CN106146916A - A kind of antibacterial and deodouring rubber soles material and preparation method thereof - Google Patents
A kind of antibacterial and deodouring rubber soles material and preparation method thereof Download PDFInfo
- Publication number
- CN106146916A CN106146916A CN201510192944.8A CN201510192944A CN106146916A CN 106146916 A CN106146916 A CN 106146916A CN 201510192944 A CN201510192944 A CN 201510192944A CN 106146916 A CN106146916 A CN 106146916A
- Authority
- CN
- China
- Prior art keywords
- parts
- rubber
- deodouring
- antibacterial
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The open a kind of antibacterial and deodouring rubber soles material of the present invention, including following component: natural rubber 35 ~ 50 parts；Nitrile rubber 10 ~ 20 parts；White carbon 5 ~ 10 parts；White oil 5 ~ 10 parts；Zinc oxide 2 ~ 4 parts；Accelerator 1 ~ 3 part；2 ~ 4 parts of age resistor；Zinc stearate 1 ~ 3 part；2 ~ 2.4 parts of sulfur, each component is in parts by weight.The present invention elastomeric material is plasticated after again remaining each component with formula carry out mill, banburying and vulcanisation operation, the physical property of material for sole of shoe can guaranteed simultaneously, improve the plasticity of elastomeric material, make elastomeric material fully be combined with each additive, reach the effect of antibacterial and deodouring.
Description
Technical field
The present invention relates to a kind of material for sole of shoe, especially a kind of rubber soles material.
Background technology
Shoes belong to the requirement in people's life, development and progress along with science and technology, people are more and more higher for the performance requirement of shoes, and the comfortableness of shoes, elasticity, wearability are all the emphasis that people consider, simultaneously more and more higher to the deodorant performance requirement of material for sole of shoe.In the daily production of people, life process, owing to foot perspires, breed bacteria in footwear can be caused, thus produce foot odor problem.
Summary of the invention
Goal of the invention: present invention aim at for the deficiencies in the prior art, it is provided that the rubber soles material of a kind of antibacterial and deodouring；
It is still another object of the present invention to provide a kind of preparation method preparing this material for sole of shoe.
Technical scheme: antibacterial and deodouring rubber soles material of the present invention, including following component:
Natural rubber 35 ~ 50 parts；
Nitrile rubber 10 ~ 20 parts；
White carbon 5 ~ 10 parts；
White oil 5 ~ 10 parts；
Zinc oxide 2 ~ 4 parts；
Accelerator 1 ~ 3 part；
2 ~ 4 parts of age resistor；
Zinc stearate 1 ~ 3 part；
2 ~ 2.4 parts of sulfur,
Each component is in parts by weight.
The present invention further preferably technical scheme is, described antibacterial and deodouring rubber soles material, including following component:
Natural rubber 45 parts；
Nitrile rubber 15 parts；
White carbon 8 parts；
White oil 8 parts；
Zinc oxide 3 parts；
Accelerator 2 parts；
3 parts of age resistor；
Zinc stearate 2 parts；
2.2 parts of sulfur.
The preparation method of antibacterial and deodouring rubber soles material of the present invention, comprises the steps:
(1) first natural rubber and nitrile rubber are plasticated, improve the plasticity of rubber；
(2) each component is prepared by weight that to put into mill mixing, melting temperature 105 ~ 115 DEG C, mixing to each component mix homogeneously；
(3) after mill completes, carrying out banburying in blend glue stuff puts into banbury, banbury temperature is 120 ~ 140 DEG C, banburying 20 ~ 30 minutes；
(4) after banburying, sizing material is poured in footwear mould, cool down 12 hours；
(5) sizing material cooled down is put into vulcanizer and is vulcanized, curing temperature 150 ~ 170 DEG C, vulcanizes 350 ~ 400 seconds, vulcanizer board pressure 160Mpa.
Beneficial effect: the present invention elastomeric material is plasticated after again remaining each component with formula carry out mill, banburying and vulcanisation operation, the physical property of material for sole of shoe can guaranteed simultaneously, improve the plasticity of elastomeric material, make elastomeric material fully be combined with each additive, reach the effect of antibacterial and deodouring.
Detailed description of the invention
Below technical solution of the present invention is described in detail, but protection scope of the present invention is not limited to described embodiment.
Embodiment 1 :A kind of antibacterial and deodouring rubber soles material, including following component:
Natural rubber 35 parts；
Nitrile rubber 10 parts；
White carbon 5 parts；
White oil 5 parts；
Zinc oxide 2 parts；
Accelerator 1 part；
2 parts of age resistor；
Zinc stearate 1 part；
2 parts of sulfur,
Each component is in parts by weight.
