CN106147587B - 一种含有蓖麻油基的抗菌uv涂料及其制备方法和应用 - Google Patents
一种含有蓖麻油基的抗菌uv涂料及其制备方法和应用 Download PDFInfo
- Publication number
- CN106147587B CN106147587B CN201610553021.5A CN201610553021A CN106147587B CN 106147587 B CN106147587 B CN 106147587B CN 201610553021 A CN201610553021 A CN 201610553021A CN 106147587 B CN106147587 B CN 106147587B
- Authority
- CN
- China
- Prior art keywords
- castor oil
- base
- mass parts
- antimicrobial
- prepared
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开一种含有蓖麻油基的抗菌UV涂料，包括以下质量份数的原料组分：蓖麻油基UV固化聚氨酯丙烯酸酯32～35份、有机硅改性聚氨酯丙烯酸酯16～21份、三羟甲基丙烷三丙烯酸酯8～10份、三丙二醇二丙烯酸酯5～6份、乙酸乙酯15～16份、乙酸丁酯14～15份、聚醚改性聚硅氧烷流平剂0.4～0.6份、光引发剂2.5～3份、纳米银抗菌助剂0.95～1份。通过聚醚改性聚硅氧烷流平剂配合由蓖麻油基UV固化聚氨酯丙烯酸酯和有机硅改性聚氨酯丙烯酸酯组成的混合溶液反应而成的涂料，其流平效果好、挥发性有机物质排放少，还具有耐水性、耐低温，而且其电绝缘性和附着力更是优越，是一种综合性能优良的涂料。
Description
技术领域
本发明涉及一种涂料，特别是涉及一种含有蓖麻油基的抗菌UV涂料及其制备方法和应用。
背景技术
涂料因其用途广泛，对其性能要求也是因不同的用途而有所区别，有的要求具有高附着力、有的要求具有耐低温或高温性能、有的要求具有优越的电绝缘性、有的要求具有良好的耐水性、有的要求具有抗菌性、有的要求具有较好的流平性、有的要求挥发性有机物质排放少等等，而大多时候，需要涂料同时具备多种优良性能，而不是单一性能，但目前市面上使用的涂料绝大多数还是性能比较单一的，这就需要开发一种能同时拥有多种优良性能的全新涂料。
发明内容
本发明的目的是克服现有技术中的不足之处，本发明的首要目的在于提供一种含有蓖麻油基的抗菌UV涂料，该涂料不仅流平效果好、固化速度快、挥发性有机物质排放少，还具有抗菌性、耐水性、耐低温，而且其电绝缘性和附着力更是优越，是一种综合性能优良的涂料。
实现该目的的技术方案是：
一种含有蓖麻油基的抗菌UV涂料，由包括以下质量份数的原料组分制备而成：
更进一步的，所述含有蓖麻油基的抗菌UV涂料由包括以下质量份数的原料组分制备而成：
进一步的，所述含有蓖麻油基的抗菌UV涂料所用的蓖麻油基UV固化聚氨酯丙烯酸酯由包括以下摩尔份数的原料组分制备而成：
更进一步的，所述蓖麻油基UV固化聚氨酯丙烯酸酯由包括以下摩尔份数的原料组分制备而成：
进一步的，所述含有蓖麻油基的抗菌UV涂料所用的有机硅改性聚氨酯丙烯酸酯由包括以下质量份数的原料组分制备而成：
