CN106084403A - A kind of anticorrosion plastic wood sheet - Google Patents

A kind of anticorrosion plastic wood sheet Download PDF

Info

Publication number
CN106084403A
CN106084403A CN201610487390.9A CN201610487390A CN106084403A CN 106084403 A CN106084403 A CN 106084403A CN 201610487390 A CN201610487390 A CN 201610487390A CN 106084403 A CN106084403 A CN 106084403A
Authority
CN
China
Prior art keywords
parts
wood sheet
powder
plastic wood
corvic
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610487390.9A
Other languages
Chinese (zh)
Inventor
张树芳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Mingguang City Sunshine Wood Industry Co Ltd
Original Assignee
Mingguang City Sunshine Wood Industry Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mingguang City Sunshine Wood Industry Co Ltd filed Critical Mingguang City Sunshine Wood Industry Co Ltd
Priority to CN201610487390.9A priority Critical patent/CN106084403A/en
Publication of CN106084403A publication Critical patent/CN106084403A/en
Pending legal-status Critical Current

Abstract

The invention discloses a kind of anticorrosion plastic wood sheet, be made up of according to the raw material of weight portion following: polyethylene 5 15 parts, wood powder 3 13 parts, Corvic 5 15 parts, glass fibre 2 12 parts, nano titanium oxide 3 13 parts, bamboo powder 2 10 parts, lavandula angustifolia 3 13 parts, Ramulus Cinnamomi 17 parts, silicon oxide 39 parts, plasticizer 17 parts, foaming agent 2 12 parts, lubricant 39 parts, stabilizer 2 12 parts.The present invention has preferable Corrosion Protection and environmental-protecting performance.

Description

A kind of anticorrosion plastic wood sheet
Technical field
The present invention relates to wood processing field, particularly relate to a kind of anticorrosion plastic wood sheet.
Background technology
At present, along with the enhancing of people's environmental consciousness, the environmental-protecting performance of family product is required more and more higher, moulds wood by people Sheet material is liked by people because it has preferable environmental-protecting performance, but existing plastic wood sheet performance is undesirable, is using Cheng Zhong, it is impossible to enough have preferable Corrosion Protection, is easily used to the situation occurring being corroded for a long time, is unfavorable for people's Use.
Summary of the invention
In order to overcome the defect of above-mentioned prior art, it is an object of the invention to provide a kind of anticorrosion plastic wood sheet.
The present invention takes techniques below scheme to realize: a kind of anticorrosion plastic wood sheet, by following according to weight portion Raw material composition: polyethylene 5-15 part, wood powder 3-13 part, Corvic 5-15 part, glass fibre 2-12 part, nano-silica Change titanium 3-13 part, bamboo powder 2-10 part, lavandula angustifolia 3-13 part, Ramulus Cinnamomi 1-7 part, silicon oxide 3-9 part, plasticizer 1-7 part, foaming agent 2- 12 parts, lubricant 3-9 part, stabilizer 2-12 part.
Above-mentioned a kind of anticorrosion plastic wood sheet, is made up of according to the raw material of weight portion following: polyethylene 5-12 part, wood powder 3-11 part, Corvic 5-12 part, glass fibre 2-10 part, nano titanium oxide 3-11 part, bamboo powder 2-8 part, lavandula angustifolia 3-11 part, Ramulus Cinnamomi 1-5 part, silicon oxide 3-7 part, plasticizer 1-5 part, foaming agent 2-10 part, lubricant 3-7 part, stabilizer 2-10 Part.
Above-mentioned a kind of anticorrosion plastic wood sheet, is made up of according to the raw material of weight portion following: polyethylene 10 parts, wood powder 8 Part, Corvic 10 parts, glass fibre 7 parts, nano titanium oxide 8 parts, bamboo powder 6 parts, lavandula angustifolia 8 parts, Ramulus Cinnamomi 4 parts, oxygen SiClx 6 parts, plasticizer 4 parts, foaming agent 7 parts, lubricant 6 parts, stabilizer 7 parts.
The method have the advantages that the present invention has preferable Corrosion Protection and the feature of environmental protection in sum Can, enable people to use for a long time, and do not have situation about being corroded, reduce use cost.
Detailed description of the invention
A kind of anticorrosion plastic wood sheet, is made up of according to the raw material of weight portion following: polyethylene 5-15 part, wood powder 3-13 Part, Corvic 5-15 part, glass fibre 2-12 part, nano titanium oxide 3-13 part, bamboo powder 2-10 part, lavandula angustifolia 3-13 Part, Ramulus Cinnamomi 1-7 part, silicon oxide 3-9 part, plasticizer 1-7 part, foaming agent 2-12 part, lubricant 3-9 part, stabilizer 2-12 part.
Above-mentioned a kind of anticorrosion plastic wood sheet, is made up of according to the raw material of weight portion following: polyethylene 5-12 part, wood powder 3-11 part, Corvic 5-12 part, glass fibre 2-10 part, nano titanium oxide 3-11 part, bamboo powder 2-8 part, lavandula angustifolia 3-11 part, Ramulus Cinnamomi 1-5 part, silicon oxide 3-7 part, plasticizer 1-5 part, foaming agent 2-10 part, lubricant 3-7 part, stabilizer 2-10 Part.
Above-mentioned a kind of anticorrosion plastic wood sheet, is made up of according to the raw material of weight portion following: polyethylene 10 parts, wood powder 8 Part, Corvic 10 parts, glass fibre 7 parts, nano titanium oxide 8 parts, bamboo powder 6 parts, lavandula angustifolia 8 parts, Ramulus Cinnamomi 4 parts, oxygen SiClx 6 parts, plasticizer 4 parts, foaming agent 7 parts, lubricant 6 parts, stabilizer 7 parts.
The present invention has preferable Corrosion Protection and environmental-protecting performance, enables people to use for a long time, and will not go out Situation about being now corroded, reduces use cost.
The above is embodiments of the invention, therefore all according to the structure described in the present patent application scope, feature and principle institute The equivalence change done or modification, in the range of being all included in present patent application.