The preparation method of this antibacterial and deodouring rubber soles material, comprises the steps:
(1) first natural rubber and nitrile rubber are plasticated, improve the plasticity of rubber；
(2) each component is prepared by weight that to put into mill mixing, melting temperature 105 DEG C, mixing to each component mix homogeneously；
(3) after mill completes, carrying out banburying in blend glue stuff puts into banbury, banbury temperature is 120 DEG C, banburying 20 minutes；
(4) after banburying, sizing material is poured in footwear mould, cool down 12 hours；
(5) sizing material cooled down is put into vulcanizer and is vulcanized, curing temperature 150 DEG C, vulcanizes 350 seconds, vulcanizer board pressure 160Mpa.
Embodiment 2 :A kind of antibacterial and deodouring rubber soles material, including following component:
Natural rubber 50 parts；
Nitrile rubber 20 parts；
White carbon 10 parts；
White oil 10 parts；
Zinc oxide 4 parts；
Accelerator 3 parts；
4 parts of age resistor；
Zinc stearate 3 parts；
2.4 parts of sulfur,
Each component is in parts by weight.
The preparation method of this antibacterial and deodouring rubber soles material, comprises the steps:
(1) first natural rubber and nitrile rubber are plasticated, improve the plasticity of rubber；
(2) each component is prepared by weight that to put into mill mixing, melting temperature 115 DEG C, mixing to each component mix homogeneously；
(3) after mill completes, carrying out banburying in blend glue stuff puts into banbury, banbury temperature is 140 DEG C, banburying 30 minutes；
(4) after banburying, sizing material is poured in footwear mould, cool down 12 hours；
(5) sizing material cooled down is put into vulcanizer and is vulcanized, curing temperature 170 DEG C, vulcanizes 400 seconds, vulcanizer board pressure 160Mpa.
Embodiment 3 :A kind of antibacterial and deodouring rubber soles material, including following component:
Natural rubber 45 parts；
Nitrile rubber 15 parts；
White carbon 8 parts；
White oil 8 parts；
Zinc oxide 3 parts；
Accelerator 2 parts；
3 parts of age resistor；
Zinc stearate 2 parts；
2.2 parts of sulfur,
Each component is in parts by weight.
The preparation method of this antibacterial and deodouring rubber soles material, comprises the steps:
(1) first natural rubber and nitrile rubber are plasticated, improve the plasticity of rubber；
(2) each component is prepared by weight that to put into mill mixing, melting temperature 110 DEG C, mixing to each component mix homogeneously；
(3) after mill completes, carrying out banburying in blend glue stuff puts into banbury, banbury temperature is 130 DEG C, banburying 25 minutes；
(4) after banburying, sizing material is poured in footwear mould, cool down 12 hours；
(5) sizing material cooled down is put into vulcanizer and is vulcanized, curing temperature 160 DEG C, vulcanizes 380 seconds, vulcanizer board pressure 160Mpa.
Although as it has been described above, represented and described the present invention with reference to specific preferred embodiment, but it shall not be construed as the restriction to the present invention self.Under the spirit and scope of the present invention premise defined without departing from claims, can various changes can be made in the form and details to it.
Claims (3)
1. an antibacterial and deodouring rubber soles material, it is characterised in that include following component:
Natural rubber 35 ~ 50 parts；
Nitrile rubber 10 ~ 20 parts；
White carbon 5 ~ 10 parts；
White oil 5 ~ 10 parts；
Zinc oxide 2 ~ 4 parts；
Accelerator 1 ~ 3 part；
2 ~ 4 parts of age resistor；
Zinc stearate 1 ~ 3 part；
2 ~ 2.4 parts of sulfur,
Each component is in parts by weight.
Antibacterial and deodouring rubber soles material the most according to claim 1, it is characterised in that include following component:
Natural rubber 45 parts；
Nitrile rubber 15 parts；
White carbon 8 parts；
White oil 8 parts；
Zinc oxide 3 parts；
Accelerator 2 parts；
3 parts of age resistor；
Zinc stearate 2 parts；
2.2 parts of sulfur.
3. the preparation method of the antibacterial and deodouring rubber soles material described in a claim 1, it is characterised in that comprise the steps:
(1) first natural rubber and nitrile rubber are plasticated, improve the plasticity of rubber；
(2) each component is prepared by weight that to put into mill mixing, melting temperature 105 ~ 115 DEG C, mixing to each component mix homogeneously；
(3) after mill completes, carrying out banburying in blend glue stuff puts into banbury, banbury temperature is 120 ~ 140 DEG C, banburying 20 ~ 30 minutes；
(4) after banburying, sizing material is poured in footwear mould, cool down 12 hours；
(5) sizing material cooled down is put into vulcanizer and is vulcanized, curing temperature 150 ~ 170 DEG C, vulcanizes 350 ~ 400 seconds, vulcanizer board pressure 160Mpa.