CN106121126A - Continuous lod polycarbonate plate - Google Patents
Continuous lod polycarbonate plate Download PDFInfo
- Publication number
- CN106121126A CN106121126A CN201610688080.3A CN201610688080A CN106121126A CN 106121126 A CN106121126 A CN 106121126A CN 201610688080 A CN201610688080 A CN 201610688080A CN 106121126 A CN106121126 A CN 106121126A
- Authority
- CN
- China
- Prior art keywords
- adjuvant
- reinforcing fiber
- polycarbonate plate
- merlon
- continuous
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of continuous lod polycarbonate plate, raw material including following percentage by weight: Merlon 15% 98%, reinforcing fiber 1% 80% and adjuvant 0.1% 5%, forms tabular or profile structure with continuous reinforcing fiber co-extrusion after the Merlon of above-mentioned percentage by weight and adjuvant mixing again；By using reinforcing fiber as inner skeleton, using polycarbonate resin as extruded major ingredient, and it is mixed into adjuvant, use mould is extruded, the number of plies of reinforcing fiber can be selected according to performance requirement, through test determination, the polycarbonate plate tensile strength that the present invention is formed can reach 100 400 MPas, bending strength can reach 100 300 MPas, impact strength is 20 200KJ/, and oxygen index (OI) can reach more than 30, and service life is longer, this material is that thermoplastic is easy to recycling, more environmentally-friendly.
Description
Technical field
The present invention relates to strengthen plate or strengthen component technology field, particularly relate to a kind of continuous lod Merlon
Plate.
Background technology
Polycarbonate plate weak acid resistant, is with Merlon as main component, uses coextrusion techniques molding, polycarbonate plate
Resistance to neutral oil, is weak to strong acid, the most alkaline-resisting.But it is high temperature resistant, daylighting is effective, polycarbonate plate (also known as polycarbonate multi-wall sheet,
Glass caprone plate, PC hollow sheeting) it is to process with high performance engineering plastics-----Merlon (PC) resin, have
The features such as transparency height, light weight, shock resistance, sound insulation, combustion heat insulation, difficult, aging resistance, are that a kind of high-tech, combination property are the tallest and the most erect
More, energy saving and environment friendly plastic plate, be the most commonly used plastic building materials, have other building and ornament materials
The advantage that (such as glass, lucite etc.) are incomparable.
But although existing polycarbonate plate disclosure satisfy that common occasion uses, its intensity and machinability far away can not
Meeting the target of " to mould Dai Gang ", such as tensile strength, bending strength and aspect in service life also have a certain distance, Zhi Neng
Building field uses as ornament materials, it is impossible to as high-strength structure materials'use.
Summary of the invention
The technical problem to be solved is to provide a kind of continuous lod polycarbonate plate, at existing poly-carbon
Continuously and uniformly add reinforcing fiber and adjuvant on the basis of acid esters plate, be effectively improved the mechanical strength of polycarbonate plate, permissible
Meet the requirement of strength as structural material.
For solving above-mentioned technical problem, the technical solution used in the present invention is: a kind of continuous lod Merlon
Plate, including the raw material of following percentage by weight: Merlon 15%-98%, reinforcing fiber 1%-80% and adjuvant 0.1%-5%, by upper
Tabular or profile structure is formed with continuous reinforcing fiber co-extrusion again after stating the Merlon of percentage by weight and adjuvant mixing.
Described continuous reinforcing fiber is fiber cloth, axial cloth, fiber felt, fabric or silvalin.
Described adjuvant is toughener or color masterbatch mixture.
Described Merlon 20%, reinforcing fiber 75% and adjuvant 5%.
Described Merlon 80%, reinforcing fiber 15% and adjuvant 5%.
Use and have the beneficial effects that produced by technique scheme: by using continuous reinforcing fiber as interior bone
Frame, then using polycarbonate resin as extruded major ingredient, and is mixed into adjuvant as required, uses mould extruded, increases
The number of plies of strong fiber can be selected according to performance requirement, and through test determination, the polycarbonate plate tension that the present invention is formed is strong
Degree can reach 100-400 MPa, and bending strength can reach 100-300 MPa, and impact strength is 20-200KJ/, and oxygen refers to
Number can reach more than 30, and service life is longer.
Detailed description of the invention
Below in conjunction with embodiments of the invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise,
Broadly fall into the scope of protection of the invention.
Elaborate a lot of detail in the following description so that fully understanding the present invention, but the present invention is all right
Using other to be different from alternate manner described here to implement, those skilled in the art can be without prejudice to intension of the present invention
In the case of do similar popularization, therefore the present invention is not limited by following public specific embodiment.
Embodiment one, the invention discloses a kind of continuous lod polycarbonate plate, including following percentage by weight
Raw material: Merlon 15%-98%, reinforcing fiber 1%-80% and adjuvant 0.1%-5%, by the Merlon of above-mentioned percentage by weight and
Tabular or profile structure is formed with continuous reinforcing fiber co-extrusion again after adjuvant (can be added according to actual needs) mixing；Described
Reinforcing fiber is fiber cloth, axial cloth, fiber felt, fabric or silvalin etc. continuously；Described adjuvant is toughener or color masterbatch
Mixture etc..
Merlon 20%, reinforcing fiber 75% and adjuvant 5% in embodiment two, the present embodiment.
Merlon 80%, reinforcing fiber 15% and adjuvant 5% in embodiment three, the present embodiment.
In concrete production process, the present invention can be used for producing conventional sheet or section bar, conventional sheet and section bar can roots
According to requiring that the mould designing respective shapes is extruded.
In a word, by the present invention in that by continuous reinforcing fiber as inner skeleton, then using polycarbonate resin as squeezing
Molded major ingredient, and it is mixed into adjuvant, use mould extruded, the number of plies of continuous reinforcing fiber can be selected according to performance requirement
Fixed, through test determination, the polycarbonate plate tensile strength that the present invention is formed can reach 100-400 MPa, bending strength
Can reach 100-300 MPa, impact strength is 20-200KJ/, and oxygen index (OI) can reach more than 30, and service life is longer,
The continuous lod polycarbonate plate of the present invention is extruded by mould, it is simple to production sheet material or section bar, and other one
Aspect, this material is that thermoplastic is easy to recycling, more environmentally-friendly.
Claims (5)
1. a continuous lod polycarbonate plate, it is characterised in that: include the raw material of following percentage by weight: Merlon
15%-98%, reinforcing fiber 1%-80% and adjuvant 0.1%-5%, by after the Merlon of above-mentioned percentage by weight and adjuvant mixing again
Tabular or profile structure is formed with continuous reinforcing fiber co-extrusion.
Continuous lod polycarbonate plate the most according to claim 1, it is characterised in that: described continuous reinforcing fiber is
Fiber cloth, axial cloth, fiber felt, fabric or silvalin.
Continuous lod polycarbonate plate the most according to claim 2, it is characterised in that: described adjuvant be toughener or
Color masterbatch mixture.
Continuous lod polycarbonate plate the most according to claim 3, it is characterised in that: described Merlon 20%, increasing
Strong fiber 75% and adjuvant 5%.
Continuous lod polycarbonate plate the most according to claim 3, it is characterised in that: described Merlon 80%, increasing
Strong fiber 15% and adjuvant 5%.