更进一步的，所述有机硅改性聚氨酯丙烯酸酯由包括以下质量份数的原料组分制备而成：
进一步的，所述含有蓖麻油基的抗菌UV涂料所用的聚醚改性聚硅氧烷流平剂由包括以下质量份数的原料组分制备而成：
更进一步的，所述聚醚改性聚硅氧烷流平剂由包括以下质量份数的原料组分制备而成：
本发明的目的还在于提供上述含有蓖麻油基的抗菌UV涂料的制备方法。
上述含有蓖麻油基的抗菌UV涂料的制备方法包括如下步骤：
S1、制备蓖麻油基UV固化聚氨酯丙烯酸酯：
S11、将5.5～5.8摩尔份数的聚乙二醇、1.5～2摩尔份数的聚酯二醇和1摩尔份数的蓖麻油混合搅拌均匀并升温至110～115℃，减压脱水2.5～3h后降温至72～75℃，再分别加入1摩尔份数的异氟尔酮二异氰酸酯和0.002摩尔份数的月桂酸铋催化剂，控制滴加速度在1.5h内滴完，反应2.5～3h，得到混合溶液M；
S12、将0.3摩尔份数的N，N-二甲基甲酰胺溶于2～3摩尔份数的双酚A溶剂和0.3摩尔份数的2,2-二羟甲基丙酸溶剂中再与2～3摩尔份数的丁酮混合均匀，得到混合溶液N；
S13、将通过S12步骤配置好的混合溶液N加入S11步骤配置好的混合溶液M中，继续反应，当异氰酸基团含量达到8～13％时降温至60℃，搅拌下逐滴加入2.2～2.5摩尔份数的丙烯酸羟乙酯和0.2摩尔份数的对苯二胺阻聚剂的混合溶液，在8min内加完，继续反应3h后监测异氰酸基团含量，当游离的异氰酸基团含量低于0.1％时，停止反应蒸出溶剂既得所述蓖麻油基UV固化聚氨酯丙烯酸酯；
S2、制备有机硅改性聚氨酯丙烯酸酯：
S21、将16～22质量份的烷羟基硅油和13～16质量份的丙烯酸-β-羟乙酯混合均匀，得到混合溶液P；
S22、将30～34质量份的异氟尔酮二异氰酸酯溶于4～6质量份的异丁醇溶剂中，加热至86～90℃，在通氮气的条件下逐滴加入通过S21配制好的混合溶液P，于2.5h滴完，恒温反应1.5h后升温到83～86℃，然后再加入4～6质量份的异丁醇溶剂和2～4质量份的过氧化苯甲酸叔丁酯引发剂，再恒温反应2.5h，待转化率达到99％后停止反应，在加热条件下减压抽滤出异丁醇溶剂，在搅拌条件下加入8～11质量份的水和4～7质量份的三乙醇胺，既得所述有机硅改性聚氨酯丙烯酸酯；
S3、制备聚醚改性聚硅氧烷流平剂：
S31、将28～33质量份的烯丙基聚醚溶于31～35质量份的***溶剂中，并加入2～3质量份的氯铂酸催化剂，得到混合溶液Q；
S32、将1～2质量份的氯铂酸催化剂加入32～37质量份的含氢硅油中，在通氮气的条件下搅拌，并升温至110～115℃时逐滴加入通过S31配制好的混合溶液Q，1.5h滴完，然后在110～115℃下恒温反应4.5～5h，冷却过滤既得所述聚醚改性聚硅氧烷流平剂；
S4、制备含有蓖麻油基的抗菌UV涂料：
S41、依次加入32～35质量份的通过S1制备而成的蓖麻油基UV固化聚氨酯丙烯酸酯、16～21质量份的通过S2制备而成的有机硅改性聚氨酯丙烯酸酯、8～10质量份的三羟甲基丙烷三丙烯酸酯稀释剂、5～6质量份的三丙二醇二丙烯酸酯稀释剂和15～16质量份的乙酸乙酯溶剂，在800～1000r/min下分散30min；
S42、然后加入0.4～0.6质量份的通过S3制备而成的聚醚改性聚硅氧烷流平剂和2.5～3质量份的光引发剂，在600～800r/min下分散30min；
