CN106147438A - 一种水性电缆防火涂料的制造方法 - Google Patents
一种水性电缆防火涂料的制造方法 Download PDFInfo
- Publication number
- CN106147438A CN106147438A CN201510157292.4A CN201510157292A CN106147438A CN 106147438 A CN106147438 A CN 106147438A CN 201510157292 A CN201510157292 A CN 201510157292A CN 106147438 A CN106147438 A CN 106147438A
- Authority
- CN
- China
- Prior art keywords
- fire retardant
- manufacture method
- cable
- parts
- retardant coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及防火涂料制造方法,具体是一种水性电缆防火涂料的制造方法。该环保型电缆防火涂料,其起始原料配方按重量计为:水1~50份;弹性丙烯酸乳液10~90份;填料1~10份;阻燃剂10~90份;三聚氰铵1~10份;金红石型钛白粉1~10份;双季戊四醇1~10份;触变剂1~10份;增稠剂1~10份。本发明的环保型电缆防火涂料是水基防火涂料、具有无卤、无毒、无腐蚀、安全环保、高效阻燃、遇火体积膨胀、施工方便等一系列优点,而且从根本上消除了溶剂型涂料在生产和施工中因溶剂挥发而产生的火灾隐患,也减少了有害有机溶剂对人的危害和对环境的污染。
Description
技术领域
本发明涉及防火涂料制造方法,具体是一种环保型电缆防火涂料及其制造方法。
背景技术
目前电线电缆的防火涂料主要采用溶剂型电缆防火涂料进行防火保护,但溶剂型电缆防火涂料中含有大量的挥发性有机溶剂,在生产、施工时存在着明显的安全隐患,主要存在以下三方面弊端:一是溶剂型电缆防火涂料在车船运输时被列为危险品。二是有毒溶剂的挥发性对环境造成污染,对人体造成危害。三是溶剂的可燃性,给生产、施工和贮存带来了危险性。而市面上的部分水性电缆防火涂料粘接性不够,且含卤,对电缆表皮有一定损伤,如200610053130.7号中国专利,其工艺比较复杂,组分中加入的52度氯化石蜡就是含卤元素。
发明内容
本发明提供一种水基、无卤、无毒、无腐蚀、安全环保、高效阻燃、遇火体积膨胀、施工方便的环保型电缆防火涂料及其制造方法。
本发明的环保型电缆防火涂料,其起始原料配方按重量计为:
水 1~50份
弹性丙烯酸乳液 10~90份
填料 1~10份
阻燃剂 10~90份
三聚氰铵 1~10份
金红石型钛白粉 1~10份
双季戊四醇 1~10份
触变剂 1~10份
增稠剂 1~10份
所述填料为碳酸钙、膨润土、活性粘土、硅微粉和/或滑石粉中的至少一种。
所述阻燃剂为碱式碳酸锌、硼酸锌、氢氧化铝、氢氧化镁、氧化铁红、十溴联苯醚、聚磷酸铵、赤磷和/或氯化石蜡中的至少一种或多种。
所述触变剂为二氧化硅、氢化蓖麻油和/或聚乙烯蜡中的至少一种。
所述增稠剂为聚丙烯酸钠、聚氧化乙烯、聚乙烯吡咯烷酮、聚乙烯醇、低分子聚乙烯蜡和/或聚丙烯酰胺中的至少一种或多种。
本发明的一种水性电缆防火涂料的制作方法包括以下步骤:
a.将水1~50份和弹性丙烯酸乳液10~90份抽入多功能搅拌机中搅拌混合,转速200rpm左右,分批加入阻燃剂10~90份,三聚氰胺1~10份,金红石型钛白粉1~10份,填料1~10份,双季戊四醇1~10份和触变剂1~10份,充分搅拌2~4小时,转速200~800rpm。
