CN106084576A - A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material - Google Patents
A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material Download PDFInfo
- Publication number
- CN106084576A CN106084576A CN201610450202.5A CN201610450202A CN106084576A CN 106084576 A CN106084576 A CN 106084576A CN 201610450202 A CN201610450202 A CN 201610450202A CN 106084576 A CN106084576 A CN 106084576A
- Authority
- CN
- China
- Prior art keywords
- parts
- resisting
- cell phone
- heat
- plastic material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
nullThe invention discloses a kind of heat-resisting ageing-resisting protective casing of cell phone plastic material，Its raw material includes by weight: ethylene ethyl acrylate copolymer 18 26 parts，Polytrifluorochloroethylene 10 30 parts，Merlon 5 18 parts，Bentonite 5 15 parts，Glass fibre 8 16 parts，Modified fish skin collagen 12 18 parts，Nano silicon 10 20 parts，Lignin 5 15 parts，Cumyl peroxide 12 parts，1,3 pairs of (tert-butyl peroxy isopropyl) benzene 0.2 0.8 parts，N，Penylene BMI 0.2 0.8 parts between N '，Stearic acid 13 parts，Cerium oxide 0.1 0.6 parts，Lanthana 0.1 0.6 parts，Three acrylic acid trihydroxy methyl esters 0.2 0.8 parts，Antioxidant TNP 0.5 1.2 parts，Antioxidant 1010 0.5 1.2 parts.It is difficult to bending when the present invention is hit, the components and parts of interior of mobile phone can not be played preferably protection, and thermostability, resistance to ag(e)ing are good.
Description
Technical field
The present invention relates to protective casing of cell phone technical field, particularly relate to a kind of heat-resisting ageing-resisting protective casing of cell phone with moulding
Material material.
Background technology
Mobile phone has become as part indispensable in people's life as a kind of means of communication commonly used, along with existing
Popularizing at smart mobile phone, mobile phone is increasingly wider to range of application in daily life, and smart mobile phone is as science and technology integrated level
Higher equipment, this just protection to mobile phone propose huge challenge, when mobile phone is by clashing into, the damage to circuit board is special
The biggest, it is possible to be possible to mobile phone cannot be repaired between the most casual collision, plastics are because of its light weight, cheap etc. excellent
Point and at mobile phone protecting case field broad development, but existing mobile phone shell plastic construction intensity is low, drops at mobile phone or is subject to
Be susceptible to bending phenomenon during impact, the components and parts of interior of mobile phone can not be played preferably protection, and thermostability own, resistance to always
The property changed is poor, and higher temperature downforce reduction, bearing capacity is low, and the protective effect to mobile phone can not meet demand.
Summary of the invention
The present invention proposes a kind of heat-resisting ageing-resisting protective casing of cell phone plastic material, the most easy to break when goods are hit
Curved, the components and parts of interior of mobile phone can not be played preferably protection, and thermostability, resistance to ag(e)ing are good.
A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material that the present invention proposes, its raw material includes by weight:
Ethylene-ethyl acrylate copolymer 18-26 part, polytrifluorochloroethylene 10-30 part, Merlon 5-18 part, bentonite 5-15 part,
Glass fibre 8-16 part, modified fish skin collagen 12-18 part, nano silicon 10-20 part, lignin 5-15 part, peroxide
Change diisopropylbenzene (DIPB) 1-2 part, 1,3-double (tert-butyl peroxy isopropyl) benzene 0.2-0.8 parts, N, N '-penylene BMI 0.2-
0.8 part, stearic acid 1-3 part, cerium oxide 0.1-0.6 part, lanthana 0.1-0.6 part, three acrylic acid trihydroxy methyl ester 0.2-0.8
Part, antioxidant TNP 0.5-1.2 part, antioxidant 1010 0.5-1.2 part.