S43、在400～500r/min下缓慢加入0.95～1质量份的纳米银抗菌助剂，继续分散30min；
S44、最后加入14～15质量份的乙酸丁酯溶剂在岩田2#杯，25℃的条件下调整粘度至20-22s，既得所述含有蓖麻油基的抗菌UV涂料。
本发明还提供上述含有蓖麻油基的抗菌UV涂料的应用。
具体的，上述含有蓖麻油基的抗菌UV涂料使用方法为：
用乙酸乙酯溶剂将所述含有蓖麻油基的抗菌UV涂料在岩田2#杯，25℃条件下稀释到9s后喷涂在塑胶素材上，控制膜厚在20～30μm，在45～50℃下烘烤3-5min，然后用能量为800-1000mj/c㎡的紫外光照射固化成膜。
与现有技术相比，本发明的优点在于：
1、蓖麻油是一种天然的可再生资源，用它代替传统的石化资源可以缓解日趋紧张的全球性石化资源危机问题，而且蓖麻油的使用不会给环境造成污染，不会给企业造成环保治理的成本压力；
2、采用双酚A溶剂和异氟尔酮二异氰酸酯同时配合蓖麻油合成蓖麻油基UV固化聚氨酯丙烯酸酯，合成的蓖麻油基UV固化聚氨酯丙烯酸酯不仅具有优良的耐水性、耐低温、固化速度快而且其电绝缘性和附着力更是优越；
3、采用异氟尔酮二异氰酸酯、烷羟基硅油和丙烯酸-β-羟乙酯作为主要原料在异丁醇溶剂下合成的有机硅改性聚氨酯丙烯酸酯属于水性材料，对环境污染小，几乎不产生对人体有害的挥发性物质，其他溶剂则达不到如此优良效果，其与184光引发剂的配合杜绝了其本身固化时间长的缺点；
4、采用***作为溶剂，将含氢硅油和烯丙基聚醚在氯铂酸催化剂的催化下合成的聚醚改性聚硅氧烷流平剂具有良好的低表面张力和相容性，其表面状态控制能力优越，其它溶剂和催化剂的配合得到的聚醚改性聚硅氧烷流平剂却不能达到如此效果；
5、通过聚醚改性聚硅氧烷流平剂配合由蓖麻油基UV固化聚氨酯丙烯酸酯和有机硅改性聚氨酯丙烯酸酯按一定比例配比而成的混合溶液聚合出的涂料，其流平效果好、挥发性有机物质排放少，还具有耐水性、耐低温，而且其电绝缘性和附着力更是优越，是一种综合性能优良的涂料；
6、通过加入纳米银抗菌助剂，使得制备出的含有蓖麻油基的抗菌UV涂料同时具有优良的抗菌作用。
附图说明
无。
具体实施方式
下面结合实施例对本发明作进一步详细的描述，但本发明的实施方式不限于此。
实施例1
传统抗菌光固化涂料的制备方法：
①依次加入51g的水性聚氨酯丙烯酸酯、10g的三羟甲基丙烷三丙烯酸酯稀释剂、8g的三丙二醇二丙烯酸酯稀释剂和14g的乙酸乙酯溶剂，在1000r/min下分散30min；
②然后加入0.5g的丙烯酸树脂流平剂和2.5g的光引发剂，在800r/min下分散30min；
③在400r/min下缓慢加入2g的纳米银抗菌助剂，继续分散30min；
④最后加入12g的乙酸丁酯溶剂在岩田2#杯，25℃条件下调整粘度至20s，既得传统抗菌光固化涂料。
实施例2
一种含有蓖麻油基的抗菌UV涂料，其由以下组分配比及制备方法制备而成：
S1、制备蓖麻油基UV固化聚氨酯丙烯酸酯：
S11、将5.8mol的聚乙二醇、1.5mol的聚酯二醇和1mol的蓖麻油混合搅拌均匀并升温至115℃，减压脱水2.5h后降温至75℃，再分别加入1mol的异氟尔酮二异氰酸酯和0.002mol的月桂酸铋催化剂，控制滴加速度在1.5h内滴完，反应3h，得到混合溶液M；
