate is low, and adhesive lining is low through broadwise washing shrinkage, dissociates and hydrolysis formaldehyde is little,
To eco-friendly, production technology processing ease.Tow sides in polyester-cotton blend base fabric have adhesive layer, can be of the same race or not
Two pieces of fabrics of the same race are bonded together, to obtain harder feel, higher separation strength and other performances, through the xeothermic size of broadwise
Rate of change-0.8%～+0.5%；Dissociate and hydrolysis formaldehyde≤40mg/kg；Through broadwise washing size changing rate be-1.0%～+
0.5%。
Below in conjunction with embodiment, the invention will be further described.
Detailed description of the invention
Embodiment 1:
The grey cloth specification of polyester-cotton blend (65/35) lining cloth is: door width is 48.5 inches, yarn count is 21s × 21s, density is 60
× 58 pieces/inch.
The production method of a kind of polyester-cotton blend adhered by double sided plaster lining, includes that turning over seam → pre-treatment → heat setting → chemistry prevents successively
Contracting hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized.During heat setting, pass through
Open width enters cloth, needle plate on overfeeding-0.5%～0%, eight lattice hot blast setting, wherein first and second lattice temperature 180 DEG C, third and fourth lattice
Temperature 190 DEG C, the 5th～eight lattice temperature 200 DEG C, two cylinder cooling cropping steps, speed is 33～35m/min.
During the shrinkproof hard finishing of chemistry, consisting of of shrinkproof hard finishing liquid:
Fabric resin finishing agent KH-1 60～70 g/L(example 60 g/L, 65 g/L, 70 g/L)
Auxiliary agent STN 170～200 g/L(example 170 g/L, 180 g/L, 200 g/L)
MgCl2·6H2O 9～10.5 g/L(example 9 g/L, 10 g/L, 10.5g/L)
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8～4.2 with citric acid.
Entering cloth by open width during the shrinkproof hard finishing of chemistry, two soak two rolls shrinkproof hard finishing liquid, liquid carrying rate 65%～
70%, 110～130 DEG C of loose formula drying, needle plate on overfeeding-0.5%～0%, eight lattice hot blasts bake, wherein the first lattice temperature 150
DEG C, the second lattice temperature 160 DEG C, the 3rd～eight lattice temperature 170 DEG C, two cylinders cooling cropping steps, speed be 35～
40m/min.During applying coating, HDPE PUR is after the melted tank of temperature 155-160 DEG C is melted, by spout liquid hot melt adhesive
It is coated on cloth cover, coated weight 70～80 g/L.
Embodiment 2:
The grey cloth specification of polyester-cotton blend (65/35) lining cloth is: door width is 48.5 inches, yarn count is 16 s × 16s, density be 50 ×
45 pieces/inch.
The production method of a kind of polyester-cotton blend adhered by double sided plaster lining, includes that turning over seam → pre-treatment → heat setting → chemistry prevents successively
Contracting hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized.During heat setting, pass through
Open width enters cloth, needle plate on overfeeding-0.5%～0%, eight lattice hot blast setting, wherein first and second lattice temperature 180 DEG C, third and fourth lattice
Temperature 190 DEG C, the 5th～eight lattice temperature 200 DEG C, two cylinder cooling cropping steps, speed is 30～32m/min.
During the shrinkproof hard finishing of chemistry, consisting of of shrinkproof hard finishing liquid:
Fabric is with resin finishing agent KH-1 70～80 g/L (example 70 g/L, 75 g/L, 80 g/L)
Auxiliary agent STN 150～180 g/L(example 150 g/L, 165 g/L, 180 g/L)
MgCl2·6H2O 10.5～12 g/L(example 10.5 g/L, 11g/L, 12 g/L)
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8～4.2 with citric acid.
Entering cloth by open width during the shrinkproof hard finishing of chemistry, two soak two rolls shrinkproof hard finishing liquid, liquid carrying rate 65%～
70%, 110～130 DEG C of loose formula drying, needle plate on overfeeding-0.5%～0%, eight lattice hot blasts bake, wherein the first lattice temperature 150
DEG C, the second lattice temperature 160 DEG C, the 3rd～eight lattice temperature 170 DEG C, two cylinders cooling cropping steps, speed be 30～
35m/min.During applying coating, HDPE PUR is after the melted tank of temperature 155-160 DEG C is melted, by spout liquid hot melt adhesive
It is coated on cloth cover, coated weight 75～90 g/L.
Claims (5)
1. a polyester-cotton blend adhered by double sided plaster lining, is characterized in that: the tow sides in polyester-cotton blend base fabric have adhesive layer；Xeothermic through broadwise
Size changing rate-0.8%～+0.5%；Dissociate and hydrolysis formaldehyde≤40mg/kg；Through broadwise washing size changing rate be-1.0%～
+0.5%。
Polyester-cotton blend adhered by double sided plaster the most according to claim 1 serves as a contrast, and it is characterized in that: the grey cloth specification of polyester-cotton blend lining cloth is following two
One in kind: the first width is 48.5 inches, yarn count is 21s × 21s, density is 60 × 58 pieces/inch, second
Kind of door width is 48.5 inches, yarn count is 16 s × 16s, density is 50 × 45 pieces/inch.
3. a production method for polyester-cotton blend adhered by double sided plaster lining, includes turning over seam → pre-treatment → heat setting → chemistry shrinkproof successively
Hard finishing → front powder point coating or applying coating → reverse side applying coating → sanforized；It is characterized in that: heat setting
Time, entering cloth, needle plate on overfeeding-0.5%～0% by open width, eight lattice hot blasts shape, wherein first and second lattice temperature 180 DEG C, the
Three, four lattice temperature 190 DEG C, the 5th～eight lattice temperature 200 DEG C, two cylinder cooling cropping steps, speed is 30～35m/
min。
4. the production method served as a contrast according to the polyester-cotton blend adhered by double sided plaster described in claim 3, is characterized in that: chemistry is shrinkproof stiffening whole
During reason, consisting of of shrinkproof hard finishing liquid:
Fabric resin finishing agent KH-1 60～80 g/L
Auxiliary agent STN 150～200 g/L
MgCl2·6H2O 9～12 g/L
Ethylene urea 4.0g/L
NON IONIC SOFTNER V-12 0.5g/L
Remaining is water, and adjusts pH to 3.8～4.2 with citric acid.
5. the production method served as a contrast according to the polyester-cotton blend adhered by double sided plaster described in claim 3, is characterized in that: during applying coating,
HDPE PUR, after the melted tank of temperature 155-160 DEG C is melted, is coated in liquid hot melt adhesive on cloth cover by spout, coated weight
70～90 g/L.