CN106087092A - A kind of preparation method of antibacterial, ventilating functional fibre - Google Patents
A kind of preparation method of antibacterial, ventilating functional fibre Download PDFInfo
- Publication number
- CN106087092A CN106087092A CN201610682052.0A CN201610682052A CN106087092A CN 106087092 A CN106087092 A CN 106087092A CN 201610682052 A CN201610682052 A CN 201610682052A CN 106087092 A CN106087092 A CN 106087092A
- Authority
- CN
- China
- Prior art keywords
- antibacterial
- fibroin
- cellulose
- titanium dioxide
- ventilating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to textile material field, disclose the preparation method of a kind of antibacterial, ventilating functional fibre, sequentially include the following steps: step 1: carry the preparation of silver γ cyclodextrin;Step 2: the preparation of cellulose fibroin titanium dioxide xerogel particles;Step 3: the preparation of antibacterial, ventilating master batch;Step 4: spinning.The antibacterial, ventilating functional fibre that the present invention prepares has sustained-release antibacterial effect, and timeliness is long;And not interfering with compliance and the comfortableness of fiber, fibre strength is also strengthened in addition.
Description
Technical field
The present invention relates to textile material field, particularly relate to the preparation method of a kind of antibacterial, ventilating functional fibre.
Background technology
Along with the raising day by day of people's living standard, people also improve constantly for the requirement of dress.Nowadays people for
Style is not only particular about by dress ornament, and the functional requirements for the fabric of dress ornament is more and more higher.
Especially for healthy aspect, in life, people inevitably touch various antibacterial, fungus etc.
Microorganism, these microorganisms, under suitable external condition, are spread disease by modes such as contacts, thus affect the health of people
Healthy and normal work, studying and living.Additionally, the breathability of textile material is the most critically important for health, if spun
Knit the poor air permeability of material, the dampness of skin surface can be caused to get rid of in time, thus cause various disease.
Antibacterial functions to be reached, current common practice is that practicality has the dressing liquid of antibacterial functions and enters to textile material
Row dipping, makes antimicrobial component be attached to textile material surface, so that textile material has antibiotic property.But so way
Can have a strong impact on the comfortableness of textile material, textile material feel can be partially hard, and breathability degradation.Additionally, antimicrobial component
Being attached to textile material surface, its fastness is relatively low, the most water-fastness, easily runs off, poor in timeliness.
Summary of the invention
In order to solve above-mentioned technical problem, the invention provides the preparation method of a kind of antibacterial, ventilating functional fibre.This
Bright prepared antibacterial, ventilating functional fibre has sustained-release antibacterial effect, and timeliness is long;And do not interfere with the compliance of fiber and comfortable
Property, fibre strength is also strengthened in addition.
The concrete technical scheme of the present invention is: the preparation method of a kind of antibacterial, ventilating functional fibre, sequentially includes the following steps:
Step 1: gamma-cyclodextrin is formulated as the gamma-cyclodextrin solution that mass concentration is 4-6%, to gamma-cyclodextrin solution
Middle interpolation quality is the silver nitrate of gamma-cyclodextrin 0.3-0.5 times, after stirring, solution ph is controlled at 4-6, in lucifuge
Under the conditions of, it is heated to 50-60 DEG C and is incubated 2-3h, being then centrifuged for isolated solid, solid is clean, dried, it is dissolved in hydrogen
In sodium hydroxide solution, in sodium hydroxide solution, add the sodium borohydride that quality is solid 0.5-1.5%, regulate pH to 7-8, so
After be stirred, recentrifuge separates and prepares the most after drying and carries silver-colored gamma-cyclodextrin.
