CN106185796A - A kind of two-dimensional nano carbon plate and there is the potentiometer of two-dimensional nano carbon plate - Google Patents
A kind of two-dimensional nano carbon plate and there is the potentiometer of two-dimensional nano carbon plate Download PDFInfo
- Publication number
- CN106185796A CN106185796A CN201610510299.4A CN201610510299A CN106185796A CN 106185796 A CN106185796 A CN 106185796A CN 201610510299 A CN201610510299 A CN 201610510299A CN 106185796 A CN106185796 A CN 106185796A
- Authority
- CN
- China
- Prior art keywords
- dimensional nano
- carbon plate
- rotating mechanism
- nano carbon
- centre bore
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of potentiometer with two-dimensional nano carbon plate, including: housing, rotary shaft, rotating mechanism one, rotating mechanism two, two-dimensional nano carbon plate and three the carbon plate terminals being arranged on two-dimensional nano carbon plate；Housing includes upper shell and lower house；Rotating mechanism one, rotating mechanism two, two-dimensional nano carbon plate are arranged between upper shell and lower house；Two parallel planes of axostylus axostyle offset with straight flange one, straight flange two respectively, make rotary shaft rotated by rotation mechanism one and rotating mechanism two, the resistance of regulator potentiometer.The potentiometer with two-dimensional nano carbon plate that the present invention provides, switch part is few, and resistance to elevated temperatures is good, can be the most indeformable, it is to avoid rivet the most yielding deficiency.The electric conductivity of the potentiometer of two-dimensional nano carbon plate is excellent.
Description
Technical field
The present invention relates to potentiometer field, particularly relate to a kind of two-dimensional nano carbon plate and there is the electricity of two-dimensional nano carbon plate
Position device.
Background technology
Film type carbon potentiometer is widely used in the electronic equipments such as multi-media sound system, radio cassette player, sound console making volume, sound
Adjust, balance controls and electric current, voltage-regulation, also can realize remote control adjustment.
In prior art, at nano-sized carbon surface grafting about 1～the chemical group of 20%, it is desirable to utilize these groups increase with
The interface cohesion of different subjects material, but this has bigger use limitation, and it is not amenable to hot environment, nano-sized carbon surface
Quantity the most limited, its strength when polymer is combined is big not, when the stretching of composite stress or bending, carbon nanometer
Pipe still can skid off, and impact is normal to be used.
Summary of the invention
In order to overcome above-mentioned deficiency of the prior art, it is an object of the invention to, it is provided that a kind of two-dimensional nano carbon plate, bag
Include: constituent content is: metal oxide nanotubes 0.1%～20%, conductive carbon black or content of graphite are 0.5%～15%, oxygen
Change zirconium nano-powder content be 0.5%～8%, activated carbon be 0.1%～99%, activated carbon nano fiber be 80%～
98%, nano metal nickel powder body is 1%～3%, carbon nitrogen presoma is 5%～30%, polyethylene is 15%～20%, Colophonium is molten
It is 15%～30% in dimethylbenzene.
Preferably, described carbon nitrogen presoma includes: selected from by carbamide, cyanamid dimerization, tripolycyanamide and each of which
With at least one in the group of the mixture composition of low-dimensional nano-sized carbon.
Preferably, one or more during nano metal is Al or Ni or Li or Zn or Cu or Ti or Fe.
Preferably, one during metal oxide nanotubes is Al2O3 or ZrO2 or TiO2 or MnO2 or V2O5 or
Several, its pore diameter range is 1nm～100nm.
Preferably, the granularity of described activated carbon is in 1nm～80 μ m, and specific surface area is 500m2/g～2000m2/g,
Density is 1.0g/cm3～1.5g/cm3.
Preferably, the density of described activated carbon is 0.3g/cm3～1.0g/cm3, middle micropore ＞ 40%, middle micropore is 30nm
～the hole of 60nm scope.
Preferably, in described carbon nitrogen presoma, nitrogen mass percent in described carbon nitrogen presoma is 5%～25%.