S12、将0.3mol的N，N-二甲基甲酰胺溶于2mol的双酚A溶剂和0.3mol的2,2-二羟甲基丙酸溶剂中再与3mol的丁酮混合均匀,得到混合溶液N；
S13、将通过S12步骤配置好的混合溶液N加入S11步骤配置好的混合溶液M中，继续反应，当异氰酸基团含量达到8％时降温至60℃，搅拌下逐滴加入2.5mol的丙烯酸羟乙酯和0.2mol的对苯二胺阻聚剂的混合溶液，在8min内加完，继续反应3h后监测异氰酸基团含量，当游离的异氰酸基团含量低于0.1％时，停止反应蒸出溶剂既得所述蓖麻油基UV固化聚氨酯丙烯酸酯；
S2、制备有机硅改性聚氨酯丙烯酸酯：
S21、将16g的烷羟基硅油和13g的丙烯酸-β-羟乙酯混合均匀，得到混合溶液P；
S22、将34g的异氟尔酮二异氰酸酯溶于6g的异丁醇溶剂中，加热至86℃，在通氮气的条件下逐滴加入通过S21配制好的混合溶液P，于2.5h滴完，恒温反应1.5h后升温到86℃，然后再加入6g的异丁醇溶剂和4g的过氧化苯甲酸叔丁酯引发剂，再恒温反应2.5h，待转化率达到99％后停止反应，在加热条件下减压抽滤出异丁醇溶剂，在搅拌条件下加入8g的水和4g的三乙醇胺，既得所述有机硅改性聚氨酯丙烯酸酯；
S3、制备聚醚改性聚硅氧烷流平剂：
S31、将33g的烯丙基聚醚溶于35g的***溶剂中，并加入3g的氯铂酸催化剂，得到混合溶液Q；
S32、将1g的氯铂酸催化剂加入32g的含氢硅油中，在通氮气的条件下搅拌，并升温至110℃时逐滴加入通过S31配制好的混合溶液Q，1.5h滴完，然后在110℃下恒温反应4.5h，冷却过滤既得所述聚醚改性聚硅氧烷流平剂；
S4、制备含有蓖麻油基的抗菌UV涂料：
S41、依次加入32g的通过S1制备而成的蓖麻油基UV固化聚氨酯丙烯酸酯、21g的通过S2制备而成的有机硅改性聚氨酯丙烯酸酯、10g的三羟甲基丙烷三丙烯酸酯稀释剂、6g的三丙二醇二丙烯酸酯稀释剂和16g的乙酸乙酯溶剂，在800r/min下分散30min；
S42、然后加入0.4g的通过S3制备而成的聚醚改性聚硅氧烷流平剂和3g的184光引发剂，在600r/min下分散30min；
S43、在500r/min下缓慢加入0.95g的纳米银抗菌助剂，继续分散30min；
S44、最后加入15g的乙酸丁酯溶剂在岩田2#杯，25℃条件下调整粘度至20s，既得所述含有蓖麻油基的抗菌UV涂料。
实施例3
一种含有蓖麻油基的抗菌UV涂料，其由以下组分配比及制备方法制备而成：
S1、制备蓖麻油基UV固化聚氨酯丙烯酸酯：
S11、将5.5mol的聚乙二醇、2mol的聚酯二醇和1mol的蓖麻油混合搅拌均匀并升温至110℃，减压脱水3h后降温至72℃，再分别加入1mol的异氟尔酮二异氰酸酯和0.002mol的月桂酸铋催化剂，控制滴加速度在1.5h内滴完，反应2.5h，得到混合溶液M；
S12、将0.3mol的N，N-二甲基甲酰胺溶于3mol的双酚A溶剂和0.3mol的2,2-二羟甲基丙酸溶剂中再与2mol的丁酮混合均匀,得到混合溶液N；
S13、将通过S12步骤配置好的混合溶液N加入S11步骤配置好的混合溶液M中，继续反应，当异氰酸基团含量达到13％时降温至60℃，搅拌下逐滴加入2.2mol的丙烯酸羟乙酯和0.2mol的对苯二胺阻聚剂的混合溶液，在8min内加完，继续反应3h后监测异氰酸基团含量，当游离的异氰酸基团含量低于0.1％时，停止反应蒸出溶剂既得所述蓖麻油基UV固化聚氨酯丙烯酸酯；
