CN106189797A - High ferro antibacterial polyurethane water-repellent paint - Google Patents
High ferro antibacterial polyurethane water-repellent paint Download PDFInfo
- Publication number
- CN106189797A CN106189797A CN201610656308.0A CN201610656308A CN106189797A CN 106189797 A CN106189797 A CN 106189797A CN 201610656308 A CN201610656308 A CN 201610656308A CN 106189797 A CN106189797 A CN 106189797A
- Authority
- CN
- China
- Prior art keywords
- high ferro
- repellent paint
- polyethers
- polyurethane water
- antibacterial polyurethane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high ferro antibacterial polyurethane water-repellent paint, described high ferro antibacterial polyurethane water-repellent paint is prepared from by the raw material of following weight parts: be made up of 42 48wt% base polyurethane prepolymer for use as components and 52 58wt%% curing agent components.The high ferro antibacterial polyurethane water-repellent paint that the present invention provides, preparation method is simple, easy to use, with low cost, has mechanical property, light resistance, weatherability, water proofing property and the prominent wearability of excellence, has a good application prospect.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of high ferro antibacterial polyurethane water-repellent paint.
Background technology
High ferro, fast ferrum (speed rail), general ferrum (general speed train, low speed railway) are the big class of Chinese Railway three.Speed per hour 160
Kilometer is above-and the most simply speed rail (being second to high ferro is " Asia high ferro ") of speed per hour less than 250 kilometers is quickly compared to speed per hour
The low speed railway of less than 160 kilometers i.e. usual speed railway." the railroad safety management bar of enforcement plays on January 1st, 2014 in China
Example " regulation: high-speed railway (high ferro) refers to that (containing reserved) is started speed per hour more than 250 kilometers in design, and initial stage operation speed per hour 200
The passenger train special line railway that kilometer is above.High-speed railway except at train in addition to operation reaches speed certain standard, vehicle, road
Rail, operation are required for coordinating and promote.
Waterproof material has the advantages that low temperature flexibility, self-healing property and adhesive property are good, can room temperature construction, speed of application fast and
Meet environmental requirement.Especially without Hot-melt construction, remove the melancholy of fire from.Waterproof material resistance to low temperature is good, it is adaptable to work
Industry is waterproof, moistureproof with the roofing of civil building, basement, indoor, municipal works, cistern, swimming pool, subway and tunnel
And sealing.It is particularly suited for needing the military installations of cold construction and the oil depot of naked light, chemical plant, textile mills, grain should not being employed
The water-tight corrosion-proof engineerings such as storehouse.
In the construction of high-speed railway, bridge floor arranges waterproof layer, is acknowledged as the most in the world, be can
Improve the maximally effective measure of bridge durability.The waterproof layer of bridge floor is easy to be destroyed.The waterproof layer of bridge floor is most commonly seen
Defect be exactly waterproof layer local breaking point occurs.The bridge surface waterproof layer of high-speed railway suffer local destruction after, if anti-
The bonding attachment of water layer and bridge deck concrete is unable to bear again the long-term infiltration of water and obscission occurs, such face meeting that comes off
Prolongation over time constantly expands, and then area hollowing occurs, also will appear from seeping phenomenon below waterproof layer, in driving
In the case of dynamic load, hydrops will produce corresponding pulse hydraulic pressure, and such reciprocating pressure time length will cause
The face that comes off of waterproof layer expands further, and concrete also has the destruction of corrosion.
Summary of the invention
For above-mentioned deficiency present in prior art, the technical problem to be solved is to provide a kind of high ferro and uses
Antibacterial polyurethane water-repellent paint.
The present invention seeks to be achieved through the following technical solutions:
A kind of high ferro antibacterial polyurethane water-repellent paint, by 42-48wt% base polyurethane prepolymer for use as component and 52-58wt%%
Curing agent component forms.
Preferably, described base polyurethane prepolymer for use as component is prepared from by the raw material of following weight parts: polyethers HSH-220
28-32 part, polyethers MN-3050D 6-9 part, isophorone diisocyanate 10-20 part.
Preferably, described curing agent component is prepared from by the raw material of following weight parts: polyethers EP-330N (G) 10-18
Part, polyvinyl alcohol 5-15 part, Pulvis Talci 15-25 part, adipic acid dibutyl ester 1-5 part, 1,1,1-trimethylolpropane 3-7 part, different
Lead octoate 0.3-0.9 part, inorganic antiseptic 2-8 part, ultraviolet absorber 1-5 part.
Preferably, described inorganic antiseptic is the mixture of one or more in silver nitrate, Firebrake ZB, zinc niobate.
It is highly preferred that described inorganic antiseptic is mixed by silver nitrate, Firebrake ZB, zinc niobate, described silver nitrate, boron
Acid zinc, the mass ratio of zinc niobate are (1-3): (1-3): (1-3).
