CN106189572A - Internal wall paint for cleaning room and preparation method thereof - Google Patents
Internal wall paint for cleaning room and preparation method thereof Download PDFInfo
- Publication number
- CN106189572A CN106189572A CN201610564643.8A CN201610564643A CN106189572A CN 106189572 A CN106189572 A CN 106189572A CN 201610564643 A CN201610564643 A CN 201610564643A CN 106189572 A CN106189572 A CN 106189572A
- Authority
- CN
- China
- Prior art keywords
- internal wall
- cleaning room
- wall paint
- parts
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of internal wall paint for cleaning room, described internal wall paint for cleaning room includes following components: water, emulsion, titanium dioxide, tourmaline powder, firming agent, defoamer, wetting agent and levelling agent；Wherein, in parts by weight, the water relative to 20 parts, emulsion 45 48 parts, titanium dioxide 20 23 parts, tourmaline powder 12 15 parts, 2.5 4 parts of firming agent, defoamer 1.5 2 parts, wetting agent 1.5 2 parts, levelling agent 1.5 2 parts.The internal wall paint for cleaning room that the present invention provides, can not only play the effect of decorated wall surface, has again some specific functions and such as adsorbs some indoor suspension micronic dusts, reduces house dust number, and the decorated metope of the most described coating also has easy to clean, the performance of washability.
Description
Technical field
The present invention relates to coating, in particular it relates to a kind of internal wall paint for cleaning room and preparation method thereof.
Background technology
Toilet, also known as dust-free workshop, dust free room or clean room, refer to the microgranule in air in the range of certain space
The contaminant exclusion such as son, noxious air, antibacterial, and by indoor temperature, cleanliness factor, room pressure, air velocity and air flow method,
Noise vibration and illumination, Electrostatic Control is in a certain range of needs, and is given specially designed room.Toilet generally exists
In fields such as pharmacy, medical treatment, food, cosmetics, biological detection, scientific researches, the major function of toilet is indoor pollution control
System, does not has toilet, and operation cannot be carried out, food and medicine cannot cannot be given birth to according to the instrument of standard production and some precisions
Produce and application.
Global design standard based on toilet and use requirement, during the construction and interior decoration of toilet
Selecting material to require the most strictly, the finishing coating of such as toilet's interior wall selects requirement to be different from common body of wall
Coating.At present, common coating for wall surface is in depositing dust, dust suction and easy to clean, and it is not the highest that these aspects of washability require, and clean
Clean room interior wall coating is then the highest at depositing dust, dust suction and aspect easy to clean, and common wall coating then can not meet requirement.
Summary of the invention
It is an object of the invention to provide a kind of internal wall paint for cleaning room and preparation method thereof, the cleaning prepared by the method
Indoor wall coating can play good depositing dust, pick-up performance and easy cleaning washability.
To achieve these goals, the invention provides a kind of internal wall paint for cleaning room, this internal wall paint for cleaning room includes
Following components: water, emulsion, titanium dioxide, tourmaline powder, firming agent, defoamer, wetting agent and levelling agent；Wherein, according to weight portion
Number meter, the water relative to 20 parts, emulsion 45-48 part, titanium dioxide 20-23 part, tourmaline powder 12-15 part, firming agent 2.5-4 part,
Defoamer 1.5-2 part, wetting agent 1.5-2 part, levelling agent 1.5-2 part.
Present invention also offers the preparation method of internal wall paint for cleaning room described above, with water in the preparation process of the method
As disperse medium, firming agent, defoamer, wetting agent and levelling agent are obtained component one with water-dispersible；By emulsion and titanium dioxide
Join in described component one and obtain component two；Finally tourmaline powder is joined stirring in described component two and obtains described cleaning
Indoor wall coating.
By technique scheme, the present invention strengthen by adding tourmaline powder in the component of coating coating depositing dust,
Dust removal ability, and use the mode of stirring to make each component raw material be sufficiently mixed in a reservoir, disperse, thus prepare described clean
Clean room interior wall coating.Internal wall paint for cleaning room prepared by the method can play the effect of decorated wall surface, has again some special
Function is as reduced the dry linting degree of indoor wall, it is also possible to adsorbing some indoor suspension micronic dusts, the most described coating is decorated
Metope also has easy to clean, the performance of washability.
Other features and advantages of the present invention will be described in detail in detailed description of the invention part subsequently.
Detailed description of the invention
Hereinafter the detailed description of the invention of the present invention is described in detail.It should be appreciated that described herein specifically
Embodiment is merely to illustrate and explains the present invention, is not limited to the present invention.
The invention provides a kind of internal wall paint for cleaning room, this internal wall paint for cleaning room includes following components: water, emulsion,
Titanium dioxide, tourmaline powder, firming agent, defoamer, wetting agent and levelling agent；
Wherein, in parts by weight, the water relative to 20 parts, described emulsion 45-48 part, described titanium dioxide 20-23 part,
Described tourmaline powder 12-15 part, described firming agent 2.5-4 part, described defoamer 1.5-2 part, described wetting agent 1.5-2 part, institute
State levelling agent 1.5-2 part.