Step 2: cellulose, fibroin albumen are formulated as cellulose mass concentration be 2-4%, fibroin albumen quality concentration be
The mixed solution of 1-3%, successively adds the load silver gamma-cyclodextrin list aldehyde of mixed solution quality 0.5-1.5% in mixed solution
With the Ethylene glycol diglycidyl ether of mixed solution quality 0.1-0.3%, prepare mixed sols after being uniformly dispersed, by mixed sols
Mix with titania hydrosol 4-6:1 in mass ratio, be transferred to after stirring in the environment of-10 DEG C to-6 DEG C freeze 2-3
My god, thaw after frost, prepare cellulose-fibroin-titanium dioxide hydrogel;With ethanol to cellulose-fibroin-titanium dioxide
After hydrogel carries out solvent displacement for several times, prepare cellulose-fibroin-titanium dioxide alcogel;To cellulose-fibroin-titanium dioxide
Titanium alcogel carries out supercritical fluid drying, eventually passes through grinding and prepares cellulose-fibroin-titanium dioxide xerogel particles.
Step 3: be the dispersion liquid of 3-5% in mass concentration by cellulose-fibroin-titanium dioxide xerogel particles preparation,
In dispersion liquid, add acrylic acid, Polyethylene Glycol and Ammonium persulfate. respectively, under the stirring condition of 55-65 DEG C, react 2-4h;Its
Middle cellulose-fibroin-titanium dioxide xerogel particles, acrylic acid, Polyethylene Glycol and Ammonium persulfate. mass ratio are 1:0.3-0.4:
0.3-0.4:0.02-0.03;Natural cooling after reaction, when reactant is mucus shape, is vacuum dried mucus, and carries out powder
Broken, prepare antibacterial, ventilating master batch.
Step 4: mixed with viscose rayon spinning liquid by antibacterial, ventilating master batch, carries out melt spinning by spinning-drawing machine, prepares
Antibacterial, ventilating functional fibre.
Step 1 of the present invention utilizes the complexing power of cyclodextrin to carry out carrying silver, prepares and carries silver gamma-cyclodextrin, thus has anti-
Bacterium function;Step 2 cellulose, fibroin albumen, load silver gamma-cyclodextrin prepare cellulose-fibroin-titanium dioxide xerogel particles,
There is extra specific surface area and three-dimensional open-framework, there is good breathability, and select cellulose, fibroin albumen as mainly
Material, it is possible to promoting the tensile strength of fiber, titanium dioxide also has outstanding antibiotic property and anti-light aging;Ethylene glycol bisthioglycolate contracts
Water glycerin ether can improve the degree of cross linking in hydrogel forming process, and stability is more preferable.Step 3 is by cellulose-fibroin-titanium dioxide
Titanium xerogel particles and acrylic acid, the compound prepared antibacterial, ventilating master batch of Polyethylene Glycol, this antibacterial, ventilating master batch is in spinning liquid
Good dispersion.Step 4 is by antibacterial, ventilating master batch and the common spinning of rayon spinning liquid.Owing to viscose rayon is mainly composed of alpha fibre
Element, and cellulose-fibroin-titanium dioxide xerogel particles also contains cellulose, therefore affinity, good dispersion, in conjunction with jail
Degree height.
Further, the particle diameter of described cellulose-fibroin-titanium dioxide xerogel particles is less than or equal to 1 micron.
Further, the particle diameter of described antibacterial, ventilating master batch is 2-3 micron.
Further, described antibacterial, ventilating master batch mixes with viscose rayon spinning liquid 4-8:92-96 in mass ratio.
It is compared with the prior art, the invention has the beneficial effects as follows: the antibacterial, ventilating functional fibre that the present invention prepares has slow
Releasing antibacterial effect, timeliness is long;And not interfering with compliance and the comfortableness of fiber, fibre strength is also strengthened in addition.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment 1
The preparation method of a kind of antibacterial, ventilating functional fibre, sequentially includes the following steps:
Step 1: gamma-cyclodextrin is formulated as the gamma-cyclodextrin solution that mass concentration is 5%, in gamma-cyclodextrin solution
Add the silver nitrate that quality is gamma-cyclodextrin 0.4 times, after stirring, solution ph is controlled 5, under the conditions of lucifuge, add
Heat is to 55 DEG C and is incubated 2.5h, is then centrifuged for isolated solid, solid is clean, dried, is dissolved in sodium hydroxide solution,
In sodium hydroxide solution, add the sodium borohydride that quality is solid 1%, regulate pH to 7.5, be then stirred, recentrifuge
Separate and prepare after drying and carry silver gamma-cyclodextrin.