Claims (3)

1. an anticorrosion plastic wood sheet, it is characterised in that be made up of according to the raw material of weight portion following: polyethylene 5-15 part, Wood powder 3-13 part, Corvic 5-15 part, glass fibre 2-12 part, nano titanium oxide 3-13 part, bamboo powder 2-10 part, smoke Clothing grass 3-13 part, Ramulus Cinnamomi 1-7 part, silicon oxide 3-9 part, plasticizer 1-7 part, foaming agent 2-12 part, lubricant 3-9 part, stabilizer 2-12 part.
A kind of anticorrosion plastic wood sheet the most according to claim 1, it is characterised in that by the following raw material according to weight portion Composition: polyethylene 5-12 part, wood powder 3-11 part, Corvic 5-12 part, glass fibre 2-10 part, nano titanium oxide 3- 11 parts, bamboo powder 2-8 part, lavandula angustifolia 3-11 part, Ramulus Cinnamomi 1-5 part, silicon oxide 3-7 part, plasticizer 1-5 part, foaming agent 2-10 part, profit Lubrication prescription 3-7 part, stabilizer 2-10 part.
A kind of anticorrosion plastic wood sheet the most according to claim 1, it is characterised in that by the following raw material according to weight portion Composition: polyethylene 10 parts, wood powder 8 parts, Corvic 10 parts, glass fibre 7 parts, nano titanium oxide 8 parts, bamboo powder 6 parts, Lavandula angustifolia 8 parts, Ramulus Cinnamomi 4 parts, silicon oxide 6 parts, plasticizer 4 parts, foaming agent 7 parts, lubricant 6 parts, stabilizer 7 parts.
CN201610487390.9A 2016-06-29 2016-06-29 A kind of anticorrosion plastic wood sheet Pending CN106084403A (en)