Preferably, described ultraviolet absorber is 2-chloro-4,6-diamino-1,3,5-triazines, 2-hydroxyl-4-methoxyl group-
The mixture of one or more in 5-sulfonic acid benzophenone, 2,4,6-tri-(amino caproyl)-1,3,5-triazine.
It is highly preferred that described ultraviolet absorber is by 2-chloro-4,6-diamino-1,3,5-triazines, 2-hydroxyl-4-methoxy
Base-5-sulfonic acid benzophenone, 2,4,6-tri-(amino caproyl)-1,3,5-triazines mix, described 2-chloro-4,6-diamino
Base-1,3,5-triazine, 2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid, 2,4,6-tri-(amino caproyl)-1,3,5-triazine
Mass ratio be (1-3): (1-3): (1-3).
Present invention also offers the preparation method of above-mentioned high ferro antibacterial polyurethane water-repellent paint, comprise the following steps:
(1) polyethers HSH-220, polyethers MN-3050D being added in reactor by proportioning, being heated to temperature is 100-110
DEG C, with rotating speed for 300-600 rev/min stir 15-25 minute, temperature is risen to 115-125 DEG C and be decompressed to-0.092MPa~-
0.096MPa vacuum dehydration removed vacuum after 1.5-2.5 hour, is cooled to 75-85 DEG C and adds isophorone diisocyanate reaction
1.5-2.5 hour, stop stirring, cool to 55-65 DEG C, vacuum defoamation 10-20 minute under-0.03~-0.09MPa,
Obtain base polyurethane prepolymer for use as component;
(2) by proportioning by polyethers EP-330N (G), polyvinyl alcohol, Kaolin, calcium carbonate, inorganic antiseptic, uv absorption
Agent adds in reactor, is heated to temperature and is 100-110 DEG C, stirs 5-15 minute with rotating speed for 300-600 rev/min, by temperature
Remove vacuum after rising to 115-125 DEG C and being decompressed to-0.092MPa~-0.096MPa vacuum dehydration 1.5-2.5 hour, be cooled to
75-85 DEG C of addition adipic acid dibutyl ester, isooctyl acid lead stir 15-25 minute with rotating speed for 300-600 rev/min, add 1, and 1,
1-trimethylolpropane stirs 3-7 minute with rotating speed for 300-600 rev/min, obtains curing agent component.
The high ferro antibacterial polyurethane water-repellent paint that the present invention provides, preparation method is simple, easy to use, with low cost,
There is mechanical property, light resistance, weatherability, water proofing property and the prominent wearability of excellence, have a good application prospect.
Detailed description of the invention
Each raw material introduction in embodiment:
Polyethers HSH-220, the trade mark using Jiangsu Hai'an Petrochemical Plant to provide is HSH-220, and hydroxyl value is 53-
The polyether polyol of 59mgKOH/g.
Polyethers MN-3050D, the trade mark using Shandong Lanxing Dongda Chemical Co., Ltd to provide is MN-3050D, hydroxyl
Value is the polyether polyol of 54.5-57.5mgKOH/g.
Isophorone diisocyanate, No. CAS: 614-90-4.
Polyethers EP-330N (G), the trade mark using Shandong Lanxing Dongda Chemical Co., Ltd to provide is EP-330N
(G), hydroxyl value is the polyether polyol of 32.5-35.5mgKOH/g.
Polyvinyl alcohol, polyvinyl alcohol, No. CAS: 9002-89-5, specifically employing Renqiu City Shuo Da Chemical Co., Ltd. provides
The polyvinyl alcohol that model is PVA (2488).
Pulvis Talci, No. CAS: 14807-96-6, use 3000 mesh that Shanghai Liang Jiang titanium white heavy chemicals company limited produces
Pulvis Talci.
Adipic acid dibutyl ester, No. CAS: 103-23-1.
Isooctyl acid lead, No. CAS: 301-08-6.
1,1,1-trimethylolpropane, No. CAS: 919-30-2.
Silver nitrate, No. CAS: 7761-88-8, particle diameter 800 mesh.
Firebrake ZB, No. CAS: 1332-07-6, particle diameter 800 mesh.
Zinc niobate, No. CAS: 12201-66-0, particle diameter 800 mesh.
2-chloro-4,6-diamino-1,3,5-triazines, No. CAS: 3397-62-4.
2,3', 4,4', 6-pentahydroxybenzophenone, No. CAS: 519-34-6.
2,4,6-tri-(amino caproyl)-1,3,5-triazines, No. CAS: 80584-91-4.
Embodiment 1
High ferro antibacterial polyurethane water-repellent paint, by 45wt% base polyurethane prepolymer for use as component and 55wt% curing agent component group
Become.It is that 400 revs/min of stirrings i.e. obtain high ferro for 40 minutes with anti-with rotating speed after base polyurethane prepolymer for use as component and curing agent component are mixed
Bacterium polyurethane water-proof paint.