Step 2: cellulose, fibroin albumen are formulated as cellulose mass concentration be 3%, fibroin albumen quality concentration be
The mixed solution of 2%, load silver gamma-cyclodextrin list aldehyde and the mixing of successively adding mixed solution quality 1% in mixed solution are molten
The Ethylene glycol diglycidyl ether of liquid quality 0.2%, prepares mixed sols after being uniformly dispersed, by mixed sols and titanium dioxide water
Colloidal sol 5:1 in mass ratio mixes, and is transferred in the environment of-8 DEG C frost 2.5 days, thaws after frost after stirring, and prepares
Cellulose-fibroin-titanium dioxide hydrogel;With ethanol, cellulose-fibroin-titanium dioxide hydrogel is carried out solvent for several times to replace
After, prepare cellulose-fibroin-titanium dioxide alcogel;Cellulose-fibroin-titanium dioxide alcogel is carried out supercritical fluid
It is dried, eventually passes through and grind the cellulose-fibroin-titanium dioxide xerogel particles preparing particle diameter less than or equal to 1 micron.
Step 3: be the dispersion liquid of 4% in mass concentration by cellulose-fibroin-titanium dioxide xerogel particles preparation, to
Dispersion liquid adds acrylic acid, Polyethylene Glycol and Ammonium persulfate. respectively, under the stirring condition of 60 DEG C, reacts 3h;Wherein fiber
Element-fibroin-titanium dioxide xerogel particles, acrylic acid, Polyethylene Glycol and Ammonium persulfate. mass ratio are 1:0.35:0.35:
0.025;Natural cooling after reaction, when reactant is mucus shape, is vacuum dried mucus, and pulverizes, and prepared particle diameter is
The antibacterial, ventilating master batch of 2-3 micron.
Step 4: antibacterial, ventilating master batch is mixed with viscose rayon spinning liquid 6:94 in mass ratio, is melted by spinning-drawing machine
Melt spinning, prepare antibacterial, ventilating functional fibre.
Embodiment 2
The preparation method of a kind of antibacterial, ventilating functional fibre, sequentially includes the following steps:
Step 1: gamma-cyclodextrin is formulated as the gamma-cyclodextrin solution that mass concentration is 4%, in gamma-cyclodextrin solution
Add the silver nitrate that quality is gamma-cyclodextrin 0.3 times, after stirring, solution ph is controlled 4, under the conditions of lucifuge, add
Heat is to 50 DEG C and is incubated 3h, is then centrifuged for isolated solid, solid is clean, dried, is dissolved in sodium hydroxide solution, to
Adding the sodium borohydride that quality is solid 0.5% in sodium hydroxide solution, regulate pH to 7, be then stirred, recentrifuge divides
From and after drying prepare carry silver gamma-cyclodextrin.
Step 2: cellulose, fibroin albumen are formulated as cellulose mass concentration be 2%, fibroin albumen quality concentration be
The mixed solution of 1%, successively adds load silver gamma-cyclodextrin list aldehyde and the mixing of mixed solution quality 0.5% in mixed solution
The Ethylene glycol diglycidyl ether of solution quality 0.1%, prepares mixed sols, by mixed sols and titanium dioxide after being uniformly dispersed
Hydrosol 4:1 in mass ratio mixes, and is transferred in the environment of-10 DEG C frost 2 days, thaws after frost after stirring, system
Obtain cellulose-fibroin-titanium dioxide hydrogel;With ethanol, cellulose-fibroin-titanium dioxide hydrogel is carried out solvent for several times to put
After changing, prepare cellulose-fibroin-titanium dioxide alcogel;Cellulose-fibroin-titanium dioxide alcogel is carried out shooting flow
Soma is dry, eventually passes through and grinds the cellulose-fibroin-titanium dioxide xerogel particles preparing particle diameter less than or equal to 1 micron.
