CN106182297A - A kind of method improving wicker products hardness - Google Patents
A kind of method improving wicker products hardness Download PDFInfo
- Publication number
- CN106182297A CN106182297A CN201610551272.XA CN201610551272A CN106182297A CN 106182297 A CN106182297 A CN 106182297A CN 201610551272 A CN201610551272 A CN 201610551272A CN 106182297 A CN106182297 A CN 106182297A
- Authority
- CN
- China
- Prior art keywords
- wicker
- parts
- temperature
- hardness
- mass fraction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of method improving wicker products hardness, comprise the steps: that the peeling of (1) wicker, the braiding of (2) sofening treatment, (3) wicker, (4) hardness process.The collocation of the inventive method each step is scientific and reasonable, the wicker products insect protected, the anti-mold effect that prepare are preferable, case hardness is higher, and compared with prior art, its case hardness can improve about 25%, service life under normal service condition can extend about 30%, service life under high humidity conditions can extend more than 50%, and stability in use is preferable, and anti-deformation ability is stronger, corrosion resistance and good, use value is higher.
Description
Technical field
The invention belongs to wicker plaiting article manufacture field, be specifically related to a kind of method improving wicker products hardness.
Background technology
Wicker plaiting article is China's one traditional technology, and present wicker products is commercially popular, and the kind of wicker products is numerous
Many, the polytypes such as seat, basket, basket, dustpan, round-bottomed basket, crate, shallow basket made of wicker or thin bamboo strips, the gaily decorated basket, bamboo strainer, food dish are had at domestic aspect.Export trade side
Face, has formed buck basket, flower pot coat, picnic tableware basket, hanging basket, lampshade, kennel, cat litter, Bird's Nest etc. through developing and design many
Kind, foreign trade is formed the appreciation effect that low-grade goods become high-grade, very popular.Wicker products is main with wicker
Raw material, but wicker is the most infested, mouldy, causes knitting shortening in service life.Easy in order to solve wicker
Infested, mouldy phenomenon, the most employing chemical agents carry out immersion treatment, but its toxicity is relatively strong, remains more serious, in braiding
Product often cause toxic residue to leak during using, and affect user healthy, although people attempt using herbal mediciment
Carry out immersion treatment, have a better effect, it also avoid the problem that chemical agent toxicity is stronger, but its prepared composition
Complex with method, cost is the highest, is not easy to promote, and the wicker products after above two mode processes is higher in humidity
Under the conditions of effect the most poor.Additionally, existing wicker products also exists the problem that hardness is relatively low, the most wear-resisting more, most reasons are
In order to allow wicker be more easy to braiding and the sofening treatment that carries out, the hardness causing final finished is relatively low, reduces ruggedness, simultaneously because of
For the decline of hardness, once there is damage in surface, mouldy infested phenomenon still easily occurs.
Summary of the invention
In order to solve the problems referred to above, the invention provides a kind of method improving wicker products hardness.
