CN106079847B - The preparation method of wear-resisting puncture-resistant halftone - Google Patents
The preparation method of wear-resisting puncture-resistant halftone Download PDFInfo
- Publication number
- CN106079847B CN106079847B CN201610418029.0A CN201610418029A CN106079847B CN 106079847 B CN106079847 B CN 106079847B CN 201610418029 A CN201610418029 A CN 201610418029A CN 106079847 B CN106079847 B CN 106079847B
- Authority
- CN
- China
- Prior art keywords
- layer
- emulsion layer
- parts
- pattern
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of preparation methods of wear-resisting puncture-resistant halftone, include the following steps:1)Screen cloth is fixed on screen frame;2)Using emulsion as raw material, one layer of first emulsion layer is covered on the patch print face of screen cloth;3)Using emulsion as raw material, one layer of second emulsion layer is covered in above-mentioned first emulsion layer surface;4)It is bonded one layer of endless rubber belt layer in the second emulsion layer surface;The endless rubber belt layer is made of the adhesive tape for being fitted in the second emulsion layer surface;Adhesive tape printing along the second emulsion layer is arranged with area of the pattern outer, and surrounds the printing area of the pattern.Halftone prepared by the present invention has the endless rubber belt layer of wear-resisting puncture-resistant, can effectively improve the wear-resisting puncture resistance in halftone patch print face, improve the service life of halftone.
Description
Technical field
The present invention relates to the preparation methods of wear-resisting puncture-resistant halftone.
Background technology
Halftone is the common tool of printing, and halftone includes screen frame and screen cloth, and the patch print face of screen cloth is equipped with band printing and schemes
The emulsion layer of case, emulsion layer will recline object to be printed when printing, and emulsion layer is easy to be worn and puncture, to seriously affect printing quality
Amount, therefore emulsion layer needs to carry out effective protection.
Invention content
The purpose of the present invention is to provide a kind of preparation method of wear-resisting puncture-resistant halftone, the halftone prepared has wear-resisting
The endless rubber belt layer of puncture-resistant can effectively improve the wear-resisting puncture resistance in halftone patch print face, improve the service life of halftone.
To achieve the above object, the technical scheme is to design a kind of preparation method of wear-resisting puncture-resistant halftone, packets
Include following steps:
1)Screen cloth is fixed on screen frame;
2)Using emulsion as raw material, coating, drying, exposure, imaging, baking operation are passed sequentially through, is printed in the patch of screen cloth
One layer of first emulsion layer is covered on face, which is equipped with printing area of the pattern, is equipped in printing area of the pattern
If dry printing pattern;
3)Using emulsion as raw material, coating, drying, exposure, imaging, baking operation are passed sequentially through, in above-mentioned first breast
Oxidant layer surface covers one layer of second emulsion layer, and first emulsion layer is located between screen cloth patch print face and the second emulsion layer;Second
Emulsion layer also is provided with printing area of the pattern, if also being provided with dry printing pattern in printing area of the pattern;Second emulsion layer
Printing corresponded with area of the pattern with area of the pattern with the printing of the first emulsion layer, and on the second emulsion layer respectively printing scheme
Case is corresponded with each printing on the first emulsion layer with pattern;
4)It is bonded one layer of endless rubber belt layer in the second emulsion layer surface, second emulsion layer is located at the first emulsion layer and ring
Between shape adhesive tape layer;The endless rubber belt layer is made of the adhesive tape for being fitted in the second emulsion layer surface;The adhesive tape is along the second breast
Printing is arranged with area of the pattern outer in oxidant layer, and surrounds the printing area of the pattern.
Preferably, the thickness of the endless rubber belt layer is 0.01~0.012mm.
Preferably, the width of the endless rubber belt layer is 10~15mm.
Preferably, one layer of endless rubber belt layer is bonded in the second emulsion layer surface by adhesive-tape application machine.
Preferably, the adhesive-tape application machine is equipped with CCD para-position system, which controls the bonding position of adhesive tape.
Preferably, the adhesive-tape application machine is equipped with displacement mechanism, which moves adhesive tape and supreme state bonding position.
Preferably, the adhesive-tape application machine is equipped with rubber roll, which is pressed on the second emulsion layer surface by adhesive tape,
Adhesive tape is set to combine closely with the second emulsion layer.
Preferably, institute's displacement mechanism includes servo motor, precise guide rail and precise ball screw;The precise guide rail packet
Include orthogonal X-axis guide rail and Y-axis guide rail.
Preferably, the adhesive tape is macromolecule compound adhesive tape.