A kind of potentiometer with two-dimensional nano carbon plate, including: housing, rotary shaft, rotating mechanism one, rotating mechanism two,
Two-dimensional nano carbon plate and three the carbon plate terminals being arranged on two-dimensional nano carbon plate；Described two-dimensional nano carbon plate is claim
Two-dimensional nano carbon plate described in 1 to claim 7；
Described housing includes upper shell and lower house；Rotating mechanism one, rotating mechanism two, two-dimensional nano carbon plate are arranged on upper shell
And between lower house；
Described upper shell, lower house, rotating mechanism one, rotating mechanism two, the center of two-dimensional nano carbon plate are respectively equipped with centre bore,
Rotary shaft sequentially passes through upper shell centre bore, rotating mechanism one centre bore, two-dimensional nano carbon plate centre bore, rotating mechanism two center
Hole, lower house centre bore, be fixed on lower house centre bore；
It is evenly distributed with five boss on described rotating mechanism one edge, described rotating mechanism two edge is evenly distributed with five
Boss, described rotating mechanism one is corresponding with the lug boss position of described rotating mechanism two；
Described rotary shaft is provided with axle cap and axostylus axostyle, and axostylus axostyle is provided with two parallel planes, and the centre bore of rotating mechanism one is provided with two
Individual parallel straight flange one, the centre bore of rotating mechanism two is provided with two parallel straight flanges two, two parallel putting down of axostylus axostyle
Face offsets with straight flange one, straight flange two respectively, makes described rotary shaft rotated by rotation mechanism one and rotating mechanism two, regulation electricity
The resistance of position device.
Preferably, described rotating mechanism one is provided with rubber cushion one, and described rotating mechanism two is provided with rubber cushion two；
Described rubber cushion one contacts with described two-dimensional nano carbon plate；
Described rubber cushion two contacts with described two-dimensional nano carbon plate.
As can be seen from the above technical solutions, the invention have the advantages that
In two-dimensional nano carbon plate, nano metal and activated carbon nano fiber improve the electric conductivity of carbon-based material, reduce electrode
The internal resistance of material, is simultaneously introduced metal oxide nanotubes, on the basis of the effective ratio area improving carbon-based electrode material,
Utilize the nanometer cooperative effect on nano carbon-base material surface and metal oxide nanotubes surface, considerably increase active substance table
The utilization rate of area.
It is amenable to hot environment, improves the dynamics that nano-sized carbon is combined with polymer, expanded two-dimensional nano carbon plate at each
The application in field.
Accompanying drawing explanation
In order to be illustrated more clearly that technical scheme, will the accompanying drawing used required in describing be made simple below
Ground is introduced, it should be apparent that, the accompanying drawing in describing below is only some embodiments of the present invention, for ordinary skill
From the point of view of personnel, on the premise of not paying creative work, it is also possible to obtain other accompanying drawing according to these accompanying drawings.
Fig. 1 is the overall structure figure of the potentiometer with two-dimensional nano carbon plate；
Fig. 2 is the explosive view of the potentiometer with two-dimensional nano carbon plate.
Detailed description of the invention
For making the goal of the invention of the present invention, feature, the advantage can be the most obvious and understandable, concrete by using below
Embodiment and accompanying drawing, be clearly and completely described the technical scheme of present invention protection, it is clear that enforcement disclosed below
Example is only a part of embodiment of the present invention, and not all embodiment.Based on the embodiment in this patent, the common skill in this area
All other embodiments that art personnel are obtained under not making creative work premise, broadly fall into the model of this patent protection
Enclose.
The present embodiment provides a kind of two-dimensional nano carbon plate, including: constituent content is: metal oxide nanotubes 0.1%～
20%, conductive carbon black or content of graphite be 0.5%～15%, the content of nm-class powder of zirconium oxide be 0.5%～8%, activated carbon
Be 0.1%～99%, activated carbon nano fiber be 80%～98%, nano metal nickel powder body is 1%～3%, carbon nitrogen presoma
Be 5%～30%, polyethylene be 15%～20%, to be dissolved in dimethylbenzene be 15%～30% to Colophonium.
Preferably, two-dimensional nano carbon plate, including: constituent content is: metal oxide nanotubes 0.1%, conductive carbon black or
Content of graphite is 5%, the content of nm-class powder of zirconium oxide is 8%, activated carbon is 29%, activated carbon nano fiber is 80%, receives
Rice metallic nickel powder body is 1%, carbon nitrogen presoma is 15%, polyethylene is 15%, to be dissolved in dimethylbenzene be 15% to Colophonium.
Preferably, two-dimensional nano carbon plate, including: constituent content is: metal oxide nanotubes 20%, conductive carbon black or stone
Ink content is 15%, the content of nm-class powder of zirconium oxide is 8%, activated carbon is 78%, activated carbon nano fiber is 88%, nanometer
Metallic nickel powder body is 3%, carbon nitrogen presoma is 30%, polyethylene is 20%, to be dissolved in dimethylbenzene be 20% to Colophonium.
Preferably, two-dimensional nano carbon plate, including: constituent content is: metal oxide nanotubes 10%, conductive carbon black or stone
Ink content is 5%, the content of nm-class powder of zirconium oxide is 6%, activated carbon is 69%, activated carbon nano fiber is 98%, nanometer
Metallic nickel powder body is 2%, carbon nitrogen presoma is 23%, polyethylene is 17%, to be dissolved in dimethylbenzene be 21% to Colophonium.