The present invention is achieved through the following technical solutions:
A kind of method improving wicker products hardness, comprises the steps:
(1) wicker peeling: harvested wicker is carried out peeling operation, then puts it into the salt solution that mass fraction is 3%
Middle soaking and washing 20min, standby after being placed under the sun dry in the sun with clear water after being finally drawn off rinsing well 1 ~ 2 day；
(2) sofening treatment:
A. the wicker after dry in the sun is put into temperature be 140 ~ 150 DEG C, pressure be 5.5 ~ 6.5MPa, relative humidity be 70 ~ 75% close
Close in tank, after heat-insulation pressure keeping 1h, be promptly restored to the state of normal temperature and pressure, put into after taking-up fill mass fraction be 3% compound
In enzyme aqueous solution, keeping aqueous temperature is 38 ~ 42 DEG C, puts it in vapor tight tank, by above-mentioned ginseng after soaking enzymolysis 10min again
Said conditions processes, and this is a circulation, amounts to circulation operation 3 times；Containing cellulase, tannin in described compound enzyme
Enzyme, pectase, the weight ratio of three is 6:2:3；
B. the wicker after being processed by operation a is put in the phosphoric acid solution that mass fraction is 3.5%, and heating keeps solution temperature to be 50
DEG C, immersion treatment 15min, put it in the hydrofluoric acid solution that mass fraction is 5% after taking-up, heating holding solution temperature is
65 DEG C, immersion treatment 15min, put it in the sulfuric acid solution that mass fraction is 6% after taking-up, heating holding solution temperature is
70 DEG C, immersion treatment 15min, to put in the sodium hydroxide solution that mass fraction is 8% after taking-up, heating holding solution temperature is
75 DEG C, immersion treatment 15min, rinse well standby after finally taking out with clear water；
C. will operation b process after wicker put into bating liquor dries after immersion treatment 2h standby；Described bating liquor is by weighing as follows
The material composition of amount part: 1 part of potassium peroxydisulfate, 3 parts of soybean oils, 1.5 parts of butyl acrylate, 2 parts of sodium benzoate, 1.5 parts of epoxies change
Property silicone oil, 50 parts of water；First wicker is carried out multiple high temp high pressure, enzymolysis processing, can the overall organizational structure of loose wicker, and energy
Form tiny gap at wicker shallow-layer enzymolysis, and do not interfere with overall intensity, i.e. improve its pliability and bating effect,
It is beneficial to again the process of subsequent step, the most again it is carried out repeatedly, different classes of acid-alkali treatment, can effectively reduce in wicker
Content of ashes, the dependence composition of the funguses such as the content of ashes in wicker is about 2%, this type of material trichoderma just existence, so
Reduce the viable conditions of the funguses such as trichoderma, improve the insect protected of wicker, fungicidal properties；
(3) wicker braiding:
Wicker after step (2) sofening treatment is woven, after braiding, obtains semi-finished product for standby；
(4) hardness processes:
A. after step (3) being woven, the semi-finished product of gained soak in complex liquid, and heating keeps the temperature of complex liquid to be 55 DEG C, leaching
Bubble takes out after processing 1h, standby after rinsing well with clear water；Described complex liquid is made up of the material of following weight portion: 4 parts of diformazans
Ethylethanolamine, 5 parts of ethyl acetates, 3 parts of propylene glycol alginates, 8 parts of polyvinyl alcohol, 5 parts of Folium Artemisiae Argyi extracts, 100 parts of water；
B. will operation a process after semi-finished product put into dry under conditions of temperature is 48 ~ 50 DEG C to water content be 13 ~ 16%, then
Putting it into cold preservation 1h in the household freezer that temperature is-8 ~-5 DEG C, keeping the relative humidity in household freezer is 20 ~ 30%, takes after cold preservation
Go out nature and rise to room temperature, put it into the most again and household freezer is circulated operation, amount to after operating 3 times, get product.
Further, the time that step (3) weaves is within 2 days.
Further, step (4) described Folium Artemisiae Argyi extract is the water extract of Folium Artemisiae Argyi.
There is advantages that
(1) with complex liquid, semi-finished product wicker products is processed, utilize the effective ingredient in complex liquid and the material in wicker
Carry out combination reaction, be filled with gap during sofening treatment, enhance intensity and wear resistence, the Folium Artemisiae Argyi extract of interpolation of entirety
Can assist to improve the Vermins-proof mildew-proof characteristic of wicker further.
(2) the semi-finished product wicker products after processing complex liquid carries out repeatedly the warm change of " room temperature low temperature " and processes, and can increase
Strong organizational structure wicker within, beneficially complex liquid effective ingredient and wicker further combined with, while improve the most very well
The case hardness of wicker products, enhances the Vermins-proof mildew-proof characteristic of wicker from another point of view.
(3) collocation of the inventive method each step is scientific and reasonable, and the wicker products insect protected, the anti-mold effect that prepare are preferable, surface
Hardness is higher, and compared with prior art, its case hardness can improve can prolong the service life under about 25%, normal service condition
Long about 30%, service life under high humidity conditions can extend more than 50%, and stability in use is preferable, and anti-deformation ability is relatively
By force, corrosion resistance and good, use value is higher.