Preferably, the adhesive tape includes substrate layer and adhesive layer;By weight, the substrate layer is by following components group
At:
9.8 parts of chlorinated polypropylenes,
14.2 parts of butadiene-styrene rubber,
7.9 parts of butyl rubbers,
6.5 parts of emulsion polymerized styrene butadiene rubbers,
3.2 parts of vinyl bis-stearamides,
1.1 parts of zirconium oxides,
1.3 parts of calcium sulfate,
0.7 part of silicon carbide,
1.4 parts of 4- methoxyl group -3,5- dimethyl -2- hydroxymethylpyridines,
2.1 parts of γ-mercaptopropyl trimethoxysilanes,
1.7 parts of vinyltrimethoxysilanes,
0.9 part of diethyl thiourea,
1.3 parts of phenyl silicone oils,
1.6 parts of N- phenyl-1-naphthylamines,
2.1 parts of polyvinylpyrrolidones.
The advantages of the present invention are:A kind of preparation method of wear-resisting puncture-resistant halftone is provided, is prepared
Halftone has the endless rubber belt layer of wear-resisting puncture-resistant, can effectively improve the wear-resisting puncture resistance in halftone patch print face, improve halftone
Service life.
Halftone patch print of the present invention face is equipped with the second emulsion layer, and the second emulsion layer can play a protective role to the first emulsion layer.
Halftone of the present invention patch print face is additionally provided with endless rubber belt layer, and endless rubber belt layer is located at object surface to be printed and second when printing
Between emulsion layer, it can play a protective role to the second emulsion layer;And endless rubber belt layer of the present invention is made of wear-resisting puncture-resistant adhesive tape,
The wear-resisting puncture resistance in halftone patch print face can be effectively improved.The substrate layer of adhesive tape of the present invention is made by specific components with specific proportioning
At with higher wear-resisting puncture resistance.
The ring protection layer that the present invention is arranged in the second emulsion layer surface(Endless rubber belt layer), by being fitted in the second emulsion
Layer surface printing constitutes with the adhesive tape of area of the pattern outer, and ring protection is prepared using emulsion for raw material without being to continue with
Layer, can remove from again be coated with, dry, exposure, imaging, drying and etc., enormously simplify process, reduce energy consumption.And this
Invention prepares ring protection layer using adhesive tape, prepares ring protection layer as raw material relative to using emulsion, was printing
The abrasion resistance of adhesive tape and paracentesis resistance are stronger in journey, can preferably improve halftone service life.
The present invention can be by adhesive-tape application machine in the second emulsion layer surface automatic attaching ring protection layer(Endless rubber belt layer), can
The precision that adhesive tape gluing position is controlled by CCD para-position system avoids the inaccurate problem manually aligned, while utilizing machine
Joint adhesive band reduces multiple working procedure relative to manual operation, greatly shortens the production time of every halftone, improves
Production capacity and efficiency can reduce to artificial use using machine joint adhesive band, reduce cost of labor.
Specific implementation mode
With reference to embodiment, the specific embodiment of the present invention is further described.Following embodiment is only used for more
Add and clearly demonstrate technical scheme of the present invention, and not intended to limit the protection scope of the present invention.
The technical solution that the present invention embodies is:
A kind of preparation method of wear-resisting puncture-resistant halftone, includes the following steps:
1)Screen cloth is fixed on screen frame;
2)Using emulsion as raw material, coating, drying, exposure, imaging, baking operation are passed sequentially through, is printed in the patch of screen cloth
One layer of first emulsion layer is covered on face, which is equipped with printing area of the pattern, is equipped in printing area of the pattern
If dry printing pattern;
3)Using emulsion as raw material, coating, drying, exposure, imaging, baking operation are passed sequentially through, in above-mentioned first breast
Oxidant layer surface covers one layer of second emulsion layer, and first emulsion layer is located between screen cloth patch print face and the second emulsion layer;Second
Emulsion layer also is provided with printing area of the pattern, if also being provided with dry printing pattern in printing area of the pattern;Second emulsion layer
Printing corresponded with area of the pattern with area of the pattern with the printing of the first emulsion layer, and on the second emulsion layer respectively printing scheme
Case is corresponded with each printing on the first emulsion layer with pattern;
4)It is bonded one layer of endless rubber belt layer in the second emulsion layer surface, second emulsion layer is located at the first emulsion layer and ring
Between shape adhesive tape layer;The endless rubber belt layer is made of the adhesive tape for being fitted in the second emulsion layer surface;The adhesive tape is along the second breast
Printing is arranged with area of the pattern outer in oxidant layer, and surrounds the printing area of the pattern.
The thickness of the endless rubber belt layer is 0.01~0.012mm.
The width of the endless rubber belt layer is 10~15mm.
Step 4)In by adhesive-tape application machine the second emulsion layer surface be bonded one layer of endless rubber belt layer.
The adhesive-tape application machine is equipped with CCD para-position system, which controls the bonding position of adhesive tape.
The adhesive-tape application machine is equipped with displacement mechanism, which moves adhesive tape and supreme state bonding position.