Step 3: be the dispersion liquid of 3% in mass concentration by cellulose-fibroin-titanium dioxide xerogel particles preparation, to
Dispersion liquid adds acrylic acid, Polyethylene Glycol and Ammonium persulfate. respectively, under the stirring condition of 55 DEG C, reacts 4h;Wherein fiber
Element-fibroin-titanium dioxide xerogel particles, acrylic acid, Polyethylene Glycol and Ammonium persulfate. mass ratio are 1:0.3:0.3:0.02;Instead
Should natural cooling afterwards, when reactant is mucus shape, mucus is vacuum dried, and pulverizes, prepared particle diameter is 2-3 micron
Antibacterial, ventilating master batch.
Step 4: antibacterial, ventilating master batch is mixed with viscose rayon spinning liquid 4:96 in mass ratio, is melted by spinning-drawing machine
Melt spinning, prepare antibacterial, ventilating functional fibre.
Embodiment 3
The preparation method of a kind of antibacterial, ventilating functional fibre, sequentially includes the following steps:
Step 1: gamma-cyclodextrin is formulated as the gamma-cyclodextrin solution that mass concentration is 6%, in gamma-cyclodextrin solution
Add the silver nitrate that quality is gamma-cyclodextrin 0.5 times, after stirring, solution ph is controlled 6, under the conditions of lucifuge, add
Heat is to 60 DEG C and is incubated 2h, is then centrifuged for isolated solid, solid is clean, dried, is dissolved in sodium hydroxide solution, to
Adding the sodium borohydride that quality is solid 1.5% in sodium hydroxide solution, regulate pH to 8, be then stirred, recentrifuge divides
From and after drying prepare carry silver gamma-cyclodextrin.
Step 2: cellulose, fibroin albumen are formulated as cellulose mass concentration be 4%, fibroin albumen quality concentration be
The mixed solution of 3%, successively adds load silver gamma-cyclodextrin list aldehyde and the mixing of mixed solution quality 1.5% in mixed solution
The Ethylene glycol diglycidyl ether of solution quality 0.3%, prepares mixed sols, by mixed sols and titanium dioxide after being uniformly dispersed
Hydrosol 6:1 in mass ratio mixes, and is transferred in the environment of-6 DEG C frost 3 days, thaws after frost after stirring, and prepares
Cellulose-fibroin-titanium dioxide hydrogel;With ethanol, cellulose-fibroin-titanium dioxide hydrogel is carried out solvent for several times to replace
After, prepare cellulose-fibroin-titanium dioxide alcogel;Cellulose-fibroin-titanium dioxide alcogel is carried out supercritical fluid
It is dried, eventually passes through and grind the cellulose-fibroin-titanium dioxide xerogel particles preparing particle diameter less than or equal to 1 micron.
Step 3: be the dispersion liquid of 5% in mass concentration by cellulose-fibroin-titanium dioxide xerogel particles preparation, to
Dispersion liquid adds acrylic acid, Polyethylene Glycol and Ammonium persulfate. respectively, under the stirring condition of 65 DEG C, reacts 2h;Wherein fiber
Element-fibroin-titanium dioxide xerogel particles, acrylic acid, Polyethylene Glycol and Ammonium persulfate. mass ratio are 1:0.4:0.4:0.03;Instead
Should natural cooling afterwards, when reactant is mucus shape, mucus is vacuum dried, and pulverizes, prepared particle diameter is 2-3 micron
Antibacterial, ventilating master batch.
Step 4: antibacterial, ventilating master batch is mixed with viscose rayon spinning liquid 8:92 in mass ratio, is melted by spinning-drawing machine
Melt spinning, prepare antibacterial, ventilating functional fibre.