Detailed description of the invention
Embodiment 1
A kind of method improving wicker products hardness, comprises the steps:
(1) wicker peeling: harvested wicker is carried out peeling operation, then puts it into the salt solution that mass fraction is 3%
Middle soaking and washing 20min, standby after being placed under the sun dry in the sun with clear water after being finally drawn off rinsing well 2 days；
(2) sofening treatment:
A. the wicker after dry in the sun is put into temperature be 145 DEG C, pressure be 5.8MPa, relative humidity be 73 ~ 75% vapor tight tank in,
It is promptly restored to the state of normal temperature and pressure after heat-insulation pressure keeping 1h, puts into after taking-up and fill the compound enzyme aqueous solution that mass fraction is 3%
In, keeping aqueous temperature is 42 DEG C, puts it in vapor tight tank again, carry out by above-mentioned parameter condition after soaking enzymolysis 10min
Processing, this is a circulation, amounts to circulation operation 3 times；Containing cellulase, tannase, pectase in described compound enzyme,
The weight ratio of three is 6:2:3；
B. the wicker after being processed by operation a is put in the phosphoric acid solution that mass fraction is 3.5%, and heating keeps solution temperature to be 50
DEG C, immersion treatment 15min, put it in the hydrofluoric acid solution that mass fraction is 5% after taking-up, heating holding solution temperature is
65 DEG C, immersion treatment 15min, put it in the sulfuric acid solution that mass fraction is 6% after taking-up, heating holding solution temperature is
70 DEG C, immersion treatment 15min, to put in the sodium hydroxide solution that mass fraction is 8% after taking-up, heating holding solution temperature is
75 DEG C, immersion treatment 15min, rinse well standby after finally taking out with clear water；
C. will operation b process after wicker put into bating liquor dries after immersion treatment 2h standby；Described bating liquor is by weighing as follows
The material composition of amount part: 1 part of potassium peroxydisulfate, 3 parts of soybean oils, 1.5 parts of butyl acrylate, 2 parts of sodium benzoate, 1.5 parts of epoxies change
Property silicone oil, 50 parts of water；
(3) wicker braiding:
Wicker after step (2) sofening treatment is woven, after braiding, obtains semi-finished product for standby；
(4) hardness processes:
A. after step (3) being woven, the semi-finished product of gained soak in complex liquid, and heating keeps the temperature of complex liquid to be 55 DEG C, leaching
Bubble takes out after processing 1h, standby after rinsing well with clear water；Described complex liquid is made up of the material of following weight portion: 4 parts of diformazans
Ethylethanolamine, 5 parts of ethyl acetates, 3 parts of propylene glycol alginates, 8 parts of polyvinyl alcohol, 5 parts of Folium Artemisiae Argyi extracts, 100 parts of water；
B. will operation a process after semi-finished product put into dry under conditions of temperature is 50 DEG C to water content be 15 ~ 16%, then will
It puts into cold preservation 1h in the household freezer that temperature is-7 DEG C, and keeping the relative humidity in household freezer is 27 ~ 30%, takes out certainly after cold preservation
So rise to room temperature, put it into the most again in household freezer and be circulated operation, amount to after operating 3 times, get product.
Further, the time that step (3) weaves is within 2 days.
Further, step (4) described Folium Artemisiae Argyi extract is the water extract of Folium Artemisiae Argyi.
Comparative example 1
Wicker products compared with Example 1, when editorial afterword processes, is not carried out " household freezer room temperature " by this comparative example 1
Repeatedly " room temperature low temperature " temperature change process, only will put into dry under conditions of temperature is 50 DEG C to water content be 15 ~ 16%,
Method step in addition is the most identical.
Matched group
Existing wicker products processing method.