S2、制备有机硅改性聚氨酯丙烯酸酯：
S21、将22g的烷羟基硅油和16g的丙烯酸-β-羟乙酯混合均匀，得到混合溶液P；
S22、将30g的异氟尔酮二异氰酸酯溶于4g的异丁醇溶剂中，加热至90℃，在通氮气的条件下逐滴加入通过S21配制好的混合溶液P，于2.5h滴完，恒温反应1.5h后升温到83℃，然后再加入4g的异丁醇溶剂和2g的过氧化苯甲酸叔丁酯引发剂，再恒温反应2.5h，待转化率达到99％后停止反应，在加热条件下减压抽滤出异丁醇溶剂，在搅拌条件下加入11g的水和7g的三乙醇胺，既得所述有机硅改性聚氨酯丙烯酸酯；
S3、制备聚醚改性聚硅氧烷流平剂：
S31、将28g的烯丙基聚醚溶于31g的***溶剂中，并加入2g的氯铂酸催化剂，得到混合溶液Q；
S32、将2g的氯铂酸催化剂加入37g的含氢硅油中，在通氮气的条件下搅拌，并升温至115℃时逐滴加入通过S31配制好的混合溶液Q，1.5h滴完，然后在115℃下恒温反应5h，冷却过滤既得所述聚醚改性聚硅氧烷流平剂；
S4、制备含有蓖麻油基的抗菌UV涂料：
S41、依次加入35g的通过S1制备而成的蓖麻油基UV固化聚氨酯丙烯酸酯、16g的通过S2制备而成的有机硅改性聚氨酯丙烯酸酯、8g的三羟甲基丙烷三丙烯酸酯稀释剂、5g的三丙二醇二丙烯酸酯稀释剂和15g的乙酸乙酯溶剂，在1000r/min下分散30min；
S42、然后加入0.6g的通过S3制备而成的聚醚改性聚硅氧烷流平剂和2.5g的184光引发剂，在800r/min下分散30min；
S43、在400r/min下缓慢加入1g的纳米银抗菌助剂，继续分散30min；
S44、最后加入14g的乙酸丁酯溶剂在岩田2#杯，25℃条件下调整粘度至22s，既得所述含有蓖麻油基的抗菌UV涂料。
实施例4
一种含有蓖麻油基的抗菌UV涂料，其由以下组分配比及制备方法制备而成：
S1、制备蓖麻油基UV固化聚氨酯丙烯酸酯：
S11、将5.8mol的聚乙二醇、1.5mol的聚酯二醇和1mol的蓖麻油混合搅拌均匀并升温至115℃，减压脱水3h后降温至75℃，再分别加入1Mol的异氟尔酮二异氰酸酯和0.002mol的月桂酸铋催化剂，控制滴加速度在1.5h内滴完，反应3h，得到混合溶液M；
S12、将0.3mol的N，N-二甲基甲酰胺溶于2mol的双酚A溶剂和0.3mol的2,2-二羟甲基丙酸溶剂中再与2mol的丁酮混合均匀,得到混合溶液N；
S13、将通过S12步骤配置好的混合溶液N加入S11步骤配置好的混合溶液M中，继续反应，当异氰酸基团含量达到13％时降温至60℃，搅拌下逐滴加入2.5mol的丙烯酸羟乙酯和0.2mol的对苯二胺阻聚剂的混合溶液，在8min内加完，继续反应3h后监测异氰酸基团含量，当游离的异氰酸基团含量低于0.1％时，停止反应蒸出溶剂既得所述蓖麻油基UV固化聚氨酯丙烯酸酯；
S2、制备有机硅改性聚氨酯丙烯酸酯：
S21、将19g的烷羟基硅油和16g的丙烯酸-β-羟乙酯混合均匀，得到混合溶液P；
