CN106187003A - Water-fast fluorgypsum mould conjunction and preparation method thereof - Google Patents
Water-fast fluorgypsum mould conjunction and preparation method thereof Download PDFInfo
- Publication number
- CN106187003A CN106187003A CN201610522247.9A CN201610522247A CN106187003A CN 106187003 A CN106187003 A CN 106187003A CN 201610522247 A CN201610522247 A CN 201610522247A CN 106187003 A CN106187003 A CN 106187003A
- Authority
- CN
- China
- Prior art keywords
- water
- fluorgypsum
- fast
- parts
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of water-fast fluorgypsum mould to close, including following raw material: fluorgypsum 400 550 parts;250 300 parts of Gypsum Fibrosum;Breeze 100 250 parts;Cement 30 100 parts;Sulphate aluminium cement 50 100 parts;Water reducer 15 parts;Basic matterial 10 20 parts;Exciting agent 8 15 parts;Glass fibre 5 10 parts, component is poured into stirring container mix and blend 3 5min according to weight ratio, it is ready for suitable quantity of water, the component of mixing is poured into water stirring 30s, pouring the mixture into die for molding, quiet stop the demoulding after 10min, the mould obtained by covered rearing with plastic film closes 3 days and wet supports, the present invention solves the drawback that the most water-fast and intensity that fluorgypsum mould closes is low, it is provided that a kind of a large amount of process fluorgypsums and scientific utilization fluorgypsum technology.
Description
Technical field
The invention belongs to solid waste comprehensive utilization of resources and the water-fast technical field of construction material, a kind of water-fast fluorgypsum
Mould conjunction and preparation method thereof.
Background technology
Fluorgypsum is that sulphuric acid reacts, with fluorite, the waste residue produced, and acidity is very strong, and pH value is 3-4, belongs to the strongest the having of corrosivity
Evil solid waste, utilization rate is the lowest, such stores up in a large number, and how both landed property resources, again polluted underground water source and environment pass through
Research and develop effective technological means, solid waste fluorgypsum is turned waste into wealth, effectively utilizes, there is far-reaching economic and environment-friendly meaning.Another
Aspect, plaster mold closes and has commercially developed 3-5, and prospect is pretty good, and added value is the highest, but standard is put into effect not yet, deadly defect
Be completely exposed, hence it is evident that constrain development that plaster mold closes and market advances, it the most water-fast, intensity is low, long green hair three is the most fatal
Wound, have impact on mould and closes the fast development of industry, and the price causing the homogeneity product between the dissatisfied of market and enterprise compares with,
The generation of market demand new technique.
Summary of the invention
It is an object of the present invention to provide a kind of water-fast fluorgypsum mould conjunction and preparation method thereof, make full use of discarded fluorgypsum, protect
Protect can not regenerated resources, preserve the ecological environment, solve semi-hydrated gypsum mould close exist the most water-fast, intensity is low, the fraud of the easy accumulation of salt in the surface soil
Disease, promotes plaster mold to close the development of industry, meets the demand that water-proof gypsum mould is closed by market.
In order to solve above-mentioned technical problem, the technical solution used in the present invention is:
Water-fast fluorgypsum mould closes, including following raw material:
Fluorgypsum is in Fluohydric acid. enterprise production process, sulphuric acid and fluorite react the waste residue produced, and exempts to dry, exempt to forge
Burning, the most modified utilization, in acidity, pH value is 3-4.
Preferably, Gypsum Fibrosum is half water ardealite and half water desulfurated plaster, and performance is: the presetting period is 3-5min, water consumption
≤ 65%, 2h rupture strength >=3MPa, 2h comprcssive strength >=5.5MPa.
Preferably, breeze is S95 powder.
Preferably, cement is 42.5 Portland cements.
Preferably, sulphate aluminium cement is double-quick cement.
Preferably, water reducer is polycarboxylate water-reducer, water-reducing rate >=22%.
Preferably, exciting agent is one or more of calcium chloride and potassium sulfate.
Preferably, glass fibre length 3-4cm.
Preferably, basic matterial is quick lime, content >=70% of CaO.
The preparation method that a kind of water-fast fluorgypsum mould closes, comprises the following steps:
A, by component according to weight ratio pour into stirring container mix and blend 3-5min, be ready for suitable quantity of water, by mixing
Component is poured into water stirring 30s;
B, mixture step a obtained pour die for molding into, quiet stop the demoulding after 10min;
C, the mould that covered rearing with plastic film step b is obtained close 3 days wet support.
The invention has the beneficial effects as follows:
1, the present invention use Binder Materials be fluorgypsum, implement again exempt from dry, exempt from calcine technology, save equipment and
A large amount of inputs of Factory Building, decrease the discharge of carbon dioxide, decrease energy resource consumption, beneficially the protection of environment.
2, another reason that the present invention uses fluorgypsum to be Binder Materials, is that its sulfate dihydrate calcium content is all natural
Or the highest in industry by-product gypsum, so intensity is also that other Gypsum Fibrosum are incomparable.