Base polyurethane prepolymer for use as component raw material (weight portion): polyethers HSH-220 29 parts, polyethers MN-3050D7 part, different Fo Er
Ketone diisocyanate 15 parts.
Curing agent component raw material (weight portion): polyethers EP-330N (G) 14 parts, polyvinyl alcohol 8 parts, Kaolin 10 parts, carbonic acid
Calcium 10 parts, adipic acid dibutyl ester 2.5 parts, 1,1,1-trimethylolpropane 4 parts, 0.5 part of isooctyl acid lead, inorganic antiseptic 3 parts, purple
Outer absorbent 1.2 parts.
Described inorganic antiseptic is uniformly mixed for 1:1:1 in mass ratio by silver nitrate, Firebrake ZB, zinc niobate
Arrive.
Described ultraviolet absorber is by 2-chloro-4,6-diaminostilbene, 3,5-triazine, 2-hydroxyl-4-methoxyl group-5-sulfonic acid two
Benzophenone, 2,4,6-tri-(amino caproyl)-1,3,5-triazine are uniformly mixed for 1:1:1 in mass ratio and obtain.
The high ferro preparation of antibacterial polyurethane water-repellent paint:
(1) by proportioning, polyethers HSH-220, polyethers MN-3050D are added in reactor, add in reactor, be heated to temperature
Degree is 105 DEG C and controls to be 105 DEG C by temperature, is 400 revs/min with rotating speed and stirs 20 minutes;Temperature is risen to 120 DEG C and by temperature
Degree control is 120 DEG C, removes vacuum after being decompressed to-0.095MPa vacuum dehydration 2 hours;Be cooled to 80 DEG C and by temperature control be
80 DEG C, adding isophorone diisocyanate with rotating speed is 400 revs/min of stirrings 2 hours;Stop stirring, cool to 60 DEG C,
Vacuum defoamation 15 minutes under-0.05MPa, obtain base polyurethane prepolymer for use as component;
(2) by proportioning by polyethers EP-330N (G), polyvinyl alcohol, Kaolin, calcium carbonate, inorganic antiseptic, uv absorption
Agent adds in reactor, is heated to temperature and is 105 DEG C and controls to be 105 DEG C by temperature, is 400 revs/min with rotating speed and stirs 10 points
Clock;Temperature risen to 120 DEG C and controls to be 120 DEG C by temperature, after being decompressed to-0.095MPa vacuum dehydration 2 hours, removing vacuum;
Being cooled to 80 DEG C and control to be 80 DEG C by temperature, adding dioctyl phthalate, isooctyl acid lead is 400 revs/min of stirrings with rotating speed
20 minutes;Adding 1,1,1-trimethylolpropane is 400 revs/min with rotating speed and stirs 5 minutes, obtains curing agent component.
Embodiment 2
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic is by Firebrake ZB, zinc niobate in mass ratio
It is uniformly mixed for 1:1 and obtains.Obtain the high ferro antibacterial polyurethane water-repellent paint of embodiment 2.
Embodiment 3
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic is by silver nitrate, zinc niobate in mass ratio
It is uniformly mixed for 1:1 and obtains.Obtain the high ferro antibacterial polyurethane water-repellent paint of embodiment 3.
Embodiment 4
Substantially the same manner as Example 1, differ only in: described inorganic antiseptic is by silver nitrate, Firebrake ZB in mass ratio
It is uniformly mixed for 1:1 and obtains.Obtain the high ferro antibacterial polyurethane water-repellent paint of embodiment 4.
Embodiment 5
Substantially the same manner as Example 1, differ only in: described ultraviolet absorber is by 2-hydroxyl-4-methoxyl group-5-sulfonic acid
Benzophenone, 2,4,6-tri-(amino caproyl)-1,3,5-triazine are uniformly mixed for 1:1 in mass ratio and obtain.Obtain reality
Execute the high ferro antibacterial polyurethane water-repellent paint of example 5.
Embodiment 6
Substantially the same manner as Example 1, differ only in: described ultraviolet absorber by 2-chloro-4,6-diaminostilbene, 3,5-
Triazine, 2,4,6-tri-(amino caproyl)-1,3,5-triazine are uniformly mixed for 1:1 in mass ratio and obtain.Obtain embodiment 6
High ferro antibacterial polyurethane water-repellent paint.
Embodiment 7
Substantially the same manner as Example 1, differ only in: described ultraviolet absorber by 2-chloro-4,6-diaminostilbene, 3,5-
Triazine, 2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid are uniformly mixed for 1:1 in mass ratio and obtain.Obtain embodiment 7
High ferro antibacterial polyurethane water-repellent paint.