S22、将33g的异氟尔酮二异氰酸酯溶于6g的异丁醇溶剂中，加热至90℃，在通氮气的条件下逐滴加入通过S21配制好的混合溶液P，于2.5h滴完，恒温反应1.5h后升温到86℃，然后再加入6g的异丁醇溶剂和4g的过氧化苯甲酸叔丁酯引发剂，再恒温反应2.5h，待转化率达到99％后停止反应，在加热条件下减压抽滤出异丁醇溶剂，在搅拌条件下加入10g的水和6g的三乙醇胺，既得所述有机硅改性聚氨酯丙烯酸酯；
S3、制备聚醚改性聚硅氧烷流平剂：
S31、将30g的烯丙基聚醚溶于33g的***溶剂中，并加入3g的氯铂酸催化剂，得到混合溶液Q；
S32、将2g的氯铂酸催化剂加入32g的含氢硅油中，在通氮气的条件下搅拌，并升温至115℃时逐滴加入通过S31配制好的混合溶液Q，1.5h滴完，然后在115℃下恒温反应5h，冷却过滤既得所述聚醚改性聚硅氧烷流平剂；
S4、制备含有蓖麻油基的抗菌UV涂料：
S41、依次加入34g通过S1制备而成的蓖麻油基UV固化聚氨酯丙烯酸酯、19g通过S2制备而成的有机硅改性聚氨酯丙烯酸酯、9g三羟甲基丙烷三丙烯酸酯稀释剂、5g三丙二醇二丙烯酸酯稀释剂和15g乙酸乙酯溶剂，在1000r/min下分散30min；
S42、然后加入0.5g通过S3制备而成的聚醚改性聚硅氧烷流平剂和2.5g184光引发剂，在800r/min下分散30min；
S43、在500r/min下缓慢加入1g纳米银抗菌助剂，继续分散30min；
S44、最后加入14g的乙酸丁酯溶剂在岩田2#杯，25℃条件下调整粘度至22s，既得所述含有蓖麻油基的抗菌UV涂料。
所述含有蓖麻油基的抗菌UV涂料的使用方法为：
用乙酸乙酯溶剂在岩田2#杯，25℃的条件下将所述一种含有蓖麻油基的抗菌UV涂料稀释到粘度为9s后喷涂在塑胶素材上，控制膜厚在20～30μm，在45～50℃下烘烤3-5min，然后用能量为800-1000mj/c㎡的紫外光照射固化成膜。
通过常规测试方法分别对实施例1至4制备出的涂料进行测试，测试结果见下表：
上述实施例为本发明较佳的实施方式，但本发明的实施方式并不受上述实施例的限制，其他的任何未背离本发明的精神实质与原理下所作的改变、修饰、替代、组合、简化，均应为等效的置换方式，都包含在本发明的保护范围之内。
Claims (7)
1.一种含有蓖麻油基的抗菌UV涂料，其特征在于，由包括以下质量份数的原料组分制备而成：
所述蓖麻油基UV固化聚氨酯丙烯酸酯由包括以下摩尔份数的原料组分制备而成：
所述有机硅改性聚氨酯丙烯酸酯由包括以下质量份数的原料组分制备而成：
所述聚醚改性聚硅氧烷流平剂由包括以下质量份数的原料组分制备而成：
2.根据权利要求1所述一种含有蓖麻油基的抗菌UV涂料，其特征在于，由包括以下质量份数的原料组分制备而成：
3.根据权利要求1所述一种含有蓖麻油基的抗菌UV涂料，其特征在于，所述蓖麻油基UV固化聚氨酯丙烯酸酯由包括以下摩尔份数的原料组分制备而成：
4.根据权利要求1所述一种含有蓖麻油基的抗菌UV涂料，其特征在于，所述有机硅改性聚氨酯丙烯酸酯由包括以下质量份数的原料组分制备而成：
5.根据权利要求1所述一种含有蓖麻油基的抗菌UV涂料，其特征在于，所述聚醚改性聚硅氧烷流平剂由包括以下质量份数的原料组分制备而成：
6.根据权利要求1所述一种含有蓖麻油基的抗菌UV涂料的制备方法为：
S1、制备蓖麻油基UV固化聚氨酯丙烯酸酯：