In order to contrast using effect of the present invention, will process by above-mentioned three kinds of methods respectively with a collection of wicker product, enter
The humidity mycete test experiments that row is special, specific as follows: the wicker products after processing is respectively put in proof box, Control experiment
Temperature in case is 30 DEG C, normal pressure, and relative humidity is 95%, is inoculated with Trichoderma viride, aspergillus niger, aspergillus terreus, reddish brown in proof box
Mould and the white rake teeth bacterium of Malachitum, statistics by fungal infection area by 5% time total duration of being experienced, represent with mildew-resistant duration, weigh
Anti-mold effect；The case hardness of the wicker products after processing above-mentioned three kinds of methods is tested, and following table is the right of two experiments
Than data:
Table 1
| Embodiment 1 | Comparative example 1 | Matched group | |
| Mildew-resistant duration (my god) | 125 | 100 | 63 |
| Case hardness | 4H | 3H | 2H |
Claims (3)
1. the method improving wicker products hardness, it is characterised in that comprise the steps:
(1) wicker peeling: harvested wicker is carried out peeling operation, then puts it into the salt solution that mass fraction is 3%
Middle soaking and washing 20min, standby after being placed under the sun dry in the sun with clear water after being finally drawn off rinsing well 1 ~ 2 day；
(2) sofening treatment:
A. the wicker after dry in the sun is put into temperature be 140 ~ 150 DEG C, pressure be 5.5 ~ 6.5MPa, relative humidity be 70 ~ 75% close
Close in tank, after heat-insulation pressure keeping 1h, be promptly restored to the state of normal temperature and pressure, put into after taking-up fill mass fraction be 3% compound
In enzyme aqueous solution, keeping aqueous temperature is 38 ~ 42 DEG C, puts it in vapor tight tank, by above-mentioned ginseng after soaking enzymolysis 10min again
Said conditions processes, and this is a circulation, amounts to circulation operation 3 times；Containing cellulase, tannin in described compound enzyme
Enzyme, pectase, the weight ratio of three is 6:2:3；
B. the wicker after being processed by operation a is put in the phosphoric acid solution that mass fraction is 3.5%, and heating keeps solution temperature to be 50
DEG C, immersion treatment 15min, put it in the hydrofluoric acid solution that mass fraction is 5% after taking-up, heating holding solution temperature is
65 DEG C, immersion treatment 15min, put it in the sulfuric acid solution that mass fraction is 6% after taking-up, heating holding solution temperature is
70 DEG C, immersion treatment 15min, to put in the sodium hydroxide solution that mass fraction is 8% after taking-up, heating holding solution temperature is
75 DEG C, immersion treatment 15min, rinse well standby after finally taking out with clear water；
C. will operation b process after wicker put into bating liquor dries after immersion treatment 2h standby；Described bating liquor is by weighing as follows
The material composition of amount part: 1 part of potassium peroxydisulfate, 3 parts of soybean oils, 1.5 parts of butyl acrylate, 2 parts of sodium benzoate, 1.5 parts of epoxies change
Property silicone oil, 50 parts of water；
(3) wicker braiding:
Wicker after step (2) sofening treatment is woven, after braiding, obtains semi-finished product for standby；
(4) hardness processes:
A. after step (3) being woven, the semi-finished product of gained soak in complex liquid, and heating keeps the temperature of complex liquid to be 55 DEG C, leaching
Bubble takes out after processing 1h, standby after rinsing well with clear water；Described complex liquid is made up of the material of following weight portion: 4 parts of diformazans
Ethylethanolamine, 5 parts of ethyl acetates, 3 parts of propylene glycol alginates, 8 parts of polyvinyl alcohol, 5 parts of Folium Artemisiae Argyi extracts, 100 parts of water；
B. will operation a process after semi-finished product put into dry under conditions of temperature is 48 ~ 50 DEG C to water content be 13 ~ 16%, then
Putting it into cold preservation 1h in the household freezer that temperature is-8 ~-5 DEG C, keeping the relative humidity in household freezer is 20 ~ 30%, takes after cold preservation
Go out nature and rise to room temperature, put it into the most again and household freezer is circulated operation, amount to after operating 3 times, get product.
A kind of method improving wicker products hardness the most according to claim 1, it is characterised in that step (3) weaves
Time is within 2 days.
A kind of method improving wicker products hardness the most according to claim 1, it is characterised in that step (4) described Chinese mugwort
Leaf extract is the water extract of Folium Artemisiae Argyi.