CN106189937A - A kind of building water-proof reinforcement material - Google Patents
A kind of building water-proof reinforcement material Download PDFInfo
- Publication number
- CN106189937A CN106189937A CN201610497288.7A CN201610497288A CN106189937A CN 106189937 A CN106189937 A CN 106189937A CN 201610497288 A CN201610497288 A CN 201610497288A CN 106189937 A CN106189937 A CN 106189937A
- Authority
- CN
- China
- Prior art keywords
- water
- stock solution
- organosilicon
- reinforcement material
- mill base
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of building water-proof reinforcement material, the most composed of the following components: poly-second propylene 7 10%, organosilicon stock solution 0.7 1.2%, defoamer 0.1 0.2%, mill base 0.5 0.7%, remaining is water；The mass percent summation of the most each component is 100%.Can effectively solve the problem that existing building reinforcement material by moisture, or meet water occur mouldy, the accumulation of salt in the surface soil, the problem of ground dusting.
Description
Technical field
The invention belongs to building material technical field, relate to a kind of reinforcement material for building, be specifically related to a kind of for building
Waterproofing reinforcement material.
Background technology
In prior art, commonly use in building field is that the glue prepared of polyvinyl alcohol is as metope and ground
Strengthening agent.This strengthening agent can play effect bonding, that reinforce.But this glue is after usage, meet water, wet gas etc. easy
Occur mouldy, get damp, the phenomenon of the accumulation of salt in the surface soil.
Summary of the invention
It is an object of the invention to provide a kind of building water-proof reinforcement material.Can effectively solve the problem that existing building reinforces material
Material is by moisture, or meets water mouldy, the accumulation of salt in the surface soil of appearance, the problem of ground dusting.
Present invention also offers the preparation method of a kind of above-mentioned reinforcement material.
The technical solution adopted in the present invention is, a kind of building water-proof reinforcement material, by mass percentage by following group
It is grouped into: poly-second propylene 7-10%, organosilicon stock solution 0.7-1.2%, defoamer 0.1-0.2%, mill base 0.5-0.7%, remaining
For water；The mass percent summation of the most each component is 100%.
Further, the feature of the present invention also resides in:
Wherein organosilicon stock solution is JC/T902-2002 organosilicon stock solution, and the concentration of organosilicon stock solution is 60%.
Wherein polyvinyl alcohol is 10%, and organosilicon stock solution is 0.7%, and defoamer is 0.1%, and mill base is 0.7%, and remaining is
Water, the mass percent summation of above each component is 100%.
Wherein polyvinyl alcohol is 10%, and organosilicon stock solution is 0.7%, and defoamer is 0.15%, and mill base is 0.7%, remaining
For water, the mass percent summation of above each component is 100%.
Wherein polyvinyl alcohol is 10%, and organosilicon stock solution is 0.9-1.2%, and defoamer is 0.2%, and mill base is 0.7%, its
Yu Weishui, the mass percent summation of above each component is 100%.
Wherein reinforcement material is applied on wall or ground.
Another technical scheme of the present invention is, the preparation method of a kind of building water-proof reinforcement material, including to polyethylene
Alcohol adds organosilicon stock solution and defoamer, then adds mill base and water, after stirring, obtain this reinforcement material.
The invention has the beneficial effects as follows, the preparation method of a kind of building water-proof reinforcement material, including in polyvinyl alcohol
Add organosilicon stock solution and defoamer, then add mill base and water, after stirring, obtain this reinforcement material.
The invention has the beneficial effects as follows: be blended in polyvinyl alcohol glue by organosilicon, organosilicon stock solution has the strongest preventing
Water protection against the tide alkali resistant effect, polyvinyl alcohol has stronger adhesive strength, organosilicon can be made fully to invade construction wall or ground is worked as
In, reach waterproof and dampproof alkali resistant effect, good bonding interface effect can be played again, make putty with construction wall or ground it
Between bonding more firm, it is not easy to get damp or the accumulation of salt in the surface soil.
Detailed description of the invention
Below in conjunction with detailed description of the invention, the present invention is described in detail.
The invention provides a kind of building water-proof reinforcement material, by the most composed of the following components: poly-second
Propylene 7-10%, organosilicon stock solution 0.7-1.2%, defoamer 0.1-0.2%, mill base 0.5-0.7%, remaining is water；The most each
The mass percent summation of component is 100%.Wherein organosilicon stock solution is JC/T902-2002 organosilicon stock solution, and organosilicon is former
The concentration of liquid is 60%；Mill base is France's Clariant mill base.