S11、将5.5～5.8摩尔份数的聚乙二醇、1.5～2摩尔份数的聚酯二醇和1摩尔份数的蓖麻油混合搅拌均匀并升温至110～115℃，减压脱水2.5～3h后降温至72～75℃，再分别加入1摩尔份数的异氟尔酮二异氰酸酯和0.002摩尔份数的月桂酸铋催化剂，控制滴加速度在1.5h内滴完，反应2.5～3h，得到混合溶液M；
S12、将0.3摩尔份数的N，N-二甲基甲酰胺溶于2～3摩尔份数的双酚A溶剂和0.3摩尔份数的2,2-二羟甲基丙酸溶剂中再与2～3摩尔份数的丁酮混合均匀，得到混合溶液N；
S13、将通过S12步骤配置好的混合溶液N加入S11步骤配置好的混合溶液M中，继续反应，当异氰酸基团含量达到8～13％时降温至60℃，搅拌下逐滴加入2.2～2.5摩尔份数的丙烯酸羟乙酯和0.2摩尔份数的对苯二胺阻聚剂的混合溶液，在8min内加完，继续反应3h后监测异氰酸基团含量，当游离的异氰酸基团含量低于0.1％时，停止反应蒸出溶剂即 得所述蓖麻油基UV固化聚氨酯丙烯酸酯；
S2、制备有机硅改性聚氨酯丙烯酸酯：
S21、将16～22质量份的烷羟基硅油和13～16质量份的丙烯酸-β-羟乙酯混合均匀，得到混合溶液P；
S22、将30～34质量份的异氟尔酮二异氰酸酯溶于4～6质量份的异丁醇溶剂中，加热至86～90℃，在通氮气的条件下逐滴加入通过S21配制好的混合溶液P，于2.5h滴完，恒温反应1.5h后升温到83～86℃，然后再加入4～6质量份的异丁醇溶剂和2～4质量份的过氧化苯甲酸叔丁酯引发剂，再恒温反应2.5h，待转化率达到99％后停止反应，在加热条件下减压抽滤出异丁醇溶剂，在搅拌条件下加入8～11质量份的水和4～7质量份的三乙醇胺，即 得所述有机硅改性聚氨酯丙烯酸酯；
S3、制备聚醚改性聚硅氧烷流平剂：
S31、将28～33质量份的烯丙基聚醚溶于31～35质量份的***溶剂中，并加入2～3质量份的氯铂酸催化剂，得到混合溶液Q；
S32、将1～2质量份的氯铂酸催化剂加入32～37质量份的含氢硅油中，在通氮气的条件下搅拌，并升温至110～115℃时逐滴加入通过S31配制好的混合溶液Q，1.5h滴完，然后在110～115℃下恒温反应4.5～5h，冷却过滤即 得所述聚醚改性聚硅氧烷流平剂；
S4、制备含有蓖麻油基的抗菌UV涂料：
S41、依次加入32～35质量份的通过S1制备而成的蓖麻油基UV固化聚氨酯丙烯酸酯、16～21质量份的通过S2制备而成的有机硅改性聚氨酯丙烯酸酯、8～10质量份的三羟甲基丙烷三丙烯酸酯稀释剂、5～6质量份的三丙二醇二丙烯酸酯稀释剂和15～16质量份的乙酸乙酯溶剂，在800～1000r/min下分散30min；
S42、然后加入0.4～0.6质量份的通过S3制备而成的聚醚改性聚硅氧烷流平剂和2.5～3质量份的光引发剂，在600～800r/min下分散30min；
S43、在400～500r/min下缓慢加入0.95～1质量份的纳米银抗菌助剂，继续分散30min；
S44、最后加入14～15质量份的乙酸丁酯溶剂在岩田2#杯，25℃的条件下调整粘度至20-22s，即得所述含有蓖麻油基的抗菌UV涂料。
7.根据权利要求1至5任一项所述一种含有蓖麻油基的抗菌UV涂料的使用方法为：用乙酸乙酯在岩田2#杯，25℃的条件下将所述含有蓖麻油基的抗菌UV涂料稀释到粘度为9s后喷涂在塑胶素材上，控制膜厚在20～30μm，在45～50℃下烘烤3-5min，然后用能量为800-1000mJ /c㎡的紫外光照射固化成膜。