Preferably, modified fish skin collagen use following technique prepare: by weight by 5-15 part collagen protein of fish skin,
30-50 part water mix homogeneously, adds the 0.5-1.5 ultrasonic 30-60min of part Semen Vitis viniferae extract, adds the stirring of 0.5-1.5 part glycerol
Uniformly, degassing, it is incubated 1-3h in temperature 45-55 DEG C, adds 5-15 part attapulgite, 30-50 part water mix and blend 20-50min,
Whipping temp is 55-65 DEG C, filters, and the solids obtained is sent in the baking oven that temperature is 108-118 DEG C and is dried 60-80min, dry
Dry temperature is 120-130 DEG C, grinds, and adds 0.5-1.5 part silane coupler, 50-80 part water, regulation system pH value to 4.5-
5.5, stirring, mixing time is 30-55min, and whipping temp is 55-65 DEG C, and mixing speed is 400-500r/min, filters, washes
Washing, adding 80-120 part concentration is that 0.5-0.85% glutaraldehyde water solution stirs 30-60min, and whipping temp is 120-250 DEG C,
Filter, washing, be dried, obtain modified fish skin collagen.
Preferably, ethylene-ethyl acrylate copolymer, polytrifluorochloroethylene, the weight ratio of Merlon are 22-24:20-
25:12-15.
Preferably, bentonite, glass fibre, modified fish skin collagen, nano silicon, the weight ratio of lignin are
8-12:12-15:14-16:14-18:8-12.
Preferably, cumyl peroxide, 1,3-double (tert-butyl peroxy isopropyl) benzene, N, a N '-penylene bismaleimide
The weight ratio of amine is 1.4-1.6:0.3-0.6:0.3-0.6.
Preferably, stearic acid, the weight ratio of three acrylic acid trihydroxy methyl esters are 2-2.6:0.3-0.6.
Preferably, cerium oxide, the weight ratio of lanthana are 0.2-0.5:0.2-0.4.
Preferably, antioxidant TNP, the weight ratio of antioxidant 1010 are 0.6-0.9:0.6-1.
Preferably, described heat-resisting ageing-resisting protective casing of cell phone plastic material, its raw material includes by weight: second
Alkene-ethyl acrylate copolymer 22-24 part, polytrifluorochloroethylene 20-25 part, Merlon 12-15 part, bentonite 8-12 part,
Glass fibre 12-15 part, modified fish skin collagen 14-16 part, nano silicon 14-18 part, lignin 8-12 part, peroxide
Change diisopropylbenzene (DIPB) 1.4-1.6 part, 1,3-double (tert-butyl peroxy isopropyl) benzene 0.3-0.6 parts, N, N '-penylene BMI
0.3-0.6 part, stearic acid 2-2.6 part, cerium oxide 0.2-0.5 part, lanthana 0.2-0.4 part, three acrylic acid trihydroxy methyl esters
0.3-0.6 part, antioxidant TNP 0.6-0.9 part, antioxidant 1010 0.6-1 part.
In the present invention, ethylene-ethyl acrylate copolymer, polytrifluorochloroethylene, Merlon synergism as major ingredient,
Ethylene-ethyl acrylate copolymer has good filler pardon and cross linkable, above-mentioned major ingredient and modified fish skin collagen egg
White mating reaction, not only mechanical property is fabulous, and heat-resisting, ageing-resistant performance is the most excellent, wherein modified fish skin collagen is prevented
Aqueous can be good, and elongation at break is high, and anti-ultraviolet property is excellent, and harmless, and the attapulgite that it is possible to additionally incorporate is through pre-
After processing activation, form a large amount of-NH2 with silane coupler effect, processed by glutaraldehyde further, not only can form carbon nitrogen double
Key, and can react with free amine group containing-CHO, formed and pre-treated fish collagen is fixed, additionally goods have in a large number
Hydroxyl, with polytrifluorochloroethylene, ethylene-ethyl acrylate copolymer, Merlon bond strength height, with 1, double (the tertiary fourth mistake of 3-
Oxygen isopropyl) benzene, cumyl peroxide, the vulcanizing system synergism of N, N '-penylene BMI composition, crosslinking
Density is big, and mechanical property is fabulous, and the enhancing of the bentonite added, glass fibre, lignin, nano silicon composition is filled
System, on the basis of reducing cost, Mechanical Properties of Products further enhances with heat resistance, and the sun of lanthana, cerium oxide
The chlorine atom of the replaceable polytrifluorochloroethylene of ion, the radical reaction speed of the polytrifluorochloroethylene that can effectively slow down, goods are resistance to
Oxidation is fabulous, and further with stearic acid, three acrylic acid trihydroxy methyl ester effects, mobile phone shell is when dropping or impacted
It is susceptible to bending phenomenon.The present invention has higher minimum desired strength makes it have thinner wall thickness, and cost reduces notable,
Production cost is low, can save tubing cost, and bearing capacity is high, good processability, is suitable for batch production.