Present invention also offers the preparation method of a kind of building water-proof reinforcement material, there was added including in polyvinyl alcohol
Machine silicon stock solution and defoamer, then add mill base and water, obtains this reinforcement material after stirring.
The specific embodiment of the present invention is as follows:
Embodiment 1
Take by mass percentage 10% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, 0.1% disappear
Infusion, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Enter organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtain this building water-proof
Reinforcement material.
Embodiment 2
Take by mass percentage 10% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, 0.15% disappear
Infusion, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Enter organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtain this building water-proof
Reinforcement material.
Embodiment 3
Take by mass percentage 10% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.9%, 0.1% disappear
Infusion, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Enter organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtain this building water-proof
Reinforcement material.
Embodiment 4
Take by mass percentage 10% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 1.2%, 0.1% disappear
Infusion, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Enter organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtain this building water-proof
Reinforcement material.
Embodiment 5
Take by mass percentage 7% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, the froth breaking of 0.1%
Agent, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtains this building water-proof and adds
Gu material.
Embodiment 6
Take by mass percentage 8% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, the froth breaking of 0.1%
Agent, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtains this building water-proof and adds
Gu material.
Embodiment 7
Take by mass percentage 9% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, the froth breaking of 0.1%
Agent, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtains this building water-proof and adds
Gu material.
Embodiment 8
Take by mass percentage 7% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, the froth breaking of 0.2%
Agent, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtains this building water-proof and adds
Gu material.
Embodiment 9
Take by mass percentage 7% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, 0.15% disappear
Infusion, the French Clariant mill base of 0.7%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Enter organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtain this building water-proof
Reinforcement material.
Embodiment 10
Take by mass percentage 7% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, the froth breaking of 0.1%
Agent, the French Clariant mill base of 0.5%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtains this building water-proof and adds
Gu material.
Embodiment 11
Take by mass percentage 7% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 0.7%, the froth breaking of 0.1%
Agent, the French Clariant mill base of 0.6%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtains this building water-proof and adds
Gu material.
Embodiment 12
Take by mass percentage 7% polyvinyl alcohol, the JC/T902-2002 organosilicon stock solution of 1.1%, the froth breaking of 0.1%
Agent, the French Clariant mill base of 0.65%, remaining be water；Wherein the concentration of organosilicon stock solution is 60%.Add in polyvinyl alcohol
Enter organosilicon stock solution and defoamer, add mill base and water, after being sufficiently mixed and stirring, obtain this building water-proof
Reinforcement material.
Claims (7)
1. a building water-proof reinforcement material, it is characterised in that the most composed of the following components: poly-second propylene 7-
10%, organosilicon stock solution 0.7-1.2%, defoamer 0.1-0.2%, mill base 0.5-0.7%, remaining is water；The most each component
Mass percent summation is 100%.
Building water-proof reinforcement material the most according to claim 1, it is characterised in that described organosilicon stock solution is JC/
T902-2002 organosilicon stock solution, and the concentration of organosilicon stock solution is 60%.
Building water-proof reinforcement material the most according to claim 1, it is characterised in that described polyvinyl alcohol is 10%, has
Machine silicon stock solution is 0.7%, and defoamer is 0.1%, and mill base is 0.7%, and remaining is water, the mass percent summation of above each component
It is 100%.
Building water-proof reinforcement material the most according to claim 1, it is characterised in that described polyvinyl alcohol is 10%, has
Machine silicon stock solution is 0.7%, and defoamer is 0.15%, and mill base is 0.7%, and remaining is water, and the mass percent of above each component is total
With for 100%.
Building water-proof reinforcement material the most according to claim 1, it is characterised in that described polyvinyl alcohol is 10%, has
Machine silicon stock solution is 0.9-1.2%, and defoamer is 0.2%, and mill base is 0.7%, and remaining is water, the mass percent of above each component
Summation is 100%.
6. according to the building water-proof reinforcement material described in claim 1-5 any one, it is characterised in that described reinforcement material
It is applied on wall or ground.
7. the preparation method of the building water-proof reinforcement material as described in claim 1-5 any one, it is characterised in that
Including adding organosilicon stock solution and defoamer in polyvinyl alcohol, then add mill base and water, obtain this after stirring and add
Gu material.