CN106149368A - 一种针织面料的中草药抗菌整理工艺 - Google Patents
一种针织面料的中草药抗菌整理工艺 Download PDFInfo
- Publication number
- CN106149368A CN106149368A CN201610536023.3A CN201610536023A CN106149368A CN 106149368 A CN106149368 A CN 106149368A CN 201610536023 A CN201610536023 A CN 201610536023A CN 106149368 A CN106149368 A CN 106149368A
- Authority
- CN
- China
- Prior art keywords
- chinese herbal
- knitting fabric
- herbal antibacterial
- knitting
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开提供一种针织面料的中草药抗菌整理工艺，将抗菌纤维作为经线与纬线进行织造和染色得到抗菌针织面料，将抗菌针织面料浸泡在中草药抗菌液中进行抗菌预处理，阶梯法升温浸泡；将抗菌整理液涂覆在针织面料的表面，然后烘干成型后烘焙交联，抗菌整理液由活性银离子抗菌液、涂层剂和添加剂混合制成；将针织面料放入清洗溶液中进行清洗；在抗菌针织面料层上涂覆一层储汗速干层，所述储汗速干层为聚酯涂层；依次进行脱水、松式烘干、拉幅定形和检验。本发明对针织面料进行抗菌处理从而实现抗菌功能的持久性，抗菌效果好，在抗菌针织面料层上涂覆一层聚酯涂层同时还有速干的效用，舒适性和透气性较好。
Description
技术领域
本发明涉及一种针织面料的中草药抗菌整理工艺。
背景技术
近年来，随着人们生活水平的不断提高，人们对穿着的要求也逐渐多样化，消费者对针织内衣有也有更高的要求，不仅要穿着舒适，还用透气性好，吸汗，有保健抗菌性能，环保型、绿色健康面料的内衣越来越受消费者的青睐，中草药抗菌整理针织面料正是顺应了这种时代的需求。然而目前，对于针织面料的抗静电性能研究己经有了初步的成果，但对于其抗菌、抗病毒处理的研究还处于萌芽阶段，因此，开发抗菌纺织品来阻止和切断各种细菌的传播，并且保持身体的干燥度，避免温湿的皮肤成为细菌繁殖、培养的场所成为目前的研究热点。
发明内容
针对上述现有技术存在的问题，本发明提供了一种针织面料的中草药抗菌整理工艺，对针织面料进行抗菌处理从而实现抗菌功能的持久性，抗菌效果好，同时还有速干的效用，舒适性和透气性较好。
为了实现上述目的，本发明采用的技术方案是：
一种针织面料的中草药抗菌整理工艺，包括以下步骤：
步骤（1）：将抗菌纤维作为经线与纬线进行织造和染色得到抗菌针织面料，将抗菌针织面料浸泡在中草药抗菌液中进行抗菌预处理，阶梯法升温浸泡；
步骤（2）：二次抗菌处理，将抗菌整理液涂覆在针织面料的表面，然后烘干成型后烘焙交联，抗菌整理液由活性银离子抗菌液、涂层剂和添加剂混合制成；
步骤（3）：还原清洗处理，将针织面料放入清洗溶液中进行清洗；
步骤（4）：在抗菌针织面料层上涂覆一层储汗速干层，所述储汗速干层为聚酯涂层（不易起球和老化）；
步骤（5）：依次进行脱水、松式烘干、拉幅定形和检验。
优选的是，所述步骤（1）中的抗菌纤维的为竹纤维、木纤维、草本植物纤维、竹炭纤维、玉米纤维、牛奶纤维、大豆蛋白纤维、棉纤维、绿茶纤维中的至少一种。
上述任一方案优选的是，所述步骤（1）中的抗菌纤维中包含纤维总重量的0.012~0.06‰的二氧化钛粉末。
上述任一方案优选的是，所述步骤（1）中的中草药抗菌液由中草药抗菌原液稀释后获得，中草药抗菌原液是从天然药用植物：穿心莲、白头翁、茶叶、金银花、蒲公英、木芙蓉、三颗针、桔梗中采用CO2萃取法提取，各组成的重量比为：穿心莲10％～15％、白头翁8％～15％、茶叶20％～25％、金银花10％～25％、蒲公英10％～15％、木芙蓉10％～18％、三颗针10％～16％、桔梗10％～15％。
上述任一方案优选的是，穿心莲、白头翁、茶叶、金银花、蒲公英、木芙蓉、三颗针、桔梗各组成的重量比为：穿心莲11％、白头翁 10％、茶叶21％、金银花14％、蒲公英11％、木芙蓉12％、三颗针11％、桔梗10％。