Raw materials used, equipment in the present invention, unless otherwise noted, is the conventional raw material of this area, equipment;In the present invention
Method therefor, unless otherwise noted, is the conventional method of this area.
The above, be only presently preferred embodiments of the present invention, not impose any restrictions the present invention, every according to the present invention
Any simple modification, change and the equivalent transformation that above example is made by technical spirit, all still falls within the technology of the present invention side
The protection domain of case.
Claims (4)
1. the preparation method of an antibacterial, ventilating functional fibre, it is characterised in that sequentially include the following steps:
Step 1: gamma-cyclodextrin is formulated as the gamma-cyclodextrin solution that mass concentration is 4-6%, adds in gamma-cyclodextrin solution
Add the silver nitrate that quality is gamma-cyclodextrin 0.3-0.5 times, after stirring, solution ph is controlled at 4-6, in lucifuge condition
Under, it is heated to 50-60 DEG C and is incubated 2-3h, being then centrifuged for isolated solid, solid is clean, dried, it is dissolved in hydroxide
In sodium solution, in sodium hydroxide solution, add the sodium borohydride that quality is solid 0.5-1.5%, regulate pH to 7-8, then enter
Row stirring, recentrifuge separates and prepares after drying and carries silver gamma-cyclodextrin;
Step 2: cellulose, fibroin albumen are formulated as cellulose mass concentration be 2-4%, fibroin albumen quality concentration be 1-
The mixed solution of 3%, successively add in mixed solution mixed solution quality 0.5-1.5% load silver gamma-cyclodextrin list aldehyde and
The Ethylene glycol diglycidyl ether of mixed solution quality 0.1-0.3%, after being uniformly dispersed prepare mixed sols, by mixed sols with
Titania hydrosol 4-6:1 in mass ratio mixes, and is transferred in the environment of-10 DEG C to-6 DEG C frost 2-3 days after stirring,
Thaw after frost, prepare cellulose-fibroin-titanium dioxide hydrogel;With ethanol to cellulose-fibroin-titanium dioxide water
After gel carries out solvent displacement for several times, prepare cellulose-fibroin-titanium dioxide alcogel;To cellulose-fibroin-titanium dioxide
Alcogel carries out supercritical fluid drying, eventually passes through grinding and prepares cellulose-fibroin-titanium dioxide xerogel particles;
Step 3: be the dispersion liquid of 3-5% in mass concentration by cellulose-fibroin-titanium dioxide xerogel particles preparation, to dividing
Dissipate in liquid and add acrylic acid, Polyethylene Glycol and Ammonium persulfate. respectively, under the stirring condition of 55-65 DEG C, react 2-4h;Wherein fine
Dimension element-fibroin-titanium dioxide xerogel particles, acrylic acid, Polyethylene Glycol and Ammonium persulfate. mass ratio are 1:0.3-0.4:0.3-
0.4:0.02-0.03;Natural cooling after reaction, when reactant is mucus shape, is vacuum dried mucus, and pulverizes, system
Obtain antibacterial, ventilating master batch;
Step 4: mixed with viscose rayon spinning liquid by antibacterial, ventilating master batch, carries out melt spinning by spinning-drawing machine, prepares antibacterial
Airing function fiber.
The preparation method of a kind of antibacterial, ventilating functional fibre the most as claimed in claim 1, it is characterised in that described cellulose-
The particle diameter of fibroin-titanium dioxide xerogel particles is less than or equal to 1 micron.
The preparation method of a kind of antibacterial, ventilating functional fibre the most as claimed in claim 1 or 2, it is characterised in that described antibacterial
The particle diameter of air-permeable masterbatch is 2-3 micron.
The preparation method of a kind of antibacterial, ventilating functional fibre the most as claimed in claim 1 or 2, it is characterised in that described antibacterial
Air-permeable masterbatch mixes with viscose rayon spinning liquid 4-8:92-96 in mass ratio.