CN106147494A - 一种净化空气室内铜雕塑用环氧‑丙烯酸防腐水性漆及其制备方法 - Google Patents

一种净化空气室内铜雕塑用环氧‑丙烯酸防腐水性漆及其制备方法 Download PDF

Info

Publication number
CN106147494A
CN106147494A CN201610524519.9A CN201610524519A CN106147494A CN 106147494 A CN106147494 A CN 106147494A CN 201610524519 A CN201610524519 A CN 201610524519A CN 106147494 A CN106147494 A CN 106147494A
Authority
CN
China
Prior art keywords
water
air chamber
copper sculpture
soluble paint
alcohol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610524519.9A
Other languages
English (en)
Inventor
刘勇
安施军
薛焕刚
丁莉莉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tongling Qingtongshida Sculpture Co Ltd
Original Assignee
Tongling Qingtongshida Sculpture Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Tongling Qingtongshida Sculpture Co Ltd filed Critical Tongling Qingtongshida Sculpture Co Ltd
Priority to CN201610524519.9A priority Critical patent/CN106147494A/zh
Publication of CN106147494A publication Critical patent/CN106147494A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种净化空气室内铜雕塑用环氧‑丙烯酸防腐水性漆，其是由下述重量份的原料制得：环氧树脂E‑44 40‑60，乙二醇单丁醚10‑15，正丁醇15‑25，桉叶油0.1‑0.15，柠檬油0.1‑0.2，甲基丙烯酸6‑8，苯乙烯4‑6，丙烯酸丁酯3‑5，过氧化苯甲酰0.5‑1，N,N‑二甲酰基乙醇4‑6，二氧化钛纳米管4‑6，纳米锗0.1‑0.15，纳米电气石粉0.3‑0.5，苯丙三氮唑0.3‑0.5，γ‑巯丙基三乙氧基硅烷0.1‑0.15，海藻酸钠0.3‑0.5，水100‑120。本发明的铜雕塑水性漆既具有优良的防腐蚀性能、机械性能和持久有效性，还有净化空气的功效，有利于提高室内环境质量。

Description

一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆及其制 备方法
技术领域
本发明涉及铜雕塑用涂料技术领域，尤其涉及一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆及其制备方法。
背景技术
随着现代生活水平和审美意识的提高，雕塑这一传统工艺品受到越来越多的设计师和大众喜爱。其中铜雕塑不仅样式独特，并且具有很高的欣赏价值，与其他材质的雕塑相比，还有坚固耐用、不易破坏的特点，得到广泛的应用。铜雕塑无需频繁地保养和维修，但是在空气湿度过大的条件下使用会严重影响铜雕塑的质量。为减少腐蚀，延长铜雕塑的使用寿命，通常采取的预防性措施是对铜雕塑表面进行防护处理，其中涂刷油漆是目前使用较为广泛、经济实用的方法。
随着环保意识的增强，传统溶剂型防腐漆逐渐被淘汰，高性能、低污染的水性防腐漆已经成为发展趋势。目前应用较多的水性防腐漆主要有环氧树脂等。文献《丙烯酸接枝改性环氧树脂防腐乳液的研究》采用丙烯酸对环氧树脂进行接枝改性，得到的乳液兼具环氧树脂和丙烯酸树脂的优点，具有良好的附着力和耐腐蚀性能。但是，这种方法制得乳液的三维网状结构交联度较低，耐水性不足，对基体表面的防护不够，影响了其防腐性能，且无法应对涂装缺陷或者涂层破坏带来的防腐持久性下降，因此在实际应用中有待进一步改进。
发明内容
本发明目的就是为了弥补已有技术的缺陷，提供一种交联程度高、机械性能好、防护性能强并且具有优良持久性的净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆及其制备方法。
本发明是通过以下技术方案实现的：
一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆，其是由下述重量份的原料制得：
环氧树脂E-44 40-60，乙二醇单丁醚10-15，正丁醇15-25，桉叶油0.1-0.15，柠檬油0.1-0.2，甲基丙烯酸6-8，苯乙烯4-6，丙烯酸丁酯3-5，过氧化苯甲酰0.5-1，N,N-二甲酰基乙醇4-6，二氧化钛纳米管4-6，纳米锗0.1-0.15，纳米电气石粉0.3-0.5，苯丙三氮唑0.3-0.5，γ-巯丙基三乙氧基硅烷0.1-0.15，海藻酸钠0.3-0.5，水100-120；
所述二氧化钛纳米管是采用水热合成法制得，管径为5-25nm，管长为500-1000nm。
一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆的制备方法，包括以下步骤：
（1）将二氧化钛纳米管按固液重量比1:10-1:15与无水乙醇混合分散均匀，然后加入桉叶油、柠檬油、苯丙三氮唑和γ-巯丙基三乙氧基硅烷搅拌6-12h，离心后将所得固体真空干燥，得改性钛纳米管；
（2）将（1）中的改性钛纳米管、纳米锗、纳米电气石粉、N,N-二甲酰基乙醇和水混合分散均匀，得A组分，将环氧树脂E-44、乙二醇单丁醚和正丁醇混合升温至105-110℃，然后缓慢滴加甲基丙烯酸、苯乙烯、丙烯酸丁酯和过氧化苯甲酰的混合溶液，并于115-120℃保温反应2-4h，得B组分，将A组分和B组分于80-85℃混合并高速搅拌均匀，然后于50-60℃保温反应1-1.5h，得复合乳液；
（3）将（2）中的复合乳液与其余原料混合后研磨均匀，即得净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆。
本发明的优点是：
本发明先利用二氧化钛纳米管对桉叶油、柠檬油、苯丙三氮唑和γ-巯丙基三乙氧基硅烷进行负载，然后与环氧树脂和丙烯酸酯进行乳液聚合反应得到复合乳液，既能有效提升涂膜的三维网状结构交联程度，提升对基体的防护性能，又能改善涂膜的机械性能和稳定性，并且由于对复合缓蚀剂的负载，能对涂膜缺陷或者破损处的铜基体起到良好的防腐蚀作用，提高表面防护的持久性。同时，通过其余原料的添加与复配，使得到的铜雕塑水性漆能为基体表面提供全面、持久的防护，兼具优良的防腐蚀性能、机械性能和持久有效性，还有净化空气的功效，有利于提高室内的环境质量。
具体实施方式
一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆，由下列重量(kg)的组分原料制备而成：
环氧树脂E-44 40，乙二醇单丁醚10，正丁醇15，桉叶油0.1，柠檬油0.1，甲基丙烯酸6，苯乙烯4，丙烯酸丁酯3，过氧化苯甲酰0.5，N,N-二甲酰基乙醇4，二氧化钛纳米管4，纳米锗0.1，纳米电气石粉0.3，苯丙三氮唑0.3，γ-巯丙基三乙氧基硅烷0.1，海藻酸钠0.3，水100；
所述二氧化钛纳米管是采用水热合成法制得，管径为5nm，管长为500nm。
一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆的制备方法，包括以下步骤：
（1）将二氧化钛纳米管按固液重量比1:10与无水乙醇混合分散均匀，然后加入桉叶油、柠檬油、苯丙三氮唑和γ-巯丙基三乙氧基硅烷搅拌6h，离心后将所得固体真空干燥，得改性钛纳米管；
（2）将（1）中的改性钛纳米管、纳米锗、纳米电气石粉、N,N-二甲酰基乙醇和水混合分散均匀，得A组分，将环氧树脂E-44、乙二醇单丁醚和正丁醇混合升温至105℃，然后缓慢滴加甲基丙烯酸、苯乙烯、丙烯酸丁酯和过氧化苯甲酰的混合溶液，并于115℃保温反应2h，得B组分，将A组分和B组分于80℃混合并高速搅拌均匀，然后于50℃保温反应1h，得复合乳液；
（3）将（2）中的复合乳液与其余原料混合后研磨均匀，即得净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆。
外观：平整光滑，透明；
附着力：1级；
耐水性：1500h无变化；
耐盐雾性：1000h无变化。