The adhesive-tape application machine is equipped with rubber roll, which is pressed on the second emulsion layer surface by adhesive tape, makes adhesive tape
It combines closely with the second emulsion layer.
Institute's displacement mechanism includes servo motor, precise guide rail and precise ball screw;The precise guide rail includes mutual
Vertical X-axis guide rail and Y-axis guide rail.
The adhesive tape is macromolecule compound adhesive tape.
The adhesive tape includes substrate layer and adhesive layer;By weight, the substrate layer is composed of the following components:
9.8 parts of chlorinated polypropylenes,
14.2 parts of butadiene-styrene rubber,
7.9 parts of butyl rubbers,
6.5 parts of emulsion polymerized styrene butadiene rubbers,
3.2 parts of vinyl bis-stearamides,
1.1 parts of zirconium oxides,
1.3 parts of calcium sulfate,
0.7 part of silicon carbide,
1.4 parts of 4- methoxyl group -3,5- dimethyl -2- hydroxymethylpyridines,
2.1 parts of γ-mercaptopropyl trimethoxysilanes,
1.7 parts of vinyltrimethoxysilanes,
0.9 part of diethyl thiourea,
1.3 parts of phenyl silicone oils,
1.6 parts of N- phenyl-1-naphthylamines,
2.1 parts of polyvinylpyrrolidones.
The above is only a preferred embodiment of the present invention, it is noted that for the ordinary skill people of the art
For member, without departing from the technical principles of the invention, several improvements and modifications can also be made, these improvements and modifications
Also it should be regarded as protection scope of the present invention.
Claims (1)
1. the preparation method of wear-resisting puncture-resistant halftone, which is characterized in that include the following steps:
1)Screen cloth is fixed on screen frame;
2)Using emulsion as raw material, coating, drying, exposure, imaging, baking operation are passed sequentially through, on the patch print face of screen cloth
One layer of first emulsion layer is covered, which is equipped with printing area of the pattern, is equipped in the printing area of the pattern several
Printing pattern;
3)Using emulsion as raw material, coating, drying, exposure, imaging, baking operation are passed sequentially through, in above-mentioned first emulsion layer
Surface covers one layer of second emulsion layer, and first emulsion layer is located between screen cloth patch print face and the second emulsion layer;Second emulsion
Layer also is provided with printing area of the pattern, if also being provided with dry printing pattern in printing area of the pattern;The print of second emulsion layer
Brush is corresponded with area of the pattern with the printing of the first emulsion layer with area of the pattern, and on the second emulsion layer respectively printing pattern with
Each printing is corresponded with pattern on first emulsion layer;
4)It is bonded one layer of endless rubber belt layer in the second emulsion layer surface by adhesive-tape application machine, second emulsion layer is located at the first breast
Between oxidant layer and endless rubber belt layer;The endless rubber belt layer is made of the adhesive tape for being fitted in the second emulsion layer surface;The adhesive tape
Printing is arranged with area of the pattern outer along the second emulsion layer, and surrounds the printing area of the pattern;The endless rubber belt layer
Thickness is 0.01~0.012mm;The width of the endless rubber belt layer is 10~15mm;The adhesive-tape application machine is equipped with CCD para-position system
System, the CCD para-position system control the bonding position of adhesive tape;The adhesive-tape application machine is equipped with displacement mechanism, and the displacement mechanism is by adhesive tape
It is moved to above-mentioned bonding position;Institute's displacement mechanism includes servo motor, precise guide rail and precise ball screw;The precision is led
Rail includes orthogonal X-axis guide rail and Y-axis guide rail;The adhesive-tape application machine is equipped with rubber roll, and the rubber roll is by adhesive tape pressure
Tightly in the second emulsion layer surface, adhesive tape is made to combine closely with the second emulsion layer;
The adhesive tape is macromolecule compound adhesive tape;The adhesive tape includes substrate layer and adhesive layer;
By weight, the substrate layer is composed of the following components:
9.8 parts of chlorinated polypropylenes,
14.2 parts of butadiene-styrene rubber,
7.9 parts of butyl rubbers,
6.5 parts of emulsion polymerized styrene butadiene rubbers,
3.2 parts of vinyl bis-stearamides,
1.1 parts of zirconium oxides,
1.3 parts of calcium sulfate,
0.7 part of silicon carbide,
1.4 parts of 4- methoxyl group -3,5- dimethyl -2- hydroxymethylpyridines,
2.1 parts of γ-mercaptopropyl trimethoxysilanes,
1.7 parts of vinyltrimethoxysilanes,
0.9 part of diethyl thiourea,
1.3 parts of phenyl silicone oils,
1.6 parts of N- phenyl-1-naphthylamines,
2.1 parts of polyvinylpyrrolidones.