Preferably, two-dimensional nano carbon plate, including: constituent content is: metal oxide nanotubes 12%, conductive carbon black or stone
Ink content is 12%, the content of nm-class powder of zirconium oxide is 5%, activated carbon is 70%, activated carbon nano fiber is 87%, nanometer
Metallic nickel powder body is 3%, carbon nitrogen presoma is 14%, polyethylene is 19%, to be dissolved in dimethylbenzene be 21% to Colophonium.
Preferably, two-dimensional nano carbon plate, including: constituent content is: metal oxide nanotubes 12%, conductive carbon black or stone
Ink content is 12%, the content of nm-class powder of zirconium oxide is 7%, activated carbon is 36%, activated carbon nano fiber is 92%, nanometer
Metallic nickel powder body is 3%, carbon nitrogen presoma is 18%, polyethylene is 17%, to be dissolved in dimethylbenzene be 21% to Colophonium.
Preferably, two-dimensional nano carbon plate, including: constituent content is: metal oxide nanotubes 0.9%, conductive carbon black or
Content of graphite is 7%, the content of nm-class powder of zirconium oxide is 3%, activated carbon is 43%, activated carbon nano fiber is 83%, receives
Rice metallic nickel powder body is 1%, carbon nitrogen presoma is 12%, polyethylene is 20%, to be dissolved in dimethylbenzene be 19% to Colophonium.
Carbon nitrogen presoma includes: selected from by carbamide, cyanamid dimerization, tripolycyanamide and each of which and low-dimensional nano-sized carbon
Mixture composition group at least one.
Nano metal is one or more in Al or Ni or Li or Zn or Cu or Ti or Fe.
Metal oxide nanotubes is one or more in Al2O3 or ZrO2 or TiO2 or MnO2 or V2O5, its
Pore diameter range is 1nm～100nm.
The granularity of activated carbon is in 1nm～80 μ m, and specific surface area is 500m2/g～2000m2/g, and density is 1.0g/
Cm3～1.5g/cm3.
The density of activated carbon is 0.3g/cm3～1.0g/cm3, middle micropore ＞ 40%, middle micropore is 30nm～60nm scope
Hole.
In carbon nitrogen presoma, nitrogen mass percent in carbon nitrogen presoma is 5%～25%.
The present invention also provides for a kind of potentiometer with two-dimensional nano carbon plate, refers to include shown in Fig. 1 and Fig. 2: housing
1, rotary shaft 3, rotating mechanism 1, rotating mechanism 26, two-dimensional nano carbon plate 5 and be arranged on three on two-dimensional nano carbon plate 5
Individual carbon plate terminal 2；Two-dimensional nano carbon plate 5 is mentioned component and the two-dimensional nano carbon plate of content composition；Housing 1 includes upper shell 11
With lower house 12；Rotating mechanism 1, rotating mechanism 26, two-dimensional nano carbon plate 5 are arranged between upper shell 11 and lower house 12；
Upper shell 11, lower house 12, rotating mechanism 1, rotating mechanism 26, the center of two-dimensional nano carbon plate 5 are respectively equipped with center
Hole, rotary shaft 3 sequentially passes through upper shell 11 centre bore, rotating mechanism 1 centre bore, two-dimensional nano carbon plate 5 centre bore, rotating machine
Structure 26 centre bore, lower house 12 centre bore, be fixed on lower house 12 centre bore；
It is evenly distributed with five boss on rotating mechanism 1 edge, rotating mechanism 26 edge is evenly distributed with five boss,
Rotating mechanism 1 is corresponding with the lug boss position of rotating mechanism 26；
Rotary shaft 3 is provided with axle cap and axostylus axostyle, and axostylus axostyle is provided with two parallel planes, and the centre bore of rotating mechanism 1 is provided with two
Parallel straight flange one, the centre bore of rotating mechanism 26 is provided with two parallel straight flanges two, two parallel planes of axostylus axostyle
Offset with straight flange one, straight flange two respectively, make rotary shaft 3 rotated by rotation mechanism 1 and rotating mechanism 26, regulate current potential
The resistance of device.
The potentiometer with two-dimensional nano carbon plate that the present invention provides, switch part is few, and resistance to elevated temperatures is good, can be at high temperature
Under indeformable, it is to avoid rivet the most yielding deficiency.The electric conductivity of the potentiometer of two-dimensional nano carbon plate is excellent.
Rotating mechanism 1 is provided with rubber cushion one, and rotating mechanism 26 is provided with rubber cushion two；Rubber cushion one connects with two-dimensional nano carbon plate 5
Touch；Rubber cushion two contacts with two-dimensional nano carbon plate 5.Reduce rotating mechanism 1 and rotating mechanism 26 relative to two-dimensional nano carbon plate 5
Abrasion, extend potentiometer the use time, it is ensured that the serviceability of potentiometer.