b.将物料移到卧式密闭式砂磨机中砂磨,边冷却边砂磨,砂磨机中桶体压力保持在0.1MPa左右,砂磨完毕将物料移到多功能搅拌机中,边搅拌边加增稠剂1~10份,增加稠度后获得环保型电缆防火涂料。
本发明的一种水性电缆防火涂料的制造方法是水基防火涂料、具有无卤、无毒、无腐蚀、安全环保、高效阻燃、遇火体积膨胀、施工方便等一系列优点,而且从根本上消除了溶剂型涂料在生产和施工中因溶剂挥发而产生的火灾隐患,也减少了有害有机溶剂对人的危害和对环境的污染。产品达到的质量技术指标,经实际测试,环保型电缆防火涂料各项技术性能指标达到或超过行业标准要求。
具体实施方式
下面结合实例对本发明的产品及方法作进一步说明。
实施例1
将水75kg和弹性丙烯酸乳液200kg抽入多功能搅拌机中搅拌混合,转速200rpm左右,分批加入氢氧化铝阻燃剂100kg,三聚氰胺25kg,金红石型钛白粉50kg,碳酸钙10kg,双季戊四醇20kg和聚乙烯蜡15kg,充分搅拌3小时,转速600rpm。将物料移到卧式密闭式砂磨机中砂磨,边冷却边砂磨,砂磨机中桶体压力保持在0.1MPa左右,砂磨完毕将物料移到多功能搅拌机中,边搅拌边加聚丙烯酸钠5kg,增加稠度后获得环保型电缆防火涂料。
实施例2:
将水50kg和弹性丙烯酸乳液150kg抽入多功能搅拌机中搅拌混合,转速200rpm左右,分批加入氢氧化镁阻燃剂80kg,三聚氰胺30kg,金红石型钛白粉40kg,滑石粉10kg,双季戊四醇15kg和二氧化硅10kg,充分搅拌2.5小时,转速600rpm。将物料移到卧式密闭式砂磨机中砂磨,边冷却边砂磨,砂磨机中桶体压力保持在0.1MPa左右,砂磨完毕将物料移到多功能搅拌机中,边搅拌边加聚氧化乙烯3kg,增加稠度后获得环保型电缆防火涂料。
Claims (6)
1.一种水性电缆防火涂料的制造方法,其特征在于该防火涂料的起始原料配方组分(按重量计)为:
水 1~50份
弹性丙烯酸乳液 10~90份
填料 1~10份
阻燃剂 10~90份
三聚氰铵 1~10份
金红石型钛白粉 1~10份
双季戊四醇 1~10份
触变剂 1~10份
增稠剂 1~10份。
2.按照权利要求1所述一种水性电缆防火涂料的制造方法,其特性在于填料为碳酸钙、膨润土、活性粘土、硅微粉和/或滑石粉中的至少一种。
3.按照权利要求1所述一种水性电缆防火涂料的制造方法,其特性在于阻燃剂为碱式碳酸锌、硼酸锌、氢氧化铝、氢氧化镁、氧化铁红、十溴联苯醚、聚磷酸铵、赤磷和/或氯化石蜡中的至少一种或多种。
4.按照权利要求1所述一种水性电缆防火涂料的制造方法,其特性在于触变剂为二氧化硅、氢化蓖麻油和/或聚乙烯蜡中的至少一种。
5.按照权利要求1所述一种水性电缆防火涂料的制造方法,其特性在于增稠剂为聚丙烯酸钠、聚氧化乙烯、聚乙烯吡咯烷酮、聚乙烯醇、低分子聚乙烯蜡和/或聚丙烯酰胺中的至少一种或多种。
6.一种权利要求1~5之一的一种水性电缆防火涂料的制造方法,包括以下步骤:
a.将水1~50份和弹性丙烯酸乳液10~90份抽入多功能搅拌机中搅拌混合,转速200rpm左右,分批加入阻燃剂10~90份,三聚氰胺1~10份,金红石型钛白粉1~10份,填料1~10份,双季戊四醇1~10份和触变剂1~10份,充分搅拌2~4小时,转速200~800rpm;
b.将物料移到卧式密闭式砂磨机中砂磨,边冷却边砂磨,砂磨机中桶体压力保持在0.1MPa左右,砂磨完毕将物料移到多功能搅拌机中,边搅拌边加增稠剂1~10份,增加稠度后获得环保型电缆防火涂料。