Detailed description of the invention
Below, by specific embodiment, technical scheme is described in detail.
Embodiment 1
A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material, its raw material includes by weight: ethylene-acrylic acid second
Ester copolymer 18 parts, polytrifluorochloroethylene 30 parts, Merlon 5 parts, bentonite 15 parts, glass fibre 8 parts, modified fish skin collagen
Protein 18 part, nano silicon 10 parts, lignin 15 parts, cumyl peroxide 1 part, 1,3-double (tert-butyl peroxy isopropyl)
Benzene 0.8 part, N, N '-penylene BMI 0.2 part, stearic acid 3 parts, cerium oxide 0.1 part, lanthana 0.6 part, three propylene
Acid trihydroxy methyl ester 0.2 part, antioxidant TNP 1.2 parts, antioxidant 1010 0.5 part.
Embodiment 2
A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material, its raw material includes by weight: ethylene-acrylic acid second
Ester copolymer 26 parts, polytrifluorochloroethylene 10 parts, Merlon 18 parts, bentonite 5 parts, glass fibre 16 parts, modified fish skin glue
Former protein 12 part, nano silicon 20 parts, lignin 5 parts, cumyl peroxide 2 parts, 1,3-double (tert-butyl peroxy isopropyls
Base) benzene 0.2 part, N, N '-penylene BMI 0.8 part, stearic acid 1 part, cerium oxide 0.6 part, lanthana 0.1 part, three
Acrylic acid trihydroxy methyl ester 0.8 part, antioxidant TNP 0.5 part, antioxidant 1010 1.2 parts.
Embodiment 3
A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material, its raw material includes by weight: ethylene-acrylic acid second
Ester copolymer 18 parts, polytrifluorochloroethylene 30 parts, Merlon 5 parts, bentonite 15 parts, glass fibre 8 parts, modified fish skin collagen
Protein 18 part, nano silicon 10 parts, lignin 15 parts, cumyl peroxide 1 part, 1,3-double (tert-butyl peroxy isopropyl)
Benzene 0.8 part, N, N '-penylene BMI 0.2 part, stearic acid 3 parts, cerium oxide 0.1 part, lanthana 0.6 part, three propylene
Acid trihydroxy methyl ester 0.2 part, antioxidant TNP 1.2 parts, antioxidant 1010 0.5 part.
Modified fish skin collagen uses following technique to prepare: 15 parts of collagen protein of fish skin, 30 parts of water are mixed by weight
Close uniformly, add 1.5 parts of ultrasonic 30min of Semen Vitis viniferae extract, add 1.5 parts of glycerol and stir, degassing, protect at temperature 45 C
Temperature 3h, adds 5 parts of attapulgites, 50 parts of water mix and blend 20min, and whipping temp is 65 DEG C, filters, and the solids obtained is sent into
Temperature is to be dried 80min in the baking oven of 108 DEG C, and baking temperature is 120 DEG C, grinds, adds 1.5 parts of silane couplers, 50 parts of water,
Regulation system pH value is to 5.5, and stirring, mixing time is 30min, and whipping temp is 65 DEG C, and mixing speed is 400r/min, mistake
Filter, washing, adding 120 parts of concentration is 0.5% glutaraldehyde water solution stirring 60min, and whipping temp is 120 DEG C, filters, washing,
It is dried, obtains modified fish skin collagen.