上述任一方案优选的是，所述步骤（1）中的中草药抗菌液由中草药抗菌原液和水按照1：200-1200的比例稀释后获得。
上述任一方案优选的是，所述步骤（4）中的聚酯涂层的厚度为0.03~0.18mm。
上述任一方案优选的是，所述步骤（1）中阶梯法升温浸泡的具体操作为升温至35-55℃，浸泡1-2小时，然后再升温至65-85℃，浸泡2-3小时。
上述任一方案优选的是，所述步骤（2）中烘干成型在65-85℃的温度下，烘干时间为3-5分钟，烘焙交联在110-145℃的温度下进行，时间为6-8分钟。
本发明的有益效果是：对针织面料进行抗菌处理从而实现抗菌功能的持久性，抗菌效果好，在抗菌针织面料层上涂覆一层聚酯涂层同时还有速干的效用，舒适性和透气性较好。
具体实施方式
实施例一：
一种针织面料的中草药抗菌整理工艺，包括以下步骤：
步骤（1）：将抗菌纤维作为经线与纬线进行织造和染色得到抗菌针织面料，将抗菌针织面料浸泡在中草药抗菌液中进行抗菌预处理，阶梯法升温浸泡。抗菌纤维中包含纤维总重量的0.012的二氧化钛粉末。中草药抗菌液由中草药抗菌原液稀释后获得，中草药抗菌原液是从天然药用植物：穿心莲、白头翁、茶叶、金银花、蒲公英、木芙蓉、三颗针、桔梗中采用CO2萃取法提取，各组成的重量比为：穿心莲11％、白头翁 10％、茶叶21％、金银花14％、蒲公英11％、木芙蓉12％、三颗针11％、桔梗10％。中草药抗菌液由中草药抗菌原液和水按照1：200的比例稀释后获得。阶梯法升温浸泡的具体操作为升温至35℃，浸泡1小时，然后再升温至65℃，浸泡2小时；
步骤（2）：二次抗菌处理，将抗菌整理液涂覆在针织面料的表面，然后烘干成型后烘焙交联，抗菌整理液由活性银离子抗菌液、涂层剂和添加剂混合制成。烘干成型在65℃的温度下，烘干时间为3分钟，烘焙交联在110℃的温度下进行，时间为6分钟；
步骤（3）：还原清洗处理，将针织面料放入清洗溶液中进行清洗；
步骤（4）：在抗菌针织面料层上涂覆一层储汗速干层，所述储汗速干层为聚酯涂层（不易起球和老化），聚酯涂层的厚度为0.03mm；
步骤（5）：依次进行脱水、松式烘干、拉幅定形和检验。
本发明进一步优化的技术方案是，所述步骤（1）中的抗菌纤维的为竹纤维、木纤维、草本植物纤维、竹炭纤维、玉米纤维、牛奶纤维、大豆蛋白纤维、棉纤维、绿茶纤维中的至少一种。
实施例二：
一种针织面料的中草药抗菌整理工艺，包括以下步骤：
步骤（1）：将抗菌纤维作为经线与纬线进行织造和染色得到抗菌针织面料，将抗菌针织面料浸泡在中草药抗菌液中进行抗菌预处理，阶梯法升温浸泡；抗菌纤维中包含纤维总重量的0.06‰的二氧化钛粉末。中草药抗菌液由中草药抗菌原液稀释后获得，中草药抗菌原液是从天然药用植物：穿心莲、白头翁、茶叶、金银花、蒲公英、木芙蓉、三颗针、桔梗中采用CO2萃取法提取，各组成的重量比为：穿心莲12％、白头翁 8％、茶叶22％、金银花10％、蒲公英12％、木芙蓉13％、三颗针12％、桔梗11％。中草药抗菌液由中草药抗菌原液和水按照1：1200的比例稀释后获得。阶梯法升温浸泡的具体操作为升温至55℃，浸泡2小时，然后再升温至85℃，浸泡3小时。烘干成型在5℃的温度下，烘干时间为5分钟，烘焙交联在145℃的温度下进行，时间为8分钟；
步骤（2）：二次抗菌处理，将抗菌整理液涂覆在针织面料的表面，然后烘干成型后烘焙交联，抗菌整理液由活性银离子抗菌液、涂层剂和添加剂混合制成；
步骤（3）：还原清洗处理，将针织面料放入清洗溶液中进行清洗；
步骤（4）：在抗菌针织面料层上涂覆一层储汗速干层，所述储汗速干层为聚酯涂层（不易起球和老化）；聚酯涂层的厚度为0.18mm；
步骤（5）、依次进行脱水、松式烘干、拉幅定形和检验。
步骤（1）中的抗菌纤维为竹纤维、木纤维和绿茶纤维按照同等比例混合。
实施例三：
一种针织面料的中草药抗菌整理工艺，包括以下步骤：