Test case 1
The anti-yellowing property of the high ferro antibacterial polyurethane water-repellent paint preparing embodiment 1-7 is tested, resistance to
Xanthochromia presses IOS 11507:1997 test.Concrete test result is shown in Table 1.
Table 1: anti-yellowing property test table (90 DEG C, 500h)
Comparing embodiment 1 and embodiment 2-4, embodiment 1 (silver nitrate, Firebrake ZB, zinc niobate are compounding) anti-yellowing property is bright
Show and be better than embodiment 2-4 (in silver nitrate, Firebrake ZB, zinc niobate, arbitrarily the two is compounding).
Comparing embodiment 1 and embodiment 5-7, embodiment 1 (2-chloro-4,6-diamino-1,3,5-triazines, 2-hydroxyl-4-first
Epoxide-5-sulfonic acid benzophenone, 2,4,6-tri-(amino caproyl)-1,3,5-triazine are compounding) anti-yellowing property is substantially better than reality
Execute example 5-7 (2-chloro-4,6-diaminostilbene, 3,5-triazine, 2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid, 2,4,6-tri-(ammonia
Base caproyl) arbitrarily the two is compounding in-1,3,5-triazine).
Test case 2
The anti-microbial property of the high ferro antibacterial polyurethane water-repellent paint preparing embodiment 1-7 is tested, antibacterial
Performance presses GB/T21866-2008 antibiotic paint anti-microbial property assay method and antibacterial effect, HG/T 3980-2007 antibiotic paint
Measure, escherichia coli ATYCC 25922, staphylococcus aureus ATCC 6538.Concrete test result is shown in Table 2.
Table 2: high ferro antibacterial polyurethane water-repellent paint anti-microbial property tests tables of data
Escherichia coli sterilizing rate, % | Staphylococcus aureus sterilizing rate, % | |
Embodiment 1 | 99.4 | 99.3 |
Embodiment 2 | 94.6 | 94.6 |
Embodiment 3 | 94.2 | 94.2 |
Embodiment 4 | 94.1 | 94.5 |
Embodiment 5 | 96.1 | 95.8 |
Embodiment 6 | 95.8 | 96.2 |
Embodiment 7 | 95.9 | 95.6 |
Comparing embodiment 1 and embodiment 2-4, embodiment 1 (silver nitrate, Firebrake ZB, zinc niobate are compounding) anti-microbial property is obvious
It is better than embodiment 2-4 (in silver nitrate, Firebrake ZB, zinc niobate, arbitrarily the two is compounding).
Comparing embodiment 1 and embodiment 5-7, embodiment 1 (2-chloro-4,6-diamino-1,3,5-triazines, 2-hydroxyl-4-first
Epoxide-5-sulfonic acid benzophenone, 2,4,6-tri-(amino caproyl)-1,3,5-triazine are compounding) anti-microbial property is substantially better than enforcement
Example 5-7 (2-chloro-4,6-diaminostilbene, 3,5-triazine, 2-hydroxyl-4-methoxybenzophenone-5-sulfonic acid, 2,4,6-tri-(amino
Caproyl) arbitrarily the two is compounding in-1,3,5-triazine).
Claims (1)
1. a high ferro antibacterial polyurethane water-repellent paint, it is characterised in that by 42-48wt% base polyurethane prepolymer for use as component and
52-58wt%% curing agent component forms;
Described base polyurethane prepolymer for use as component is prepared from by the raw material of following weight parts: polyethers HSH-220 28-32 part, polyethers
MN-3050D 6-9 part, isophorone diisocyanate 10-20 part;
Described curing agent component is prepared from by the raw material of following weight parts: polyethers EP-330N (G) 10-18 part, polyvinyl alcohol
5-15 part, Pulvis Talci 15-25 part, adipic acid dibutyl ester 1-5 part, 1,1,1-trimethylolpropane 3-7 part, isooctyl acid lead 0.3-
0.9 part, inorganic antiseptic 2-8 part, ultraviolet absorber 1-5 part.
Described inorganic antiseptic is mixed by silver nitrate, Firebrake ZB, zinc niobate, described silver nitrate, Firebrake ZB, zinc niobate
Mass ratio is (1-3): (1-3): (1-3).
Described ultraviolet absorber is by 2-chloro-4,6-diaminostilbene, 3,5-triazine, 2-hydroxyl-4-methoxyl group-5-sulfonic acid hexichol first
Ketone, 2,4,6-tri-(amino caproyl)-1,3,5-triazines mix, described 2-chloro-4,6-diamino-1,3,5-triazines, 2-
Hydroxyl-4-methoxybenzophenone-5-sulfonic acid, the mass ratio of 2,4,6-tri-(amino caproyl)-1,3,5-triazine are (1-3):
(1-3): (1-3).