Embodiment 4
A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material, its raw material includes by weight: ethylene-acrylic acid second
Ester copolymer 26 parts, polytrifluorochloroethylene 10 parts, Merlon 18 parts, bentonite 5 parts, glass fibre 16 parts, modified fish skin glue
Former protein 12 part, nano silicon 20 parts, lignin 5 parts, cumyl peroxide 2 parts, 1,3-double (tert-butyl peroxy isopropyls
Base) benzene 0.2 part, N, N '-penylene BMI 0.8 part, stearic acid 1 part, cerium oxide 0.6 part, lanthana 0.1 part, three
Acrylic acid trihydroxy methyl ester 0.8 part, antioxidant TNP 0.5 part, antioxidant 1010 1.2 parts.
Modified fish skin collagen uses following technique to prepare: by weight by 5 parts of collagen protein of fish skin, 50 parts of water mixing
Uniformly, adding 0.5 part of ultrasonic 60min of Semen Vitis viniferae extract, add 0.5 part of glycerol and stir, degassing, in temperature 55 DEG C insulation
1h, adds 15 parts of attapulgites, 30 parts of water mix and blend 50min, and whipping temp is 55 DEG C, filters, and the solids obtained is sent into
Temperature is to be dried 60min in the baking oven of 118 DEG C, and baking temperature is 130 DEG C, grinds, adds 0.5 part of silane coupler, 80 parts of water,
Regulation system pH value is to 4.5, and stirring, mixing time is 55min, and whipping temp is 55 DEG C, and mixing speed is 500r/min, mistake
Filter, washing, adding 80 parts of concentration is 0.85% glutaraldehyde water solution stirring 30min, and whipping temp is 250 DEG C, filters, washing,
It is dried, obtains modified fish skin collagen.
Embodiment 5
A kind of heat-resisting ageing-resisting protective casing of cell phone plastic material, its raw material includes by weight: ethylene-acrylic acid second
Ester copolymer 21 parts, polytrifluorochloroethylene 21 parts, Merlon 16 parts, bentonite 12 parts, glass fibre 12 parts, modified fish skin glue
Former protein 16 part, nano silicon 16 parts, lignin 12 parts, cumyl peroxide 1.6 parts, 1,3-pair (tert-butyl peroxy is different
Propyl group) benzene 0.52 part, N, N '-penylene BMI 0.62 part, stearic acid 1.5 parts, cerium oxide 0.3 part, lanthana
0.42 part, three acrylic acid trihydroxy methyl esters 0.6 part, antioxidant TNP 0.85 part, antioxidant 1010 0.85 part.
Modified fish skin collagen uses following technique to prepare: 12 parts of collagen protein of fish skin, 36 parts of water are mixed by weight
Closing uniformly, add 1.2 parts of ultrasonic 52min of Semen Vitis viniferae extract, add 1.2 parts of glycerol and stir, degassing, temperature 52 DEG C guarantor
Temperature 1.5h, adds 12 parts of attapulgites, 42 parts of water mix and blend 35min, and whipping temp is 62 DEG C, filters, the solids obtained
Sending into temperature is to be dried 75min in the baking oven of 112 DEG C, and baking temperature is 125 DEG C, grinds, add 1.2 parts of silane couplers, 65
Part water, regulation system pH value to 5.2, stirring, mixing time is 45min, and whipping temp is 62 DEG C, and mixing speed is 460r/
Min, filters, washing, and adding 80-120 part concentration is 0.65% glutaraldehyde water solution stirring 42min, and whipping temp is 220 DEG C,
Filter, washing, be dried, obtain modified fish skin collagen.
The above, the only present invention preferably detailed description of the invention, but protection scope of the present invention is not limited thereto,
Any those familiar with the art in the technical scope that the invention discloses, according to technical scheme and
Inventive concept equivalent or change in addition, all should contain within protection scope of the present invention.
Claims (9)
1. a heat-resisting ageing-resisting protective casing of cell phone plastic material, it is characterised in that its raw material includes by weight: second
Alkene-ethyl acrylate copolymer 18-26 part, polytrifluorochloroethylene 10-30 part, Merlon 5-18 part, bentonite 5-15 part, glass
Glass fiber 8-16 part, modified fish skin collagen 12-18 part, nano silicon 10-20 part, lignin 5-15 part, peroxidating
Diisopropylbenzene (DIPB) 1-2 part, 1,3-double (tert-butyl peroxy isopropyl) benzene 0.2-0.8 parts, N, N '-penylene BMI 0.2-
0.8 part, stearic acid 1-3 part, cerium oxide 0.1-0.6 part, lanthana 0.1-0.6 part, three acrylic acid trihydroxy methyl ester 0.2-0.8
Part, antioxidant TNP 0.5-1.2 part, antioxidant 1010 0.5-1.2 part.