Claims (2)

1.一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆，其特征在于，其是由下述重量份的原料制得：
环氧树脂E-44 40-60，乙二醇单丁醚10-15，正丁醇15-25，桉叶油0.1-0.15，柠檬油0.1-0.2，甲基丙烯酸6-8，苯乙烯4-6，丙烯酸丁酯3-5，过氧化苯甲酰0.5-1，N,N-二甲酰基乙醇4-6，二氧化钛纳米管4-6，纳米锗0.1-0.15，纳米电气石粉0.3-0.5，苯丙三氮唑0.3-0.5，γ-巯丙基三乙氧基硅烷0.1-0.15，海藻酸钠0.3-0.5，水100-120；
所述二氧化钛纳米管是采用水热合成法制得，管径为5-25nm，管长为500-1000nm。
2.根据权利要求1所述的一种净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆的制备方法，其特征在于，包括以下步骤：
（1）将二氧化钛纳米管按固液重量比1:10-1:15与无水乙醇混合分散均匀，然后加入桉叶油、柠檬油、苯丙三氮唑和γ-巯丙基三乙氧基硅烷搅拌6-12h，离心后将所得固体真空干燥，得改性钛纳米管；
（2）将（1）中的改性钛纳米管、纳米锗、纳米电气石粉、N,N-二甲酰基乙醇和水混合分散均匀，得A组分，将环氧树脂E-44、乙二醇单丁醚和正丁醇混合升温至105-110℃，然后缓慢滴加甲基丙烯酸、苯乙烯、丙烯酸丁酯和过氧化苯甲酰的混合溶液，并于115-120℃保温反应2-4h，得B组分，将A组分和B组分于80-85℃混合并高速搅拌均匀，然后于50-60℃保温反应1-1.5h，得复合乳液；
（3）将（2）中的复合乳液与其余原料混合后研磨均匀，即得净化空气室内铜雕塑用环氧-丙烯酸防腐水性漆。
CN201610524519.9A 2016-07-06 2016-07-06 一种净化空气室内铜雕塑用环氧‑丙烯酸防腐水性漆及其制备方法 Pending CN106147494A (zh)