In above-mentioned internal wall paint for cleaning room, the kind of emulsion used can select in wide scope, but in order to
Improve emulsion dispersion effect in water and the feature of environmental protection of internal wall paint for cleaning room further, it is preferable that emulsion used is selected from
One or more in acrylate and vinyl acetate emulsion, styrene-acrylic emulsion, acrylic acid ester emulsion and aqueous epoxy resins.
In above-mentioned internal wall paint for cleaning room, in order to obtain more preferable film-formation result, it is preferable that titanium dioxide used is selected from
Rutile type titanium dioxide or anatase thpe white powder；Preferably, the specification of tourmaline powder used is 1250-5000 mesh.
In above-mentioned internal wall paint for cleaning room, with the addition of the adjuvant such as firming agent, defoamer, wetting agent and levelling agent,
In order to further enhance the film-formation result of described internal wall paint for cleaning room and property easy to clean, it is preferable that firming agent used is alcohol
Fat 12 or 2-methylimidazole, defoamer is emulsified silicone oil, the fatty acid ester compounded thing of higher alcohols or polyoxyethylene polyoxy Propanolamine
Ether, wetting agent is ethanol, propylene glycol or glycerol, and described levelling agent is polysiloxanes or polyacrylic acid N-butyl.
Present invention also offers the preparation method of above-mentioned internal wall paint for cleaning room, the method is situated between as dispersion using water
Matter, obtains component one by firming agent, defoamer, wetting agent and levelling agent with water-dispersible；Emulsion and titanium dioxide are joined described
Component one obtains component two；Finally tourmaline powder is joined stirring in described component two and obtains the interior wall painting of described toilet
Material.
In above-mentioned preparation method, prepare described component one and described component two all uses the mode of stirring, the most right
There is no particular limitation for the temperature of described stirring and the rotating speed of stirring, but from preparing the preparation rate of described internal wall paint for cleaning room
With operating process energy-conservation from the standpoint of, it is preferable that the temperature of described stirring is 20-35 DEG C, and the rotating speed of stirring is 400rpm-
800rpm.In order to further enable each component of coating be sufficiently mixed by stirring, it is preferable that the time of stirring is 10-
30min。
Hereinafter will be described the present invention by embodiment.
Embodiment 1
At 25 DEG C, selection of speed 500rpm, according to weight portion, first by alcohol ester 12 parts, emulsified silicone oil 1.5 parts, second
Alcohol 1.5 parts and 2 parts of water with 20 parts of polysiloxanes are stirred 20min and obtain component one；Again by acrylate and vinyl acetate emulsion and the third breast totally 46
Part join with Rutile type titanium dioxide 22 parts described component one obtains component two, finally by tourmaline that specification is 1250 mesh
12 parts of powder joins and stirs 30min in described component two and obtain described internal wall paint for cleaning room and be designated as A1.
Embodiment
At 30 DEG C, selection of speed 600rpm, according to weight, first by 2-methylimidazole 4 parts, higher alcohols fat
Acid esters complex 2 parts, propylene glycol 2 parts and polyacrylic acid N-butyl 2 parts are stirred 20min with the water with 20 parts and obtain component
One；Again by acrylic acid ester emulsion and aqueous epoxy resins totally 48 parts join in described component one with anatase thpe white powder 23 parts
To component two, finally the tourmaline powder 15 parts that specification is 5000 mesh is joined stirring 30min in described component two and obtains described
Internal wall paint for cleaning room is designated as A2.
Embodiment 3
At 35 DEG C, selection of speed 800rpm, according to weight, first by alcohol ester 12 parts, polyoxyethylene polyoxy
Propanol amidogen ether 1.8 parts, glycerol 1.8 parts and polyacrylic acid N-butyl 1.8 parts are stirred 20min with the water with 20 parts and obtain component
One；Again by styrene-acrylic emulsion and acrylic acid ester emulsion totally 47 parts join in described component one with Rutile type titanium dioxide 22 parts and to obtain
Component two, finally joins the tourmaline powder 13 parts that specification is 3000 mesh stirring 30min in described component two and obtains described clean
Clean room interior wall coating is designated as A3.
Comparative example 1
Coating B1 is prepared, except that comparative example 1 does not adds tourmaline according to the method for embodiment 1.
Comparative example 2
Coating B2 is prepared according to the method for embodiment 2, except that the weight portion 10 parts of the tourmaline powder added.
Comparative example 3
The coating B3 of comparative example 3 is prepared relative to the method for embodiment 3, except that the weight of the tourmaline powder added
Part 16 parts.