In this specification, each embodiment uses the mode gone forward one by one to describe, and what each embodiment stressed is and other
The difference of embodiment, identical similar portion reference mutually between each embodiment.
Described above to the disclosed embodiments, makes professional and technical personnel in the field be capable of or uses the present invention.
Multiple amendment to these embodiments will be apparent from for those skilled in the art, as defined herein
General Principle can realize without departing from the spirit or scope of the present invention in other embodiments.Therefore, the present invention
It is not intended to be limited to the embodiments shown herein, and is to fit to and principles disclosed herein and features of novelty phase one
The widest scope caused.
Claims (9)
1. a two-dimensional nano carbon plate, it is characterised in that including: constituent content is: metal oxide nanotubes 0.1%～
20%, conductive carbon black or content of graphite be 0.5%～15%, the content of nm-class powder of zirconium oxide be 0.5%～8%, activated carbon
Be 0.1%～99%, activated carbon nano fiber be 80%～98%, nano metal nickel powder body is 1%～3%, carbon nitrogen presoma
Be 5%～30%, polyethylene be 15%～20%, to be dissolved in dimethylbenzene be 15%～30% to Colophonium.
Two-dimensional nano carbon plate the most according to claim 1, it is characterised in that
Described carbon nitrogen presoma includes: selected from by carbamide, cyanamid dimerization, tripolycyanamide and each of which and low-dimensional nano-sized carbon
Mixture composition group at least one.
Two-dimensional nano carbon plate the most according to claim 1, it is characterised in that
Nano metal is one or more in Al or Ni or Li or Zn or Cu or Ti or Fe.
Two-dimensional nano carbon plate the most according to claim 3, it is characterised in that
Metal oxide nanotubes is one or more in Al2O3 or ZrO2 or TiO2 or MnO2 or V2O5, its aperture
Scope is 1nm～100nm.
Two-dimensional nano carbon plate the most according to claim 1, it is characterised in that
The granularity of described activated carbon is in 1nm～80 μ m, and specific surface area is 500m2/g～2000m2/g, and density is 1.0g/
Cm3～1.5g/cm3.
Two-dimensional nano carbon plate the most according to claim 1, it is characterised in that
The density of described activated carbon is 0.3g/cm3～1；
0g/cm3, middle micropore ＞ 40%, middle micropore is the hole of 30nm～60nm scope.
Two-dimensional nano carbon plate the most according to claim 1, it is characterised in that
In described carbon nitrogen presoma, nitrogen mass percent in described carbon nitrogen presoma is 5%～25%.
8. a potentiometer with two-dimensional nano carbon plate, it is characterised in that including: housing, rotary shaft, rotating mechanism one, turn
Motivation structure two, two-dimensional nano carbon plate and three the carbon plate terminals being arranged on two-dimensional nano carbon plate；Described two-dimensional nano carbon plate
For the two-dimensional nano carbon plate described in claim 1 to claim 7；
Described housing includes upper shell and lower house；Rotating mechanism one, rotating mechanism two, two-dimensional nano carbon plate are arranged on upper shell
And between lower house；
Described upper shell, lower house, rotating mechanism one, rotating mechanism two, the center of two-dimensional nano carbon plate are respectively equipped with centre bore,
Rotary shaft sequentially passes through upper shell centre bore, rotating mechanism one centre bore, two-dimensional nano carbon plate centre bore, rotating mechanism two center
Hole, lower house centre bore, be fixed on lower house centre bore；
It is evenly distributed with five boss on described rotating mechanism one edge, described rotating mechanism two edge is evenly distributed with five
Boss, described rotating mechanism one is corresponding with the lug boss position of described rotating mechanism two；
Described rotary shaft is provided with axle cap and axostylus axostyle, and axostylus axostyle is provided with two parallel planes, and the centre bore of rotating mechanism one is provided with two
Individual parallel straight flange one, the centre bore of rotating mechanism two is provided with two parallel straight flanges two, two parallel putting down of axostylus axostyle
Face offsets with straight flange one, straight flange two respectively, makes described rotary shaft rotated by rotation mechanism one and rotating mechanism two, regulation electricity
The resistance of position device.
The potentiometer with two-dimensional nano carbon plate the most according to claim 8, it is characterised in that
Described rotating mechanism one is provided with rubber cushion one, and described rotating mechanism two is provided with rubber cushion two；
Described rubber cushion one contacts with described two-dimensional nano carbon plate；
Described rubber cushion two contacts with described two-dimensional nano carbon plate.