A kind of multilayer heat shrinkable film
Technical field
The present invention relates to a kind of multilayer heat shrinkable film, belong to polymeric material field.
Background technology
Heat shrink films is for the sale of various products and transport, and its Main Function is to consolidate, hide and protect product.Shrink
Film must have higher paracentesis resistance, good contractility and certain shrinkage stress.In contraction process, thin film can not produce
Raw hole.Outdoor often it is applicable to, it is therefore desirable to add UV ultraviolet (UV) resistant agent due to shrink film.
PET: polyethylene terephthalate, English name: polyethylene terephthalate, is called for short PET.
PET sheet has excellent characteristic (thermostability, chemical proofing.Obdurability, electrical insulating property, safety etc.), low price,
So being extensively used as fiber, thin film, engineering plastics, polyester bottles etc..
PS: polystyrene Polystyrene, it is called for short PS, is a kind of water white thermoplastic.
Summary of the invention
The technical problem to be solved is to provide a kind of multilayer heat shrinkable film, a kind of Multi-layer thermal prepared by the present invention
Shrink film, not only has higher hot strength, also has stronger shrinkage, improve barrier, has the heat of excellence
Sealing property, the excellent transparency and toughness, and can recycle.
The technical scheme is that a kind of multilayer heat shrinkable film, including: top layer, centre
Layer and hot sealing layer, described top layer and hot sealing layer are binded with intermediate layer from the both sides in intermediate layer mutually by bonding coat respectively, described in
Interbed is made up of the raw material of following weight portion:
PET mylar 80-90 part, zinc stearate 1-10 part, epoxy soybean oil 1-10 part,
Described top layer is polypropylene (PP), very low density polyethylene (VLDPE), linear low density polyethylene (LLDPE), second
One or more in alkene-vinyl acetate copolymer (EVA), ethylene ' alpha '-olefin plastomer copolymers, metallocene PE are mixed
Compound,
Described hot sealing layer is made up of the raw material of following weight portion:
Polystyrene 100-200 part, dibutyl phthalate 1-5 part,
Described bonding coat is ethylene-vinyl acetate copolymer or maleic anhydride modified ethene polymers.
On the basis of technique scheme, the present invention can also do following improvement.
Further, the thickness in described intermediate layer is 1-10 micron.
Further, the thickness on described top layer is 1-10 micron.
Further, the thickness of described hot sealing layer is 20-40 micron.
Further, the thickness of described bonding coat is 1-5 micron.
Further, described bonding coat is ethylene-vinyl acetate copolymer (EVA), and the weight percent of vinylacetate contains
Amount is 2%-20%, and density is 0.9-0.95g/cm3。
The invention has the beneficial effects as follows:
A kind of multilayer heat shrinkable film prepared by the present invention, not only has higher hot strength, also has stronger contraction
Performance, improves barrier, has the heat sealability of excellence, the excellent transparency and toughness, and can recycle.
Accompanying drawing explanation
The structural representation of a kind of multilayer heat shrinkable film that Fig. 1 provides for the present invention;
In accompanying drawing, the list of parts representated by each label is as follows:
1, hot sealing layer, 2, bonding coat, 3, intermediate layer, 4, top layer.
Detailed description of the invention
Principle and feature to the present invention are described below, and example is served only for explaining the present invention, is not intended to limit
Determine the scope of the present invention.
Embodiment 1
As it is shown in figure 1, a kind of multilayer heat shrinkable film, including: top layer 4, intermediate layer 3 and hot sealing layer 1, described top layer 4 and heat
Sealing 1 is binded with intermediate layer 3 phase from the both sides in intermediate layer 3 by bonding coat 2 respectively, and the thickness in described intermediate layer 3 is 10 microns,
Described intermediate layer 3 is made up of the raw material of following weight portion: PET mylar 90 parts, zinc stearate 10 parts, epoxy soybean oil 10
Part,
The thickness on described top layer 4 is 10 microns, and described top layer 4 is vinyl-vinyl acetate copolymer (Sinopec Shanghai
Petrochemical industry limited company produces, and model is EVA15/2),
The thickness of described hot sealing layer 1 is 20 microns, and described hot sealing layer 1 is made up of the raw material of following weight portion: polystyrene
200 parts, dibutyl phthalate 5 parts,
The thickness of described bonding coat 2 is 5 microns, and described bonding coat 2 is ethylene-vinyl acetate (Sinopec Shanghai stone
Is produced from oil chemical inc, and model is EVA15/2).
Embodiment 2
As it is shown in figure 1, a kind of multilayer heat shrinkable film, including: top layer 4, intermediate layer 3 and hot sealing layer 1, described top layer 4 and heat
Sealing 1 is binded with intermediate layer 3 phase from the both sides in intermediate layer 3 by bonding coat 2 respectively, and the thickness in described intermediate layer 3 is that 1-10 is micro-
Rice, described intermediate layer 3 is made up of the raw material of following weight portion: PET mylar 80 parts, zinc stearate 5 parts, epoxy soybean oil 5
Part,
The thickness on described top layer 4 is 10 microns, and described top layer 4 is vinyl-vinyl acetate copolymer (Sinopec Shanghai
Petrochemical industry limited company produces, and model is EVA15/2),
The thickness of described hot sealing layer 1 is 40 microns, and described hot sealing layer 1 is made up of the raw material of following weight portion: polystyrene
200 parts, dibutyl phthalate 5 parts,
The thickness of described bonding coat 2 is 5 microns, and described bonding coat 2 is ethylene-vinyl acetate (Sinopec Shanghai stone
Is produced from oil chemical inc, and model is EVA15/2).
During the multilayer heat shrinkable film of production example 1 and embodiment 2, can be according to this area skill disclosed in prior art
Coextrusion method known to art personnel produces, and the production method of multilayer heat shrinkable film already belongs to the conventional skill of this area
Art, there is no particular restriction for the present invention.
Measure the performance parameter of embodiment 1-2, testing result such as table 1:
Table 1 testing result
Detection project |
Embodiment 1 |
Embodiment 2 |
Vertically and horizontally hot strength MPa |
58 |
59 |
Vertically and horizontally elongation at break |
115% |
116% |
Sealing-strength |
16N/15mm |
16N/15mm |
Transparency |
Well |
Well |
Gloss |
Well |
Well |
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all spirit in the present invention and
Within principle, any modification, equivalent substitution and improvement etc. made, should be included within the scope of the present invention.