步骤（1）：将抗菌纤维作为经线与纬线进行织造和染色得到抗菌针织面料，将抗菌针织面料浸泡在中草药抗菌液中进行抗菌预处理，阶梯法升温浸泡；抗菌纤维中包含纤维总重量的0.03‰的二氧化钛粉末。中草药抗菌液由中草药抗菌原液稀释后获得，中草药抗菌原液是从天然药用植物：穿心莲、白头翁、茶叶、金银花、蒲公英、木芙蓉、三颗针、桔梗中采用CO2萃取法提取，各组成的重量比为：穿心莲12％、白头翁 8％、茶叶22％、金银花16％、蒲公英10％、木芙蓉11％、三颗针11％、桔梗10％。中草药抗菌液由中草药抗菌原液和水按照1：600的比例稀释后获得。中阶梯法升温浸泡的具体操作为升温至45℃，浸泡1-2小时，然后再升温至72℃，浸泡2.5小时。烘干成型在80℃的温度下，烘干时间为5分钟，烘焙交联在130℃的温度下进行，时间为8分钟；
步骤（2）：二次抗菌处理，将抗菌整理液涂覆在针织面料的表面，然后烘干成型后烘焙交联，抗菌整理液由活性银离子抗菌液、涂层剂和添加剂混合制成；
步骤（3）：还原清洗处理，将针织面料放入清洗溶液中进行清洗；
步骤（4）：在抗菌针织面料层上涂覆一层储汗速干层，所述储汗速干层为聚酯涂层（不易起球和老化）；聚酯涂层的厚度为0.12mm；
步骤（5）：依次进行脱水、松式烘干、拉幅定形和检验。
优选的是，所述步骤（1）中的抗菌纤维的为竹纤维、木纤维、草本植物纤维、竹炭纤维、玉米纤维、牛奶纤维、大豆蛋白纤维、棉纤维、绿茶纤维中的至少一种。
以上对本发明实施例所提供的技术方案进行了详细介绍，本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述，以上实施例的说明只适用于帮助理解本发明实施例的原理；同时，对于本领域的一般技术人员，依据本发明实施例，在具体实施方式以及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。
Claims (9)
1.一种针织面料的中草药抗菌整理工艺，其特征在于，包括以下步骤：
步骤（1）：将抗菌纤维作为经线与纬线进行织造和染色得到抗菌针织面料，将抗菌针织面料浸泡在中草药抗菌液中进行抗菌预处理，阶梯法升温浸泡；
步骤（2）：二次抗菌处理，将抗菌整理液涂覆在针织面料的表面，然后烘干成型后烘焙交联，抗菌整理液由活性银离子抗菌液、涂层剂和添加剂混合制成；
步骤（3）：还原清洗处理，将针织面料放入清洗溶液中进行清洗；
步骤（4）：在抗菌针织面料层上涂覆一层储汗速干层，所述储汗速干层为聚酯涂层；
步骤（5）：依次进行脱水、松式烘干、拉幅定形和检验。
2.根据权利要求1所述的一种针织面料的中草药抗菌整理工艺，其特征在于，所述步骤（1）中的抗菌纤维的为竹纤维、木纤维、草本植物纤维、竹炭纤维、玉米纤维、牛奶纤维、大豆蛋白纤维、棉纤维、绿茶纤维中的至少一种。
3.根据权利要求1-2所述的一种针织面料的中草药抗菌整理工艺，其特征在于，所述步骤（1）中的抗菌纤维中包含纤维总重量的0.012~0.06‰的二氧化钛粉末。
4.根据权利要求1所述的一种针织面料的中草药抗菌整理工艺，其特征在于：所述步骤（1）中的中草药抗菌液由中草药抗菌原液稀释后获得，中草药抗菌原液是从天然药用植物：穿心莲、白头翁、茶叶、金银花、蒲公英、木芙蓉、三颗针、桔梗中采用CO2萃取法提取，各组成的重量比为：穿心莲10％～15％、白头翁 8％～15％、茶叶20％～25％、金银花10％～25％、蒲公英10％～15％、木芙蓉10％～18％、三颗针10％～16％、桔梗10％～15％。
5.根据权利要求4所述的一种针织面料的中草药抗菌整理工艺，其特征在于：穿心莲、白头翁、茶叶、金银花、蒲公英、木芙蓉、三颗针、桔梗各组成的重量比为：穿心莲11％、白头翁 10％、茶叶21％、金银花14％、蒲公英11％、木芙蓉12％、三颗针11％、桔梗10％。
6.根据权利要求1所述的一种针织面料的中草药抗菌整理工艺，其特征在于：所述步骤（1）中的中草药抗菌液由中草药抗菌原液和水按照1：200-1200的比例稀释后获得。
7.根据权利要求1所述的一种针织面料的中草药抗菌整理工艺，其特征在于：所述步骤（4）中的聚酯涂层的厚度为0.03~0.18mm。
8.根据权利要求1所述的一种针织面料的中草药抗菌整理工艺，其特征在于：所述步骤（1）中阶梯法升温浸泡的具体操作为升温至35-55℃，浸泡1-2小时，然后再升温至65-85℃，浸泡2-3小时。
9.根据权利要求1所述的一种针织面料的中草药抗菌整理工艺，其特征在于：所述步骤（2）中烘干成型在65-85℃的温度下，烘干时间为3-5分钟，烘焙交联在110-145℃的温度下进行，时间为6-8分钟。