3, this invention takes the fluorgypsum water-fast modification technology of enforcement, ensureing that prior art initial set is fast, the demoulding is fast
On the basis of, add resistance to water function, solve intensity low simultaneously, the deficiency of high, the long green hair of water absorption rate, widen range of application,
Improve product grade, meet the demand in market.
Detailed description of the invention
Hereinafter embodiments of the invention are described in detail, but what the present invention can be defined by the claims and cover
Multitude of different ways is implemented.
Embodiment one
Take fluorgypsum 480 parts, desulfurated plaster 250 parts, cement 48 parts, breeze 180 parts, sulphate aluminium cement 20 parts, poly-carboxylic
Acid water reducer 1 part, 8 parts of calcium chloride, glass fibre 5 parts, quick lime 20 parts, by above components by weight percent mix and blend 3-5min, accurate
Standby suitable quantity of water, is poured into water the component of mixing stirring 30s, is injected in mould shaping, molding after 10min, then uses plastics
Thin film covering curing 3 days, gained is water-fast, and fluorgypsum mould conjunction performance is: initial set 3-4min, water consumption 50-55%, and 3 the Heavenly Stems resisted
Folding intensity: 5.1MPa, 3 the Heavenly Stems comprcssive strength: 18.2MPa, 3 days coefficient of softing: 0.88.
Embodiment two
Take fluorgypsum 486 parts, ardealite 220 parts, cement 55 parts, breeze 185 parts, sulphate aluminium cement 30 parts, polycarboxylic acids
Water reducer 2 parts, potassium sulfate 6 parts, 6 parts of calcium chloride, quick lime 10 parts, glass fibre 5 parts, by above components by weight percent mix and blend 3-
5min, prepares suitable quantity of water, the component of mixing is poured into water stirring 30s, is injected in mould shaping, molding after 10min, then
With covered rearing with plastic film maintenance 3 days, gained is water-fast, and fluorgypsum mould conjunction performance was: initial set 3min, water consumption 52%, 3 the Heavenly Stems
Rupture strength: 4.8MPa, 3 the Heavenly Stems comprcssive strength: 16.9MPa, 3 days coefficient of softing: 0.86.
Embodiment three
Take fluorgypsum 395 parts, ardealite 150 parts, desulfurated plaster 150 parts, cement 40 parts, breeze 200 parts, aluminium sulfate water
40 parts of mud, polycarboxylate water-reducer 2 parts, potassium sulfate 8 parts, quick lime 15 parts, glass fibre 8 parts, stir the mixing of above components by weight percent
Mix 3-5min, prepare suitable quantity of water, the component of mixing is poured into water stirring 30s, be injected in mould shaping, molding after 10min,
Then with covered rearing with plastic film maintenance 3 days, gained is water-fast, and fluorgypsum mould conjunction performance is: initial set 4min, water consumption 53%, 3
The Heavenly Stems rupture strength: 4.6MPa, 3 the Heavenly Stems comprcssive strength: 16.4MPa, 3 days coefficient of softing: 0.86.
Invention described above embodiment, is not intended that limiting the scope of the present invention, any in the present invention
Spirit and principle within amendment, equivalent and the improvement etc. made, should be included in the claim protection model of the present invention
Within enclosing.
Claims (10)
- The most water-fast fluorgypsum mould closes, it is characterised in that include following raw material:Fluorgypsum is in Fluohydric acid. enterprise production process, sulphuric acid and fluorite react the waste residue produced, and exempts to dry, exempt from calcining, directly Connecing modified utilization, in acidity, pH value is 3-4.
- The most water-fast fluorgypsum mould closes, it is characterised in that Gypsum Fibrosum is half water ardealite and half water desulfurization stone Cream, performance is: the presetting period is 3-5min, water consumption≤65%, 2h rupture strength >=3MPa, 2h comprcssive strength >=5.5MPa.
- The most water-fast fluorgypsum mould closes, it is characterised in that breeze is S95 powder.
- The most water-fast fluorgypsum mould closes, it is characterised in that cement is 42.5 Portland cements.
- The most water-fast fluorgypsum mould closes, it is characterised in that sulphate aluminium cement is double-quick cement.
- The most water-fast fluorgypsum mould closes, it is characterised in that water reducer is polycarboxylate water-reducer, water-reducing rate >=22%.
- The most water-fast fluorgypsum mould closes, it is characterised in that exciting agent is the one of calcium chloride and potassium sulfate Or it is multiple.
- The most water-fast fluorgypsum mould closes, it is characterised in that glass fibre length 3-4cm.
- The most water-fast fluorgypsum mould closes, it is characterised in that basic matterial is quick lime, and the content of CaO >= 70%.
- 10. the preparation method closed such as any one water-fast fluorgypsum mould of claim 1~9, it is characterised in that include following step Rapid:A, by component according to weight ratio pour into stirring container mix and blend 3-5min, be ready for suitable quantity of water, will mixing component It is poured into water stirring 30s;B, mixture step a obtained pour die for molding into, quiet stop the demoulding after 10min;C, the mould that covered rearing with plastic film step b is obtained close 3 days wet support.