Heat-resisting ageing-resisting protective casing of cell phone plastic material the most according to claim 1, it is characterised in that modified fish skin
Collagen protein uses following technique to prepare: by weight by 5-15 part collagen protein of fish skin, 30-50 part water mix homogeneously, adds
The ultrasonic 30-60min of 0.5-1.5 part Semen Vitis viniferae extract, adds 0.5-1.5 part glycerol and stirs, and degassing, in temperature 45-55
DEG C insulation 1-3h, add 5-15 part attapulgite, 30-50 part water mix and blend 20-50min, whipping temp is 55-65 DEG C, mistake
Filtering, the solids obtained is sent in the baking oven that temperature is 108-118 DEG C and is dried 60-80min, and baking temperature is 120-130 DEG C, grinds
Mill, adds 0.5-1.5 part silane coupler, 50-80 part water, regulation system pH value to 4.5-5.5, and stirring, mixing time is 30-
55min, whipping temp is 55-65 DEG C, and mixing speed is 400-500r/min, filters, washing, adds 80-120 part concentration and is
0.5-0.85% glutaraldehyde water solution stirring 30-60min, whipping temp is 120-250 DEG C, filters, and washing is dried, is changed
Property collagen protein of fish skin.
Heat-resisting ageing-resisting protective casing of cell phone plastic material the most according to claim 1 and 2, it is characterised in that ethylene-
Ethyl acrylate copolymer, polytrifluorochloroethylene, the weight ratio of Merlon are 22-24:20-25:12-15.
4. according to the heat-resisting ageing-resisting protective casing of cell phone plastic material described in any one of claim 1-3, it is characterised in that
Bentonite, glass fibre, modified fish skin collagen, nano silicon, the weight ratio of lignin are 8-12:12-15:14-
16:14-18:8-12.
5. according to the heat-resisting ageing-resisting protective casing of cell phone plastic material described in any one of claim 1-4, it is characterised in that
Cumyl peroxide, 1, double (tert-butyl peroxy isopropyl) benzene of 3-, the weight ratio of N, a N '-penylene BMI are 1.4-
1.6:0.3-0.6:0.3-0.6.
6. according to the heat-resisting ageing-resisting protective casing of cell phone plastic material described in any one of claim 1-5, it is characterised in that
Stearic acid, the weight ratio of three acrylic acid trihydroxy methyl esters are 2-2.6:0.3-0.6.
7. according to the heat-resisting ageing-resisting protective casing of cell phone plastic material described in any one of claim 1-6, it is characterised in that
Cerium oxide, the weight ratio of lanthana are 0.2-0.5:0.2-0.4.
8. according to the heat-resisting ageing-resisting protective casing of cell phone plastic material described in any one of claim 1-7, it is characterised in that
Antioxidant TNP, the weight ratio of antioxidant 1010 are 0.6-0.9:0.6-1.
9. according to the heat-resisting ageing-resisting protective casing of cell phone plastic material described in any one of claim 1-8, it is characterised in that
Its raw material includes by weight: ethylene-ethyl acrylate copolymer 22-24 part, polytrifluorochloroethylene 20-25 part, Merlon
12-15 part, bentonite 8-12 part, glass fibre 12-15 part, modified fish skin collagen 14-16 part, nano silicon 14-
18 parts, lignin 8-12 part, cumyl peroxide 1.4-1.6 part, 1,3-double (tert-butyl peroxy isopropyl) benzene 0.3-0.6 parts,
N, N '-penylene BMI 0.3-0.6 part, stearic acid 2-2.6 part, cerium oxide 0.2-0.5 part, lanthana 0.2-0.4
Part, three acrylic acid trihydroxy methyl ester 0.3-0.6 parts, antioxidant TNP 0.6-0.9 part, antioxidant 1010 0.6-1 part.