Detection example 1
Coating A1-A3 and B1-B3 prepared according to the preparation method described in above-described embodiment 1-3 and comparative example 1-3
Carrying out functional test, method of testing is as follows:
Coating makes: coating A1, A2, A3 and B1 of equal in quality 150g, B2, B3 are fabricated to 150g/m2Coating.
Dust particle quantity is added up: by the paint coatings plate for preparing as in seal glass storehouse, uniform from Hatch Opening top
Sprinkling powder dust, then use five-spot dust particle quantity of sample in observation unit's area under high power microscope.
Washability is tested: according to the wash-resistant property of GB GB/T9756-2001 standard testing coating.
It addition, in order to contrast the performance characterizing the internal wall paint for cleaning room that the present invention provides further, in the present embodiment also
Have chosen common coating (ippon interiro wall latex paint) and prepare coating through same process.
Coating functional test results prepared by various embodiments above and comparative example is as shown in table 1:
Table 1
Being shown by above-mentioned functions test result, the dust suction of internal wall paint for cleaning room, depositing dust ability that the present invention provides are
Commonly more than 10 times of coating, and the test result of comparative example 1 show that in the present invention, the tourmaline powder of interpolation is for the suction of coating
Dirt, the raising of dust-laying effect play a major role；It addition, test result also demonstrates the internal wall paint for cleaning room of present invention offer
Washability number of times is all higher than 5000 times, specifies according to GB GB/T9756-2001 standard, and toilet's interior wall that the present invention provides is coated with
Material is at the top of one's class product, has good wash-resistant property, beneficially metope daily cleaning, maintenance, and also indicates that described cleaning
The anti-dry linting of indoor wall coating is good.
The preferred embodiment of the present invention described in detail above, but, the present invention is not limited in above-mentioned embodiment
Detail, in the technology concept of the present invention, technical scheme can be carried out multiple simple variant, this
A little simple variant belong to protection scope of the present invention.
It is further to note that each the concrete technical characteristic described in above-mentioned detailed description of the invention, at not lance
In the case of shield, can be combined by any suitable means, in order to avoid unnecessary repetition, the present invention to various can
The compound mode of energy illustrates the most separately.
Additionally, combination in any can also be carried out between the various different embodiment of the present invention, as long as it is without prejudice to this
The thought of invention, it should be considered as content disclosed in this invention equally.
Claims (9)
1. an internal wall paint for cleaning room, it is characterised in that described internal wall paint for cleaning room includes following components: water, emulsion, titanium
White lead, tourmaline powder, firming agent, defoamer, wetting agent and levelling agent；
Wherein, in parts by weight, the water relative to 20 parts, described emulsion 45-48 part, described titanium dioxide 20-23 part is described
Tourmaline powder 12-15 part, described firming agent 2.5-4 part, described defoamer 1.5-2 part, described wetting agent 1.5-2 part, described stream
Flat agent 1.5-2 part.
Internal wall paint for cleaning room the most according to claim 1, wherein, described emulsion selected from acrylate and vinyl acetate emulsion, styrene-acrylic emulsion,
One or more in acrylic acid ester emulsion and aqueous epoxy resins.
Internal wall paint for cleaning room the most according to claim 1, wherein, described titanium dioxide selected from Rutile type titanium dioxide or
Anatase thpe white powder.
Internal wall paint for cleaning room the most according to claim 1, wherein, described firming agent is alcohol ester 12 or 2-methyl miaow
Azoles；Described defoamer is emulsified silicone oil, the fatty acid ester compounded thing of higher alcohols or polyoxyethylene polyoxy propanol amidogen ether；Described
Wetting agent is ethanol, propylene glycol or glycerol；Described levelling agent is polysiloxanes or polyacrylic acid N-butyl.
Internal wall paint for cleaning room the most according to claim 1, wherein, described tourmaline powder is ultra-fine tourmaline powder, rule
Lattice are between 1250-5000 mesh.
6. the preparation method of the internal wall paint for cleaning room described in any one of claim 1-5, it is characterised in that using water as dispersion
Medium, obtains component one by firming agent, defoamer, wetting agent and levelling agent with water-dispersible；Emulsion, titanium dioxide are joined described
Component one obtains component two；Finally tourmaline powder is joined stirring in described component two and obtains the interior wall painting of described toilet
Material.
The preparation method of internal wall paint for cleaning room the most according to claim 6, wherein, prepares what described component one was used
Method is stirring, and the time of stirring is 10-30min, and the temperature of stirring is 20-35 DEG C.
The preparation method of internal wall paint for cleaning room the most according to claim 6, wherein, prepares what described component two was used
Method is stirring, and the temperature of stirring is 20-35 DEG C.
9. the preparation method of the internal wall paint for cleaning room described in claim 7 or 8, wherein, prepares described component one and component two
During, the rotating speed of stirring is all between 400rpm-800rpm.